Ultralow charge-transfer resistance with ultralow Pt loading for hydrogen evolution and oxidation using Ru@Pt core-shell nanocatalysts.

ABSTRACT: We evaluated the activities of well-defined Ru@Pt core-shell nanocatalysts for hydrogen evolution and oxidation reactions (HER-HOR) using hanging strips of gas diffusion electrode (GDE) in solution cells. With gas transport limitation alleviated by micro-porous channels in the GDEs, the charge transfer resistances (CTRs) at the hydrogen reversible potential were conveniently determined from linear fit of ohmic-loss-corrected polarization curves. In 1 M HClO4 at 23 °C, a CTR as low as 0.04 Ω cm(-2) was obtained with only 20 μg cm(-2) Pt and 11 μg cm(-2) Ru using the carbon-supported Ru@Pt with 1:1 Ru:Pt atomic ratio. Derived from temperature-dependent CTRs, the activation barrier of the Ru@Pt catalyst for the HER-HOR in acids is 0.2 eV or 19 kJ mol(-1). Using the Ru@Pt catalyst with total metal loadings <50 μg cm(-2) for the HER in proton-exchange-membrane water electrolyzers, we recorded uncompromised activity and durability compared to the baseline established with 3 mg cm(-2) Pt black.

SUBMITTER: Wang JX

PROVIDER: S-EPMC4507399 | biostudies-other | 2015

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Engineering Ru@Pt Core-Shell Catalysts for Enhanced Electrochemical Oxygen Reduction Mass Activity and Stability.

Project description:Improving the performance of oxygen reduction reaction (ORR) electrocatalysts is essential for the commercial efficacy of many renewable energy technologies, including low temperature polymer electrolyte fuel cells (PEFCs). Herein, we report highly active and stable carbon-supported Ru@Pt core-shell nanoparticles (Ru@Pt/C) prepared by a wet chemical synthesis technique. Through rotating disc electrode testing, the Ru@Pt/C achieves an ORR Pt mass-based activity of 0.50 A mgPt-1 at 0.9 V versus the reversible hydrogen electrode (RHE), which exceeds the activity of the state-of-the-art commercial Pt/C catalyst as well as the Department of Energy 2020 PEFC electrocatalyst activity targets for transportation applications. The impact of various synthetic parameters, including Pt to Ru ratios and catalyst pretreatments (i.e., annealing) are thoroughly explored. Pt-based mass activity of all prepared Ru@Pt/C catalysts was found to exceed 0.4 mgPt-1 across the range of compositions investigated, with the maximum activity catalyst having a Ru:Pt ratio of 1:1. This optimized composition of Ru@Pt/C catalyst demonstrated remarkable stability after 30,000 accelerated durability cycles (0.6 to 1.0 V vs. RHE at 125 mV s-1), maintaining 85% of its initial mass activity. Scanning transmission electron microscopy energy dispersive spectroscopy (STEM-EDS) analysis at various stages of electrochemical testing demonstrated that the Pt shell can provide sufficient protection against the dissolution of the otherwise unstable Ru core.

| S-EPMC5791125 | biostudies-literature

Dye-sensitized Pt@TiO2 core-shell nanostructures for the efficient photocatalytic generation of hydrogen.

Project description:Pt@TiO2 core-shell nanostructures were prepared through a hydrothermal method. The dye-sensitization of these Pt@TiO2 core-shell structures allows for a high photocatalytic activity for the generation of hydrogen from proton reduction under visible-light irradiation. When the dyes and TiO2 were co-excited through the combination of two irradiation beams with different wavelengths, a synergic effect was observed, which led to a greatly enhanced H2 generation yield. This is attributed to the rational spatial distribution of the three components (dye, TiO2, Pt), and the vectored transport of photogenerated electrons from the dye to the Pt particles via the TiO2 particle bridge.

| S-EPMC3999845 | biostudies-literature

Ultra-high-performance core-shell structured Ru@Pt/C catalyst prepared by a facile pulse electrochemical deposition method.

Project description:Core-shell structured catalysts, made by placing either a monolayer or a thin layer of a noble metal on relatively cheap core-metal nanoparticles, are fascinating and promising fuel cell catalysts due to their high utilization of noble metals. Here, we report our development of a core-shell structured catalyst, Ru@Pt/C, generated by a novel and facile pulse electrochemical deposition (PED) approach. We demonstrate that compared with a commercial Pt/C catalyst, this novel catalyst achieves over four times higher mass activity towards the anodic oxidation of methanol, and 3.6 times higher mass activity towards the cathodic reduction of oxygen. Importantly, we find that the intrinsic activity of Pt in this Ru@Pt/C catalyst is doubled due to the formation of the core-shell structure. The catalyst also shows superior stability: even after 2000 scans, it still retains up to 90% of the peak current. Our findings demonstrate that this novel PED approach is a promising method for preparing high-performance core-shell catalysts for fuel cell applications.

| S-EPMC4522673 | biostudies-literature

A self-supporting bimetallic Au@Pt core-shell nanoparticle electrocatalyst for the synergistic enhancement of methanol oxidation.

Project description:The morphology of Pt-Au bimetal nanostructures plays an important role in enhancing the catalytic capability, catalytic stability and utilization efficiency of the platinum. We designed and successfully prepared Au@Pt nanoparticles (NPs) through an economical, surfactant-free and efficient method of seed-mediated growth. The Au@Pt NPs displayed electrochemical performances superior to those of commercial Pt/C catalysts because their agglomeration was prevented and exhibited better long-term stability with respect to methanol oxidation in acidic media by efficiently removing intermediates. Among the obtained Au@Pt NPs, Au90@Pt10 NPs exhibited the most significantly enhanced catalytic performance for the methanol oxidation reaction (MOR). Their mass and electrochemically active surface area (ECSA)-normalized current densities are approximately 3.9 and 4.6 times higher than those of commercial Pt/C catalysts, respectively. The oxidation current densities of the Au90@Pt10 NPs are approximately 1.8 times higher than those of commercial Pt/C catalysts after 4000 s of continuous measurement because the small Pt NPs grown on the surface of the Au90@Pt10 NPs were effectively stabilized by the Au metal support. This approach may be a facile method for the synthesis of self-supported bimetallic nanostructures, which is of great significance for the development of high performance electrocatalysts and sensors.

| S-EPMC5524951 | biostudies-literature

Ultra-Low Pt Loading in PtCo Catalysts for the Hydrogen Oxidation Reaction: What Role Do Co Nanoparticles Play?

Project description:The effect of the nature of the catalyst on the performance and mechanism of the hydrogen oxidation reaction (HOR) is discussed for the first time in this work. HOR is an anodic reaction that takes place in anionic exchange membrane fuel cells (AEMFCs) and hydrogen pumps (HPs). Among the investigated catalysts, Pt exhibited the best performance in the HOR. However, the cost and the availability limit the usage. Co is incorporated as a co-catalyst due to its oxophylic nature. Five different PtCo catalysts with different Pt loading values were synthesized in order to decrease Pt loading. The catalytic activities and the reaction mechanism were studied via electrochemical techniques, and it was found that both features are a function of Pt loading; low-Pt-loading catalysts (Pt loading < 2.7%) led to a high half-wave potential in the hydrogen oxidation reaction, which is related to higher activation energy and an intermediate Tafel slope value, related to a mixed HOR mechanism. However, catalysts with moderate Pt loading (Pt loading > 3.1%) exhibited lower E1/2 than the other catalysts and exhibited a mechanism similar to that of commercial Pt catalysts. Our results demonstrate that Co plays an active role in the HOR, facilitating Hads desorption, which is the rate-determining step (RDS) in the mechanism of the HOR.

| S-EPMC8625230 | biostudies-literature

Ultralow-temperature photochemical synthesis of atomically dispersed Pt catalysts for the hydrogen evolution reaction.

Project description:Efficient control of nucleation is a prerequisite for the solution-phase synthesis of nanocrystals. Although the thermodynamics and kinetics of the formation of metal nanoparticles have been largely investigated, fully suppressing the nucleation in solution synthesis remains a major challenge due to the high surface free energy of isolated atoms. In this article, we largely decreased the reaction temperature for ultraviolet (UV) photochemical reduction of H2PtCl6 solution to -60 °C and demonstrated such a method as a fast and convenient process for the synthesis of atomically dispersed Pt. We showed that the ultralow-temperature reaction efficiently inhibited the nucleation process by controlling its thermodynamics and kinetics. Compared with commercial platinum/carbon, the synthesized atomically dispersed Pt catalyst, as a superior HER catalyst, exhibited a lower overpotential of approximately 55 mV at a current density of 100 mA cm-2 and a lower Tafel slope of 26 mV dec-1 and had higher stability in 0.5 M H2SO4.

| S-EPMC6431957 | biostudies-literature

Ultralow Threshold Room Temperature Polariton Condensation in Colloidal CdSe/CdS Core/Shell Nanoplatelets.

Project description:Room-temperature exciton-polariton Bose-Einstein condensation (BEC), a phase transition to single quantum state with strong nonlinearity, provides a new strategy for coherent light sources and ultralow threshold optic switches. In this work, colloidal CdSe/CdS 2D nanoplatelets are embedded into a microcavity, and exciton-polariton BEC is realized with an ultralow threshold of 0.5 µJ cm-2 at room temperature. The superlinear power-dependent emission, macroscopic occupation of the ground state, strong blueshift and broadening of the emission peak, and long-range coherence strongly confirm the realization of the polariton laser. This work suggests considerable prospects for colloidal nanoplatelets in low-cost, high-performance polariton devices, and coherent light sources.

| S-EPMC9218774 | biostudies-literature

Ultrasound-excited hydrogen radical from NiFe layered double hydroxide for preparation of ultrafine supported Ru nanocatalysts in hydrogen storage of N-ethylcarbazole.

Project description:Highly active Ru nanoparticles (Ru NPs) supported on NiFe layered double hydroxide (Ru/NiFe-LDH) are prepared easily using ultrasound-assisted reduction method without chemical reductants and stabilizers. The plentiful hydroxyls on NiFe-LDH are excited into hydrogen radicals (H) under the action of ultrasound for reducing Ru3+ to Ru0. Ru NPs with an average particle size of 1.26 nm highly disperse on the mesopore-like surface of NiFe-LDH, which improve the catalytic performance for N-ethylcarbazole (NEC) hydrogenation. The experimental results show that 5Ru/NiFe-LDH-300-60 exhibits the best catalytic performance with 100% conversion of NEC, 98.88% yield of dodecahydro-N-ethylcarbazole (12H-NEC) and 5.77 wt% mass hydrogen storage capacity under the reaction conditions of 110 ℃, 6 MPa and mRu:mNEC = 0.15 wt% for 80 min. The kinetics study shows that the apparent activation energy is only 25.15 kJ/mol, which is the lowest in the reported literatures. Ru complexes with O-contained groups on NiFe-LDH, improving the catalytic stability in NEC hydrogenation.

| S-EPMC8637643 | biostudies-literature

Hydrogen Isotope Exchange Catalyzed by Ru Nanocatalysts: Labelling of Complex Molecules Containing N-Heterocycles and Reaction Mechanism Insights.

Project description:Ruthenium nanocatalysis can provide effective deuteration and tritiation of oxazole, imidazole, triazole and carbazole substructures in complex molecules using D2 or T2 gas as isotopic sources. Depending on the substructure considered, this approach does not only represent a significant step forward in practice, with notably higher isotope uptakes, a broader substrate scope and a higher solvent applicability compared to existing procedures, but also the unique way to label important heterocycles using hydrogen isotope exchange. In terms of applications, the high incorporation of deuterium atoms, allows the synthesis of internal standards for LC-MS quantification. Moreover, the efficacy of the catalyst permits, even under subatmospheric pressure of T2 gas, the preparation of complex radiolabeled drugs owning high molar activities. From a fundamental point of view, a detailed DFT-based mechanistic study identifying undisclosed key intermediates, allowed a deeper understanding of C-H (and N-H) activation processes occurring at the surface of metallic nanoclusters.

| S-EPMC7187376 | biostudies-literature

Alloy Cu?Pt nanoframes through the structure evolution in Cu-Pt nanoparticles with a core-shell construction.

Project description:Noble metal nanoparticles with hollow interiors and customizable shell compositions have immense potential for catalysis. Herein, we present an unique structure transformation phenomenon for the fabrication of alloy Cu?Pt nanoframes with polyhedral morphology. This strategy starts with the preparation of polyhedral Cu-Pt nanoparticles with a core-shell construction upon the anisotropic growth of Pt on multiply twinned Cu seed particles, which are subsequently transformed into alloy Cu?Pt nanoframes due to the Kirkendall effect between the Cu core and Pt shell. The as-prepared alloy Cu?Pt nanoframes possess the rhombic dodecahedral morphology of their core-shell parents after the structural evolution. In particular, the resulting alloy Cu?Pt nanoframes are more effective for oxygen reduction reaction but ineffective for methanol oxidation reaction in comparison with their original Cu-Pt core-shell precursors.

| S-EPMC4166710 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data