Interface properties of organic para-hexaphenyl/?-sexithiophene heterostructures deposited on highly oriented pyrolytic graphite.

ABSTRACT: It was recently reported, that heterostructures of para-hexaphenyl (p-6P) and ?-sexithiophene (6T) deposited on muscovite mica exhibit the intriguing possibility to prepare lasing nanofibers of tunable emission wavelength. For p-6P/6T heterostructures, two different types of 6T emission have been observed, namely, the well-known red emission of bulk 6T crystals and additionally a green emission connected to the interface between p-6P and 6T. In this study, the origin of the green fluorescence is investigated by photoelectron spectroscopy (PES). As a prerequisite, it is necessary to prepare structurally similar organic crystals on a conductive surface, which leads to the choice of highly oriented pyrolytic graphite (HOPG) as a substrate. The similarity between p-6P/6T heterostructures on muscovite mica and on HOPG is evidenced by X-ray diffraction (XRD), scanning force microscopy (SFM), and optical spectroscopy. PES measurements show that the interface between p-6P and 6T crystals is sharp on a molecular level without any sign of interface dipole formation or chemical interaction between the molecules. We therefore conclude that the different emission colors of the two 6T phases are caused by different types of molecular aggregation.

SUBMITTER: Schwabegger G

PROVIDER: S-EPMC3842851 | biostudies-other | 2013 Nov

REPOSITORIES: biostudies-other

ACCESS DATA

Publications

Interface properties of organic para-hexaphenyl/α-sexithiophene heterostructures deposited on highly oriented pyrolytic graphite.

Schwabegger Günther G Oehzelt Martin M Salzmann Ingo I Quochi Francesco F Saba Michele M Mura Andrea A Bongiovanni Giovanni G Vollmer Antje A Koch Norbert N Sitter Helmut H Simbrunner Clemens C

Langmuir : the ACS journal of surfaces and colloids 20131111 47

It was recently reported, that heterostructures of para-hexaphenyl (p-6P) and α-sexithiophene (6T) deposited on muscovite mica exhibit the intriguing possibility to prepare lasing nanofibers of tunable emission wavelength. For p-6P/6T heterostructures, two different types of 6T emission have been observed, namely, the well-known red emission of bulk 6T crystals and additionally a green emission connected to the interface between p-6P and 6T. In this study, the origin of the green fluorescence is ...[more]

PMID: 24156627

Similar Datasets

Project description:Dual-ion batteries (DIBs) generally operate beyond 4.7 V vs Li+/Li0 and rely on the intercalation of both cations and anions in graphite electrodes. Major challenges facing the development of DIBs are linked to electrolyte decomposition at the cathode-electrolyte interface (CEI), graphite exfoliation, and corrosion of Al current collectors. In this work, X-ray photoelectron spectroscopy (XPS) is employed to gain a broad understanding of the nature and dynamics of the CEI built on anion-intercalated graphite cycled both in highly concentrated electrolytes (HCEs) of common lithium salts (LiPF6, LiFSI, and LiTFSI) in carbonate solvents and in a typical ionic liquid. Though Al metal current collectors were adequately stable in all HCEs, the Coulombic efficiency was substantially higher for HCEs based on LiFSI and LiTFSI salts. Specific capacities ranging from 80 to 100 mAh g-1 were achieved with a Coulombic efficiency above 90% over extended cycling, but cells with LiPF6-based electrolytes were characterized by <70% Coulombic efficiency and specific capacities of merely ca. 60 mAh g-1. The poor performance in LiPF6-containing electrolytes is indicative of the continual buildup of decomposition products at the interface due to oxidation, forming a thick interfacial layer rich in LixPFy, POxFy, LixPOyFz, and organic carbonates as evidenced by XPS. In contrast, insights from XPS analyses suggested that anion intercalation and deintercalation processes in the range from 3 to 5.1 V give rise to scant or extremely thin surface layers on graphite electrodes cycled in LiFSI- and LiTFSI-containing HCEs, even allowing for probing anions intercalated in the near-surface bulk. In addition, ex situ Raman, SEM and TEM characterizations revealed the presence of a thick coating on graphite particles cycled in LiPF6-based electrolytes regardless of salt concentration, while hardly any surface film was observed in the case of concentrated LiFSI and LiTFSI electrolytes.

Dataset Information

Interface properties of organic para-hexaphenyl/?-sexithiophene heterostructures deposited on highly oriented pyrolytic graphite.

Publications

Interface properties of organic para-hexaphenyl/α-sexithiophene heterostructures deposited on highly oriented pyrolytic graphite.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets