Feasibility of using phase change materials to control the heat of hydration in massive concrete structures.

ABSTRACT: This paper presents experimental results that can be applied to select a possible phase change material (PCM), such as a latent heat material (LHM), to control the hydration heat in mass concrete structures. Five experimental tests (microconduction, simplified adiabatic temperature rise, heat, and compressive strength tests) were conducted to select the most desirable LHM out of seven types of inorganic PCM used in cement mortar and to determine the most suitable mix design. The results of these experimental tests were used to assess the feasibility of using PCM to reduce hydration heat in mass concrete that was examined. The experimental results show that cement mortar containing barium- [Ba(OH)2 · 8H2O] based PCM has the lowest amount of total hydration heat of the cement pastes. The barium-based PCM provides good latent heat properties that help to prevent volume change and microcracks caused by thermal stress in mass concrete.

SUBMITTER: Choi WC

PROVIDER: S-EPMC4124213 | biostudies-other | 2014

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Electronically Reconfigurable Photonic Switches Incorporating Plasmonic Structures and Phase Change Materials.

Project description:The ever-increasing demands for data processing and storage will require seamless monolithic co-integration of electronics and photonics. Phase-change materials are uniquely suited to fulfill this function due to their dual electro-optical sensitivity, nonvolatile retention properties, and fast switching dynamics. The extreme size disparity however between CMOS electronics and dielectric photonics inhibits the realization of efficient and compact electrically driven photonic switches, logic and routing elements. Here, the authors achieve an important milestone in harmonizing the two domains by demonstrating an electrically reconfigurable, ultra-compact and nonvolatile memory that is optically accessible. The platform relies on localized heat, generated within a plasmonic structure; this uniquely allows for both optical and electrical readout signals to be interlocked with the material state of the PCM while still ensuring that the writing operation is electrically decoupled. Importantly, by miniaturization and effective thermal engineering, the authors achieve unprecedented energy efficiency, opening up a path towards low-energy optoelectronic hardware for neuromorphic and in-memory computing.

| S-EPMC9284156 | biostudies-literature

The Influence of Phase Change Materials on the Properties of Self-Compacting Concrete.

Project description:The aim of this paper is to research new thermally-efficient concrete walls, analyzing the mechanical behavior of a self-compacting concrete to manufacture an uncoated solid structural panel, with the incorporation of a micro-encapsulated phase change material as additive. Different dosages are tested and mechanical properties of the product obtained from the molding of concrete specimens are evaluated, testing mechanical compressive strength, slump flow, and density. The results reveal the optimum percentage of additive in the mixture that enables compliance with the technical specifications required by the product to be manufactured. A test is also performed for measuring the thermal conductivity for the optimal sample obtained and it evidences the reduction thereof.

| S-EPMC5521320 | biostudies-other

Excellent Temperature-Control Based on Reversible Thermochromic Materials for Light-Driven Phase Change Materials System.

Project description:Light-driven phase change materials (PCMs) have received significant attention due to their capacity to convert visible light into thermal energy, storing it as latent heat. However, continuous photo-thermal conversion can cause the PCMs to reach high thermal equilibrium temperatures after phase transition. In our study, a novel light-driven phase change material system with temperature-control properties was constructed using a thermochromic compound. Thermochromic phase change materials (TC-PCMs) were prepared by introducing 2-anilino-6-dibutylamino-3-methylfluoran (ODB-2) and bisphenol A (BPA) into 1-hexadecanol (1-HD) in various proportions. Photo-thermal conversion performance was investigated with solar radiation (low power of 0.09 W/cm2) and a xenon lamp (at a high power of 0.14 W/cm2). The TC-PCMs showed a low equilibrium temperature due to variations in absorbance. Specifically, the temperature of TC-PCM180 (ODB-2, bisphenol A and 1-HD ratio 1:2:180) could stabilize at 54 °C approximately. TC-PCMs exhibited reversibility and repeatability after 20 irradiation and cooling cycles.

| S-EPMC6526475 | biostudies-literature

Experimental Investigation on Mechanism of Latent Heat Reduction of Sodium Acetate Trihydrate Phase Change Materials.

Project description:Sodium acetate trihydrate (SAT) phase change material (PCM) has been well known for thermal energy storage due to its high latent heat and resource abundance. However, SAT suffers from severe latent heat reduction after heating and cooling cycles. Although a few of previous researches showed the reduction could be effectively inhibited by using thickeners, the mechanisms of the reduction process and thickeners' inhibition have not been deeply explored till now. In this work, SAT modified by 5 wt.% nucleating agent of disodium hydrogen phosphate dodecahydrate (SAT/5 wt.% DSP) was prepared and 200 thermal cycles were carried out. The differential scanning calorimeter, Rheometer, X-ray diffractometry, and scanning electron microscope were used to investigate the extent of latent heat reduction, viscosity, phase composition and microstructure, respectively, and the infrared thermal imaging method was used to evaluate heat storage capacity. It was found that the latent heat of SAT/5 wt.% DSP dropped dramatically and the relative decrease in latent heat was measured to be 22.44%. The lower layer of SAT/5 wt.% DSP contained 24.1 wt.% CH3COONa, which was quantitatively consistent with the reduction extent. Furthermore, the phase change endothermic time of the lower layer was only 44.1% of that of the upper. SAT/5 wt.% DSP was further modified by 3 wt.% thickener of carboxymethyl cellulose (SAT/5 wt.% DSP/3 wt.% CMC) and endured 200 thermal cycles. The extent of the latent heat reduction of SAT/5 wt.% DSP/3 wt.% CMC was only 9.29%, and phase compositions were more homogeneous. The 3 wt.% CMC increased viscosity by 14 times, which effectively prevented the Stokes sedimentation velocity of CH3COONa in melts and inhibited the final macroscopic phase separation.

| S-EPMC7040703 | biostudies-literature

Determination of Specific Heat Capacity on Composite Shape-Stabilized Phase Change Materials and Asphalt Mixtures by Heat Exchange System.

Project description:Previous research has shown that composite shape-stabilized phase change material (CPCM) has a remarkable capacity for thermal storage and stabilization, and it can be directly applied to highway construction without leakage. However, recent studies on temperature changing behaviors of CPCM and asphalt mixture cannot intuitively reflect the thermoregulation mechanism and efficiency of CPCM on asphalt mixture. The objective of this paper is to determine the specific heat capacity of CPCM and asphalt mixtures mixed with CPCM using the heat exchange system and the data acquisition system. Studies have shown that the temperature-rise curve of 5 °C CPCM has an obvious temperature plateau, while an asphalt mixture mixed with 5 °C CPCM does not; with increasing temperature, the specific heat capacities of both 5 °C CPCM and asphalt mixture first increase and then decrease, while the variation rate of 5 °C CPCM is larger than that of the asphalt mixture, and the maximum specific heat capacity of 5 °C CPCM appears around the initial phase change temperature. It is concluded that the temperature intervals of 5 °C CPCM are -18 °C-7 °C, 7 °C-25 °C and 25 °C-44 °C, respectively, and that of the asphalt mixture are -18 °C~10 °C, -10 °C~5 °C and 5 °C~28 °C. A low dosage of 5 °C CPCM has little influence on the specific heat capacity of asphalt mixture. Finally, the functions of specific heat capacities and temperature for CPCM and asphalt mixture mixed with CPCM were recommended by the sectional regression method.

| S-EPMC5503031 | biostudies-other

Polariton nanophotonics using phase-change materials.

Project description:Polaritons formed by the coupling of light and material excitations enable light-matter interactions at the nanoscale beyond what is currently possible with conventional optics. However, novel techniques are required to control the propagation of polaritons at the nanoscale and to implement the first practical devices. Here we report the experimental realization of polariton refractive and meta-optics in the mid-infrared by exploiting the properties of low-loss phonon polaritons in isotopically pure hexagonal boron nitride interacting with the surrounding dielectric environment comprising the low-loss phase change material Ge3Sb2Te6. We demonstrate rewritable waveguides, refractive optical elements such as lenses, prisms, and metalenses, which allow for polariton wavefront engineering and sub-wavelength focusing. This method will enable the realization of programmable miniaturized integrated optoelectronic devices and on-demand biosensors based on high quality phonon resonators.

| S-EPMC6776658 | biostudies-literature

Adaptive multi-temperature control for transport and storage containers enabled by phase-change materials.

Project description:The transportation of essential items, such as food and vaccines, often requires adaptive multi-temperature control to maintain high safety and efficiency. While existing methods utilizing phase change materials have shown promise, challenges related to heat transfer and materials' physicochemical properties remain. In this study, we present an adaptive multi-temperature control system using liquid-solid phase transitions to achieve highly effective thermal management using a pair of heat and cold sources. By leveraging the properties of stearic acid and distilled water, we fabricated a multi-temperature maintenance container and demonstrated temperature variations of only 0.14-2.05% over a two-hour period, underscoring the efficacy of our approach. Our findings offer a practical solution to address critical challenges in reliable transportation of goods, with potential implications for various fields in physical, engineering, and life sciences.

| S-EPMC10482904 | biostudies-literature

Fluidic phase-change materials with continuous latent heat from theoretically tunable ternary metals for efficient thermal management.

Project description:Phase-change materials (PCMs), as important energy storage materials (ESMs), have been widely used in heat dissipation for electronics. However, PCMs are encountering huge challenges since the extremely limited space in microelectronics largely suppresses the applied volume of PCMs, which demands excellent PCMs that can fully utilize the valuable latent heat. This work successfully found a universal strategy toward powerful ESMs from fluidic ternary metals (TMs, GaInSn as a representative TM in this work). TMs exhibit high thermal conductivity (20.3 W m-1 K-1) and significantly effective latent heat (115 J/cm3) and, more important, show continuous phase transition and full utilization of the valuable latent heat. Interestingly, theoretical prediction through ternary phase diagram is carried out to easily tune the melting range, latent heat, and fluidity (viscosity) of TMs to adapt with different service conditions. As a result, thermally conductive silicone grease can be conveniently fabricated via simple shear mixing of TM and polymers. Such thermally conductive TM grease inherits the merits of TM, exhibiting continuous thermal control over daily electronics according to thermal shock performance.

| S-EPMC9351464 | biostudies-literature

Effect of the PSSMA Content on the Heat Transfer Performances of Polyurea Nano-Encapsulated Phase Change Materials.

Project description:Polyurea nano-encapsulated phase change materials (PUA-NEPCMs) were prepared from an n-octadecane core and through the formation of amide bonds by the reaction of toluene 2,4-diisocyanate and poly(4-styrenesulfonic acid-co-maleic acid) sodium salt (PSSMA), followed by the subsequent formation of a PUA shell using a miniemulsion system. The effects of the synthetic conditions on the thermal properties and encapsulat ion effect of the NEPCMs were systematically investigated. Differential scanning calorimetry (DSC) revealed that the melting enthalpy and encapsulation efficiency of the PUA-NEPCMs prepared under optimal conditions reached 123.00 J/g and 54.27%, respectively. Although previous results suggested that the introduction of PSSMA results in a reduced heat transfer performance for NEPCMs, DSC analysis of the prepared PUA-NEPCMs showed that increasing PSSMA contents enhanced the heat transfer performance due to a decrease in the degree of supercooling. Our results could therefore lead to further enhancements in the heat transfer performance of PUA-NEPCMs, in addition to expanding their field of application.

| S-EPMC8227275 | biostudies-literature

Uncovering ?-relaxations in amorphous phase-change materials.

Project description:Relaxation processes are decisive for many physical properties of amorphous materials. For amorphous phase-change materials (PCMs) used in nonvolatile memories, relaxation processes are, however, difficult to characterize because of the lack of bulk samples. Here, instead of bulk samples, we use powder mechanical spectroscopy for powder samples to detect the prominent excess wings-a characteristic feature of ?-relaxations-in a series of amorphous PCMs at temperatures below glass transitions. By contrast, ?-relaxations are vanishingly small in amorphous chalcogenides of similar composition, which lack the characteristic features of PCMs. This conclusion is corroborated upon crossing the border from PCMs to non-PCMs, where ?-relaxations drop substantially. Such a distinction implies that amorphous PCMs belong to a special kind of covalent glasses whose locally fast atomic motions are preserved even below the glass transitions. These findings suggest a correlation between ?-relaxation and crystallization kinetics of PCMs, which have technological implications for phase-change memory functionalities.

| S-EPMC6954054 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data