Heterojunction photodiode fabricated from hydrogen treated ZnO nanowires grown on p-silicon substrate.

ABSTRACT: A heterojunction photodiode was fabricated from ZnO nanowires (NWs) grown on a p-type Si (100) substrate using a hydrothermal method. Post growth hydrogen treatment was used to improve the conductivity of the ZnO NWs. The heterojunction photodiode showed diode characteristics with low reverse saturation current (5.58 × 10(-7) A), relatively fast transient response, and high responsivity (22 A/W at 363 nm). Experiments show that the photoresponsivity of the photodiode is dependent on the polarity of the voltages. The photoresponsivity of the device was discussed in terms of the band diagrams of the heterojunction and the carrier diffusion process.

SUBMITTER: Shao D

PROVIDER: S-EPMC3517498 | biostudies-other | 2012 Nov

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Comparison of ZnO nanowires grown on e-beam evaporated Ag and ZnO seed layers.

Project description:In this study, ZnO nanowires with diameters ranging from 50 nm to 500 nm have been synthesized hydrothermally on Ag and ZnO seed layers deposited by electron beam evaporation. ZnO nanowires grown on hetero and homo interfaces have been studied by comparing the growth characteristics of (a) ZnO nanowires on the Ag seed layer and (b) ZnO nanowires grown on the ZnO seed layer, respectively. The surface morphology of the as-evaporated seed layers before the nanowire growth has been investigated. Electron backscatter diffraction (EBSD) has been employed to examine the crystallinity of ZnO nanowires. In addition, the integrity of the Ag-ZnO heterointerface has been investigated using high-resolution transmission electron microscopy (HR-TEM). The length, diameter, density, and alignment of nanowires grown on Ag and ZnO seed layers have been studied as a function of growth time from 0.5 hours to 18 hours and precursor concentration from 5 mM to 18 mM. Furthermore, for both the Ag-ZnO nanowire heterostructure and ZnO-ZnO nanowire homostructure, the role of defects in the optical properties in the wavelength range of 517 nm to 900 nm has been studied using photoluminescence (PL) spectroscopy.

| S-EPMC9418495 | biostudies-literature

Self-powered p-NiO/n-ZnO heterojunction ultraviolet photodetectors fabricated on plastic substrates.

Project description:A self-powered ultraviolet (UV) photodetector (PD) based on p-NiO and n-ZnO was fabricated using low-temperature sputtering technique on indium doped tin oxide (ITO) coated plastic polyethylene terephthalate (PET) substrates. The p-n heterojunction showed very fast temporal photoresponse with excellent quantum efficiency of over 63% under UV illumination at an applied reverse bias of 1.2 V. The engineered ultrathin Ti/Au top metal contacts and UV transparent PET/ITO substrates allowed the PDs to be illuminated through either front or back side. Morphology, structural, chemical and optical properties of sputtered NiO and ZnO films were also investigated.

| S-EPMC4759661 | biostudies-literature

Amorphous Silicon Nanowires Grown on Silicon Oxide Film by Annealing.

Project description:In this paper, amorphous silicon nanowires (α-SiNWs) were synthesized on (100) Si substrate with silicon oxide film by Cu catalyst-driven solid-liquid-solid mechanism (SLS) during annealing process (1080 °C for 30 min under Ar/H2 atmosphere). Micro size Cu pattern fabrication decided whether α-SiNWs can grow or not. Meanwhile, those micro size Cu patterns also controlled the position and density of wires. During the annealing process, Cu pattern reacted with SiO2 to form Cu silicide. More important, a diffusion channel was opened for Si atoms to synthesis α-SiNWs. What is more, the size of α-SiNWs was simply controlled by the annealing time. The length of wire was increased with annealing time. However, the diameter showed the opposite tendency. The room temperature resistivity of the nanowire was about 2.1 × 103 Ω·cm (84 nm diameter and 21 μm length). This simple fabrication method makes application of α-SiNWs become possible.

| S-EPMC5552620 | biostudies-other

ZnO nanowires array grown on Ga-doped ZnO single crystal for dye-sensitized solar cells.

Project description:High quality ZnO nanowires arrays were homoepitaxial grown on Ga-doped ZnO single crystal (GZOSC), which have the advantages of high conductivity, high carrier mobility and high thermal stability. When it was employed as a photoanode in the DSSCs, the cell exhibited a 1.44% power-conversion efficiency under the illumination of one sun (AM 1.5G). The performance is superior to our ZnO nanowires/FTO based DSSCs under the same condition. This enhanced performance is mainly attributed to the perfect interface between the ZnO nanowires and the GZOSC substrate that contributes to lower carrier scattering and recombination rates compared with that grown on traditional FTO substrate.

| S-EPMC4477229 | biostudies-literature

Photodetecting properties of single CuO-ZnO core-shell nanowires with p-n radial heterojunction.

Project description:CuO-ZnO core-shell radial heterojunction nanowire arrays were obtained by a simple route which implies two cost-effective methods: thermal oxidation in air for preparing CuO nanowire arrays, acting as a p-type core and RF magnetron sputtering for coating the surface of the CuO nanowires with a ZnO thin film, acting as a n-type shell. The morphological, structural, optical and compositional properties of the CuO-ZnO core-shell nanowire arrays were investigated. In order to analyse the electrical and photoelectrical properties of the metal oxide nanowires, single CuO and CuO-ZnO core-shell nanowires were contacted by employing electron beam lithography (EBL) and focused ion beam induced deposition (FIBID). The photoelectrical properties emphasize that the p-n radial heterojunction diodes based on single CuO-ZnO core-shell nanowires behave as photodetectors, evidencing a time-depending photoresponse under illumination at 520 nm and 405 nm wavelengths. The performance of the photodetector device was evaluated by assessing its key parameters: responsivity, external quantum efficiency and detectivity. The results highlighted that the obtained CuO-ZnO core-shell nanowires are emerging as potential building blocks for a next generation of photodetector devices.

| S-EPMC7596234 | biostudies-literature

Efficient Photocatalytic Hydrogen Evolution over TiO2-X Mesoporous Spheres-ZnO Nanorods Heterojunction.

Project description:Photocatalytic water splitting into hydrogen is regarded as one of the key solutions to the deterioration of the global environment and energy. Due to the significantly reduced grain boundaries, ZnO nanorods facilitate a fast electron transfer through their smooth tunnels and are well suited as a photocatalyst. However, the photocatalytic hydrogen evolution performance of pristine ZnO nanorods is still low due to the high recombination rate of photogenerated electron-hole pairs and the less light absorption. Here, a novel structure about black ZnO nanorods (NRs)/TiO2-X mesoporous spheres (MSs) heterojunction has been prepared and the photocatalytic hydrogen evolution performance has been explored. The photocatalytic activity test results showed that ZnO NRs/TiO2-X MSs exhibited higher catalytic activity than ZnO NRs for hydrogen production. Compared to the pure ZnO NRs photoanode, the photocurrent of ZnO NRs/TiO2-X MSs heterojunction photoanode could reach 0.41 mA/cm2 in view of the expanding spectral response region and effective inhibition of e-/h+ recombination at the same condition. Using a relatively integrated experimental investigation and mechanism analysis, we scrutinized that after being treated with NaBH4, TiO2 MSs introduce oxygen vacancies expanding the photocatalytic activity of pure TiO2, and improving conductivity and charge transport capabilities through coating on ZnO NRs. More importantly, the results provide a promising approach in the NRs/MSs composite structure serving as photoanodes for photocatalytic hydrogen production.

| S-EPMC7690575 | biostudies-literature

A self-assembled microbonded germanium/silicon heterojunction photodiode for 25 Gb/s high-speed optical interconnects.

Project description:A novel technique using surface tension to locally bond germanium (Ge) on silicon (Si) is presented for fabricating high performance Ge/Si photodiodes. Surface tension is a cohesive force among liquid molecules that tends to bring contiguous objects in contact to maintain a minimum surface energy. We take advantage of this phenomenon to fabricate a heterojunction optoelectronic device where the lattice constants of joined semiconductors are different. A high-speed Ge/Si heterojunction waveguide photodiode is presented by microbonding a beam-shaped Ge, first grown by rapid-melt-growth (RMG) method, on top of a Si waveguide via surface tension. Excellent device performances such as an operating bandwidth of 17 GHz and a responsivity of 0.66 and 0.70 A/W at the reverse bias of -4 and -6 V, respectively, are demonstrated. This technique can be simply implemented via modern complementary metal-oxide-semiconductor (CMOS) fabrication technologies for integrating Ge on Si devices.

| S-EPMC3828570 | biostudies-other

Photoluminescence Study of the Influence of Additive Ammonium Hydroxide in Hydrothermally Grown ZnO Nanowires.

Project description:We report the influence of ammonium hydroxide (NH4OH), as growth additive, on zinc oxide nanomaterial through the optical response obtained by photoluminescence (PL). A low-temperature hydrothermal process is employed for the growth of ZnO nanowires (NWs) on seedless Au surface. A more than two order of magnitude change in ZnO NW density is demonstrated via careful addition of NH4OH in the growth solution. Further, we show by systematic experimental study and PL characterization data that the addition of NH4OH can degrade the optical response of ZnO NWs produced. The increase of growth solution basicity with the addition of NH4OH may slowly degrade the optical response of NWs by slowly etching its surfaces, increasing the point defects in ZnO NWs. The present study demonstrates the importance of growth nutrients to obtain quality controlled density tunable ZnO NWs on seedless conducting substrates.

| S-EPMC6104415 | biostudies-literature

High Density of Quantum-Sized Silicon Nanowires with Different Polytypes Grown with Bimetallic Catalysts.

Project description:When Si nanowires (NWs) have diameters below about 10 nm, their band gap increases as their diameter decreases; moreover, it can be direct if the material adopts the metastable diamond hexagonal structure. To prepare such wires, we have developed an original variant of the vapor-liquid-solid process based on the use of a bimetallic Cu-Sn catalyst in a plasma-enhanced chemical vapor deposition reactor, which allows us to prevent droplets from coalescing and favors the growth of a high density of NWs with a narrow diameter distribution. Controlling the deposited thickness of the catalyst materials at the sub-nanometer level allows us to get dense arrays (up to 6 × 1010 cm-2) of very-small-diameter NWs of 6 nm on average (standard deviation of 1.6 nm) with crystalline cores of about 4 nm. The transmission electron microscopy analysis shows that both 3C and 2H polytypes are present, with the 2H hexagonal diamond structure appearing in 5-13% of the analyzed NWs per sample.

| S-EPMC8515598 | biostudies-literature

Hydrothermally Grown In-doped ZnO Nanorods on p-GaN Films for Color-tunable Heterojunction Light-emitting-diodes.

Project description:The incorporation of doping elements in ZnO nanostructures plays an important role in adjusting the optical and electrical properties in optoelectronic devices. In the present study, we fabricated 1-D ZnO nanorods (NRs) doped with different In contents (0% ~ 5%) on p-GaN films using a facile hydrothermal method, and investigated the effect of the In doping on the morphology and electronic structure of the NRs and the electrical and optical performances of the n-ZnO NRs/p-GaN heterojunction light emitting diodes (LEDs). As the In content increased, the size (diameter and length) of the NRs increased, and the electrical performance of the LEDs improved. From the electroluminescence (EL) spectra, it was found that the broad green-yellow-orange emission band significantly increased with increasing In content due to the increased defect states (oxygen vacancies) in the ZnO NRs, and consequently, the superposition of the emission bands centered at 415 nm and 570 nm led to the generation of white-light. These results suggest that In doping is an effective way to tailor the morphology and the optical, electronic, and electrical properties of ZnO NRs, as well as the EL emission property of heterojunction LEDs.

| S-EPMC4437377 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data