Electromechanical properties and anisotropy of single- and multi-domain 0.72Pb(Mg(1∕3)Nb(2∕3))O(3)-0.28PbTiO(3) single crystals.

ABSTRACT: Complete sets of elastic, piezoelectric, and dielectric constants of 0.72Pb(Mg(1∕3)Nb(2∕3))O(3)-0.28PbTiO(3) single crystal poled along [111](c) (single domain) as well as non-polar axes [001](c) and [011](c) (multidomain) have been measured under natural conditions. These data allowed us to evaluate accurately the extrinsic contributions to the superior piezoelectric properties. Very large extrinsic contributions to the unusual anisotropies in multidomain crystals are confirmed. We found that the instability of domain structures is the origin of the low mechanical quality factor Q for the multidomain relaxor-based ferroelectric single crystals. Our results can provide useful guidance in future design of domain engineered materials.

SUBMITTER: Liu G

PROVIDER: S-EPMC3215685 | biostudies-other | 2011 Oct

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Optical Properties of Mg, Fe, Co-Doped Near-Stoichiometric LiTaO₃ Single Crystals.

Project description:Mg, Fe co-doped near-stoichiometric lithium tantalite (SLT) single crystals were grown by employing the zone-leveling Czochralski (ZLCz) technique. The optical properties, holographic parameters, as well as the composition of the grown crystals were measured. It was found that the Li/Ta ratio decreased with the doping of Mg and Fe ions. A red shift was observed in absorption spectrum for the Mg, Fe co-doped crystals compared to the undoped and Mg-doped ones. The effect of the iron ions (Fe2+ and Fe3+) was further discussed based on the specified absorption bands. Moreover, the occupation mechanism for the defects was discussed by using the IR absorption spectrum, which was attributed to the FeTa3- defects in the highly Fe-doped crystal. In addition, the holographic parameters were also found to be improved with a higher Fe/Ta ratio in the crystals.

| S-EPMC5448910 | biostudies-other

Domain size engineering in tetragonal Pb(In(1∕2)Nb(1∕2))O(3)-Pb(Mg(1∕3)Nb(2∕3))O(3)-PbTiO(3) crystals.

Project description:The effect of domain size on the dielectric and piezoelectric properties of [111]-oriented tetragonal Pb(In(1∕2)Nb(1∕2))O(3)-Pb(Mg(1∕3)Nb(2∕3))O(3)-PbTiO(3) crystals was investigated. The dielectric permittivity (ɛ(33 ) (T)∕ɛ(0)) and piezoelectric coefficient (d(33)) were found to be on the order of 13 800 and 1630 pC∕N, respectively, for samples with domain size of ∼500 nm, a 3-fold increase to crystals with domain size of ∼50 μm. Rayleigh analysis revealed that the extrinsic contribution to the piezoelectric response increased from ∼8% to 30% with decreasing domain size, due to the increased domain wall density and associated irreversible domain wall motion. The enhanced properties were thought to relate to the fine domain structures, however, showing a poor electric field and temperature stabilities with domain size of 500 nm. Of particular significance is that samples with domain size being on the order of 5 μm exhibit field and temperature stabilities, with yet high piezoelectric properties, make it potential for transducer applications.

| S-EPMC3215687 | biostudies-other

Complete set of material properties of single domain 0.24Pb(In(1∕2)Nb(1∕2))O(3)-0.49Pb(Mg(1∕3)Nb(2∕3))O(3)-0.27PbTiO(3) single crystal and the orientation effects.

Project description:Multidomain relaxor-based single crystals have intrigued the enthusiasm of many researchers due to their superior electromechanical properties. In order to understand the physical origin of multidomain properties, one must know the complete set of material coefficients in single domain state. Previous published single domain data were all measured under bias because single domain state is unstable. Here, we report a set of single domain data without bias for rhombohedral 0.24Pb(In(1∕2)Nb(1∕2))O(3)-0.49Pb(Mg(1∕3)Nb(2∕3))O(3)-0.27PbTiO(3) single crystal. Comparing rotated coefficients from single domain data with measured multidomain material coefficients, we concluded that the orientation effects account for more than 90% of the observed multidomain properties.

| S-EPMC3155577 | biostudies-other

Optical Anisotropy and Momentum-Dependent Excitons in Dibenzopentacene Single Crystals.

Project description:High-quality single crystals of the organic semiconductor (1,2;8,9)-dibenzopentacene were grown via physical vapor transport. The crystal structure-unknown before-was determined by single-crystal X-ray diffraction; polarization-dependent optical absorption measurements display a large anisotropy in the ac plane of the crystals. The overall Davydov splitting is ∼110 meV, which is slightly lower than that in the close relative pentacene (120 meV). Momentum-dependent electron energy-loss spectroscopy measurements show a clear exciton dispersion of the Davydov components. An analysis of the dispersion using a simple 1D model indicates smaller electron- and hole-transfer integrals in dibenzopentacene as compared to pentacene. The spectral weight distribution of the excitation spectra is strongly momentum-dependent and demonstrates a strong momentum-dependent admixture of Frenkel excitons, charge-transfer excitons, and vibrational modes.

| S-EPMC9219101 | biostudies-literature

Giant reversible anisotropy changes at room temperature in a (La,Sr)MnO3/Pb(Mg,Nb,Ti)O3 magneto-electric heterostructure.

Project description:In a model artificial multiferroic system consisting of a (011)-oriented ferroelectric Pb(Mg,Nb,Ti)O3 substrate intimately coupled to an epitaxial ferromagnetic (La,Sr)MnO3 film, electric field pulse sequences of less than 6 kV/cm induce large, reversible, and bistable remanent strains. The magnetic anisotropy symmetry reversibly switches from a highly anisotropic two-fold state to a more isotropic one, with concomitant changes in resistivity. Anisotropy changes at the scale of a single ferromagnetic domain were measured using X-ray microscopy, with electric-field dependent magnetic domain reversal showing that the energy barrier for magnetization reversal is drastically lowered. Free energy calculations confirm this barrier lowering by up to 70% due to the anisotropic strain changes generated by the substrate. Thus, we demonstrate that an electric field pulse can be used to 'set' and 'reset' the magnetic anisotropy orientation and resistive state in the film, as well as to lower the magnetization reversal barrier, showing a promising route towards electric-field manipulation of multifunctional nanostructures at room temperature.

| S-EPMC4897745 | biostudies-literature

Homogeneity and variation of donor doping in Verneuil-grown SrTiO3:Nb single crystals.

Project description:The homogeneity of Verneuil-grown SrTiO3:Nb crystals was investigated. Due to the fast crystal growth process, inhomogeneities in the donor dopant distribution and variation in the dislocation density are expected to occur. In fact, for some crystals optical studies show variations in the density of Ti(3+) states on the microscale and a cluster-like surface conductivity was reported in tip-induced resistive switching studies. However, our investigations by TEM, EDX mapping, and 3D atom probe reveal that the Nb donors are distributed in a statistically random manner, indicating that there is clearly no inhomogeneity on the macro-, micro-, and nanoscale in high quality Verneuil-grown crystals. In consequence, the electronic transport in the bulk of donor-doped crystals is homogeneous and it is not significantly channelled by extended defects such as dislocations which justifies using this material, for example, as electronically conducting substrate for epitaxial oxide film growth.

| S-EPMC5006055 | biostudies-literature

Anisotropy and Strain Localization in Dynamic Impact Experiments of Tantalum Single Crystals.

Project description:Deformation mechanisms in bcc metals, especially in dynamic regimes, show unusual complexity, which complicates their use in high-reliability applications. Here, we employ novel, high-velocity cylinder impact experiments to explore plastic anisotropy in single crystal specimens under high-rate loading. The bcc tantalum single crystals exhibit unusually high deformation localization and strong plastic anisotropy when compared to polycrystalline samples. Several impact orientations - [100], [110], [111] and [[Formula: see text]] - are characterized over a range of impact velocities to examine orientation-dependent mechanical behavior versus strain rate. Moreover, the anisotropy and localized plastic strain seen in the recovered cylinders exhibit strong axial symmetries which differed according to lattice orientation. Two-, three-, and four-fold symmetries are observed. We propose a simple crystallographic argument, based on the Schmid law, to understand the observed symmetries. These tests are the first to explore the role of single-crystal orientation in Taylor impact tests and they clearly demonstrate the importance of crystallography in high strain rate and temperature deformation regimes. These results provide critical data to allow dramatically improved high-rate crystal plasticity models and will spur renewed interest in the role of crystallography to deformation in dynamics regimes.

| S-EPMC5883051 | biostudies-literature

Characterization of Mn-modified Pb(Mg(13)Nb(23))O(3)-PbZrO(3)-PbTiO(3) single crystals for high power broad bandwidth transducers.

Project description:The effect of MnO(2) addition on the dielectric and piezoelectric properties of 0.4Pb(Mg(13)Nb(23))O(3)-0.25PbZrO(3)-0.35PbTiO(3) single crystals was investigated. Analogous to acceptor doping in "hard" Pb(Zr,Ti)O(3) based polycrystalline materials, the Mn doped crystals exhibited enhanced mechanical Q ( approximately 1050) with low dielectric loss ( approximately 0.2%), while maintaining ultrahigh electromechanical coupling k(33)>90%, inherent in domain engineered single crystals. The effect of acceptor doping was also evident in the build-up of an internal bias (E(i) approximately 1.6 kVcm), shown by a horizontal offset in the polarization-field behavior. Together with the relatively high usage temperature (T(R-T) approximately 140 degrees C), the Mn doped crystals are promising candidates for high power and broad bandwidth transducers.

| S-EPMC2682751 | biostudies-other

Intrinsic Enhancement of Dielectric Permittivity in (Nb + In) co-doped TiO<sub>2</sub> single crystals.

Project description:The development of dielectric materials with colossal permittivity is important for the miniaturization of electronic devices and fabrication of high-density energy-storage devices. The electron-pinned defect-dipoles has been recently proposed to boost the permittivity of (Nb?+?In) co-doped TiO2 to 105. However, the follow-up studies suggest an extrinsic contribution to the colossal permittivity from thermally excited carriers. Herein, we demonstrate a marked enhancement in the permittivity of (Nb?+?In) co-doped TiO2 single crystals at sufficiently low temperatures such that the thermally excited carriers are frozen out and exert no influence on the dielectric response. The results indicate that the permittivity attains quadruple of that for pure TiO2. This finding suggests that the electron-pinned defect-dipoles add an extra dielectric response to that of the TiO2 host matrix. The results offer a novel approach for the development of functional dielectric materials with large permittivity by engineering complex defects into bulk materials.

| S-EPMC5509748 | biostudies-literature

Synthetic approach of ternary magnesium niobate (Mg-Nb-O) compounds.

Project description:Magnesium based niobium oxides (Mg-Nb-O) were prepared by solid-state reactions owing to understand the function of transition metal oxides as promoters/catalysts for practical application. Magnesium niobate (Mg3Nb6O11) was synthesized for the first time in nearly pure form reported in this context. MgNb2O6 and Mg4Nb2O9 were prepared in oxidizing conditions; on the contrary, Mg3Nb6O11 preferred reducing environment. Stoichiometric mixtures of the precursor materials MgO, Nb2O5 and/or metallic Nb were annealed for the syntheses which revealed the effect of temperature on phase formation, reaction kinetics and heat of reaction. The products were examined by ex-situ, in-situ X-ray diffraction (XRD) and differential scanning calorimetry (DSC). Crystallographic parameters of various binary and ternary compounds (Mg/Nb/O) formed in different calcination conditions, were extracted by Rietveld method. In-situ experiment results in single step reaction for the MgNb2O6 synthesis and the heat of formation of the solid-state reaction obtained to be minimum (93 kJ/mol). In contrast, the formation of Mg4Nb2O9 and Mg3Nb6O11 compounds towards pure phases rather complicated due to multistep reactions and corresponding heat of formation were estimated to be 140 and 190 kJ/mol. Experimental results have been discussed based on kinetic and thermodynamic constrains.

| S-EPMC8352938 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data