Understanding the Cu-Zn brass alloys using a short-range-order cluster model: significance of specific compositions of industrial alloys.

ABSTRACT: Metallic alloys show complex chemistries that are not yet understood so far. It has been widely accepted that behind the composition selection lies a short-range-order mechanism for solid solutions. The present paper addresses this fundamental question by examining the face-centered-cubic Cu-Zn α-brasses. A new structural approach, the cluster-plus-glue-atom model, is introduced, which suits specifically for the description of short-range-order structures in disordered systems. Two types of formulas are pointed out, [Zn-Cu12]Zn(1~6) and [Zn-Cu12](Zn,Cu)6, which explain the α-brasses listed in the American Society for Testing and Materials (ASTM) specifications. In these formulas, the bracketed parts represent the 1(st)-neighbor cluster, and each cluster is matched with one to six 2nd-neighbor Zn atoms or with six mixed (Zn,Cu) atoms. Such a cluster-based formulism describes the 1st- and 2nd-neighbor local atomic units where the solute and solvent interactions are ideally satisfied. The Cu-Ni industrial alloys are also explained, thus proving the universality of the cluster-formula approach in understanding the alloy selections. The revelation of the composition formulas for the Cu-(Zn,Ni) industrial alloys points to the common existence of simple composition rules behind seemingly complex chemistries of industrial alloys, thus offering a fundamental and practical method towards composition interpretations of all kinds of alloys.

SUBMITTER: Hong HL

PROVIDER: S-EPMC4233332 | biostudies-other | 2014

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Ubiquitous short-range order in multi-principal element alloys.

Project description:Recent research in multi-principal element alloys (MPEAs) has increasingly focused on the role of short-range order (SRO) on material performance. However, the mechanisms of SRO formation and its precise control remain elusive, limiting the progress of SRO engineering. Here, leveraging advanced additive manufacturing techniques that produce samples with a wide range of cooling rates (up to 107 K s-1) and an enhanced semi-quantitative electron microscopy method, we characterize SRO in three CoCrNi-based face-centered-cubic (FCC) MPEAs. Surprisingly, irrespective of the processing and thermal treatment history, all samples exhibit similar levels of SRO. Atomistic simulations reveal that during solidification, prevalent local chemical order arises in the liquid-solid interface (solidification front) even under the extreme cooling rate of 1011 K s-1. This phenomenon stems from the swift atomic diffusion in the supercooled liquid, which matches or even surpasses the rate of solidification. Therefore, SRO is an inherent characteristic of most FCC MPEAs, insensitive to variations in cooling rates and even annealing treatments typically available in experiments.

| S-EPMC11294451 | biostudies-literature

Exploration of phase structure evolution induced by alloying elements in Ti alloys via a chemical-short-range-order cluster model.

Project description:The prominent comprehensive properties of solid-solution- and intermetallic-based Ti alloys are derived from their diverse microstructures induced by multi-component alloying, which results in a chemical composition complexity. A cluster-plus-glue-atom model, characterizing the chemical short-range orders, was introduced to explore the relationships among the local atomic distributions of alloying elements in different phase structures of Ti alloys, including α-Ti, β-Ti, ω-Ti, α2-Ti3Al, γ-TiAl, O-Ti2AlNb, and B2-Ti(Al,Nb). Specific cluster structural units, i.e., cluster formulas, for these phases were determined with the guide of the Friedel oscillation theory for electron-structure stabilization. It is due to the change of cluster structural units that induces the phase transformation, which is attributed to the amounts of primary alloying elements of Al and Nb. The total atom number (Z) values in these cluster structural units, calculated by the Fermi vector kF, are all very close to the integer of Z = 16. Furthermore, the composition rules of industrial multi-component Ti alloys based on these phases were generalized in light of the cluster formula approach, which will open up a new route towards designing high-performance Ti alloys with complex compositions.

| S-EPMC6399271 | biostudies-literature

Biocompatibility Assessment of Novel Bioresorbable Alloys Mg-Zn-Se and Mg-Zn-Cu for Endovascular Applications: In- Vitro Studies.

Project description:Previous studies have shown that using biodegradable magnesium alloys such as Mg-Zn and Mg-Zn-Al possess the appropriate mechanical properties and biocompatibility to serve in a multitude of biological applications ranging from endovascular to orthopedic and fixation devices. The objective of this study was to evaluate the biocompatibility of novel as-cast magnesium alloys Mg-1Zn-1Cu wt.% and Mg-1Zn-1Se wt.% as potential implantable biomedical materials, and compare their biologically effective properties to a binary Mg-Zn alloy. The cytotoxicity of these experimental alloys was evaluated using a tetrazolium based- MTS (3-(4,5-dimethylthiazol-2-yl)-5-(3-carboxymethoxyphenyl)-2-(4-sulfophenyl)-2H-tetrazolium) assay and a lactate dehydrogenase membrane integrity assay (LDH). The MTS assay was performed on extract solutions obtained from a 30-day period of alloy immersion and agitation in simulated body fluid to evaluate the major degradation products eluted from the alloy materials. Human foreskin fibroblast cell growth on the experimental magnesium alloys was evaluated for a 72 hour period, and cell death was quantified by measuring lactate dehydrogenase concentrations. Both Mg-Zn-Se and Mg-Zn-Cu alloys exhibit low cytotoxicity levels which are suitable for biomaterial applications. The Mg-Zn-Cu alloy was found to completely degrade within 72 hours, resulting in lower human foreskin fibroblast cell viability. The Mg-Zn-Se alloy was shown to be less cytotoxic than both the Mg-Zn-Cu and Mg-Zn alloys.

| S-EPMC3777539 | biostudies-literature

Characterization of Zr-Containing Dispersoids in Al-Zn-Mg-Cu Alloys by Small-Angle Scattering.

Project description:The characterization of Zr-containing dispersoids in aluminum alloys is challenging due to their broad size distribution, low volume fraction, and heterogeneous distribution within the grains. In this work, small-angle X-ray scattering (SAXS) and small-angle neutron scattering (SANS) were compared to scanning electron microscopy (SEM) and transmission electron microscopy (TEM) regarding their capability to characterize Zr-containing dispersoids in aluminum alloys. It was demonstrated that both scattering techniques are suitable tools to characterize dispersoids in a multi-phase industrial 7xxx series aluminum alloy. While SAXS is more sensitive than SANS due to the high electron density of Zr-containing dispersoids, SANS has the advantage of being able to probe a much larger sample volume. The combination of both scattering techniques allows for the verification that the contribution from dispersoids can be separated from that of other precipitate phases such as the S-phase or GP-zones. The size distributions obtained from SAXS, SANS and TEM showed good agreement. The SEM-derived size distributions were, however, found to significantly deviate from those of the other techniques, which can be explained by considering the resolution-limited restrictions of the different techniques.

| S-EPMC9919802 | biostudies-literature

Zn-Mg and Zn-Cu alloys for stenting applications: From nanoscale mechanical characterization to <i>in vitro</i> degradation and biocompatibility.

Project description:In the recent decades, zinc (Zn) and its alloys have been drawing attention as promising candidates for bioresorbable cardiovascular stents due to its degradation rate more suitable than magnesium (Mg) and iron (Fe) alloys. However, its mechanical properties need to be improved in order to meet the criteria for vascular stents. This work investigates the mechanical properties, biodegradability and biocompatibility of Zn-Mg and Zn-Cu alloys in order to determine a proper alloy composition for optimal stent performance. Nanoindentation measurements are performed to characterize the mechanical properties at the nanoscale as a function of the Zn microstructure variations induced by alloying. The biodegradation mechanisms are discussed and correlated to microstructure, mechanical performance and bacterial/cell response. Addition of Mg or Cu alloying elements refined the microstructure of Zn and enhanced yield strength (YS) and ultimate tensile strength (UTS) proportional to the volume fraction of secondary phases. Zn-1Mg showed the higher YS and UTS and better performance in terms of degradation stability in Hanks' solution. Zn-Cu alloys presented an antibacterial effect for S. aureus controlled by diffusion mechanisms and by contact. Biocompatibility was dependent on the degradation rate and the nature of the corrosion products.

| S-EPMC8121665 | biostudies-literature

Contact Characteristics and Tribological Properties of the Weaving Surface of Mn-Cu and Fe-Zn Damping Alloys.

Project description:In this paper, laser texturing is performed on the surface of Mn-Cu and Fe-Zn damping alloys and the tribological properties of the samples with various surface weaves under dry-sliding conditions are investigated. The results show that the surface weave parameters affect the size of the contact surface and change the number of micro-convex bodies at the contact interface. This leads to changes in the tangential damping of the contact and further affects the magnitude of the friction coefficient. Additionally, the damping properties significantly affect the wear mechanism and make it more prone to adhesive wear.

| S-EPMC9105199 | biostudies-literature

Atomic Structure of Hardening Precipitates in Al-Mg-Si Alloys: Influence of Minor Additions of Cu and Zn.

Project description:Shifting toward sustainability and low carbon emission necessitates recycling. Aluminum alloys can be recycled from postconsumer scrap with approximately 5% of the energy needed to produce the same amount of primary alloys. However, the presence of certain alloying elements, such as copper and zinc, as impurities in recycled Al-Mg-Si alloys is difficult to avoid. This work has investigated the influence of tiny concentrations of Cu (0.05 wt %) and Zn (0.06 wt %), individually and in combination, on the precipitate crystal structures in Al-Mg-Si alloys in peak aged and overaged conditions. To assess whether such concentrations can affect the hardening precipitate structures, atomic resolution high-angle annular dark-field scanning transmission electron microscopy and atom probe tomography were adopted. The results indicate that low levels of Cu or Zn have a significant influence. Both elements showed a relatively high tendency to incorporate into precipitate structures, where Cu occupies specific atomic sites, creating its own local atomic configurations. However, Zn exhibited distinct behavior through the formation of extended local areas with 2-fold symmetry and mirror planes, not previously observed in precipitates in Al-Mg-Si alloys. Incorporation of Cu and/or Zn will influence the precipitates' electrochemical potential relative to matrix- and precipitate-free zones and thus the corrosion resistance. Furthermore, the presence of Cu/Zn structures (e.g., β'Cu, Q'/C) enhances the thermal stability of these precipitates and, accordingly, the mechanical properties of the material. The results obtained from this work are highly relevant to the topic of recycling of aluminum alloys, where accumulation of certain alloying elements is almost unavoidable; thus, tight compositional control might be critical to avoid quality degradation.

| S-EPMC10722592 | biostudies-literature

The influence of Ca and Cu additions on the microstructure, mechanical and degradation properties of Zn-Ca-Cu alloys for absorbable wound closure device applications.

Project description:Novel ternary Zn-Ca-Cu alloys were studied for the development of absorbable wound closure device material due to Ca and Cu's therapeutic values to wound healing. The influence of Ca and Cu on the microstructure, mechanical and degradation properties of Zn were investigated in the as-cast state to establish the fundamental understanding on the Zn-Ca-Cu alloy system. The microstructure of Zn-0.5Ca-0.5Cu, Zn-1.0Ca-0.5Cu, and Zn0.5Ca-1.0Cu is composed of intermetallic phase CaZn13 distributed within the Zn-Cu solid solution. The presence of CaZn13 phase and Cu as solute within the Zn matrix, on the one hand, exhibited a synergistic effect on the grain refinement of Zn, reducing the grain size of pure Zn by 96%; on the other hand, improved the mechanical properties of the ternary alloys through solid solution strengthening, second phase strengthening, and grain refinement. The degradation properties of Zn-Ca-Cu alloys are primarily influenced by the micro-galvanic corrosion between Zn-Cu matrix and CaZn13 phase, where the 0.5% and 1.0% Ca addition increased the corrosion rate of Zn from 11.5 μm/y to 19.8 μm/y and 29.6 μm/y during 4 weeks immersion test.

| S-EPMC7658446 | biostudies-literature

Model Protective Films on Cu-Zn Alloys Simulating the Inner Surfaces of Historical Brass Wind Instruments by EIS and XPS.

Project description:The present work focuses on the characterization of brass surfaces after contact with artificial saliva solution at pH 7.4 and phosphate buffer solution at pH 7 simulating two extreme conditions that might occur when playing ancient brass wind instruments in the context of historically informed performance practice. The composition and the morphology of the film formed following the contact with the solutions for 1, 3, and 16 h were investigated by ex situ X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM) to shed a light on the surface changes upon time. In situ electrochemical impedance spectroscopy (EIS) was used to study the mechanism of corrosion and protection of the alloys. The results could be interpreted using a reliable equivalent electrical circuit; they provided evidence that the alloys behave differently when in contact to the various solutions. In saliva solution the formation on the brass surface of a thick surface film was observed, composed of crystallites of about 200 nm size mainly composed of CuSCN and Zn3(PO4)2. This layer hinders the alloy dissolution. The contact of the alloys with the buffer solution originated a much thinner layer composed of Cu2O, ZnO, and a small amount of Zn3(PO4)2. This film is rapidly formed and does not evolve upon time in a protective film.

| S-EPMC7174669 | biostudies-literature

Atomistic simulations of dislocation mobility in refractory high-entropy alloys and the effect of chemical short-range order.

Project description:Refractory high-entropy alloys (RHEAs) are designed for high elevated-temperature strength, with both edge and screw dislocations playing an important role for plastic deformation. However, they can also display a significant energetic driving force for chemical short-range ordering (SRO). Here, we investigate mechanisms underlying the mobilities of screw and edge dislocations in the body-centered cubic MoNbTaW RHEA over a wide temperature range using extensive molecular dynamics simulations based on a highly-accurate machine-learning interatomic potential. Further, we specifically evaluate how these mechanisms are affected by the presence of SRO. The mobility of edge dislocations is found to be enhanced by the presence of SRO, whereas the rate of double-kink nucleation in the motion of screw dislocations is reduced, although this influence of SRO appears to be attenuated at increasing temperature. Independent of the presence of SRO, a cross-slip locking mechanism is observed for the motion of screws, which provides for extra strengthening for refractory high-entropy alloy system.

| S-EPMC8357793 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data