First-principles prediction and experimental verification of glass-forming ability in Zr-Cu binary metallic glasses.
Ontology highlight
ABSTRACT:
SUBMITTER: Yu CY
PROVIDER: S-EPMC3699808 | biostudies-other | 2013
REPOSITORIES: biostudies-other
Similar Datasets
Project description:Glass is a freezing phase of a deeply supercooled liquid. Despite its simple definition, the origin of glass forming ability (GFA) is still ambiguous, even for binary Cu-Zr alloys. Here, we directly study the stability of the supercooled Cu-Zr liquids where we find that Cu64Zr36 at a supercooled temperature shows deeper undercoolability and longer persistence than other neighbouring compositions with an equivalent driving Gibbs free energy. This observation implies that the GFA of the Cu-Zr alloys is significantly affected by crystal-liquid interfacial free energy. In particular, the crystal-liquid interfacial free energy of Cu64Zr36 in our measurement was higher than that of other neighbouring liquids and, coincidently a molecular dynamics simulation reveals a larger glass-glass interfacial energy value at this composition, which reflects more distinct configuration difference between liquid and crystal phase. The present results demonstrate that the higher crystal-liquid interfacial free energy is a prerequisite of good GFA of the Cu-Zr alloys.
| S-EPMC4044622 | biostudies-literature
Project description:It is known that the glass forming-ability (GFA) of bulk metallic glasses (BMGs) can be greatly enhanced via minor element additions. However, direct evidence has been lacking to reveal its structural origin despite different theories hitherto proposed. Through the high-resolution transmission-electron-microscopy (HRTEM) analysis, here we show that the content of local crystal-like orders increases significantly in a Cu-Zr-Al BMG after a 2-at% Y addition. Contrasting the previous studies, our current results indicate that the formation of crystal-like order at the atomic scale plays an important role in enhancing the GFA of the Cu-Zr-Al base BMG.
| S-EPMC3983660 | biostudies-literature
Project description:The analysis of the enthalpy changes for vaporization (?Hvap) of Al-based metallic glass (MG) can provide insight into the origin of the MG's glass forming ability (GFA). The ?Hvap of three Al-based MGs, Al84.5 ± x(Y10Ni5.5)15.5 ± x, Al85 ± x(Y8Ni5Co2)15 ± x, and Al86 ± x(Y4.5Ni6Co2La1.5)14 ± x, (hereafter referred to as AYNx, AYNCx, and AYNCLx, respectively), is analyzed by measuring their weight losses below their glass transition temperatures. The relationship between ?Hvap and aluminum concentration exhibit minimum values in the range of 83-85?at.% of Al, and the ?Hvap increases, becoming saturated at 320-350?kJ/mol, as the percentage of Al deviates from this range. The depth of the enthalpy well, referring to the bottom of the parabolic graph of ?Hvap against the Al concentration, is proportional to the viscosity of clusters showing liquid-like behavior. The amount of weight loss is proportional to the concentration of these clusters. The cluster viscosity and concentration influences the overall viscosity of the MGs, and thus determines the GFA.
| S-EPMC7058064 | biostudies-literature
Project description:The use of machine learning techniques to expedite the discovery and development of new materials is an essential step towards the acceleration of a new generation of domain-specific highly functional material systems. In this paper, we use the test case of bulk metallic glasses to highlight the key issues in the field of high throughput predictions and propose a new probabilistic analysis of rules for glass forming ability using rough set theory. This approach has been applied to a broad range of binary alloy compositions in order to predict new metallic glass compositions. Our data driven approach takes into account not only a broad variety of thermodynamic, structural and kinetic based criteria, but also incorporates qualitative and descriptive attributes associated with eutectic points in phase diagrams. For the latter, we demonstrate the use of automated machine learning methods that go far beyond text recognition approaches by also being able to interpret phase diagrams. When combined with structural descriptors, this approach provides the foundations to develop a hierarchical probabilistic predication tool that can rank the feasibility of glass formation.
| S-EPMC6344582 | biostudies-literature
Project description:Metallic alloys are normally composed of multiple constituent elements in order to achieve integration of a plurality of properties required in technological applications. However, conventional alloy development paradigm, by sequential trial-and-error approach, requires completely unrelated strategies to optimize compositions out of a vast phase space, making alloy development time consuming and labor intensive. Here, we challenge the conventional paradigm by proposing a combinatorial strategy that enables parallel screening of a multitude of alloys. Utilizing a typical metallic glass forming alloy system Zr-Cu-Al-Ag as an example, we demonstrate how glass formation and antibacterial activity, two unrelated properties, can be simultaneously characterized and the optimal composition can be efficiently identified. We found that in the Zr-Cu-Al-Ag alloy system fully glassy phase can be obtained in a wide compositional range by co-sputtering, and antibacterial activity is strongly dependent on alloy compositions. Our results indicate that antibacterial activity is sensitive to Cu and Ag while essentially remains unchanged within a wide range of Zr and Al. The proposed strategy not only facilitates development of high-performing alloys, but also provides a tool to unveil the composition dependence of properties in a highly parallel fashion, which helps the development of new materials by design.
| S-EPMC4882501 | biostudies-literature
Project description:Forming complex geometries using the casting process is a big challenge for bulk metallic glasses (BMGs), because of a lack of time of the window for shaping under the required high cooling rate. In this work, we open an approach named the "entire process vacuum high pressure die casting" (EPV-HPDC), which delivers the ability to fill die with molten metal in milliseconds, and create solidification under high pressure. Based on this process, various Zr-based BMGs were prepared by using industrial grade raw material. The results indicate that the EPV-HPDC process is feasible to produce a glassy structure for most Zr-based BMGs, with a size of 3 mm × 10 mm and with a high strength. In addition, it has been found that EPV-HPDC process allows complex industrial BMG parts, some of which are hard to be formed by any other metal processes, to be net shaped precisely. The BMG components prepared by the EVP-HPDC process possess the advantages of dimensional accuracy, efficiency, and cost compared with the ones formed by other methods. The EVP-HPDC process paves the way for the large-scale application of BMGs.
| S-EPMC6265695 | biostudies-literature
Project description:The appearance of thin film metallic glasses (TFMGs) is gaining increasing interest because of their unique mechanical and anticorrosion properties and potential engineering applications. In this study, Cu-Zr-Al ternary thin film metallic glasses were fabricated by using DC magnetron sputtering equipment with various target powers. The evolution of the structure was systematically investigated by grazing incidence X-ray diffractometer, scanning electron microscopy, and transmission electron microscopy. The deposition rate increases with the increasing of applied target power. The as-deposited thin films show an amorphous structure. The compositional fluctuations on the nanometer scale indicate the presence of two Cu- and Zr-rich amorphous phases. The electrochemical corrosion measurements indicated that Cu-Zr-Al thin film metallic glasses had good corrosion resistance in the sulfuric acid solution. Nanoindentation results showed that the mechanical deformation was found to be homogenous and reproducible with a high value range for the hardness and modulus.
| S-EPMC6947152 | biostudies-literature
Project description:In the present study, we investigated the role of an aliovalent dopant upon stabilizing the amorphous oxide film. We added beryllium into the Zr50Cu50 metallic glass system, and found that the amorphous oxide layer of Be-rich phase can be stabilized even at elevated temperature above Tg of the glass matrix. The thermal stability of the amorphous oxide layer is substantially enhanced due to Be addition. As confirmed by high-temperature cross-section HR-TEM, fully disordered Be-added amorphous layer is observed, while the rapid crystallization is observed without Be. To understand the role of Be, we employed ab-initio molecular dynamics to compare the mobility of ions with/without Be dopant, and propose a disordered model where Be dopant occupies Zr vacancy and induces structural disorder to the amorphous phase. We find that the oxygen mobility is slightly suppressed due to Be dopant, and Be mobility is unexpectedly lower than that of oxygen, which we attribute to the aliovalent nature of Be dopant whose diffusion always accompany multiple counter-diffusion of other ions. Here, we explain the origin of superior thermal stability of amorphous oxide film in terms of enhanced structural disorder and suppressed ionic mobility due to the aliovalent dopant.
| S-EPMC4677381 | biostudies-other
Project description:Zirconium–Copper-based metallic glass thin films represent promising coatings in the biomedical sector for their combination of antibacterial property and wear resistance. However, finding a Zr–Cu metallic glass composition with desirable cytocompatibility and antibacterial property is extremely challenging. In this work, we have created a cytocompatible and (super-)hydrophobic Zr–Cu–Ag metallic glass coating with ≈95% antifouling properties. First, a range of different chemical compositions were prepared via Physical Vapor Deposition magnetron by co-sputtering Zr, Cu, and Ag onto a Polybutylene terephthalate (PBT) substrate among which Zr93·5Cu6·2Ag0.2, Zr76·7Cu22·7Ag0.5, and Zr69·3Cu30·1Ag0.6 were selected to be further investigate for their surface properties, antibacterial activity, and cytocompatibility. Scanning electron microscopy (SEM) images revealed a micro-roughness fibrous structure holding superhydrophobic properties demonstrated by specimens' static and dynamic contact angle measurements ranging from 130° to 150°. The dynamic contact angle measurements have shown hysteresis below 10° for all coated samples which indicated the superhydrophobicity of the samples. To distinguish between antifouling and bactericidal effect of the coating, ions release from coatings into Luria Bertani Broth (LB), and Dulbecco's Modified Eagle Medium (DMEM) solutions were evaluated by inductively coupled plasma mass spectrometry (ICP-MS) measurements after 24 h and 5 days. Antifouling properties were evaluated by infecting the specimens' surface with the Gram-positive Staphylococcus aureus and the Gram-negative Escherichia coli strain reporting a ≈95% reduction of bacteria adhesion as visually confirmed by FESEM and fluorescent live/dead staining. Human mesenchymal stem cells (hMSC) were used for direct cytocompatibility evaluation of coated samples and their metabolic activity was evaluated via relative fluorescence unit after 24 h and 5 days confirming that it was comparable to the controls (>97% viable cells). The results were further visualized by FESEM, fluorescent staining by Live/Dead Viability/Cytotoxicity Kit and confirmed the cytocompatibility of all coated samples. Finally, hMSC′ cytoplasm was stained by May Grunwald and Giemsa after 5days to detect and visualize the released ions which have diffused through the cells' membrane. Graphical abstract Image 1
| S-EPMC8573186 | biostudies-literature
Project description:Bulk metallic glasses (BMGs) are known to have extraordinary merits such as ultrahigh strength and dynamic toughness etc. but tied to the detrimental brittleness, which has become a critical issue to the engineering application and understanding the glass nature. In this article, we report a new class of Zr-Cu-Al-Mo BMGs with extraordinary plastic strain above 20%. "Work-hardening" effect after yielding in a wide range of plastic deformation process has been detected for this kind of BMGs. Compositional heterogeneity, which can be classified into ZrMo- and Cu-rich zones, was differentiated in this kind of BMG. Pronounced humps have been observed on the high frequency kinetic spectrum in Mo containing BMGs, which is the indicator of β-relaxation transition. The underlying mechanism for the excellent plastic deforming ability of this class of BMGs is ascribed to the synergistic effects of soft ZrMo-rich glass formed through phase separation and abundant flow units which related to β-relaxation.
| S-EPMC5430678 | biostudies-literature