A nontransferring dry adhesive with hierarchical polymer nanohairs.

ABSTRACT: We present a simple yet robust method for fabricating angled, hierarchically patterned high-aspect-ratio polymer nanohairs to generate directionally sensitive dry adhesives. The slanted polymeric nanostructures were molded from an etched polySi substrate containing slanted nanoholes. An angled etching technique was developed to fabricate slanted nanoholes with flat tips by inserting an etch-stop layer of silicon dioxide. This unique etching method was equipped with a Faraday cage system to control the ion-incident angles in the conventional plasma etching system. The polymeric nanohairs were fabricated with tailored leaning angles, sizes, tip shapes, and hierarchical structures. As a result of controlled leaning angle and bulged flat top of the nanohairs, the replicated, slanted nanohairs showed excellent directional adhesion, exhibiting strong shear attachment (approximately 26 N/cm(2) in maximum) in the angled direction and easy detachment (approximately 2.2 N/cm(2)) in the opposite direction, with a hysteresis value of approximately 10. In addition to single scale nanohairs, monolithic, micro-nanoscale combined hierarchical hairs were also fabricated by using a 2-step UV-assisted molding technique. These hierarchical nanoscale patterns maintained their adhesive force even on a rough surface (roughness <20 microm) because of an increase in the contact area by the enhanced height of hierarchy, whereas simple nanohairs lost their adhesion strength. To demonstrate the potential applications of the adhesive patch, the dry adhesive was used to transport a large-area glass (47.5 x 37.5 cm(2), second-generation TFT-LCD glass), which could replace the current electrostatic transport/holding system with further optimization.

SUBMITTER: Jeong HE

PROVIDER: S-EPMC2667085 | biostudies-other | 2009 Apr

REPOSITORIES: biostudies-other

ACCESS DATA

Publications

A nontransferring dry adhesive with hierarchical polymer nanohairs.

Jeong Hoon Eui HE Lee Jin-Kwan JK Kim Hong Nam HN Moon Sang Heup SH Suh Kahp Y KY

Proceedings of the National Academy of Sciences of the United States of America 20090320 14

We present a simple yet robust method for fabricating angled, hierarchically patterned high-aspect-ratio polymer nanohairs to generate directionally sensitive dry adhesives. The slanted polymeric nanostructures were molded from an etched polySi substrate containing slanted nanoholes. An angled etching technique was developed to fabricate slanted nanoholes with flat tips by inserting an etch-stop layer of silicon dioxide. This unique etching method was equipped with a Faraday cage system to contr ...[more]

PMID: 19304801

Similar Datasets

Project description:BackgroundFunctional electrical stimulation (FES) can be used in rehabilitation to aid or improve function in people with paralysis. In clinical settings, it is common practice to use transcutaneous electrodes to apply the electrical stimulation, since they are non-invasive, and can be easily applied and repositioned as necessary. However, the current electrode options available for transcutaneous FES are limited and can have practical disadvantages, such as the need for a wet interface with the skin for better comfort and performance. Hence, we were motivated to develop a dry stimulation electrode which could perform equivalently or better than existing commercially available options.MethodsWe manufactured a thin-film dry polymer nanocomposite electrode, characterized it, and tested its performance for stimulation purposes with thirteen healthy individuals. We compared its functionality in terms of stimulation-induced muscle torque and comfort level against two other types of transcutaneous electrodes: self-adhesive hydrogel and carbon rubber. Each electrode type was also tested using three different stimulators and different intensity levels of stimulation.ResultsWe found the proposed dry polymer nanocomposite electrode to be functional for stimulation, as there was no statistically significant difference between its performance to the other standard electrodes. Namely, the proposed dry electrode had comparable muscle torque generated and comfort level as the self-adhesive hydrogel and carbon rubber electrodes. From all combinations of electrode type and stimulators tested, the dry polymer nanocomposite electrode with the MyndSearch stimulator had the most comfortable average rating.ConclusionsThe dry polymer nanocomposite electrode is a durable and flexible alternative to existing self-adhesive hydrogel and carbon rubber electrodes, which can be used without the addition of a wet interfacing agent (i.e., water or gel) to perform as well as the current electrodes used for stimulation purposes.

Dataset Information

A nontransferring dry adhesive with hierarchical polymer nanohairs.

Publications

A nontransferring dry adhesive with hierarchical polymer nanohairs.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets