Hierarchical oriented anatase TiO2 nanostructure arrays on flexible substrate for efficient dye-sensitized solar cells.

ABSTRACT: The vertically oriented anatase single crystalline TiO2 nanostructure arrays (TNAs) consisting of TiO2 truncated octahedrons with exposed {001} facets or hierarchical TiO2 nanotubes (HNTs) consisting of numerous nanocrystals on Ti-foil substrate were synthesized via a two-step hydrothermal growth process. The first step hydrothermal reaction of Ti foil and NaOH leads to the formation of H-titanate nanowire arrays, which is further performed the second step hydrothermal reaction to obtain the oriented anatase single crystalline TiO2 nanostructures such as TiO2 nanoarrays assembly with truncated octahedral TiO2 nanocrystals in the presence of NH4F aqueous or hierarchical TiO2 nanotubes with walls made of nanocrystals in the presence of pure water. Subsequently, these TiO2 nanostructures were utilized to produce dye-sensitized solar cells in a backside illumination pattern, yielding a significant high power conversion efficiency (PCE) of 4.66% (TNAs, J(SC) = 7.46 mA cm(-2), V(OC) = 839 mV, FF = 0.75) and 5.84% (HNTs, J(SC) = 10.02 mA cm(-2), V(OC) = 817 mV, FF = 0.72), respectively.

SUBMITTER: Wu WQ

PROVIDER: S-EPMC3665963 | biostudies-other | 2013

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Hydrothermal fabrication of hierarchically anatase TiO2 nanowire arrays on FTO glass for dye-sensitized solar cells.

Project description:Hierarchical anatase TiO(2) nano-architecture arrays consisting of long TiO(2) nanowire trunk and numerous short TiO(2) nanorod branches on transparent conductive fluorine-doped tin oxide glass are successfully synthesized for the first time through a facile one-step hydrothermal route without any surfactant and template. Dye-sensitized solar cells based on the hierarchical anatase TiO(2) nano-architecture array photoelectrode of 18 ?m in length shows a power conversion efficiency of 7.34% because of its higher specific surface area for adsorbing more dye molecules and superior light scattering capacity for boosting the light-harvesting efficiency. The present photovoltaic performance is the highest value for the reported TiO(2) nanowires array photoelectrode.

| S-EPMC3583000 | biostudies-literature

Solvothermally synthesized anatase TiO2 nanoparticles for photoanodes in dye-sensitized solar cells.

Project description:Many researchers working on the development of Dye-sensitized solar cells (DSCs) continue to focus on the synthesis of photoanode materials with high surface area, along with high light scattering ability to enhance light harvesting efficiency (LHE). On the other hand, dye packing density, which can also affect the LHE significantly, is often overlooked. Solvothermally synthesized anatase TiO2 nanoparticles (SANP) were obtained by a new and simple approach using a mixed solvent, ethanol and acetic acid. SANP were applied as a photoanodes material in DSCs using a metal-free organic dye (D149) or organometallic dye (N719) dyes. The dye loading (packing density) was examined in term of the isoelectric point (IEP) and the contribution of this, in addition to light scattering effects were shown to control the devices photovoltaic efficiency of the devices; specifically when compared with ones employing commercially available TiO2 nanoparticles (either transparent or a bilayer structure with a transparent layer and a scattering one). SANP photoanodes sensitized with D149 dye were found to be optimised at 10 µm, yielding photovoltaic conversion efficiencies of 6.9%, superior to for transparent or transparent + scattering films from the commercial source (5.6% and 5.9%, respectively). Further to this, an efficiency of 7.7% PCE was achieved using a SANP photoanode sensitized with N719 dye, with 7.2% seen for the transparent photoanode and 7.9% with a scattering layer. The high efficiencies of devices based on of SANP photoanode are attributed to the high dye loading capability in addition to good light scattering. A further point of interest is that even with the increased reactivity of the surface towards dye adsorption, we did not observe any significant increase in recombination with the redox mediator, presumably due to this increased dye loading providing better shielding.

| S-EPMC7952064 | biostudies-literature

Anatase TiO2 Nanoparticles with Exposed {001} Facets for Efficient Dye-Sensitized Solar Cells.

Project description:Anatase TiO2 nanoparticles with exposed {001} facets were synthesized from Ti powder via a sequential hydrothermal reaction process. At the first-step hydrothermal reaction, H-titanate nanowires were obtained in NaOH solution with Ti powder, and at second-step hydrothermal reaction, anatase TiO2 nanoparticles with exposed {001} facets were formed in NH4F solution. If the second-step hydrothermal reaction was carried out in pure water, the H-titanate nanowires were decomposed into random shape anatase-TiO2 nanostructures, as well as few impurity of H2Ti8O17 phase and rutile TiO2 phase. Then, the as-prepared TiO2 nanostructures synthesized in NH4F solution and pure water were applied to the photoanodes of dye-sensitized solar cells (DSSCs), which exhibited power conversion efficiency (PCE) of 7.06% (VOC of 0.756 V, JSC of 14.80 mA/cm(2), FF of 0.631) and 3.47% (VOC of 0.764 V, JSC of 6.86 mA/cm(2), FF of 0.662), respectively. The outstanding performance of DSSCs based on anatase TiO2 nanoparticles with exposed {001} facets was attributed to the high activity and large special surface area for excellent capacity of dye adsorption.

| S-EPMC4507182 | biostudies-literature

Performance Enhancement of CdS/CdSe Quantum Dot-Sensitized Solar Cells with (001)-Oriented Anatase TiO2 Nanosheets Photoanode.

Project description:CdS/CdSe quantum dot-sensitized solar cells (QDSSCs) were fabricated on two types of TiO2 photoanodes, namely nanosheets (NSs) and nanoparticles. The TiO2 NSs with high (001)-exposed facets were prepared via a hydrothermal method, while the TiO2 nanoparticles used the commercial Degussa P-25. It was found that the pore size, specific surface area, porosity, and electron transport properties of TiO2 NSs were generally superior to those of P-25. As a result, the TiO2 NS-based CdS/CdSe QDSSC has exhibited a power conversion efficiency of 4.42%, which corresponds to a 54% improvement in comparison with the P-25-based reference cell. This study provides an effective photoanode design using nanostructure approach to improve the performance of TiO2-based QDSSCs.

| S-EPMC6329687 | biostudies-other

3D hierarchical rutile TiO2 and metal-free organic sensitizer producing dye-sensitized solar cells 8.6% conversion efficiency.

Project description:Three-dimensional (3D) hierarchical nanoscale architectures comprised of building blocks, with specifically engineered morphologies, are expected to play important roles in the fabrication of 'next generation' microelectronic and optoelectronic devices due to their high surface-to-volume ratio as well as opto-electronic properties. Herein, a series of well-defined 3D hierarchical rutile TiO2 architectures (HRT) were successfully prepared using a facile hydrothermal method without any surfactant or template, simply by changing the concentration of hydrochloric acid used in the synthesis. The production of these materials provides, to the best of our knowledge, the first identified example of a ledgewise growth mechanism in a rutile TiO2 structure. Also for the first time, a Dye-sensitized Solar Cell (DSC) combining a HRT is reported in conjunction with a high-extinction-coefficient metal-free organic sensitizer (D149), achieving a conversion efficiency of 5.5%, which is superior to ones employing P25 (4.5%), comparable to state-of-the-art commercial transparent titania anatase paste (5.8%). Further to this, an overall conversion efficiency 8.6% was achieved when HRT was used as the light scattering layer, a considerable improvement over the commercial transparent/reflector titania anatase paste (7.6%), a significantly smaller gap in performance than has been seen previously.

| S-EPMC5385835 | biostudies-literature

Impact of TiO2 Nanostructures on Dye-Sensitized Solar Cells Performance.

Project description:The effect of TiO2 nanostructures such as nanoparticles, nanowires, nanotubes on photoanode properties, and dye-sensitized solar cells photovoltaic parameters were studied. The series of dye-sensitized solar cells based on two dyes, that is, commercially N719 and synthesized 3,7'-bis(2-cyano-1-acrylic acid)-10-ethyl-phenothiazine were tested. Additionally, the devices containing a mixture of this sensitizer and chenodeoxycholic acid as co-adsorbent were fabricated. The amount of adsorbed dye molecules to TiO2 was evaluated. The prepared photoanodes with different TiO2 nanostructures were investigated using UV-Vis spectroscopy, optical, atomic force, and scanning electron microscopes. Photovoltaic response of constructed devices was examined based on current-voltage characteristics and electrochemical impedance spectroscopy measurements. It was found that the highest UV-Vis absorption exhibited the photoanode with nanotubes addition. This indicates the highest number of sensitizer molecules anchored to the titanium dioxide photoanode, which was subsequently confirmed by dye-loading tests. The highest power conversion efficiency was (6.97%) for solar cell containing nanotubes and a mixture of the dyes with a co-adsorbent.

| S-EPMC8036646 | biostudies-literature

Effect of Au Nanoparticles and Scattering Layer in Dye-Sensitized Solar Cells Based on Freestanding TiO2 Nanotube Arrays.

Project description:The development of high efficiency dye-sensitized solar cells (DSSCs) has received tremendous attention. Many researchers have introduced new materials for use in DSSCs to achieve high efficiency. In this study, the change in power conversion efficiency (PCE) of DSSCs was investigated by introducing two types of materials-Au nanoparticles (Au NPs) and a scattering layer. A DSSC fabricated without neither Au NPs nor a scattering layer achieved a PCE of 5.85%. The PCE of a DSSC based on freestanding TiO2 nanotube arrays (f-TNTAs) with Au NPs was 6.50% due to better electron generation because the plasmonic absorption band of Au NPs is 530 nm, which matches the dye absorbance. Thus, more electrons were generated at 530 nm, which affected the PCE of the DSSC. The PCE of DSSCs based on f-TNTAs with a scattering layer was 6.61% due to better light harvesting by scattering. The scattering layer reflects all wavelengths of light that improve the light harvesting in the active layer in DSSCs. Finally, the PCE of DSSCs based on the f-TNTAs with Au NPs and a scattering layer was 7.12% due to the synergy of better electron generation and light harvesting by plasmonics and scattering. The application of Au NPs and a scattering layer is a promising research area for DSSCs as they can increase the electron generation and light harvesting ability.

| S-EPMC7911132 | biostudies-literature

Influence of Tin Doped TiO2 Nanorods on Dye Sensitized Solar Cells.

Project description:The one-step hydrothermal method was used to synthesize Sn-doped TiO2 (Sn-TiO2) thin films, in which the variation in Sn content ranged from 0 to 7-wt % and, further, its influence on the performance of a dye-sensitized solar cell (DSSC) photoanode was studied. The deposited samples were analyzed by X-ray diffraction (XRD) and Raman spectroscopy, which confirmed the existence of the rutile phase of the synthesized samples with crystallite size ranges in between 20.1 to 22.3 nm. In addition, the bare and Sn-TiO2 thin films showed nanorod morphology. A reduction in the optical band gap from 2.78 to 2.62 eV was observed with increasing Sn content. The X-ray photoelectron spectroscopy (XPS) analysis confirmed Sn4+ was successfully replaced at the Ti4+ site. The 3-wt % Sn-TiO2 based DSSC showed the optimum efficiency of 4.01%, which was superior to 0.87% of bare and other doping concentrations of Sn-TiO2 based DSSCs. The present work reflects Sn-TiO2 as an advancing material with excellent capabilities, which can be used in photovoltaic energy conversion devices.

| S-EPMC8585088 | biostudies-literature

ZnO Hierarchical Nanostructure Photoanode in a CdS Quantum Dot-Sensitized Solar Cell.

Project description:A hierarchical array of ZnO nanocones covered with ZnO nanospikes was hydrothermally fabricated and employed as the photoanode in a CdS quantum dot-sensitized solar cell (QDSSC). This QDSSC outperformed the QDSSC based on a simple ZnO nanocone photoanode in all the four principal photovoltaic parameters. Using the hierarchical photoanode dramatically increased the short circuit current density and also slightly raised the open circuit voltage and the fill factor. As a result, the conversion efficiency of the QDSSC based on the hierarchical photoanode was more than twice that of the QDSSC based on the simple ZnO nanocone photoanode. This improvement is attributable to both the enlarged specific area of the photoanode and the reduction in the recombination of the photoexcited electrons.

| S-EPMC4574909 | biostudies-literature

Metal-free organic dyes for TiO2 and ZnO dye-sensitized solar cells.

Project description:We report the synthesis and characterization of new metal-free organic dyes (namely B18, BTD-R, and CPTD-R) which designed with D-?-A concept to extending the light absorption region by strong conjugation group of ?-linker part and applied as light harvester in dye sensitized solar cells (DSSCs). We compared the photovoltaic performance of these dyes in two different photoanodes: a standard TiO2 mesoporous photoanode and a ZnO photoanode composed of hierarchically assembled nanostructures. The results demonstrated that B18 dye has better photovoltaic properties compared to other two dyes (BTD-R and CPTD-R) and each dye has higher current density (Jsc) when applied to hierarchical ZnO nanocrystallites than the standard TiO2 mesoporous film. Transient photocurrent and photovoltage decay measurements (TCD/TVD) were applied to systematically study the charge transport and recombination kinetics in these devices, showing the electron life time (?R) of B18 dye in ZnO and TiO2 based DSSCs is higher than CPTD-R and BTD-R based DSSCs, which is consistent with the photovoltaic performances. The conversion efficiency in ZnO based DSSCs can be further boosted by 35%, when a compact ZnO blocking layer (BL) is applied to inhibit electron back reaction.

| S-EPMC4704050 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data