Engineering of bio-hybrid materials by electrospinning polymer-microbe fibers.

ABSTRACT: Although microbes have been used in industrial and niche applications for several decades, successful immobilization of microbes while maintaining their usefulness for any desired application has been elusive. Such a functionally bioactive system has distinct advantages over conventional batch and continuous-flow microbial reactor systems that are used in various biotechnological processes. This article describes the use of polyethylene oxide(99)-polypropylene oxide(67)-polyethylene oxide(99) triblock polymer fibers, created via electrospinning, to encapsulate microbes of 3 industrially relevant genera, namely, Pseudomonas, Zymomonas, and Escherichia. The presence of bacteria inside the fibers was confirmed by fluorescence microscopy and SEM. Although the electrospinning process typically uses harsh organic solvents and extreme conditions that generally are harmful to bacteria, we describe techniques that overcome these limitations. The encapsulated microbes were viable for several months, and their metabolic activity was not affected by immobilization; thus they could be used in various applications. Furthermore, we have engineered a microbe-encapsulated cross-linked fibrous polymeric material that is insoluble. Also, the microbe-encapsulated active matrix permits efficient exchange of nutrients and metabolic products between the microorganism and the environment. The present results demonstrate the potential of the electrospinning technique for the encapsulation and immobilization of bacteria in the form of a synthetic biofilm, while retaining their metabolic activity. This study has wide-ranging implications in the engineering and use of novel bio-hybrid materials or biological thin-film catalysts.

SUBMITTER: Liu Y

PROVIDER: S-EPMC2732800 | biostudies-other | 2009 Aug

REPOSITORIES: biostudies-other

ACCESS DATA

Publications

Engineering of bio-hybrid materials by electrospinning polymer-microbe fibers.

Liu Ying Y Rafailovich Miriam H MH Malal Ram R Cohn Daniel D Chidambaram Dev D

Proceedings of the National Academy of Sciences of the United States of America 20090810 34

Although microbes have been used in industrial and niche applications for several decades, successful immobilization of microbes while maintaining their usefulness for any desired application has been elusive. Such a functionally bioactive system has distinct advantages over conventional batch and continuous-flow microbial reactor systems that are used in various biotechnological processes. This article describes the use of polyethylene oxide(99)-polypropylene oxide(67)-polyethylene oxide(99) tr ...[more]

PMID: 19667172

Similar Datasets

Project description:Interest in the use of renewable raw materials in the preparation of materials has been growing uninterruptedly in recent decades. The aim of this strategy is to offer alternatives to the use of fossil fuel-based raw materials and to meet the demand for materials that are less detrimental to the environment after disposal. In this context, several studies have been carried out on the use of lignocellulosic biomass and its main components (cellulose, hemicelluloses, and lignin) as raw materials for polymeric materials. Lignocellulosic fibers have a high content of cellulose, but there has been a notable lack of investigations on application of the electrospinning technique for solutions prepared from raw lignocellulosic biomass, even though the presence of cellulose favors the alignment of the fiber chains during electrospinning. In this investigation, ultrathin (submicrometric) and nanoscale aligned fibers were successfully prepared via electrospinning (room temperature) of solutions prepared with different contents of lignocellulosic sisal fibers combined with recycled poly(ethylene terephthalate) (PET) using trifluoroacetic acid (TFA) as solvent. The "macro" fibers were deconstructed by the action of TFA, resulting in solutions containing their constituents, i.e., cellulose, hemicelluloses, and lignin, in addition to PET. The "macro" sisal fibers were reconstructed at the nanometer and submicrometric scale from these solutions. The SEM micrographs of the mats containing the components of sisal showed distinct fiber networks, likely due to differences in the solubility of these components in TFA and in their dielectric constants. The mechanical properties of the mats (dynamic mechanical analysis, DMA, and tensile properties) were evaluated with the samples positioned both in the direction (dir) of and in opposition (op) to the alignment of the nano and ultrathin fibers, which can be considered a novelty in the analysis of this type of material. DMA showed superior values of storage modulus (E' at 30 °C) for the mats characterized in the preferential direction of fiber alignment. For example, for mats obtained from solutions prepared from a 0.4 ratio of sisal fibers/PET, Sisal/PET0.40dir presented a high E' value of 765 MPa compared to Sisal/PET0.40op that presented an E' value of 88.4 MPa. The fiber alignment did not influence the Tg values (from tan ? peak) of electrospun mats with the same compositions, as they presented similar values for this property. The tensile properties of the electrospun mats were significantly impacted by the alignment of the fibers: e.g., Sisal/PET0.40dir presented a high tensile strength value of 15.72 MPa, and Sisal/PET0.40op presented a value of approximately 2.5 MPa. An opposite trend was observed regarding the values of elongation at break for these materials. Other properties of the mats are also discussed; such as the index of fiber alignment, average porosity, and surface contact angle. To our knowledge, this is the first time that the influence of fiber alignment on the properties of electrospun mats based on untreated lignocellulosic biomass combined with a recycled polymer, such as PET, has been evaluated. The mats obtained in this study have potential for diversified applications, such as reinforcement for polymeric matrices in nanocomposites, membranes for filtration, and support for enzymes, wherein the fiber alignment, together with other evaluated properties, can impact their effectiveness in these applications.

Dataset Information

Engineering of bio-hybrid materials by electrospinning polymer-microbe fibers.

Publications

Engineering of bio-hybrid materials by electrospinning polymer-microbe fibers.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure