Effects of Difluoro(oxalato)borate-Based Ionic Liquid as Electrolyte Additive for Li-Ion Batteries.

ABSTRACT: In this work, the use of N-methyl-N-propylpiperidinium difluoro(oxalato)borate Pip₁₃DFOB ionic liquid (IL), originally synthesized in our laboratory, as an additive for liquid electrolytes in lithium-ion batteries (LIBs), is proposed. The synthesized IL exhibits glass and melting transitions at -70.9 °C and 17.1 °C, respectively, and a thermal decomposition temperature over 230 °C. A mixture based on 1.0 M LiPF₆ in 1:1 v/v ethylene carbonate (EC): dimethyl carbonate (DMC) electrolyte solution (so called LP30) and the IL was prepared and tested in lithium metal cells versus two different commercially available carbonaceous electrodes, i.e., graphite (KS6) and graphene (GnP), and versus a high voltage LiNi_0.5Mn_1.5O₄ (LNMO) cathode. A noticeable improvement was observed for Li|LNMO cells with an IL-added electrolyte, which exhibited a high specific capacity above 120 mAh g^-1 with a Coulombic efficiency above 93% throughout 200 cycles, while the efficiency fell below 80% after 80 cycles with the absence of IL. The results confirm that the IL is promising additive for the electrolyte, especially for a longer cycle life of high-voltage cells.

SUBMITTER: Di Donato G

PROVIDER: S-EPMC9967885 | biostudies-literature | 2023 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Effects of Difluoro(oxalato)borate-Based Ionic Liquid as Electrolyte Additive for Li-Ion Batteries.

Di Donato Graziano G Maresca Giovanna G Palluzzi Matteo M Tsurumaki Akiko A Navarra Maria Assunta MA

Materials (Basel, Switzerland) 20230208 4

In this work, the use of N-methyl-N-propylpiperidinium difluoro(oxalato)borate Pip13DFOB ionic liquid (IL), originally synthesized in our laboratory, as an additive for liquid electrolytes in lithium-ion batteries (LIBs), is proposed. The synthesized IL exhibits glass and melting transitions at -70.9 °C and 17.1 °C, respectively, and a thermal decomposition temperature over 230 °C. A mixture based on 1.0 M LiPF6 in 1:1 v/v ethylene carbonate (EC) ...[more]

PMID: 36837039

Similar Datasets

Project description:Fluorinated electrolytes based on fluoroethylene carbonate (FEC) have been considered as promising alternative electrolytes for high-voltage and high-energy capacity lithium-ion batteries (LIBs). However, the compatibility of the fluorinated electrolytes with graphite negative electrodes is unclear. In this paper, we have systematically investigated, for the first time, the stability of fluorinated electrolytes with graphite negative electrodes, and the result shows that unlike the ethylene carbonate (EC)-based electrolyte, the FEC-based electrolyte (EC was totally replaced by FEC) is incapable of forming a protective and effective solid electrolyte interphase (SEI) that protects the electrolyte from runaway reduction on the graphite surface. The reason is that the lowest unoccupied molecular orbital energy levels are also lowered by the introduction of fluorine into the solvent, and the FEC solvent has poorer resistance against reduction, leading to instability on the graphite negative electrode. To tackle this problem, two lithium salts of lithium bis(oxalato)borate and lithium difluoro(oxalato)borate (LiDFOB) have been investigated as negative-electrode film-forming additives. Incorporation of only 0.5 wt % LiDFOB to a FEC-based electrolyte [1.0 M LiPF6 in 3:7 (FEC-ethyl methyl carbonate)] results in excellent cycling performance of the graphite negative electrode. This improved property originates from the generation of a thinner and better quality SEI film with little LiF by the sacrificial reduction of the LiDFOB additive on the graphite negative electrode surface. On the other hand, this additive can stabilize the electrolyte by scavenging HF. Meanwhile, the incorporated LiDFOB additive has positive influence on the interphase layer on the positive electrode surface and significantly decreases the amount of HF formation, finally leading to improved cycling stability and rate capability of LiNi0.5Mn1.5O4 electrodes at a high cutoff voltage of 5 V. The data demonstrate that the LiDFOB additive not only exhibits a superior compatibility with graphite but also improves the electrochemical properties of high-voltage spinel LiNi0.5Mn1.5O4 positive electrodes considerably, confirming its potential as a prospective, multifunctional additive for 5 V fluorinated electrolytes in high-energy capacity lithium-ion batteries (LIBs).

Project description:With the development of mobile electronic devices, there are more and more requirements for high-energy storage equipment. Traditional lithium-ion batteries, like lithium-iron phosphate batteries, are limited by their theoretical specific capacities and might not meet the requirements for high energy density in the future. Lithium-sulfur batteries (LSBs) might be ideal next-generation energy storage devices because they have nearly 10 times the theoretical specific capacities of lithium-ion batteries. However, the severe capacity decay of LSBs limits their application, especially at high currents. In this study, an ionic liquid (IL) electrolyte additive, TDA+TFSI, was reported. When 5% of the TDA+TFSI additive was added to a traditional ether-based organic electrolyte, the cycling performance of the LSBs was significantly improved compared with that of the LSBs with the pure traditional organic electrolyte. At a rate of 0.5 C, the discharge specific capacity in the first cycle of the LSBs with the 5% TDA+TFSI electrolyte additive was 1167 mAh g-1; the residual specific capacities after 100 cycles and 300 cycles were 579 mAh g-1 and 523 mAh g-1, respectively; and the average capacity decay rate per cycle was only 0.18% in 300 cycles. Moreover, the electrolyte with the TDA+TFSI additive had more obvious advantages than the pure organic ether-based electrolyte at high charge and discharge currents of 1.0 C. The residual discharge specific capacities were 428 mAh g-1 after 100 cycles and 399 mAh g-1 after 250 cycles, which were 13% higher than those of the LSBs without the TDA+TFSI additive. At the same time, the Coulombic efficiencies of the LSBs using the TDA+TFSI electrolyte additive were more stable than those of the LSBs using the traditional organic ether-based electrolyte. The results showed that the LSBs with the TDA+TFSI electrolyte additive formed a denser and more uniform solid electrolyte interface (SEI) film during cycling, which improved the stability of the electrochemical reaction.

Dataset Information

Effects of Difluoro(oxalato)borate-Based Ionic Liquid as Electrolyte Additive for Li-Ion Batteries.

Publications

Effects of Difluoro(oxalato)borate-Based Ionic Liquid as Electrolyte Additive for Li-Ion Batteries.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets