Molecular dynamics studies of polyethylene oxide and polyethylene glycol: hydrodynamic radius and shape anisotropy.

ABSTRACT: A revision (C35r) to the CHARMM ether force field is shown to reproduce experimentally observed conformational populations of dimethoxyethane. Molecular dynamics simulations of 9, 18, 27, and 36-mers of polyethylene oxide (PEO) and 27-mers of polyethylene glycol (PEG) in water based on C35r yield a persistence length lambda = 3.7 A, in quantitative agreement with experimentally obtained values of 3.7 A for PEO and 3.8 A for PEG; agreement with experimental values for hydrodynamic radii of comparably sized PEG is also excellent. The exponent upsilon relating the radius of gyration and molecular weight (R(g) proportional, variantM(w)(upsilon)) of PEO from the simulations equals 0.515 +/- 0.023, consistent with experimental observations that low molecular weight PEG behaves as an ideal chain. The shape anisotropy of hydrated PEO is 2.59:1.44:1.00. The dimension of the middle length for each of the polymers nearly equals the hydrodynamic radius R(h)obtained from diffusion measurements in solution. This explains the correspondence of R(h) and R(p), the pore radius of membrane channels: a polymer such as PEG diffuses with its long axis parallel to the membrane channel, and passes through the channel without substantial distortion.

SUBMITTER: Lee H

PROVIDER: S-EPMC2483782 | biostudies-other | 2008 Aug

REPOSITORIES: biostudies-other

ACCESS DATA

Publications

Molecular dynamics studies of polyethylene oxide and polyethylene glycol: hydrodynamic radius and shape anisotropy.

Lee Hwankyu H Venable Richard M RM Mackerell Alexander D AD Pastor Richard W RW

Biophysical journal 20080502 4

A revision (C35r) to the CHARMM ether force field is shown to reproduce experimentally observed conformational populations of dimethoxyethane. Molecular dynamics simulations of 9, 18, 27, and 36-mers of polyethylene oxide (PEO) and 27-mers of polyethylene glycol (PEG) in water based on C35r yield a persistence length lambda = 3.7 A, in quantitative agreement with experimentally obtained values of 3.7 A for PEO and 3.8 A for PEG; agreement with experimental values for hydrodynamic radii of compar ...[more]

PMID: 18456821

Similar Datasets

Project description:Phase change materials (PCMs) in the form of fibers or fibrous mats with exceptional thermal energy storage ability and tunable working temperature are of high interest to produce smart thermoregulating textiles, useful for increasing human thermal comfort while avoiding energy waste. Common organic PCMs suffer from instability in their molten state, which limits their applicability as highly performing fibrous systems. In this work, electrospun fibrous mats made of polyethylene oxide (PEO), a PCM with excellent thermal properties and biocompatibility, were fabricated and their shape instability in the molten state was improved through UV photo-crosslinking. The characterization aimed to assess the performance of these shape-stable electrospun mats as nanofibrous PCMs for thermal management applications. In addition to an enhanced resistance to water-based solvents, UV-cured electrospun PEO mats demonstrated a remarkable latent heat (≈112 J/g), maintained over 80 heating/cooling cycles across the phase change temperature. Moreover, their morphological stability above their melting point was demonstrated both macroscopically and microscopically, with the retention of the initial nanofibrous morphology. Tensile mechanical tests demonstrated that the UV crosslinking considerably enhanced the ultimate properties of the fibrous mat, with a five-fold increase in both the tensile strength (from 0.15 MPa to 0.74 MPa) and the strain at break (from 2.5% to 12.2%) compared to the uncrosslinked mat. In conclusion, the photo-crosslinked electrospun PEO material exhibited high thermal properties and good shape stability without displaying leakage; accordingly, in the proposed PCM system, the necessity for encapsulation or use of a supporting layer has been eliminated. Photo-crosslinking thus proved itself as an effective, fast, and environmentally friendly method to dramatically improve the shape-stability of nanofibrous PEO electrospun mats for smart thermoregulating textiles.

Project description:The addition of polyethylene glycol (PEG) chains to poly(lactic-co-glycolic acid) (PLGA) matrices is extensively used to modulate the biodegradation, drug loading and release, mechanical properties, and chemical stability of the original system. Multiple parameters, including the molecular weight, relative concentration, polarity, and solubility, affect the physicochemical properties of the polymer blend. Here, molecular dynamics simulations with the united-atom 2016H66 force field are used to model the behavior of PLGA and PEG chains and thus predict the overall physicochemical features of the resulting blend. First, the model accuracy is validated against fundamental properties of pure PLGA and PEG samples. In agreement with previous experimental and theoretical observations, the PLGA solubility results to be higher in acetonitrile than in water, with Flory parameters νACN = 0.63 ± 0.01 and νW = 0.21 ± 0.02, and the Young's modulus of PLGA and PEG equal to Y = 2.0 ± 0.43 and 0.32 ± 0.34 GPa, respectively. Next, four PEG/PLGA blending regimes are identified by varying the relative concentrations and molecular weights of the individual polymers. The computational results demonstrate that at low PEG concentrations (<8% w/w), homogeneous blends are generated for both low and high PEG molecular weights. In contrast, at comparable PEG and PLGA concentrations (∼50% w/w), short PEG chains are only partially miscible whereas long PEG chains segregate within the PLGA matrix. This behavior has been confirmed experimentally via differential scanning calorimetry and is in agreement with previous observations. Finally, the computed Young's modulus of PLGA/PEG blends is observed to decrease with the PEG content returning the lowest values for the partial and fully segregated regimens (Y ≈ 1.3 GPa). This work proposes a computational scheme for predicting the physicochemical properties of PLGA/PEG blends paving the way toward the rational design of polymer mixtures for biomedical applications.

Dataset Information

Molecular dynamics studies of polyethylene oxide and polyethylene glycol: hydrodynamic radius and shape anisotropy.

Publications

Molecular dynamics studies of polyethylene oxide and polyethylene glycol: hydrodynamic radius and shape anisotropy.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets