Synthesis and Characterization of Benzene- and Triazine-Based Azo-Bridged Porous Organic Polymers

ABSTRACT: Porous organic polymers incorporating nitrogen-rich functionalities have recently emerged as promising materials for efficient and highly selective CO2 capture and separation. Herein, we report synthesis and characterization of new two-dimensional (2D) benzene- and triazine-based azo-bridged porous organic polymers. Different synthetic approaches towards the porous azo-bridged polymers were tested, including reductive homocoupling of aromatic nitro monomers, oxidative homocoupling of aromatic amino monomers and heterocoupling of aromatic nitro monomers and a series of aromatic diamines of different lengths and rigidity. IR spectroscopy, 13C CP/MAS NMR spectroscopy, powder X-ray diffraction, elemental analysis, thermogravimetric analysis, nitrogen adsorption–desorption experiments and computational study were used to characterize structures and properties of the resulting polymers. The synthesized azo-bridged polymers are all amorphous solids of good thermal stability, exhibiting various surface areas (up to 351 m2 g−1). The obtained results indicated that the synthetic methods and building units have a pronounced effect on the porosity of the final materials. Reductive and oxidative homocoupling of aromatic nitro and amino building units, respectively, lead to 2D azo-bridged polymers of substantially higher porosity when compared to those produced by heterocoupling reactions. Periodic DFT calculations and Grand-canonical Monte Carlo (GCMC) simulations suggested that, within the used approximations, linear linkers of different lengths do not significantly affect CO2 adsorption properties of model azo-bridged polymers.

SUBMITTER:

PROVIDER: S-EPMC9824540 | biostudies-literature | 2023 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Insight into the Synthesis and Characterization of Organophosphorus-Based Bridged Triazine Compounds.

Project description:In this article, we report the synthesis of 2,4,6-substituted s-triazine-based organophosphorus compounds via a two-step process, which enables their production in high yields, and with a high purity as solids. In the first step, a Michaelis-Arbuzov rearrangement of cyanuric chloride with triethyl phosphite afforded 2,4,6-trisdiethoxyphosphinyl-1,3,5-triazine (HEPT). Subsequently, the nucleophilic substitution reaction on the triazine carbon was achieved, owing to the electron-withdrawing ability of the phosphonate groups. This characteristic of HEPT facilitated its derivatization with bi-functional amines, producing novel P-C containing bridged triazine organophosphorus compounds. The molecular structures of all of the compounds were confirmed by NMR spectroscopy, CHN elemental analysis, and single crystal X-ray analysis. In the thermogravimetric analysis in an N2 environment, >33% char formation was observed for the bridged compounds. The chemical composition analysis of the char obtained under the oxidative thermal decomposition of the bridged compounds confirmed the presence of phosphorus- and nitrogen-enriched species, which indicate their function in the condensed phase. Comparatively, the detection of HPO and H-C≡P in the gas phase during the pyrolysis of the bridged compounds can act as a source for PO•, which is known for its gas phase flame inhibition reactions. The synergy of significant char formation and the generation of intermediates leading to PO• during pyrolysis makes these molecules promising flame-retardant additives.

| S-EPMC6681112 | biostudies-literature

Triazine-based porous organic polymers for reversible capture of iodine and utilization in antibacterial application.

Project description:The capture and safe storage of radioactive iodine (129I or 131I) are of a compelling significance in the generation of nuclear energy and waste storage. Because of their physiochemical properties, Porous Organic Polymers (POPs) are considered to be one of the most sought classes of materials for iodine capture and storage. Herein, we report on the preparation and characterization of two triazine-based, nitrogen-rich, porous organic polymers, NRPOP-1 (SABET = 519 m2 g-1) and NRPOP-2 (SABET = 456 m2 g-1), by reacting 1,3,5-triazine-2,4,6-triamine or 1,4-bis-(2,4-diamino-1,3,5-triazine)-benzene with thieno[2,3-b]thiophene-2,5-dicarboxaldehyde, respectively, and their use in the capture of volatile iodine. NRPOP-1 and NRPOP-2 showed a high adsorption capacity of iodine vapor with an uptake of up to 317 wt % at 80 °C and 1 bar and adequate recyclability. The NRPOPs were also capable of removing up to 87% of iodine from 300 mg L-1 iodine-cyclohexane solution. Furthermore, the iodine-loaded polymers, I2@NRPOP-1 and I2@NRPOP-2, displayed good antibacterial activity against Micrococcus luteus (ML), Escherichia coli (EC), and Pseudomonas aeruginosa (PSA). The synergic functionality of these novel polymers makes them promising materials to the environment and public health.

| S-EPMC8850422 | biostudies-literature

Azo-Linked Porous Organic Polymers for Selective Carbon Dioxide Capture and Metal Ion Removal.

Project description:The facile and environmentally friendly synthesis of porous organic polymers with designed polar functionalities decorating the interior frameworks as an excellent adsorbent for selective carbon dioxide capture and metal ion removal is a target worth pursuing for environmental applications. In this regard, two azo-linked porous organic polymers denoted man-Azo-P1 and man-Azo-P2 were synthesized in water by the azo-linking of 4,4'-diaminobiphenyl (benzidine) and 4,4'-methylenedianiline, respectively, with 1,3,5-trihydroxybenzene. The resulting polymers showed good BET surface areas of 290 and 78 m2 g-1 for man-Azo-P1 and man-Azo-P2, respectively. Due to the enriched core functionality of the azo (-N=N-) and hydroxyl groups along with the porous frameworks, man-Azo-P1 exhibited a good CO2 uptake capacity of 32 cm3 g-1 at 273 K and 1 bar, in addition to the remarkable removal of lead (Pd), chromium (Cr), arsenic (As), nickel (Ni), copper (Cu), and mercury (Hg) ions. This performance of the synthesized man-Azo-P1 and man-Azo-P2 in the dual application of CO2 capture and heavy metal ion removal highlights the unique properties of azo-linked POPs as excellent and stable sorbent materials for the current challenging environmental applications.

| S-EPMC9088788 | biostudies-literature

Synthesis, Characterization, and Environmental Applications of Novel Per-Fluorinated Organic Polymers with Azo- and Azomethine-Based Linkers via Nucleophilic Aromatic Substitution.

Project description:This study reports on the synthesis and characterization of novel perfluorinated organic polymers with azo- and azomethine-based linkers using nucleophilic aromatic substitution. The polymers were synthesized via the incorporation of decafluorobiphenyl and hexafluorobenzene linkers with diphenols in the basic medium. The variation in the linkers allowed the synthesis of polymers with different fluorine and nitrogen contents. The rich fluorine polymers were slightly soluble in THF and have shown molecular weights ranging from 4886 to 11,948 g/mol. All polymers exhibit thermal stability in the range of 350-500 °C, which can be attributed to their structural geometry, elemental contents, branching, and cross-linking. For instance, the cross-linked polymers with high nitrogen content, DAB-Z-1h and DAB-Z-1O, are more stable than azomethine-based polymers. The cross-linking was characterized by porosity measurements. The azo-based polymer exhibited the highest surface area of 770 m2/g with a pore volume of 0.35 cm3/g, while the open-chain azomethine-based polymer revealed the lowest surface area of 285 m2/g with a pore volume of 0.0872 cm3/g. Porous structures with varied hydrophobicities were investigated as adsorbents for separating water-benzene and water-phenol mixtures and selectively binding methane/carbon dioxide gases from the air. The most hydrophobic polymers containing the decafluorbiphenyl linker were suitable for benzene separation, while the best methane uptake values were 6.14 and 3.46 mg/g for DAB-Z-1O and DAB-A-1O, respectively. On the other hand, DAB-Z-1h, with the highest surface area and being rich in nitrogen sites, has recorded the highest CO2 uptake at 298 K (17.25 mg/g).

| S-EPMC10610692 | biostudies-literature

Ionic Porous Organic Polymers Based on Functionalized Tetraarylborates.

Project description:Lithium tetrakis(4-boronatoaryl)borates were subjected to polycondensation reactions with selected polyhydroxyl monomers such as 2,3,6,7,10,11-hexahydroxytriphenylene (HHTP) and 2,3,6,7-tetrahydroxy-9,10-dimethylanthracene (THDMA). Obtained boronate-type ionic porous polymers TAB1-4 were characterized by PXRD, 6Li and 11B magic-angle spinning nuclear magnetic resonance (MAS NMR), FT-IR, SEM, and TGA. They exhibit relatively good sorption of H2 (up to 75 cm3/g STP), whereas N2 uptake at 77 K for lower pressure range is relatively poor (up to 50 cm3/g STP below P/P0 = 0.8). In addition, the effect of elongation of aryl arms in the tetraarylborate core on the materials' properties was studied. Thus, it was found that replacement of the 4-boronatophenyl with 4-boronatobiphenylyl group has a negative impact on the sorption characteristics.

| S-EPMC6630441 | biostudies-literature

Carbonized Aminal-Linked Porous Organic Polymers Containing Pyrene and Triazine Units for Gas Uptake and Energy Storage.

Project description:Porous organic polymers (POPs) have plenteous exciting features due to their attractive combination of microporosity with π-conjugation. Nevertheless, electrodes based on their pristine forms suffer from severe poverty of electrical conductivity, precluding their employment within electrochemical appliances. The electrical conductivity of POPs may be significantly improved and their porosity properties could be further customized by direct carbonization. In this study, we successfully prepared a microporous carbon material (Py-PDT POP-600) by the carbonization of Py-PDT POP, which was designed using a condensation reaction between 6,6'-(1,4-phenylene)bis(1,3,5-triazine-2,4-diamine) (PDA-4NH2) and 4,4',4'',4'''-(pyrene-1,3,6,8-tetrayl)tetrabenzaldehyde (Py-Ph-4CHO) in the presence of dimethyl sulfoxide (DMSO) as a solvent. The obtained Py-PDT POP-600 with a high nitrogen content had a high surface area (up to 314 m2 g-1), high pore volume, and good thermal stability based on N2 adsorption/desorption data and a thermogravimetric analysis (TGA). Owing to the good surface area, the as-prepared Py-PDT POP-600 showed excellent performance in CO2 uptake (2.7 mmol g-1 at 298 K) and a high specific capacitance of 550 F g-1 at 0.5 A g-1 compared with the pristine Py-PDT POP (0.24 mmol g-1 and 28 F g-1).

| S-EPMC10146094 | biostudies-literature

Microwave-assisted reductive homocoupling of aromatic nitro monomers: synthesis of azo-linked porous organic polymers for CO<sub>2</sub> capture.

Project description:An optimized protocol for the rapid synthesis of azo-linked porous organic polymers (POPs) containing trigonal triphenylpyridine (AZO-P-M), triphenyltriazine (AZO-T-M), and tetragonal tetraphenylethylene (AZO-E-M) central units by microwave-assisted NaBH4-mediated reductive homocoupling of the corresponding aromatic nitro monomers is presented. The structural and functional features of the azo-linked polymers prepared under microwave heating were directly compared to their counterparts obtained by conventional synthesis. Similar to azo-linked polymers synthesized by conventional reductive homocoupling of nitro monomers with NaBH4, the polymers prepared under microwave irradiation are amorphous solids of good thermal stability showing moderate (e.g., AZO-E-M with BET surface area of 302.1 m2 g-1) to modest (e.g., AZO-P-M with BET surface area of 22.9 m2 g-1) porosities. Although the microwave-assisted procedure for the synthesis of azo-linked polymers described in this work did not result in systems with improved porosities, their efficiency for CO2 adsorption (up to 29 mg g-1 at 306 K) is comparable to that of POPs synthesized by conventional heating. Therefore, the herein reported protocol could be used for the fast and efficient synthesis of new azo-linked POPs with potential for CO2 capture.

| S-EPMC11886775 | biostudies-literature

Template-free synthesis of porous carbon from triazine based polymers and their use in iodine adsorption and CO<sub>2</sub> capture.

Project description:A series of novel triazine-containing pore-tunable carbon materials (NT-POP@800-1-6), which was synthesized via pyrolysis of porous organic polymers (POPs) without any templates. NT-POP@800-1-6 possess moderate BET surface areas of 475-736 m2 g-1, have permanent porosity and plenty of nitrogen units in the skeletons as effective sorption sites, and display relatively rapid guest uptake of 56-192 wt% in iodine vapour in the first 4 h. In addition, all the samples exhibit the outstanding CO2 adsorption capacity of 2.83-3.96 mmol g-1 at 273 K and 1.05 bar. Furthermore, NT-POP@800-1-6 show good selectivity ratios of 21.2-36.9 and 3.3-7.5 for CO2/N2 or CH4/N2, respectively. We believe that our new building block design provides a general strategy for the construction of triazine-containing carbon materials from various extended building blocks, thereby greatly expanding the range of applicable molecules.

| S-EPMC5789819 | biostudies-literature

Porous inorganic-organic shape memory polymers.

Project description:Thermoresponsive shape memory polymers (SMPs) are a type of stimuli-sensitive materials that switch from a temporary shape back to their permanent shape upon exposure to heat. While the majority of SMPs have been fabricated in the solid form, porous SMP foams exhibit distinct properties and are better suited for certain applications, including some in the biomedical field. Like solid SMPs, SMP foams have been restricted to a limited group of organic polymer systems. In this study, we prepared inorganic-organic SMP foams based on the photochemical cure of a macromer comprised of inorganic polydimethylsiloxane (PDMS) segments and organic poly(?-caprolactone) (PCL) segments, diacrylated PCL(40)-block-PDMS(37)-block-PCL(40). To achieve tunable pore size with high interconnectivity, the SMP foams were prepared via a refined solvent-casting/particulate-leaching (SCPL) method. By varying design parameters such as degree of salt fusion, macromer concentration in the solvent and salt particle size, the SMP foams with excellent shape memory behavior and tunable pore size, pore morphology, and modulus were obtained.

| S-EPMC3433079 | biostudies-literature

Vinylene-bridged donor-acceptor type porous organic polymers for enhanced photocatalysis of amine oxidative coupling reactions under visible light.

Project description:Porous organic polymers (POPs), owing to their abundant porosity, high stability and well-tunable properties, are promising candidates as heterogeneous photocatalysts for organic transformations. Here we report two vinylene-bridged donor-acceptor (D-A) structural POPs (TpTc-POP and TbTc-POP) that are facilely constructed by the electron-rich triarylamine and electron-deficient tricyanomesitylene as key building blocks by the organic base catalyzed Knoevenagel condensation. Both TpTc-POP and TbTc-POP possess hierarchical meso- and micro-pores with a high surface area. Furthermore, the unsubstituted vinylene linkages of D-A moieties in their polymer backbones extend their π-conjugation and render their broad absorption range in the visible-light region. Thus, these DA-POPs exhibited highly effective photocatalytic activities for aerobic oxidative coupling of amines to imines under visible light irradiation. This study shows the great potential of conjugated POPs with a D-A structural feature in designing highly efficient and active heterogeneous photocatalytic systems.

| S-EPMC9042297 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data