Development of very high Jc in Ba(Fe1-xCox)2As2 thin films grown on CaF2.

ABSTRACT: Ba(Fe(1-x)Co(x))(2)As(2) is the most tunable of the Fe-based superconductors (FBS) in terms of acceptance of high densities of self-assembled and artificially introduced pinning centres which are effective in significantly increasing the critical current density, J(c). Moreover, FBS are very sensitive to strain, which induces an important enhancement in critical temperature, T(c), of the material. In this paper we demonstrate that strain induced by the substrate can further improve J(c) of both single and multilayer films by more than that expected simply due to the increase in T(c). The multilayer deposition of Ba(Fe(1-x)Co(x))(2)As(2) on CaF2 increases the pinning force density (F(p) = J(c) × µ0H) by more than 60% compared to a single layer film, reaching a maximum of 84 GN/m(3) at 22.5 T and 4.2 K, the highest value ever reported in any 122 phase.

SUBMITTER: Tarantini C

PROVIDER: S-EPMC4252889 | biostudies-other | 2014

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

High field superconducting properties of Ba(Fe1-xCox)2As2 thin films.

Project description:In general, the critical current density, Jc, of type II superconductors and its anisotropy with respect to magnetic field orientation is determined by intrinsic and extrinsic properties. The Fe-based superconductors of the '122' family with their moderate electronic anisotropies and high yet accessible critical fields (Hc2 and Hirr) are a good model system to study this interplay. In this paper, we explore the vortex matter of optimally Co-doped BaFe2As2 thin films with extended planar and c-axis correlated defects. The temperature and angular dependence of the upper critical field is well explained by a two-band model in the clean limit. The dirty band scenario, however, cannot be ruled out completely. Above the irreversibility field, the flux motion is thermally activated, where the activation energy U0 is going to zero at the extrapolated zero-kelvin Hirr value. The anisotropy of the critical current density Jc is both influenced by the Hc2 anisotropy (and therefore by multi-band effects) as well as the extended planar and columnar defects present in the sample.

| S-EPMC4661601 | biostudies-literature

Strain evolution of each type of grains in poly-crystalline (Ba,Sr)TiO(3) thin films grown by sputtering.

Project description:The strain states of [111]-, [110]-, and [002]-oriented grains in poly-crystalline sputtered (Ba,Sr)TiO(3) thin films on highly [111]-oriented Pt electrode/Si substrates were carefully examined by X-ray diffraction techniques. Remarkably, [002]-oriented grains respond more while [110]- and [111]-oriented grains do less than the theoretically estimated responses, which is understandable from the arrangement of the TiO(6) octahedra with respect to the stress direction. Furthermore, such mechanical responses are completely independent of the degree of crystallization and film thickness. The transition growth temperature between the positive and negative strains was also different depending on the grain orientation. The unstrained lattice parameter for each type of grain was different suggesting that the oxygen vacancy concentration for each type of grain is different, too. The results reveal that polycrystalline (Ba,Sr)TiO(3) thin films are not an aggregation of differently oriented grains which simply follow the mechanical behavior of single crystal with different orientations.

| S-EPMC3516808 | biostudies-other

Highly Reduced Saturation Magnetization in Epitaxially Grown Ferrimagnetic Heusler Thin Films.

Project description:The key of spintronic devices using the spin-transfer torque phenomenon is the effective reduction of switching current density by lowering the damping constant and the saturation magnetization while retaining strong perpendicular magnetic anisotropy. To reduce the saturation magnetization, particular conditions such as specific substitutions or buffer layers are required. Herein, we demonstrate highly reduced saturation magnetization in tetragonal D022 Mn3-x Ga thin films prepared by rf magnetron sputtering, where the epitaxial growth is examined on various substrates without any buffer layer. As the lattice mismatch between the sample and the substrate decreases from LaAlO3 and (LaAlO3)0.3(Sr2AlTaO6)0.7 to SrTiO3, the quality of Mn3-x Ga films is improved together with the magnetic and electronic properties. Especially, the Mn3-x Ga thin film epitaxially grown on the SrTiO3 substrate, fully oriented along the c axis perpendicular to the film plane, exhibits significantly reduced saturation magnetization as low as 0.06 ?B, compared to previous results. By the structural and chemical analyses, we find that the predominant removal of Mn II atoms and the large population of Mn3+ ions affect the reduced saturation magnetization. Our findings provide insights into the magnetic properties of Mn3-x Ga crystals, which promise great potential for spin-related device applications.

| S-EPMC6788061 | biostudies-literature

Skyrmion Phase in MnSi Thin Films Grown on Sapphire by a Conventional Sputtering.

Project description:Topologically protected chiral skyrmions are an intriguing spin texture that has attracted much attention because of fundamental research and future spintronic applications. MnSi with a non-centrosymmetric structure is a well-known material hosting a skyrmion phase. To date, the preparation of MnSi crystals has been investigated by using special instruments with an ultrahigh vacuum chamber. Here, we introduce a facile way to grow MnSi films on a sapphire substrate using a relatively low vacuum environment of conventional magnetron sputtering. Although the as-grown MnSi films have a polycrystalline nature, a stable skyrmion phase in a broad range of temperatures and magnetic fields is observed via magnetotransport properties including phenomenological scaling analysis of the Hall resistivity contribution. Our findings provide not only a general way to prepare the materials possessing skyrmion phases but also insight into further research to stimulate more degrees of freedom in our inquisitiveness.

| S-EPMC7788108 | biostudies-literature

Very high commutation quality factor and dielectric tunability in nanocomposite SrTiO3 thin films with Tc enhanced to >300 °C.

Project description:We report on nanoengineered SrTiO3-Sm2O3 nanocomposite thin films with the highest reported values of commutation quality factor (CQF or K-factor) of >2800 in SrTiO3 at room temperature. The films also had a large tunability of dielectric constant (49%), low tangent loss (tan?? = 0.01) and a Curie temperature for SrTiO3 > 300 °C, making them very attractive for tunable RF applications. The enhanced properties originate from the unique nanostructure in the films, with <20 nm diameter strain-controlling Sm2O3 nanocolumns embedded in a SrTiO3 matrix. Very large out-of-plane strains (up to 2.6%) and high tetragonality (c/a) (up to 1.013) were induced in the SrTiO3. The K-factor was further enhanced by adding 1 at% Sc3+ (acceptor) dopant in SrTiO3 to a value of 3300 with the tangent loss being ?0.01 up to 1000 kV cm-1.

| S-EPMC5815283 | biostudies-literature

Oxygen-vacancy-induced antiferromagnetism to ferromagnetism transformation in Eu₀.₅Ba₀.₅TiO₃₋δ multiferroic thin films.

Project description:Oxygen vacancies (V(O)) effects on magnetic ordering in Eu₀.₅Ba₀.₅TiO₃₋δ (EBTO₃₋δ) thin films have been investigated using a combination of experimental measurements and first-principles density-functional calculations. Two kinds of EBTO₃₋δ thin films with different oxygen deficiency have been fabricated. A nuclear resonance backscattering spectrometry technique has been used to quantitatively measure contents of the V(O). Eu₀.₅Ba₀.₅TiO₃ ceramics have been known to exhibit ferroelectric (FE) and G-type antiferromagnetic (AFM) properties. While, a ferromagnetic (FM) behavior with a Curie temperature of 1.85 K has been found in the EBTO₃₋δ thin films. Spin-polarized Ti(3+) ions, which originated from the V(O), has been proven to mediate a FM coupling between the local Eu 4f spins and were believed to be responsible for the great change of the magnetic ordering. Considering the easy formation of V(O), our work opens up a new avenue for achieving co-existence of FM and FE orders in oxide materials.

| S-EPMC3767944 | biostudies-literature

Enhanced Thermoelectric Performance of c-Axis-Oriented Epitaxial Ba-Doped BiCuSeO Thin Films.

Project description:We reported the epitaxial growth of c-axis-oriented Bi1-xBaxCuSeO (0?? x ??10%) thin films and investigated the effect of Ba doping on the structure, valence state of elements, and thermoelectric properties of the films. X-ray photoelectron spectroscopy analysis reveal that Bi3+ is partially reduced to the lower valence state after Ba doping, while Cu and Se ions still exist as +?1 and -?2 valence state, respectively. As the Ba doping content increases, both resistivity and Seebeck coefficient decrease because of the increased hole carrier concentration. A large power factor, as high as 1.24 mWm-1 K-2 at 673 K, has been achieved in the 7.5% Ba-doped BiCuSeO thin film, which is 1.5 times higher than those reported for the corresponding bulk samples. Considering that the nanoscale-thick Ba-doped films should have a very low thermal conductivity, high ZT can be expected in the films.

| S-EPMC6261905 | biostudies-other

High electron mobility and low carrier concentration of hydrothermally grown ZnO thin films on seeded a-plane sapphire at low temperature.

Project description:Hydrothermal zinc oxide (ZnO) thick films were successfully grown on the chemical vapor deposition (CVD)-grown thick ZnO seed layers on a-plane sapphire substrates using the aqueous solution of zinc nitrate dehydrate (Zn(NO3)2). The use of the CVD ZnO seed layers with the flat surfaces seems to be a key technique for obtaining thick films instead of vertically aligned nanostructures as reported in many literatures. All the hydrothermal ZnO layers showed the large grains with hexagonal end facets and were highly oriented towards the c-axis direction. Photoluminescence (PL) spectra of the hydrothermal layers were composed of the ultraviolet (UV) emission (370 to 380 nm) and the visible emission (481 to 491 nm), and the intensity ratio of the former emission (I UV) to the latter emission (I VIS) changed, depending on both the molarity of the solution and temperature. It is surprising that all the Hall mobilities for the hydrothermal ZnO layers were significantly larger than those for their corresponding CVD seed films. It was also found that, for the hydrothermal films grown at 70°C to 90°C, the molarity dependences of I UV/I VIS resembled those of mobilities, implying that the mobility in the film is affected by the structural defects. The highest mobility of 166 cm(2)/Vs was achieved on the hydrothermal film with the carrier concentration of 1.65?×?10(17) cm(-3) grown from the aqueous solution of 40 mM at 70°C.

| S-EPMC4312313 | biostudies-literature

Transparent and conducting boron doped ZnO thin films grown by aerosol assisted chemical vapor deposition.

Project description:ZnO based transparent conducting oxides are important as they provide an alternative to the more expensive Sn : In2O3 that currently dominates the industry. Here, we investigate B-doped ZnO thin films grown via aerosol assisted chemical vapour deposition. B : ZnO films were produced from zinc acetate and triethylborane using either tetrahydrofuran or methanol (MeOH) as the solvent. The lowest resistivity of 5.1 × 10-3 Ω cm along with a visible light transmittance of ∼75-80% was achieved when using MeOH as the solvent. XRD analysis only detected the wurtzite phase of ZnO suggesting successful solid solution formation with B3+ substituting Zn2+ sites in the lattice. Refinement of the XRD patterns showed minimal distortion to the ZnO unit cell upon doping when MeOH was the solvent due to the immiscibility of the [BEt3] solution (1.0 M solution in hexane) in methanol that limited the amount of B going into the films, thus preventing excessive doping.

| S-EPMC9671099 | biostudies-literature

Localized Strain Measurement in Molecular Beam Epitaxially Grown Chalcogenide Thin Films by Micro-Raman Spectroscopy.

Project description:We developed an experimental metrology for measuring local strain in molecular beam epitaxially (MBE) grown crystalline chalcogenide thin films through micro-Raman spectroscopy. For In2Se3 and Bi2Se3 on c-plane sapphire substrates, the transverse-optical vibrational mode (A1 phonon) is most sensitive to strain. We first calibrated the phonon frequency-strain relationship in each material by introducing strain in flexible substrates. The Raman shift-strain coefficient is -1.97 cm-1/% for the In2Se3 A1(LO + TO) mode and -1.68 cm-1/% for the Bi2Se3 A1g 2 mode. In2Se3 and Bi2Se3 samples exhibit compressive strain and tensile strain, respectively. The observations are compliant with predictions from the opposite relative thermal expansion coefficient between the sample and the substrate. We also map strain cartography near the edge of as-grown MBE samples. In In2Se3, the strain accumulates with increasing film thickness, while a low strain is observed in thicker Bi2Se3 films.

| S-EPMC7161023 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data