Surface profile analysis of laminated transfemoral prosthetic socket fabricated with different ratios of epoxy resin and acrylic resin.

ABSTRACT: Acrylic and epoxy are common types of resin used in fabricating sockets. Different types of resin will affect the internal surface of a laminated socket. This paper is to determine the best combination of ratio for epoxy and acrylic resin for a laminated prosthesis socket and to evaluate the surface profile analysis of different combinations of laminated prosthetic sockets for surface roughness. Transfemoral sockets were created using various resin-to-hardener ratios of 2:1, 3:1, 3:2, 2:3, and 1:3 for epoxy resin and 100:1, 100:2, 100:3, 100:4, and 100:5 for acrylic resin. Eight layers of stockinette consisting of four elastic stockinette and four Perlon stockinette were used. A sample with a size of 4 cm × 6 cm was cut out from the socket on the lateral side below the Greater Trochanter area. The Mitutoyo Sj-210 Surface Tester stylus was run through the sample and gave the Average Surface Roughness value (Ra), Root Mean Square Roughness value (Rq), and Ten-Point Mean Roughness value (Rz). Epoxy resin shows a smoother surface compared to acrylic resin with Ra values of is 0.766 µm, 0.9716 µm, 0.9847 µm and 1.5461 µm with 3:2, 3:1, 2:1 and 2:3 ratio respectively. However, for epoxy resin with ratio 1:3, the resin does not cure with the hardener. As for acrylic resin the Ra values are 1.0086 µm, 2.362 µm, 3.372 µm, 4.762 µm and 6.074 µm with 100: 1, 100:2, 100:5, 100:4 and 100:3 ratios, respectively. Epoxy resin is a better choice in fabricating a laminated socket considering the surface produced is smoother.

SUBMITTER: Zainuddin NAMN

PROVIDER: S-EPMC9932096 | biostudies-literature | 2023 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Surface profile analysis of laminated transfemoral prosthetic socket fabricated with different ratios of epoxy resin and acrylic resin.

Zainuddin Nik Abdul Muiz Nik NAMN Razak Nasrul Anuar Abd NAA Karim Mohd Sayuti Ab MSA Osman Noor Azuan Abu NAA

Scientific reports 20230215 1

Acrylic and epoxy are common types of resin used in fabricating sockets. Different types of resin will affect the internal surface of a laminated socket. This paper is to determine the best combination of ratio for epoxy and acrylic resin for a laminated prosthesis socket and to evaluate the surface profile analysis of different combinations of laminated prosthetic sockets for surface roughness. Transfemoral sockets were created using various resin-to-hardener ratios of 2:1, 3:1, 3:2, 2:3, and 1 ...[more]

PMID: 36792914

Similar Datasets

Project description:BackgroundAmong the different factors affecting socket comfort, the pressure applied on residual limb tissues is a crucial parameter for the success or failure of any prosthetic device. However, only a few incomplete data are available on people with transfemoral amputation, in this regard. This work aims at filling this gap in the literature.MethodsTen people with transfemoral amputation wearing 3 different socket designs were recruited in this study: 2 ischial containment sockets featured by proximal trim lines that contain the ischial tuberosity and ramus and greater trochanter, 2 subischial sockets with proximal trim lines under the ischium level, and 6 quadrilateral sockets with proximal trim lines that contain the greater trochanter and create a horizontal seat for the ischial tuberosity. The pressure values at the anterior, lateral, posterior, and medial areas of the socket interface were recorded during 5 locomotion tasks (ie, horizontal, ascent, and descent walking, upstairs and downstairs) by using an F-Socket System (Tekscan Inc., Boston, MA). Gait segmentation was performed by exploiting plantar pressure, which was acquired by an additional sensor under the foot. Mean and standard deviation of minimum and maximum values were calculated for each interface area, locomotion task, and socket design. The mean pressure patterns during different locomotion tasks were reported, as well.ResultsConsidering all subjects irrespective of socket design, the mean pressure range resulted 45.3 (posterior)-106.7 (posterior) kPa in horizontal walking; 48.3 (posterior)-113.8 (posterior) kPa in ascent walking; 50.8 (posterior)-105.7 (posterior) kPa in descent walking; 47.9 (posterior)-102.9 (lateral) kPa during upstairs; and 41.8 (posterior)-84.5 (anterior) kPa during downstairs. Qualitative differences in socket designs have been found.ConclusionsThese data allow for a comprehensive analysis of pressures acting at the tissue-socket interface in people with transfemoral amputation, thus offering essential information for the design of novel solutions or to improve existing ones, in this field.

Dataset Information

Surface profile analysis of laminated transfemoral prosthetic socket fabricated with different ratios of epoxy resin and acrylic resin.

Publications

Surface profile analysis of laminated transfemoral prosthetic socket fabricated with different ratios of epoxy resin and acrylic resin.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets