Electromagnetic wave absorbing properties of amorphous carbon nanotubes.

ABSTRACT: Amorphous carbon nanotubes (ACNTs) with diameters in the range of 7-50 nm were used as absorber materials for electromagnetic waves. The electromagnetic wave absorbing composite films were prepared by a dip-coating method using a uniform mixture of rare earth lanthanum nitrate doped ACNTs and polyvinyl chloride (PVC). The microstructures of ACNTs and ACNT/PVC composites were characterized using transmission electron microscope and X-ray diffraction, and their electromagnetic wave absorbing properties were measured using a vector-network analyzer. The experimental results indicated that the electromagnetic wave absorbing properties of ACNTs are superior to multi-walled CNTs, and greatly improved by doping 6 wt% lanthanum nitrate. The reflection loss (R) value of a lanthanum nitrate doped ACNT/PVC composite was -25.02 dB at 14.44 GHz, and the frequency bandwidth corresponding to the reflector loss at -10 dB was up to 5.8 GHz within the frequency range of 2-18 GHz.

SUBMITTER: Zhao T

PROVIDER: S-EPMC4090627 | biostudies-other | 2014

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Superb electromagnetic wave-absorbing composites based on large-scale graphene and carbon nanotube films.

Project description:ABSTARCT:Graphene has sparked extensive research interest for its excellent physical properties and its unique potential for application in absorption of electromagnetic waves. However, the processing of stable large-scale graphene and magnetic particles on a micrometer-thick conductive support is a formidable challenge for achieving high reflection loss and impedance matching between the absorber and free space. Herein, a novel and simple approach for the processing of a CNT film-Fe3O4-large scale graphene composite is studied. The Fe3O4 particles with size in the range of 20-200 nm are uniformly aligned along the axial direction of the CNTs. The composite exhibits exceptionally high wave absorption capacity even at a very low thickness. Minimum reflection loss of -44.7 dB and absorbing bandwidth of 4.7 GHz at -10 dB are achieved in composites with one-layer graphene in six-layer CNT film-Fe3O4 prepared from 0.04 M FeCl3. Microstructural and theoretical studies of the wave-absorbing mechanism reveal a unique Debye dipolar relaxation with an Eddy current effect in the absorbing bandwidth.

| S-EPMC5443822 | biostudies-literature

Heteronanostructured Co@carbon nanotubes-graphene ternary hybrids: synthesis, electromagnetic and excellent microwave absorption properties.

Project description:In order to explore high efficiency microwave absorption materials, heteronanostructured Co@carbon nanotubes-graphene (Co@CNTs-G) ternary hybrids were designed and produced through catalytic decomposition of acetylene at the designed temperature (400, 450, 500 and 550 °C) over Co3O4/reduced graphene oxide (Co3O4/RGO). By regulating the reaction temperatures, different CNT contents of Co@CNTs-G ternary hybrids could be synthesized. The investigations indicated that the as-prepared heteronanostructured Co@CNTs-G ternary hybrids exhibited excellent microwave absorption properties, and their electromagnetic and microwave absorption properties could be tuned by the CNT content. The minimum reflection loss (RL) value reached approximately -65.6, -58.1, -41.1 and -47.5 dB for the ternary hybrids synthesized at 400, 450, 500 and 550 °C, respectively. And RL values below -20 dB (99% of electromagnetic wave attenuation) could be obtained over the as-prepared Co@CNTs-G ternary hybrids in the large frequency range. Moreover, based on the obtained results, the possible enhanced microwave absorption mechanisms were discussed in details. Therefore, a simple approach was proposed to explore the high performance microwave absorbing materials as well as to expand the application field of graphene-based materials.

| S-EPMC5125104 | biostudies-literature

Hydrogenated amorphous silicon nitride photonic crystals for improved-performance surface electromagnetic wave biosensors.

Project description:We exploit the properties of surface electromagnetic waves propagating at the surface of finite one dimensional photonic crystals to improve the performance of optical biosensors with respect to the standard surface plasmon resonance approach. We demonstrate that the hydrogenated amorphous silicon nitride technology is a versatile platform for fabricating one dimensional photonic crystals with any desirable design and operating in a wide wavelength range, from the visible to the near infrared. We prepared sensors based on photonic crystals sustaining either guided modes or surface electromagnetic waves, also known as Bloch surface waves. We carried out for the first time a direct experimental comparison of their sensitivity and figure of merit with surface plasmon polaritons on metal layers, by making use of a commercial surface plasmon resonance instrument that was slightly adapted for the experiments. Our measurements demonstrate that the Bloch surface waves on silicon nitride photonic crystals outperform surface plasmon polaritons by a factor 1.3 in terms of figure of merit.

| S-EPMC3469992 | biostudies-literature

Drawing circuits with carbon nanotubes: scratch-induced graphoepitaxial growth of carbon nanotubes on amorphous silicon oxide substrates.

Project description:Controlling the orientations of nanomaterials on arbitrary substrates is crucial for the development of practical applications based on such materials. The aligned epitaxial growth of single-walled carbon nanotubes (SWNTs) on specific crystallographic planes in single crystalline sapphire or quartz has been demonstrated; however, these substrates are unsuitable for large scale electronic device applications and tend to be quite expensive. Here, we report a scalable method based on graphoepitaxy for the aligned growth of SWNTs on conventional SiO?/Si substrates. The "scratches" generated by polishing were found to feature altered atomic organizations that are similar to the atomic alignments found in vicinal crystalline substrates. The linear and circular scratch lines could promote the oriented growth of SWNTs through the chemical interactions between the C atoms in SWNT and the Si adatoms in the scratches. The method presented has the potential to be used to prepare complex geometrical patterns of SWNTs by 'drawing' circuits using SWNTs without the need for state-of-the-art equipment or complicated lithographic processes.

| S-EPMC4055888 | biostudies-other

Biomass-Derived Carbon Heterostructures Enable Environmentally Adaptive Wideband Electromagnetic Wave Absorbers.

Project description:Although advances in wireless technologies such as miniature and wearable electronics have improved the quality of our lives, the ubiquitous use of electronics comes at the expense of increased exposure to electromagnetic (EM) radiation. Up to date, extensive efforts have been made to develop high-performance EM absorbers based on synthetic materials. However, the design of an EM absorber with both exceptional EM dissipation ability and good environmental adaptability remains a substantial challenge. Here, we report the design of a class of carbon heterostructures via hierarchical assembly of graphitized lignocellulose derived from bamboo. Specifically, the assemblies of nanofibers and nanosheets behave as a nanometer-sized antenna, which results in an enhancement of the conductive loss. In addition, we show that the composition of cellulose and lignin in the precursor significantly influences the shape of the assembly and the formation of covalent bonds, which affect the dielectric response-ability and the surface hydrophobicity (the apparent contact angle of water can reach 135°). Finally, we demonstrate that the obtained carbon heterostructure maintains its wideband EM absorption with an effective absorption frequency ranging from 12.5 to 16.7 GHz under conditions that simulate the real-world environment, including exposure to rainwater with slightly acidic/alkaline pH values. Overall, the advances reported in this work provide new design principles for the synthesis of high-performance EM absorbers that can find practical applications in real-world environments.

| S-EPMC8643388 | biostudies-literature

Nitrogen-Doped Magnetic-Dielectric-Carbon Aerogel for High-Efficiency Electromagnetic Wave Absorption.

Project description:Carbon-based aerogels derived from biomass chitosan are encountering a flourishing moment in electromagnetic protection on account of lightweight, controllable fabrication and versatility. Nevertheless, developing a facile construction method of component design with carbon-based aerogels for high-efficiency electromagnetic wave absorption (EWA) materials with a broad effective absorption bandwidth (EAB) and strong absorption yet hits some snags. Herein, the nitrogen-doped magnetic-dielectric-carbon aerogel was obtained via ice template method followed by carbonization treatment, homogeneous and abundant nickel (Ni) and manganese oxide (MnO) particles in situ grew on the carbon aerogels. Thanks to the optimization of impedance matching of dielectric/magnetic components to carbon aerogels, the nitrogen-doped magnetic-dielectric-carbon aerogel (Ni/MnO-CA) suggests a praiseworthy EWA performance, with an ultra-wide EAB of 7.36 GHz and a minimum reflection loss (RLmin) of - 64.09 dB, while achieving a specific reflection loss of - 253.32 dB mm-1. Furthermore, the aerogel reveals excellent radar stealth, infrared stealth, and thermal management capabilities. Hence, the high-performance, easy fabricated and multifunctional nickel/manganese oxide/carbon aerogels have broad application aspects for electromagnetic protection, electronic devices and aerospace.

| S-EPMC10656410 | biostudies-literature

Molecular Dynamics Modeling of Interfacial Interactions between Flattened Carbon Nanotubes and Amorphous Carbon: Implications for Ultra-Lightweight Composites.

Project description:Flattened carbon nanotubes (flCNTs) naturally form in many carbon nanotube-based materials and can exhibit mechanical properties similar to round carbon nanotubes but with tighter packing and alignment. To facilitate the design, fabrication, and testing of flCNT-based composites for aerospace structures, computational modeling can be used to efficiently and accurately predict their performance as a function of processing parameters, such as reinforcement/matrix cross-linking. In this study, molecular dynamics modeling is used to predict the load transfer characteristics of the interface region between the flat region of flCNTs (i.e., bi-layer graphene) and amorphous carbon (AC) with various levels and locations of covalent bond cross-linking and AC mass density. The results of this study show that increasing the mass density of AC at the interface improves the load transfer capability of the interface. However, a much larger improvement is observed when cross-linking is added both to the flCNT-AC interface and between the flCNT sheets. With both types of cross-linking, substantial improvements in interfacial shear strength, transverse tension strength, and transverse tension toughness are predicted. The results of this study are important for optimizing the processing of flCNT/AC composites for demanding engineering applications.

| S-EPMC9039962 | biostudies-literature

Tensile properties of millimeter-long multi-walled carbon nanotubes.

Project description:There have been a number of theoretical and experimental studies on tensile properties of carbon nanotubes (CNT), reporting the Young's modulus of the individual CNT up to 1 TPa. Although CNT shows the promise to be used as reinforcement in a high modulus/strength composite material, it exhibits quite disappointing in terms of modulus or strength. Along with recent advance in CNT growth technique, we will be able to directly measure tensile properties of millimeter-long MWCNTs. This study firstly tackles the direct measurement of the tensile properties of millimeter-long MWCNTs that can be used as reinforcement in a composite system. A carefully designed tensile testing technique for the MWCNTs is developed, which allows us to obtain more accurate and reliable measured values. The average tensile strength and Young's modulus of the CNTs investigated in this study are measured to be 0.85?GPa and 34.65?GPa, respectively. Also, this work statistically investigates the effect of the CNT dimensions including length, diameter and volume on the tensile properties. To the best of our knowledge, this is the very first report on the tensile properties of macroscopically long and continuous CNTs.

| S-EPMC5573399 | biostudies-literature

Torsional Properties of Bundles with Randomly Packed Carbon Nanotubes.

Project description:Carbon nanotube (CNT) bundles/fibers possess promising applications in broad fields, such as artificial muscles and flexible electronics, due to their excellent mechanical properties. The as-prepared CNT bundles contain complex structural features (e.g., different alignments and components), which makes it challenging to predict their mechanical performance. Through in silico studies, this work assessed the torsional performance of CNT bundles with randomly packed CNTs. It is found that CNT bundles with varying constituent CNTs in terms of chirality and diameter exhibit remarkably different torsional properties. Specifically, CNT bundles consisting of CNTs with a relatively large diameter ratio possess lower gravimetric energy density and elastic limit than their counterpart with a small diameter ratio. More importantly, CNT bundles with the same constituent CNTs but different packing morphologies can yield strong variation in their torsional properties, e.g., up to 30%, 16% and 19% difference in terms of gravimetric energy density, elastic limit and elastic constants, respectively. In addition, the separate fracture of the inner and outer walls of double-walled CNTs is found to suppress the gravimetric energy density and elastic limit of their corresponding bundles. These findings partially explain why the experimentally measured mechanical properties of CNT bundles vary from each other, which could benefit the design and fabrication of high-performance CNT bundles.

| S-EPMC8911843 | biostudies-literature

Polyimide-based porous carbon and cobalt nanoparticle composites as high-performance electromagnetic wave absorbers.

Project description:This study successfully utilized a straightforward approach, choosing liquid-liquid phase separation to build a porous structure and synthesize composite absorbers based on polyimide-based porous carbon and cobalt nanoparticles (designated as PPC/Co-700 and PPC/Co-800). A fine porous structure was achieved as a result of the excellent heat resistance of polyimide resulting in an excellent electromagnetic wave absorption ability of PPC/Co composites. The results obtained clearly indicated that PPC/Co-700 and PPC/Co-800 exhibit a porous structure with coral-like pores, enhancing both impedance matching properties and microwave attenuation abilities. This improvement in impedance matching conditions and dissipation capability is attributed to the synergistic effect of dielectric loss induced by carbon and magnetic loss induced by Co nanoparticles. PPC/Co-700 showed the strongest absorption performance with a minimum reflection loss of -59.85 dB (30 wt% loading, thickness of 3.42 mm) and an effective absorption bandwidth (EABW, RL ≤ -10 dB) of 6.24 GHz (30 wt% loading, thickness of 2.78 mm). Therefore, this work provides a facile strategy for the development of a promising absorbing material with outstanding electromagnetic wave absorption performance.

| S-EPMC10958461 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data