A Temperature-Dependent Viscoplasticity Model for the Hot Work Steel X38CrMoV5-3, Including Thermal and Cyclic Softening under Thermomechanical Fatigue Loading
Ontology highlight
ABSTRACT:
SUBMITTER: Schlayer M
PROVIDER: S-EPMC9918193 | biostudies-literature | 2023 Jan
REPOSITORIES: biostudies-literature
Similar Datasets
Project description:In this article, the data obtained from the uniaxial fully-reversed fatigue experiments conducted on polyether ether ketone (PEEK), a semi-crystalline thermoplastic, are presented. The tests were performed in either strain-controlled or load-controlled mode under various levels of loading. The data are categorized into four subsets according to the type of tests, including (1) strain-controlled fatigue tests with adjusted frequency to obtain the nominal temperature rise of the specimen surface, (2) strain-controlled fatigue tests with various frequencies, (3) load-controlled fatigue tests without step loadings, and (4) load-controlled fatigue tests with step loadings. Accompanied data for each test include the fatigue life, the maximum (peak) and minimum (valley) stress-strain responses for each cycle, and the hysteresis stress-strain responses for each collected cycle in a logarithmic increment. A brief description of the experimental method is also given.
| S-EPMC4752734 | biostudies-literature
Project description:This article presents the strain-based experimental data for Ti-6Al-4V ELI under non-constant amplitude cyclic loading. Uniaxial strain-controlled fatigue experiments were conducted under three different loading conditions, including two-level block loading (i.e. high-low and low-high), periodic overload, and variable amplitude loading. Tests were performed under fully-reversed, and mean strain/stress conditions. For each test conducted, two sets of data were collected; the cyclic stress-strain response (i.e. hysteresis loops) in log10 increments, and the peak and valley values of stress and strain for each cycle. Residual fatigue lives are reported for tests with two-level block loading, while for periodic overload and variable amplitude experiments, fatigue lives are reported in terms of number of blocks to failure.
| S-EPMC5458061 | biostudies-literature
Project description:Some tendons, such as the human Achilles and equine superficial digital flexor tendon (SDFT), act as energy stores, stretching and recoiling to increase efficiency during locomotion. Our previous observations of rotation in response to applied strain in SDFT fascicles suggest a helical structure, which may provide energy-storing tendons with a greater ability to extend and recoil efficiently. Despite this specialization, energy-storing tendons are prone to age-related tendinopathy. The aim of this study was to assess the effect of cyclic fatigue loading (FL) on the microstructural strain response of SDFT fascicles from young and old horses. The data demonstrate two independent age-related mechanisms of fatigue failure; in young horses, FL caused low levels of matrix damage and decreased rotation. This suggests that loading causes alterations to the helix substructure, which may reduce their ability to recoil and recover. By contrast, fascicles from old horses, in which the helix is already compromised, showed greater evidence of matrix damage and suffer increased fibre sliding after FL, which may partially explain the age-related increase in tendinopathy. Elucidation of helix structure and the precise alterations occurring owing to both ageing and FL will help to develop appropriate preventative and repair strategies for tendinopathy.
| S-EPMC3899876 | biostudies-literature
Project description:We propose a mechanisms-based viscoplasticity approach for metals and alloys. First, we derive a stochastic model for thermally-activated motion of dislocations and, then, introduce power-law flow rules. The overall plastic deformation includes local plastic slip events taken with an appropriate weight assigned to each angle of the plane misorientation from the direction of maximum shear stress. As deformation progresses, the material experiences successive reorganizations of the slip systems. The microstructural evolution causes that a portion of energy expended on plastic deformation is dissipated and the rest is stored in the defect structures. We show that the reorganizations are stable in a homogeneously deformed material. The concept is tested for steel 304L, where we reproduce experimentally obtained stress-strain responses, we construct the Frost-Ashby deformation map and predict the rate of the energy storage. The storage is assessed in terms of synchronized measurements of temperature and displacement distributions on the specimen surface during tensile loading.
| S-EPMC4812260 | biostudies-other
Project description:The interior defect-induced fracture of surface-hardened metallic materials in the long life region has become a key issue on engineering design. In the present study, the axial loading test with fully reversed condition was performed to examine the fatigue property of a surface-carburized low alloy gear steel in the long life region. Results show that this steel represents the duplex S-N (stress-number of cycles) characteristics without conventional fatigue limit related to 10⁷ cycles. Fatigue cracks are all originated from the interior inclusions in the matrix region due to the inhabitation effect of carburized layer. The inclusion induced fracture with fisheye occurs in the short life region below 5 × 10⁵ cycles, whereas the inclusion induced fracture with fine granular area (FGA) and fisheye occurs in the long life region beyond 10⁶ cycles. The stress intensity factor range at the front of FGA can be regarded as the threshold value controlling stable growth of interior long crack. The evaluated maximum inclusion size in the effective damage volume of specimen is about 27.29 μm. Considering the size relationships between fisheye and FGA, and inclusion, the developed life prediction method involving crack growth can be acceptable on the basis of the good agreement between the predicted and experimental results.
| S-EPMC5456646 | biostudies-other
Project description:Mechanical testing based on ISO 14801 standard is generally used to evaluate the performance of the dental implant system according to material and design changes. However, the test method is difficult to reflect on the clinical environment because the ISO 14801 standard does not take into account the various loads from different directions during chewing motion. In addition, the fracture pattern of the implant system can occur both in the horizontal and the vertical directions. Therefore, the purpose of this study was to compare fatigue characteristics and fracture patterns between single directional loading conditions based on the ISO 14801 standard and multi-directional loading condition. Firstly, the static test was performed on five specimens to derive the fatigue load, and the fatigue load was chosen as 40% of the maximum load measured in the static test. Subsequently, the fatigue test was performed considering the single axial/occlusal (AO), AO with facial/lingual (AOFL) and AO with mesial/distal (AOMD) directions, and five specimens were used for each fatigue loading modes. In order to analyze the fatigue characteristics, the fatigue cycle at the time of specimen fracture and displacement change of the specimen every 500 cycles were measured. Field emission scanning electron microscopy (FE-SEM) was used to analyze the fracture patterns and the fracture surface. Compared to the AO group, the fatigue cycle of the AOFL and AOMD groups showed lower about five times, while the displacement gradually increased with every 500 cycles. From FE-SEM results, there were no different surface morphology characteristics among three groups. However, the AOMD group showed a vertical slip band. Therefore, our results suggest that the multi-directional loading mode under the worst-case environment can reproduce the vertical fracture pattern in the clinical situation and may be essential to reflect on the dental implant design including connection types and surface treatments.
| S-EPMC7177857 | biostudies-literature
Project description:Soft materials fail by crack propagation under external loads. While fracture toughness of a soft material can be enhanced by orders of magnitude, its fatigue threshold remains insusceptible. In this work, we demonstrate a crack tip softening (CTS) concept to simultaneously improve the toughness and threshold of a single polymeric network. Polyacrylamide hydrogels have been selected as a model material. The polymer network is cured by two kinds of crosslinkers: a normal crosslinker and a light-degradable crosslinker. We characterize the pristine sample and light-treated sample by shear modulus, fracture toughness, fatigue threshold, and fractocohesive length. Notably, we apply light at the crack tip of a sample so that the light-sensitive crosslinkers degrade, resulting in a CTS sample with a softer and elastic crack tip. The pristine sample has a fracture toughness of 748.3 ± 15.19 J/m2 and a fatigue threshold of 9.3 J/m2. By comparison, the CTS sample has a fracture toughness of 2,774.6 ± 127.14 J/m2 and a fatigue threshold of 33.8 J/m2. Both fracture toughness and fatigue threshold have been enhanced by about four times. We attribute this simultaneous enhancement to stress de-concentration and elastic shielding at the crack tip. Different from the "fiber/matrix composite" concept and the "crystallization at the crack tip" concept, the CTS concept in the present work provides another option to simultaneously enhance the toughness and threshold, which improves the reliability of soft devices during applications.
| S-EPMC9963307 | biostudies-literature
Project description:Given the development of precast structures for low-rise residential buildings, this study explores a new structure-namely, an integrated precast structure of lightweight recycled concrete wall with single-row reinforcement-under a lightweight steel frame filled with recycled concrete (integrated precast structure for short). The lightweight steel frame and lightweight wall cooperate to bear the forces. The applied concealed bracing, either a rebar bracing or a steel plate bracing, increases the shear resistance of the wall. The lightweight steel frame is designed to bear the vertical loading, whereas the seismic load in the horizontal direction is jointly borne by the frame and wall. This study presents the results of low reversed cyclic loading tests on nine specimens of integrated precast structures. An analysis is then carried out to investigate the mechanical properties of the specimens; based on these results, a formula for the force-bearing performance of the inclined section is developed. The results show satisfactory performance as an integrated piece; the proposed structure has two seismic lines of defence, with the lightweight wall restraint by the side frame being the first line and the steel frame being the second line. Because the failure of the wall can be categorized as shear failure, the restraint of the lightweight steel frame significantly reduces the potential damage of the wall. As the beams and columns of the steel frame tend to bend against failure, the wall filling helps resist sliding. Therefore, the reinforced joints of the connecting beams and columns show no visible signs of damage, indicating that the connection between the beams and columns is reliable. The narrow spacing of rebars and the setting of concealed bracing contribute to the increase in ductility and energy efficiency of the integrated structure and the evident reduction in the failure process. Furthermore, the recycled concrete increases the seismic resistance of the structure.
| S-EPMC6227948 | biostudies-literature
Project description:The hot deformation behavior and dynamic softening mechanism of 7B50 aluminum alloy were studied via isothermal compression experiments in the range of 320-460 °C/0.001-1.0 s-1. According to the flow curves obtained from the experiments, the flow behavior of this alloy was analyzed, and the Zener-Hollomon (Z) parameter equation was established. The hot processing maps of this alloy were developed based on the dynamic material model, and the optimal hot working region was determined to be 410-460 °C/0.01-0.001 s-1. The electron backscattered diffraction (EBSD) microstructure analysis of the deformed sample shows that the dynamic softening mechanism and microstructure evolution strongly depend on the Z parameter. Meanwhile, a correlation between the dynamic softening mechanism and the lnZ value was established. Dynamic recovery (DRV) was the only softening mechanism during isothermal compression with lnZ ≥ 20. Discontinuous dynamic recrystallization (DDRX) becomes the dominant dynamic recrystallization (DRX) mechanism under deformation conditions of 15 < lnZ < 20. Meanwhile, the size and percentage of DDRXed grains increased with decreasing lnZ values. The geometric dynamic recrystallization (GDRX) mechanism and continuous dynamic recrystallization (CDRX) mechanism coexist under deformation conditions with lnZ ≤ 15.
| S-EPMC10456416 | biostudies-literature
Project description:In this paper, the fatigue damage and lifetime of 2D SiC/SiC ceramic-matrix composites (CMCs) under cyclic fatigue loading at 750, 1000, 1100, 1200 and 1300 °C in air and in steam atmosphere have been investigated. The damage evolution versus applied cycles of 2D SiC/SiC composites were analyzed using fatigue hysteresis dissipated energy, fatigue hysteresis modulus, fatigue peak strain and interface shear stress. The presence of steam accelerated the damage development inside of SiC/SiC composites, which increased the increasing rate of the fatigue hysteresis dissipated energy and the fatigue peak strain, and the decreasing rate of the fatigue hysteresis modulus and the interface shear stress. The fatigue life stress-cycle (S-N) curves and fatigue limit stresses of 2D SiC/SiC composites at different temperatures in air and in steam condition have been predicted. The fatigue limit stresses approach 67%, 28%, 39% 17% and 28% tensile strength at 750, 1000, 1100, 1200 and 1300 °C in air, and 49%, 10%, 9% and 19% tensile strength at 750, 1000, 1200 and 1300 °C in steam conditions, respectively.
| S-EPMC5506978 | biostudies-other