Low Temperature Vacuum Synthesis of Triangular CoO Nanocrystal/Graphene Nanosheets Composites with Enhanced Lithium Storage Capacity.

ABSTRACT: CoO nanocrystal/graphene nanosheets (GNS) composites, consisting of a triangular CoO nanocrystal of 2~20 nm on the surface of GNS, are synthesized by a mild synthetic method. First, cobalt acetate tetrahydrate is recrystallized in the alcohol solution at a low temperature. Then, graphene oxide mixed with cobalt-precursor followed by high vacuum annealing to form the CoO nanocrystal/GNS composites. The CoO nanocrystal/GNS composites exhibit a high reversible capacity of 1481.9 m Ah g(-1) after 30 cycles with a high Coulombic efficiency of over 96% when used as anode materials for lithium ion battery. The excellent electrochemical performances may be attributed to the special structure of the composites. The well-dispersed triangular CoO nanocrystal on the substrate of conductive graphene can not only have a shorter diffusion length for lithium ions, better stress accommodation capability during the charge-discharge processes and more accessible active sites for lithium-ion storage and electrolyte wetting, but also possess a good conductive network, which can significantly improve the whole electrochemical performance.

SUBMITTER: Guan Q

PROVIDER: S-EPMC4426703 | biostudies-other | 2015

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:The practical application of polymer composites in the electronic and communications industries often requires multi-properties, such as high thermal conductivity (TC), efficient electromagnetic interference (EMI) shielding ability with low electrical conductivity, superior tribological performance, reliable thermal stability and excellent mechanical properties. However, the integration of these mutually exclusive properties is still a challenge, ascribed to their different requirement on the incorporated nanofillers, composite microstructure as well as processing process. Herein, a well-designed boron nitride nanosheet (BN)/graphene nanosheet (GNP)/polyphenylene sulfide (PPS) composite with a dual-segregated structure is fabricated via high-pressure molding. Rather than homogenous mixing of the hybrid fillers, GNP is first coated on PPS particles and followed by encapsulating the conductive GNP layers with insulating BN, forming a BN shell-GNP layer-PPS core composite particles. After hot-pressing, a dual segregated structure is constructed, in which GNP and BN are distinctly separated and arranged in the interfaces of PPS, which on the one hand gives rise to high thermal conductivity, and on the other hand, the aggregated BN layer can act as an “isolation belt” to effectively reduce the electronic transmission. Impressively, high-pressure is loaded and it has a more profound effect on the EMI shielding and thermal conductive properties of PPS composites with a segregated structure than that with homogenous mixed-structure composites. Intriguingly, the synergetic enhancement effect of BN and GNP on both thermal conductive performance and EMI shielding is stimulated by high pressure. Consequently, PPS composites with 30 wt% GNP and 10 wt% BN hot-pressed under 600 MPa present the most superior comprehensive properties with a high TC of 6.4 W/m/K, outstanding EMI SE as high as 70 dB, marvelous tribological performance, reliable thermal stability and satisfactory mechanical properties, which make it promising for application in miniaturized electronic devices in complex environments.

Dataset Information

Low Temperature Vacuum Synthesis of Triangular CoO Nanocrystal/Graphene Nanosheets Composites with Enhanced Lithium Storage Capacity.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets