Nanoporous gold as an active low temperature catalyst toward CO oxidation in hydrogen-rich stream.

ABSTRACT: Preferential CO oxidation (PROX) was investigated by using dealloyed nanoporous gold (NPG) catalyst under ambient conditions. Systematic investigations were carried out to characterize its catalytic performance by varying reaction parameters such as temperature and co-existence of CO2 and H2O, which revealed that NPG was a highly active and selective catalyst for PROX, especially at low temperature. At 20°C, the exit CO concentration could be reduced to less than 2 ppm with a turnover frequency of 4.1 × 10(-2) s(-1) at a space velocity of 120,000 mL h(-1) g(-1)cat. and its high activity could retain for more than 24 hours. The presence of residual Ag species in the structure did not seem to improve the intrinsic activity of NPG for PROX; however, they contributed to the stabilization of the NPG structure and apparent catalytic activity. These results indicated that NPG might be readily applicable for hydrogen purification in fuel cell applications.

SUBMITTER: Li D

PROVIDER: S-EPMC3804851 | biostudies-other | 2013

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Toward digitally controlled catalyst architectures: Hierarchical nanoporous gold via 3D printing.

Project description:Monolithic nanoporous metals, derived from dealloying, have a unique bicontinuous solid/void structure that provides both large surface area and high electrical conductivity, making them ideal candidates for various energy applications. However, many of these applications would greatly benefit from the integration of an engineered hierarchical macroporous network structure that increases and directs mass transport. We report on 3D (three-dimensional)-printed hierarchical nanoporous gold (3DP-hnp-Au) with engineered nonrandom macroarchitectures by combining 3D printing and dealloying. The material exhibits three distinct structural length scales ranging from the digitally controlled macroporous network structure (10 to 1000 μm) to the nanoscale pore/ligament morphology (30 to 500 nm) controlled by dealloying. Supercapacitance, pressure drop, and catalysis measurements reveal that the 3D hierarchical nature of our printed nanoporous metals markedly improves mass transport and reaction rates for both liquids and gases. Our approach can be applied to a variety of alloy systems and has the potential to revolutionize the design of (electro-)chemical plants by changing the scaling relations between volume and catalyst surface area.

| S-EPMC6118649 | biostudies-literature

Promotion of Pt/CeO<sub>2</sub> catalyst by hydrogen treatment for low-temperature CO oxidation.

Project description:Low temperature CO oxidation reaction is known to be facilitated over platinum supported on a reducible cerium oxide. Pt species act as binding sites for reactant CO molecules, and oxygen vacancies on surface of cerium oxide atomically activate the reactant O2 molecules. However, the impacts of size of Pt species and concentration of oxygen vacancy at the surface of cerium oxide on the CO oxidation reaction have not been clearly distinguished, thereby various diverse approaches have been suggested to date. Here using the co-precipitation method we have prepared pure ceria support and infiltrated it with Pt solution to obtain 0.5 atomic% Pt supported on cerium oxide catalyst, and then systematically varied the size of Pt from single atom to ∼1.7 nm sized nanoparticles and oxygen vacancy concentration at surface of cerium oxide by controlling the heat-treatment conditions, which are temperature and oxygen partial pressure. It is found that Pt nanoparticles in range of 1-1.7 nm achieve 100% of CO oxidation reaction at ∼100 °C lower temperature compared to Pt single atom owing to the facile adsorption of CO but weaker binding strength between Pt and CO molecules, and the oxygen vacancy in the vicinity of Pt accelerates CO oxidation below 150 °C. Based on this understanding, we show that a simple hydrogen reduction at 550 °C for the single atom Pt supported on CeO2 catalyst induces the formation of highly dispersed Pt nanoparticles with size of 1.7 ± 0.2 nm and the higher concentration of surface oxygen vacancies simultaneously, enabling 100% conversion from CO to CO2 at 200 °C as well as 16% conversion even at 150 °C owing to the synergistic effects of Pt nanoparticles and oxygen vacancies.

| S-EPMC9070415 | biostudies-literature

Complex Three-Dimensional Co?O? Nano-Raspberry: Highly Stable and Active Low-temperature CO Oxidation Catalyst.

Project description:Highly stable and active low-temperature CO oxidation catalysts without noble metals are desirable to achieve a sustainable society. While zero-dimensional to three-dimensional Co?O? nanoparticles show high catalytic activity, simple-structured nanocrystals easily self-aggregate and become sintered during catalytic reaction. Thus, complex three-dimensional nanostructures with high stability are of considerable interest. However, the controlled synthesis of complex nanoscale shapes remains a great challenge as no synthesis theory has been established. In this study, 100 nm raspberry-shaped nanoparticles composed of 7?8 nm Co?O? nanoparticles were synthesized by hydrothermally treating cobalt glycolate solution with sodium sulfate. Surface single nanometer-scale structures with large surface areas of 89 m²·g-1 and abundant oxygen vacancies were produced. The sulfate ions functioned as bridging ligands to promote self-assembly and suppress particle growth. The Co?O? nano-raspberry was highly stable under catalytic tests at 350 °C and achieved nearly 100% CO conversion at room temperature. The addition of bridging ligands is an effective method to control the formation of complex but ordered three-dimensional nanostructures that possessed extreme thermal and chemical stability and exhibited high performance.

| S-EPMC6164048 | biostudies-literature

Tungsten-Embedded Graphene: Theoretical Study on a Potential High-Activity Catalyst toward CO Oxidation.

Project description:The oxidation mechanism of CO on W-embedded graphene was investigated by M06-2X density functional theory. Two models of tungsten atom embedded in single and double vacancy (W-SV and W-DV) graphene sheets were considered. It was found that over W-SV-graphene and W-DV-graphene, the oxidation of CO prefers to Langmuir-Hinshelwood (LH) and Eley-Rideal (ER) mechanism, respectively. The two surfaces exhibit different catalytic activity during different reaction stages. The present results imply that W-embedded graphene is a promising catalyst for CO oxidation, which provides a useful reference for the design of a high-efficiency catalyst in detecting and removing of toxic gases.

| S-EPMC6213162 | biostudies-literature

Gold oxide formation on Au(111) under CO oxidation conditions at room temperature.

Project description:Although gold-based catalysts are promising candidates for selective low-temperature CO oxidation, the reaction mechanism is not fully understood. On a Au(111) model catalyst, we observe the formation of gold oxide islands under exposure to atmospheric pressures of oxygen or CO oxidation reaction conditions in an in situ scanning tunneling microscope. The gold oxide formation is interpreted in line with the water-enabled dissociation of O2 on the step edges of Au(111). Contaminants on the gold surface can strongly promote the gold oxide formation even on the terraces. On the other hand, TiO2 nanoparticles on the Au(111) do not show any influence on the formation of the gold oxide and are thus not providing a significant amount of atomic oxygen to the gold at room temperature. Overall, the presence of gold oxide is likely under industrial conditions.

| S-EPMC11359969 | biostudies-literature

Catalytic activity of nanostructured Au: Scale effects versus bimetallic/bifunctional effects in low-temperature CO oxidation on nanoporous Au.

Project description:The catalytic properties of nanostructured Au and their physical origin were investigated by using the low-temperature CO oxidation as a test reaction. In order to distinguish between structural effects (structure-activity correlations) and bimetallic/bifunctional effects, unsupported nanoporous gold (NPG) samples prepared from different Au alloys (AuAg, AuCu) by selective leaching of a less noble metal (Ag, Cu) were employed, whose structure (surface area, ligament size) as well as their residual amount of the second metal were systematically varied by applying different potentials for dealloying. The structural and chemical properties before and after 1000 min reaction were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). The catalytic behavior was evaluated by kinetic measurements in a conventional microreactor and by dynamic measurements in a temporal analysis of products (TAP) reactor. The data reveal a clear influence of the surface contents of residual Ag and Cu species on both O2 activation and catalytic activity, while correlations between activity and structural parameters such as surface area or ligament/crystallite size are less evident. Consequences for the mechanistic understanding and the role of the nanostructure in these NPG catalysts are discussed.

| S-EPMC3596058 | biostudies-literature

Ag surface segregation in nanoporous Au catalysts during CO oxidation.

Project description:The present study focuses on the modification of surface compositional profiles induced in nanoporous (NP) Au catalysts by the catalytic oxidation of carbon monoxide to carbon dioxide in the presence of oxygen. The phenomenon has deep implications concerning the catalytic behavior of NP Au foams in particular, and more in general for the design of more efficient catalysts. Aimed at gaining deeper insight into the mechanisms governing surface segregation, we exposed NP Au foams containing residual Ag to a mixture of gaseous carbon monoxide and oxygen at different temperature. Structural and surface composition analyses pointed out the concomitant occurrence of both NP Au coarsening and Ag surface segregation processes. Experimental findings suggest for Ag surface segregation a two-stage kinetics. During the initial, rapid coarsening of the NP Au structure, Ag surface segregation is mediated by surface rearrangements, which allow the Ag atoms to reach the surface at anomalously fast rate. As coarsening decelerates, the slower diffusion of buried Ag atoms towards the surface predominates, due to favorable chemical interactions with adsorbed oxygen. This novel mechanism's understanding can benefit strategic areas of science and technology.

| S-EPMC6185915 | biostudies-literature

Octahedral gold-silver nanoframes with rich crystalline defects for efficient methanol oxidation manifesting a CO-promoting effect.

Project description:Three-dimensional bimetallic nanoframes with high spatial diffusivity and surface heterogeneity possess remarkable catalytic activities owing to their highly exposed active surfaces and tunable electronic structure. Here we report a general one-pot strategy to prepare ultrathin octahedral Au3Ag nanoframes, with the formation mechanism explicitly elucidated through well-monitored temporal nanostructure evolution. Rich crystalline defects lead to lowered atomic coordination and varied electronic states of the metal atoms as evidenced by extensive structural characterizations. When used for electrocatalytic methanol oxidation, the Au3Ag nanoframes demonstrate superior performance with a high specific activity of 3.38?mA?cm-2, 3.9 times that of the commercial Pt/C. More intriguingly, the kinetics of methanol oxidation on the Au3Ag nanoframes is counter-intuitively promoted by carbon monoxide. The enhancement is ascribed to the altered reaction pathway and enhanced OH- co-adsorption on the defect-rich surfaces, which can be well understood from the d-band model and comprehensive density functional theory simulations.

| S-EPMC6706449 | biostudies-literature

Low-Temperature Vapor-Phase Synthesis of Single-Crystalline Gold Nanostructures: Toward Exceptional Electrocatalytic Activity for Methanol Oxidation Reaction.

Project description:Au nanostructures (Au NSs) have been considered promising materials for applications in fuel cell catalysis, electrochemistry, and plasmonics. For the fabrication of high-performance Au NS-based electronic or electrochemical devices, Au NSs should have clean surfaces and be directly supported on a substrate without any mediating molecules. Herein, we report the vapor-phase synthesis of Au NSs on a fluorine-doped tin oxide (FTO) substrate at 120 °C and their application to the electrocatalytic methanol oxidation reaction (MOR). By employing AuCl as a precursor, the synthesis temperature for Au NSs was reduced to under 200 °C, enabling the direct synthesis of Au NSs on an FTO substrate in the vapor phase. Considering that previously reported vapor-phase synthesis of Au NSs requires a high temperature over 1000 °C, this proposed synthetic method is remarkably simple and practical. Moreover, we could selectively synthesize Au nanoparticles (NPs) and nanoplates by adjusting the location of the substrate, and the size of the Au NPs was controllable by changing the reaction temperature. The synthesized Au NSs are a single-crystalline material with clean surfaces that achieved a high methanol oxidation current density of 14.65 mA/cm² when intimately supported by an FTO substrate. We anticipate that this novel synthetic method can widen the applicability of vapor-phase synthesized Au NSs for electronic and electrochemical devices.

| S-EPMC6523424 | biostudies-literature

Transition-Metal Doped Ceria Microspheres with Nanoporous Structures for CO Oxidation.

Project description:Catalytic oxidation of carbon monoxide (CO) is of great importance in many different fields of industry. Until now it still remains challenging to use non-noble metal based catalysts to oxidize CO at low temperature. Herein, we report a new class of nanoporous, uniform, and transition metal-doped cerium (IV) oxide (ceria, CeO2) microsphere for CO oxidation catalysis. The porous and uniform microsphere is generated by sacrificed polymer template. Transition-metals, like Cu, Co, Ni, Mn and Fe, were doped into CeO2 microspheres. The combination of hierarchical structure and metal doping afford superior catalytic activities of the doped ceria microspheres, which could pave a new way to advanced non-precious metal based catalysts for CO oxidation.

| S-EPMC4814921 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data