Three-dimensional printed acrylonitrile butadiene styrene framework coated with Cu-BTC metal-organic frameworks for the removal of methylene blue.

ABSTRACT: Three-dimensional (3D) printing was applied for the fabrication of acrylonitrile butadiene styrene (ABS) framework. Functionalization of the ABS framework was then performed by coating of porous Cu-BTC (BTC = benzene tricarboxylic acid) metal-organic frameworks on it using a step-by-step in-situ growth. The size of the Cu-BTC particles on ABS was ranged from 200 nm to 900 nm. The Cu-BTC/ABS framework can take up most of the space of the tubular reactor that makes the adsorption effective with no need of stirring. Methylene blue (MB) can be readily removed from aqueous solution by this Cu-BTC/ABS framework. The MB removal efficiency for solutions with concentrations of 10 and 5 mg/L was 93.3% and 98.3%, respectively, within 10 min. After MB adsorption, the Cu-BTC/ABS composite can easily be recovered without the need for centrifugation or filtration and the composite is reusable. In addition the ABS framework can be recovered for subsequent reuse. A significant advantage of 3D-printed frameworks is that different frameworks can be easily fabricated to meet the needs of different applications. This is a promising strategy to synthesize new frameworks using MOFs and polymers to develop materials for applications beyond adsorption.

SUBMITTER: Wang Z

PROVIDER: S-EPMC4123204 | biostudies-other | 2014

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Mechanical Properties of 3D-Printed Acrylonitrile-Butadiene-Styrene TiO2 and ATO Nanocomposites.

Project description:In order to enhance the mechanical performance of three-dimensional (3D) printed structures fabricated via commercially available fused filament fabrication (FFF) 3D printers, novel nanocomposite filaments were produced herein following a melt mixing process, and further 3D printed and characterized. Titanium Dioxide (TiO2) and Antimony (Sb) doped Tin Oxide (SnO2) nanoparticles (NPs), hereafter denoted as ATO, were selected as fillers for a polymeric acrylonitrile butadiene styrene (ABS) thermoplastic matrix at various weight % (wt%) concentrations. Tensile and flexural test specimens were 3D printed, according to international standards. It was proven that TiO2 filler enhanced the overall tensile strength by 7%, the flexure strength by 12%, and the micro-hardness by 6%, while for the ATO filler, the corresponding values were 9%, 13%, and 6% respectively, compared to unfilled ABS. Atomic force microscopy (AFM) revealed the size of TiO2 (40 ± 10 nm) and ATO (52 ± 11 nm) NPs. Raman spectroscopy was performed for the TiO2 and ATO NPs as well as for the 3D printed nanocomposites to verify the polymer structure and the incorporated TiO2 and ATO nanocrystallites in the polymer matrix. The scope of this work was to fabricate novel nanocomposite filaments using commercially available materials with enhanced overall mechanical properties that industry can benefit from.

| S-EPMC7407130 | biostudies-literature

Highly Efficient Removal for Methylene Blue and Cu<sup>2+</sup> onto UiO-66 Metal-Organic Framework/Carboxylated Graphene Oxide-Incorporated Sodium Alginate Beads.

Project description:Herein, we report a new metal-organic framework (MOF)-based composite beads adsorbent made via incorporating UiO-66 MOF, carboxylated graphene oxide (GOCOOH) into sodium alginate for efficient removal of methylene blue dye, and Cu2+ ions. The successful fabrication of the synthesized UiO-66/GOCOOH@SA composite beads was confirmed by means of X-ray diffraction, Fourier transform infrared, scanning electron microscopy, zeta potential, X-ray photoelectron spectroscopy analysis, and thermogravimetric analysis and BET measurement. The incorporation of both UiO-66 and GOCOOH into SA beads greatly increased their adsorption efficiency for the removal of both MB and Cu2+ with maximum adsorption capacities of 490.72 and 343.49 mg/g, respectively. The removal process of both MB and Cu2+ follows the pseudo-second-order model and Freundlich isotherm model. A plausible adsorption mechanism was discussed in detail. Regeneration tests clarified that the removal efficiencies toward both MB and Cu2+ remained higher than 87% after five cycles. These results reveal the potentiality of UiO-66/GOCOOH@SA beads as an excellent adsorbent.

| S-EPMC8444308 | biostudies-literature

A Three-dimensionally Printed Acrylonitrile Butadiene Styrene Model for the Reduction of Nasomaxillary Fracture.

Project description:The successful reduction of a nasomaxillary fracture was performed using a three-dimensional printed model. A 16-year-old boy was struck in the left orbit by a baseball; subsequently, he was diagnosed with the nasal bone fracture at a hospital, and was referred to the authors' department. A left nasomaxillary fracture and nasal bone fracture were diagnosed by computed tomography. Standard triangulated language data for the mirror image of the frontal process of the right maxilla were obtained from digital imaging and communications in medicine data for preparing a three-dimensional printed acrylonitrile butadiene styrene model. On postinjury day 13, the frontal process fracture was reduced via transconjunctival and intraoral approaches. After the reduction of the fracture, an absorbable plate fitting to the shape of three-dimensional printed acrylonitrile butadiene styrene model was molded, and the maxillary frontal process and infraorbital rim were reduced and fixed with an absorbable plate and screws. Postoperative computed tomography demonstrated a favorable reduction. The intraoperative use of the 3D printed acrylonitrile butadiene styrene model was helpful in the nasomaxillary fracture reduction and fixation.

| S-EPMC8522875 | biostudies-literature

Synthesis of TiO2NWS@AuNPS Composite Catalyst for Methylene Blue Removal.

Project description:In this article, HBP-NH₂-modified titania nanowire (TiO2NWS)-decorated Au nanoparticles (TiO2NWS@AuNPS) were synthesized by one-step method. The role of HBP-NH₂ concentration in the formation of TiO2NWS was investigated. The fineness and uniformity of pure TiO2NWS were enhanced by absorbed amino groups from amino-terminated hyperbranched polymer (HBP-NH₂). The morphology and crystal structure of TiO2NWS and TiO2NWS@AuNPS were examined by transmission electron microscopy (TEM), X-ray diffraction (XRD), and Fournier transform infrared (FTIR) spectroscopy. The chemical states of gold, titanium and oxygen were analyzed by X-ray photoelectron spectroscopy (XPS). The results showed that at the concentration of HBP-NH₂ 100 g/L, the mean diameter of TiO2NWS was nearly 72 nm and Au nanoparticles were uniformly distributed on the surface of TiO2NWS. The presence of AuNPS improved the photocatalytic properties of TiO2NWS under UV light irradiation. The Au load was believed to improve the utilization rate of the photoelectron and activated the adsorbed oxygen. The obtained TiO2NWS@AuNPS decomposed 99.6% methylene blue (MB) after 300 min when subjected to UV light irradiation. After five cycles of the catalyzing process, the TiO2NWS@AuNPS still retained over 90% of its catalytic ability for MB. The Au deposition was found responsible for the high catalytic activity of TiO2NWS@AuNPS.

| S-EPMC6025176 | biostudies-literature

Glassy Powder Derived from Waste Printed Circuit Boards for Methylene Blue Adsorption.

Project description:Electronic waste (e-waste) is one of the fastest-growing waste streams in the world and Europe is classified as the first producer in terms of per capita amount. To reduce the environmental impact of e-waste, it is important to recycle it. This work shows the possibility of reusing glassy substrates, derived from the MW-assisted acidic leaching of Waste Printed Circuit Boards (WPCBs), as an adsorbent material. The results revealed an excellent adsorption capability against methylene blue (MB; aqueous solutions in the concentration range 10-5 M-2 × 10-5 M, at pH = 7.5). Comparisons were performed with reference samples such as activated carbons (ACs), the adsorbent mostly used at the industrial level; untreated PCB samples; and ground glass slides. The obtained results show that MW-treated WPCB powder outperformed both ground glass and ground untreated PCBs in MB adsorption, almost matching AC adsorption. The use of this new adsorbent obtained through the valorization of e-waste offers advantages not only in terms of cost but also in terms of environmental sustainability.

| S-EPMC10821274 | biostudies-literature

Prediction of Methylene Blue Removal by Nano TiO2 Using Deep Neural Network.

Project description:This paper deals with the prediction of methylene blue (MB) dye removal under the influence of titanium dioxide nanoparticles (TiO2 NPs) through deep neural network (DNN). In the first step, TiO2 NPs were prepared and their morphological properties were analysed by scanning electron microscopy. Later, the influence of as synthesized TiO2 NPs was tested against MB dye removal and in the final step, DNN was used for the prediction. DNN is an efficient machine learning tools and widely used model for the prediction of highly complex problems. However, it has never been used for the prediction of MB dye removal. Therefore, this paper investigates the prediction accuracy of MB dye removal under the influence of TiO2 NPs using DNN. Furthermore, the proposed DNN model was used to map out the complex input-output conditions for the prediction of optimal results. The amount of chemicals, i.e., amount of TiO2 NPs, amount of ehylene glycol and reaction time were chosen as input variables and MB dye removal percentage was evaluated as a response. DNN model provides significantly high performance accuracy for the prediction of MB dye removal and can be used as a powerful tool for the prediction of other functional properties of nanocomposites.

| S-EPMC8473325 | biostudies-literature

The effects of printing orientation on the electrochemical behaviour of 3D printed acrylonitrile butadiene styrene (ABS)/carbon black electrodes.

Project description:Additive manufacturing also known as 3D printing is being utilised in electrochemistry to reproducibly develop complex geometries with conductive properties. In this study, we explored if the electrochemical behavior of 3D printed acrylonitrile butadiene styrene (ABS)/carbon black electrodes was influenced by printing direction. The electrodes were printed in both horizontal and vertical directions. The horizsontal direction resulted in a smooth surface (HPSS electrode) and a comparatively rougher surface (HPRS electrode) surface. Electrodes were characterized using cyclic voltammetry, electrochemical impedance spectroscopy and chronoamperometry. For various redox couples, the vertical printed (VP) electrode showed enhanced current response when compared the two electrode surfaces generated by horizontal print direction. No differences in the capacitive response was observed, indicating that the conductive surface area of all types of electrodes were identical. The VP electrode had reduced charge transfer resistance and uncompensated solution resistance when compared to the HPSS and HPRS electrodes. Overall, electrodes printed in a vertical direction provide enhanced electrochemical performance and our study indicates that print orientation is a key factor that can be used to enhance sensor performance.

| S-EPMC6002470 | biostudies-literature

Influence of Ultraviolet Radiation Exposure Time on Styrene-Ethylene-Butadiene-Styrene (SEBS) Copolymer.

Project description:The effect of ultraviolet radiation on styrene-ethylene-butadiene-styrene (SEBS) has been studied at different exposures times in order to obtain a better understanding of the mechanism of ageing. The polymer materials were mechanically tested and then their surfaces were analyzed using a scanning electron microscope (SEM) and atomic force microscopy (AFM). Moreover, the optical analysis of contact angle (OCA) was used to evaluate the surface energy (?s) and the yellowing index (YI) and attenuated total reflectance infrared spectroscopy (ATR-FTIR) were used to observe structural and physical changes in aging SEBS. The results obtained for the SEBS, in relation to the duration of exposure, showed superficial changes that cause a decrease in the surface energy (?s) and, therefore, a decrease in surface roughness. This led to a reduction in mechanical performance, decreasing the tensile strength by about 50% for exposure times of around 200 h.

| S-EPMC7240548 | biostudies-literature

Synthesis of activated carbon from biowaste of fir bark for methylene blue removal.

Project description:Activated carbon (AC) was successfully prepared from low-cost forestry fir bark (FB) waste using KOH activation method. Morphology and texture properties of ACFB were studied by scanning and high-resolution transmission electron microscopies (SEM and HRTEM), respectively. The resulting fir bark-based activated carbon (ACFB) demonstrated high surface area (1552 m2 g-1) and pore volume (0.84 cm3 g-1), both of which reflect excellent potential adsorption properties of ACFB towards methylene blue (MB). The effect of various factors, such as pH, initial concentration, adsorbent content as well as adsorption duration, was studied individually. Adsorption isotherms of MB were fitted using all three nonlinear models (Freundlich, Langmuir and Tempkin). The best fitting of MB adsorption results was obtained using Freundlich and Temkin. Experimental results showed that kinetics of MB adsorption by our ACFB adsorbent followed pseudo-second-order model. The maximum adsorption capacity obtained was 330 mg g-1, which indicated that FB is an excellent raw material for low-cost production of AC suitable for cationic dye removal.

| S-EPMC6774956 | biostudies-literature

Lignin Nanoparticles and Alginate Gel Beads: Preparation, Characterization and Removal of Methylene Blue.

Project description:A novel and effective green system consisting of deep eutectic solvent (DES) was proposed to prepare lignin nanoparticles (LNPs) without any lignin modification. The LNPs are obtained through the dialysis of the kraft lignin-DES solution. The particle size distribution, Zeta potential and morphology of the LNPs are characterized by using dynamic light scattering (DLS), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The average diameter of LNPs is in the range 123.6 to 140.7 nm, and the LNPs show good stability and dispersibility in water. The composite beads composed of LNPs and sodium alginate (SA) are highly efficient (97.1%) at removing methylene blue (MB) from the aqueous solution compared to 82.9% and 77.4% by the SA/bulk kraft lignin composite and pure SA, respectively. Overall, the LNPs-SA bio-nanocomposite with high adsorption capacity (258.5 mg/g) could be useful in improving water quality and other related applications.

| S-EPMC8746983 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data