Visualizing size-dependent deformation mechanism transition in Sn.

ABSTRACT: Displacive deformation via dislocation slip and deformation twinning usually plays a dominant role in the plasticity of crystalline solids at room temperature. Here we report in situ quantitative transmission electron microscope deformation tests of single crystal Sn samples. We found that when the sample size was reduced from 450 nm down to 130 nm, diffusional deformation replaces displacive plasticity as the dominant deformation mechanism at room temperature. At the same time, the strength-size relationship changed from "smaller is stronger" to "smaller is much weaker". The effective surface diffusivity calculated based on our experimental data matches well with that reported in literature for boundary diffusion. The observed change in the deformation mode arises from the sample size-dependent competition between the Hall-Petch-like strengthening of displacive processes and Coble diffusion softening processes. Our findings have important implications for the stability and reliability of nanoscale devices such as metallic nanogaps.

SUBMITTER: Tian L

PROVIDER: S-EPMC3699790 | biostudies-other | 2013

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Size-dependent deformation behavior in nanosized amorphous metals suggesting transition from collective to individual atomic transport.

Project description:The underlying atomistic mechanism of deformation is a central problem in mechanics and materials science. Whereas deformation of crystalline metals is fundamentally understood, the understanding of deformation of amorphous metals lacks behind, particularly identifying the involved temporal and spatial scales. Here, we reveal that at small scales the size-dependent deformation behavior of amorphous metals significantly deviates from homogeneous flow, exhibiting increasing deformation rate with reducing size and gradually shifted composition. This transition suggests the deformation mechanism changes from collective atomic transport by viscous flow to individual atomic transport through interface diffusion. The critical length scale of the transition is temperature dependent, exhibiting a maximum at the glass transition. While viscous flow does not discriminate among alloy constituents, diffusion does and the constituent element with higher diffusivity deforms faster. Our findings yield insights into nano-mechanics and glass physics and may suggest alternative processing methods to epitaxially grow metallic glasses.

| S-EPMC10522620 | biostudies-literature

Tension-dependent structural deformation alters single-molecule transition kinetics.

Project description:We analyze the response of a single nucleosome to tension, which serves as a prototypical biophysical measurement where tension-dependent deformation alters transition kinetics. We develop a statistical-mechanics model of a nucleosome as a wormlike chain bound to a spool, incorporating fluctuations in the number of bases bound, the spool orientation, and the conformations of the unbound polymer segments. With the resulting free-energy surface, we perform dynamic simulations that permit a direct comparison with experiments. This simple approach demonstrates that the experimentally observed structural states at nonzero tension are a consequence of the tension and that these tension-induced states cease to exist at zero tension. The transitions between states exhibit substantial deformation of the unbound polymer segments. The associated deformation energy increases with tension; thus, the application of tension alters the kinetics due to tension-induced deformation of the transition states. This mechanism would arise in any system where the tether molecule is deformed in the transition state under the influence of tension.

| S-EPMC3033304 | biostudies-literature

Size-Dependent Role of Surfaces in the Deformation of Platinum Nanoparticles.

Project description:The mechanical behavior of nanostructures is known to transition from a Hall-Petch-like "smaller-is-stronger" trend, explained by dislocation starvation, to an inverse Hall-Petch "smaller-is-weaker" trend, typically attributed to the effect of surface diffusion. Yet recent work on platinum nanowires demonstrated the persistence of the smaller-is-stronger behavior down to few-nanometer diameters. Here, we used in situ nanomechanical testing inside of a transmission electron microscope (TEM) to study the strength and deformation mechanisms of platinum nanoparticles, revealing the prominent and size-dependent role of surfaces. For larger particles with diameters from 41 nm down to approximately 9 nm, deformation was predominantly displacive yet still showed the smaller-is-weaker trend, suggesting a key role of surface curvature on dislocation nucleation. For particles below 9 nm, the weakening saturated to a constant value and particles deformed homogeneously, with shape recovery after load removal. Our high-resolution TEM videos revealed the role of surface atom migration in shape change during and after loading. During compression, the deformation was accommodated by atomic motion from lower-energy facets to higher-energy facets, which may indicate that it was governed by a confined-geometry equilibration; when the compression was removed, atom migration was reversed, and the original stress-free equilibrium shape was recovered.

| S-EPMC10173686 | biostudies-literature

Size-Dependent Melting Behavior of Colloidal In, Sn, and Bi Nanocrystals.

Project description:Colloidal nanocrystals are a technologically important class of nanostructures whose phase change properties have been largely unexplored. Here we report on the melting behavior of In, Sn, and Bi nanocrystals dispersed in a polymer matrix. This polymer matrix prevents the nanocrystals from coalescing with one another and enables previously unaccessed observations on the melting behavior of colloidal nanocrystals. We measure the melting temperature, melting enthalpy, and melting entropy of colloidal nanocrystals with diameters of approximately 10 to 20?nm. All of these properties decrease as nanocrystal size decreases, although the depression rate for melting temperature is comparatively slower than that of melting enthalpy and melting entropy. We also observe an elevated melting temperature during the initial melt-freeze cycle that we attribute to surface stabilization from the organic ligands on the nanocrystal surface. Broad endothermic melting valleys and very large supercoolings in our calorimetry data suggest that colloidal nanocrystals exhibit a significant amount of surface pre-melting and low heterogeneous nucleation probabilities during freezing.

| S-EPMC4648084 | biostudies-other

DRM2 mediates CHH DNA methylation via a substrate deformation mechanism

Project description:This study investigated the structural basis for DRM2 mediated CHH methylation in Arabidopsis thaliana

2021-05-01 | GSE146700 | GEO

Effects of Pore Size on Fatigue Deformation Mechanism of Open-Cell Copper Foam at Low Stress Amplitude.

Project description:Axial compression-compression fatigue experiments on open-cell copper foams with different pore size were investigated in this paper. The effects of the strain amplitude on the fatigue properties were studied and found that there is an exponential relationship between the fatigue life and strain amplitude. The experimental results indicate that a smaller pore size is related to a lower fatigue life. The microstructures of failed copper foam tested at low stress amplitude were observed by optical microscope and scanning electron microscopy (SEM), suggests that different pore size related to different fatigue behavior. The fatigue failure mechanism of the open-cell copper foams were compared by experimental research.

| S-EPMC6164098 | biostudies-literature

Size-dependent phase transition in methylammonium lead iodide perovskite microplate crystals.

Project description:Methylammonium lead iodide perovskite has attracted considerable recent interest for solution processable solar cells and other optoelectronic applications. The orthorhombic-to-tetragonal phase transition in perovskite can significantly alter its optical, electrical properties and impact the corresponding applications. Here, we report a systematic investigation of the size-dependent orthorhombic-to-tetragonal phase transition using a combined temperature-dependent optical, electrical transport and transmission electron microscopy study. Our studies of individual perovskite microplates with variable thicknesses demonstrate that the phase transition temperature decreases with reducing microplate thickness. The sudden decrease of mobility around phase transition temperature and the presence of hysteresis loops in the temperature-dependent mobility confirm that the orthorhombic-to-tetragonal phase transition is a first-order phase transition. Our findings offer significant fundamental insight on the temperature- and size-dependent structural, optical and charge transport properties of perovskite materials, and can greatly impact future exploration of novel electronic and optoelectronic devices from these materials.

| S-EPMC4844678 | biostudies-literature

Visualizing cell state transition using Raman spectroscopy.

Project description:System level understanding of the cell requires detailed description of the cell state, which is often characterized by the expression levels of proteins. However, understanding the cell state requires comprehensive information of the cell, which is usually obtained from a large number of cells and their disruption. In this study, we used Raman spectroscopy, which can report changes in the cell state without introducing any label, as a non-invasive method with single cell capability. Significant differences in Raman spectra were observed at the levels of both the cytosol and nucleus in different cell-lines from mouse, indicating that Raman spectra reflect differences in the cell state. Difference in cell state was observed before and after the induction of differentiation in neuroblastoma and adipocytes, showing that Raman spectra can detect subtle changes in the cell state. Cell state transitions during embryonic stem cell (ESC) differentiation were visualized when Raman spectroscopy was coupled with principal component analysis (PCA), which showed gradual transition in the cell states during differentiation. Detailed analysis showed that the diversity between cells are large in undifferentiated ESC and in mesenchymal stem cells compared with terminally differentiated cells, implying that the cell state in stem cells stochastically fluctuates during the self-renewal process. The present study strongly indicates that Raman spectral morphology, in combination with PCA, can be used to establish cells' fingerprints, which can be useful for distinguishing and identifying different cellular states.

| S-EPMC3883674 | biostudies-literature

The sample size effect in metallic glass deformation.

Project description:The sample size effect on deformation mode of glasses is one of the most misunderstood properties of this class of material. This effect is intriguing, since materials deemed macroscopically brittle become plastic at small size. We propose an explanation of this phenomenon for metallic glasses. A thermodynamic description of the local rearrangement zones activated under an applied stress is proposed. Using the Poisson distribution to describe the statistics of these zones and the statistical physics to associate entropy, we define a critical sample size for the change in the deformation mode. Predictions are in agreement with experimental observations and reveal hidden structural parameters describing the glassy state.

| S-EPMC7330049 | biostudies-literature

Inverse size scaling of the nucleolus by a concentration-dependent phase transition.

Project description:Just as organ size typically increases with body size, the size of intracellular structures changes as cells grow and divide. Indeed, many organelles, such as the nucleus [1, 2], mitochondria [3], mitotic spindle [4, 5], and centrosome [6], exhibit size scaling, a phenomenon in which organelle size depends linearly on cell size. However, the mechanisms of organelle size scaling remain unclear. Here, we show that the size of the nucleolus, a membraneless organelle important for cell-size homeostasis [7], is coupled to cell size by an intracellular phase transition. We find that nucleolar size directly scales with cell size in early C. elegans embryos. Surprisingly, however, when embryo size is altered, we observe inverse scaling: nucleolar size increases in small cells and decreases in large cells. We demonstrate that this seemingly contradictory result arises from maternal loading of a fixed number rather than a fixed concentration of nucleolar components, which condense into nucleoli only above a threshold concentration. Our results suggest that the physics of phase transitions can dictate whether an organelle assembles, and, if so, its size, providing a mechanistic link between organelle assembly and cell size. Since the nucleolus is known to play a key role in cell growth, this biophysical readout of cell size could provide a novel feedback mechanism for growth control.

| S-EPMC4348177 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data