Dissimilar Friction Stir Welding of AA2519 and AA5182.

ABSTRACT: In this study, the friction-stir welding (FSW) technique was successfully applied for joining of AA2519 to AA5181 alloy. Microstructure and mechanical properties of dissimilar FSW joints were investigated by optical microscopy, microhardness, and tensile testing. The deformation behaviour of the welded joints was elucidated via the digital image correlation technique. After welding, the ultimate tensile strength of joints was ~300 MPa and ductility was ~16%. The microhardness values observed at the stir zone were higher than those in the base material AA5182. The produced welds demonstrate nearly 100% (based on AA5182) joint efficiency.

SUBMITTER: Zuiko IS

PROVIDER: S-EPMC9786200 | biostudies-literature | 2022 Dec

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Dissimilar Friction Stir Welding of AA2519 and AA5182.

Zuiko Ivan S IS Malopheyev Sergey S Mironov Sergey S Kaibyshev Rustam R

Materials (Basel, Switzerland) 20221208 24

In this study, the friction-stir welding (FSW) technique was successfully applied for joining of AA2519 to AA5181 alloy. Microstructure and mechanical properties of dissimilar FSW joints were investigated by optical microscopy, microhardness, and tensile testing. The deformation behaviour of the welded joints was elucidated via the digital image correlation technique. After welding, the ultimate tensile strength of joints was ~300 MPa and ductility was ~16%. The microhardness values observed at ...[more]

PMID: 36556581

Similar Datasets

Tailoring of Dissimilar Friction Stir Lap Welding of Aluminum and Titanium

Project description:An approach was proposed to optimize dissimilar friction stir lap welding of aluminum and titanium alloys. The basic concept of the new technique included (i) the plunging of the welding tool solely into the aluminum part (i.e., no direct contact with the titanium side) and (ii) the welding at a relatively high-heat input condition. It was shown that sound welds could be readily produced using an ordinary cost-effective tool, with no tool abrasion and no dispersion of harmful titanium fragments within the aluminum side. Moreover, the intermetallic layer was found to be as narrow as ~0.1 µm, thus giving rise to excellent bond strength between aluminum and titanium. On the other hand, several important shortcomings were also revealed. First of all, the high-heat input condition provided significant microstructural changes in the aluminum part, thereby resulting in essential material softening. Furthermore, the new approach was not feasible in the case of highly alloyed aluminum alloys due to the relatively low rate of self-diffusion in these materials. An essential issue was also a comparatively narrow processing window.

| S-EPMC9738075 | biostudies-literature

Friction Stir Welding and Friction Spot Stir Welding Processes of Polymers-State of the Art.

Project description:In the last decade, the friction stir welding of polymers has been increasingly investigated by the means of more and more sophisticated approaches. Since the early studies, which were aimed at proving the feasibility of the process for polymers and identifying suitable processing windows, great improvements have been achieved. This owes to the increasing care of academic researchers and industrial demands. These improvements have their roots in the promising results from pioneer studies; however, they are also the fruits of the adoption of more comprehensive approaches and the multidisciplinary analyses of results. The introduction of instrumented machines has enabled the online measurement of processing loads and temperature, and critical understanding of the principal aspects affecting the material flow and welds quality. Such improvements are also clearly demonstrated by the increase of the strength of recent joints (up to 99% of joining efficiency) as compared to those reached in early researches (almost 47%). This article provides a comprehensive review of the recent progresses on the process fundamentals, quality assessment and the influence of process parameters on the mechanical behavior. In addition, emphasis is given to new developments and future perspectives.

| S-EPMC7288317 | biostudies-literature

Analysis and Comparison of Friction Stir Welding and Laser Assisted Friction Stir Welding of Aluminum Alloy.

Project description:Friction Stir Welding (FSW) is a solid-state joining process; i.e., no melting occurs. The welding process is promoted by the rotation and translation of an axis-symmetric non-consumable tool along the weld centerline. Thus, the FSW process is performed at much lower temperatures than conventional fusion welding, nevertheless it has some disadvantages. Laser Assisted Friction Stir Welding (LAFSW) is a combination in which the FSW is the dominant welding process and the laser pre-heats the weld. In this work FSW and LAFSW tests were conducted on 6 mm thick 5754H111 aluminum alloy plates in butt joint configuration. LAFSW is studied firstly to demonstrate the weldability of aluminum alloy using that technique. Secondly, process parameters, such as laser power and temperature gradient are investigated in order to evaluate changes in microstructure, micro-hardness, residual stress, and tensile properties. Once the possibility to achieve sound weld using LAFSW is demonstrated, it will be possible to explore the benefits for tool wear, higher welding speeds, and lower clamping force.

| S-EPMC5452731 | biostudies-other

Optimization of Friction Stir Welding Tool Advance Speed via Monte-Carlo Simulation of the Friction Stir Welding Process.

Project description:Recognition of the friction stir welding process is growing in the aeronautical and aero-space industries. To make the process more available to the structural fabrication industry (buildings and bridges), being able to model the process to determine the highest speed of advance possible that will not cause unwanted welding defects is desirable. A numerical solution to the transient two-dimensional heat diffusion equation for the friction stir welding process is presented. A non-linear heat generation term based on an arbitrary piecewise linear model of friction as a function of temperature is used. The solution is used to solve for the temperature distribution in the Al 6061-T6 work pieces. The finite difference solution of the non-linear problem is used to perform a Monte-Carlo simulation (MCS). A polynomial response surface (maximum welding temperature as a function of advancing and rotational speed) is constructed from the MCS results. The response surface is used to determine the optimum tool speed of advance and rotational speed. The exterior penalty method is used to find the highest speed of advance and the associated rotational speed of the tool for the FSW process considered. We show that good agreement with experimental optimization work is possible with this simplified model. Using our approach an optimal weld pitch of 0.52 mm/rev is obtained for 3.18 mm thick AA6061-T6 plate. Our method provides an estimate of the optimal welding parameters in less than 30 min of calculation time.

| S-EPMC5453204 | biostudies-other

Investigation of the Effects of Tool Positioning Factors on Peak Temperature in Dissimilar Friction Stir Welding of AA6061-T6 and AA7075-T6 Aluminum Alloys.

Project description:Among the emerging new welding techniques, friction stir welding (FSW) is used frequently for welding high-strength aluminum alloys that are difficult to weld by conventional fusion-welding techniques. This paper investigated the effects of tool-positioning factors on the maximum temperature generated in the dissimilar FSW joint of AA6061-T6 and AA7075-T6 aluminum alloys. Three factors of plunge depth, tool offset, and tilt angle were used as the input parameters. Numerical simulation of the FSW process was performed in ABAQUS software using the coupled Eulerian-Lagrangian (CEL) approach. Central composite design (CCD) based on response surface methodology (RSM) was used to analyze and design the experiments. Comparison of the numerical and experimental results showed that numerical simulations were in good agreement with the experimental ones. Based on the statistical model results, plunge depth, tilt angle, and tool offset were the most significant factors on maximum process temperature, respectively. It was found that increasing the plunge depth caused a sharp increase in the maximum process temperature due to increased contact surfaces and the frictional interaction between the tool and workpiece.

| S-EPMC8837093 | biostudies-literature

Grain Structure Evolution in 6013 Aluminum Alloy during High Heat-Input Friction-Stir Welding.

Project description:This work was undertaken to evaluate the influence of friction-stir welding (FSW) under a high-heat input condition on microstructural evolution. Given the extreme combination of deformation conditions associated with such an FSW regime (including the highest strain, temperature, and strain rate), it was expected to result in an unusual structural response. For this investigation, a commercial 6013 aluminum alloy was used as a program material, and FSW was conducted at a relatively high spindle rate of 1100 rpm and an extremely low feed rate of 13 mm/min; moreover, a Ti-6Al-4V backing plate was employed to reduce heat loss during welding. It was found that the high-heat-input FSW resulted in the formation of a pronounced fine-grained layer at the upper weld surface. This observation was attributed to the stirring action exerted by the shoulder of the FSW tool. Another important issue was the retardation of continuous recrystallization. This interesting phenomenon was explained in terms of a competition between recrystallization and recovery at high temperatures. Specifically, the activation of recovery should reduce dislocation density and thus retard the development of deformation-induced boundaries.

| S-EPMC10488852 | biostudies-literature

Friction stir welding of Haynes 282 Ni superalloy by using a novel hemispherical tool.

Project description:In the present investigation, friction stir welding (FSW) of a gamma prime (γ') strengthened Haynes 282 nickel-base superalloy by using a novel hemispherical tool is documented. A joint efficiency of ~ 96% was achieved in the as-welded condition, which further increased to ~ 100% after two-step post-weld aging heat treatment. An extremely fine (~ 2 μm) grained microstructure was observed in the FSWed region compared with the coarse (~ 48 μm) grain base metal region. The carbides (MC and M23C6) and γ' precipitates are identified as the important microstructural constituent phases observed in the welded region. The aging heat treatment resulted in the precipitation of the γ' strengthening phase and altered the morphology of the M23C6 carbide phase in the welded region from a continuous film to discrete particles at the grain boundaries. The preliminary results concerning tool life suggest that no significant tool wear occurs at least up to a welding distance of 200 mm. Therefore, the novel hemispherical tool design allows the successful FSW of high-temperature application materials without any significant tool wear or high heat generation.

| S-EPMC11560929 | biostudies-literature

Interfacial reaction during friction stir assisted scribe welding of immiscible Fe and Mg alloy system.

Project description:We report on interfacial characteristics and chemistry of bonded Mg-Fe interfaces welded using friction stir assisted scribe technique (FaST). Two pairs of dissimilar joints: (AZ31-DP590) and (Pure Mg-DP590) were studied to shed light on joining mechanisms responsible for bonding of "immiscible" pairs of Mg and Fe. We present first direct experimental evidence of presence of oxide layer, Al segregation by atom probe tomography and nano steel grains close to interface by transmission electron microscopy study.

| S-EPMC7810708 | biostudies-literature

Welding Characteristics Analysis and Application on Spacecraft of Friction Stir Welded 2A14-T6 Aluminum Alloy.

Project description:According to the actual size parameters, the finite element model (FEM) of friction stir welding (FSW) was established, and the FEM was updated by experiments. The FSW of the 2A14-T6 high-strength aluminum alloy was simulated under a reasonable welding process parameter range, and the welding process parameters with good simulation effect were determined. The test was carried out under the same parameters, and the axial force of the FSW tool and temperature of the workpiece measuring point were collected. The comparison between the simulated data and the experimental data is reasonable, indicating the correctness of the FEM. The microstructure analysis of the welded joint shows that the grain size in the upper part of the weld nugget was smaller than that in the middle and lower parts, and there are obvious boundaries of grain size in each region of the joint. The hardness of the joint in the upper layer is higher than that in the middle and lower layers, and the minimum Vickers hardness value of the joint appears near the interface between the thermo-mechanically affected zone and the heat-affected zone on both sides of the weld. Tensile testing shows that the strength coefficient of the joint reaches 82.5% under this process parameter, and the sample breaks at the intersection of the material flow during stretching. After analyzing the final mechanical properties of the joint, we found that a degree of aerospace application can be achieved. Under this parameter, the welding test was carried out on the top cover of the rocket fuel tank. Firstly, melon valve welding, which is relatively difficult in welding conditions, was carried out, and a high-quality joint with good surface and no defects was obtained.

| S-EPMC6384982 | biostudies-literature

EBSD Characterization of the Microstructure of 7A52 Aluminum Alloy Joints Welded by Friction Stir Welding.

Project description:The microstructure and texture of materials significantly influence the mechanical properties and fracture behavior; the effect of microstructure in different zones of friction stir-welded joints of 7A52 aluminum alloy on fracture behavior was investigated in this paper. The microstructural characteristics of sections of the welded joints were tested using the electron backscattered diffraction (EBSD) technique. The results indicate that the fracture is located at the advancing side of the thermomechanically affected zone (AS-TMAZ) and the stir zone (SZ) interface. The AS-TMAZ microstructure is vastly different from the microstructure and texture of other areas. The grain orientation is disordered, and the grain shape is seriously deformed under the action of stirring force. The grain size grows unevenly under the input of friction heat, resulting in a large amount of recrystallization, and there is a significant difference in the Taylor factor between adjacent grains and the AS-TMAZ-SZ interface. On the contrary, there are fine and uniform equiaxed grains in the nugget zone, the microstructure is uniform, and the Taylor factor is small at adjacent grains. Therefore, the uneven transition of microstructure and texture in the AS-TMAZ and the SZ provide conditions for crack initiation, which become the weak point of mechanical properties.

| S-EPMC8585471 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data