Ultrasensitive non-enzymatic glucose sensor based on three-dimensional network of ZnO-CuO hierarchical nanocomposites by electrospinning.

ABSTRACT: Three-dimensional (3D) porous ZnO-CuO hierarchical nanocomposites (HNCs) nonenzymatic glucose electrodes with different thicknesses were fabricated by coelectrospinning and compared with 3D mixed ZnO/CuO nanowires (NWs) and pure CuO NWs electrodes. The structural characterization revealed that the ZnO-CuO HNCs were composed of the ZnO and CuO mixed NWs trunk (~200?nm), whose outer surface was attached with small CuO nanoparticles (NPs). Moreover, a good synergetic effect between CuO and ZnO was confirmed. The nonenzymatic biosensing properties of as prepared 3D porous electrodes based on fluorine doped tin oxide (FTO) were studied and the results indicated that the sensing properties of 3D porous ZnO-CuO HNCs electrodes were significantly improved and depended strongly on the thickness of the HNCs. At an applied potential of + 0.7?V, the optimum ZnO-CuO HNCs electrode presented a high sensitivity of 3066.4??AmM(-1)cm(-2), the linear range up to 1.6?mM, and low practical detection limit of 0.21??M. It also showed outstanding long term stability, good reproducibility, excellent selectivity and accurate measurement in real serum sample. The formation of special hierarchical heterojunction and the well-constructed 3D structure were the main reasons for the enhanced nonenzymatic biosensing behavior.

SUBMITTER: Zhou C

PROVIDER: S-EPMC4260231 | biostudies-other | 2014

REPOSITORIES: biostudies-other

ACCESS DATA

Publications

Ultrasensitive non-enzymatic glucose sensor based on three-dimensional network of ZnO-CuO hierarchical nanocomposites by electrospinning.

Zhou Chunyang C Xu Lin L Song Jian J Xing Ruiqing R Xu Sai S Liu Dali D Song Hongwei H

Scientific reports 20141209

Three-dimensional (3D) porous ZnO-CuO hierarchical nanocomposites (HNCs) nonenzymatic glucose electrodes with different thicknesses were fabricated by coelectrospinning and compared with 3D mixed ZnO/CuO nanowires (NWs) and pure CuO NWs electrodes. The structural characterization revealed that the ZnO-CuO HNCs were composed of the ZnO and CuO mixed NWs trunk (~200 nm), whose outer surface was attached with small CuO nanoparticles (NPs). Moreover, a good synergetic effect between CuO and ZnO was ...[more]

PMID: 25488502

Similar Datasets

Project description:The synthesis of optoelectrically enhanced nanomaterials should be continuously improved by employing time- and energy-saving techniques. The porous zinc oxide (ZnO) and copper-doped ZnO nanocomposites (NCs) were synthesized by the time- and energy-efficient solution combustion synthesis (SCS) approach. In this SCS approach, once the precursor-surfactant complex ignition point is reached, the reaction starts and ends within a short time without the need for any external energy. The TGA-DTA analysis confirmed that 500 °C was the point at which stable metal oxide was obtained. The doping and heterojunction strategy improved the optoelectric properties of the NCs more than the individual constituents, which then enhanced the materials' charge transfer and optical absorption capabilities. The porosity, nanoscale crystallite size (15-50 nm), and formation of Cu/CuO-ZnO NCs materials were confirmed from the XRD, SEM, and TEM/HRTEM analyses. The obtained d-spacing values of 0.275 and 0.234 nm confirm the formation of ZnO and CuO crystals, respectively. The decrease in photoluminescence intensity for the doped NCs corroborates a reduction in electron-hole recombination. On the Mott-Schottky analysis, the positive slope for ZnO confirms the n-type character, while the negative and positive slopes of the NCs confirm the p- and n-type characters, respectively. A diffusion-controlled type of charge transfer process on the electrode surface was confirmed from the cyclic voltammetric analysis. Thus, the overall analysis shows the applicability of the less expensive and more efficient SCS for several applications, such as catalysis and sensors. To confirm this, an organic catalytic reduction reaction of 4-nitrophenol to 4-aminophenol was tested. Within three and a half minutes, the catalytic reduction result showed the great potential of NCs over ZnO NPs. Thus, the energy- and time-saving SCS approach has a great future outlook as an industrial pollutant catalytic reduction application.

Dataset Information

Ultrasensitive non-enzymatic glucose sensor based on three-dimensional network of ZnO-CuO hierarchical nanocomposites by electrospinning.

Publications

Ultrasensitive non-enzymatic glucose sensor based on three-dimensional network of ZnO-CuO hierarchical nanocomposites by electrospinning.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets