Enhanced thermal properties of novel shape-stabilized PEG composite phase change materials with radial mesoporous silica sphere for thermal energy storage.

ABSTRACT: Radial mesoporous silica (RMS) sphere was tailor-made for further applications in producing shape-stabilized composite phase change materials (ss-CPCMs) through a facile self-assembly process using CTAB as the main template and TEOS as SiO2 precursor. Novel ss-CPCMs composed of polyethylene glycol (PEG) and RMS were prepared through vacuum impregnating method. Various techniques were employed to characterize the structural and thermal properties of the ss-CPCMs. The DSC results indicated that the PEG/RMS ss-CPCM was a promising candidate for building thermal energy storage applications due to its large latent heat, suitable phase change temperature, good thermal reliability, as well as the excellent chemical compatibility and thermal stability. Importantly, the possible formation mechanisms of both RMS sphere and PEG/RMS composite have also been proposed. The results also indicated that the properties of the PEG/RMS ss-CPCMs are influenced by the adsorption limitation of the PEG molecule from RMS sphere with mesoporous structure and the effect of RMS, as the impurities, on the perfect crystallization of PEG.

SUBMITTER: Min X

PROVIDER: S-EPMC4531330 | biostudies-other | 2015

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Novel PEG<sub>6000</sub>-Silica-MWCNTs Shape-Stabilized Composite Phase-Change Materials (ssCPCMs) for Thermal-Energy Storage.

Project description:This paper describes the preparation of new PEG6000-silica-MWCNTs composites as shape-stabilized phase change materials (ssPCMs) for application in latent heat storage. An innovative method was employed to obtain the new organic-inorganic hybrid materials, in which both a part of the PEG chains, used as the phase change material, and a part of the hydroxyl functionalized multiwall carbon nanotubes (MWCNTs-OH), used as thermo-conductive fillers, were covalently connected by newly formed urethane bonds to the in-situ-generated silica matrix. The study's main aim was to investigate the optimal amount of PEG6000 that can be added to the fixed sol-gel reaction mixture so that no leakage of PEG occurs after repeated heating-cooling cycles. The findings show that the optimum PEG6000/NCOTEOS molar ratio was 2/1 (~91.5% PEG6000), because both the connected and free PEG chains interacted strongly with the in-situ-generated silica matrix to form a shape-stabilized material while preserving high phase-transition enthalpies (~153 J/G). Morphological and structural findings obtained by SEM, X-ray and Raman techniques indicated a distribution of the silica component in the amorphous phase (~27% for the optimum composition) located among the crystalline lamellae built by the folded chains of the PEG component. This composite maintained good chemical stability after a 450-cycle thermal test and had a good storage efficiency (~84%).

| S-EPMC10386010 | biostudies-literature

Biomass-Based Shape-Stabilized Composite Phase-Change Materials with High Solar-Thermal Conversion Efficiency for Thermal Energy Storage.

Project description:To alleviate the increasing energy crisis and achieve energy saving and consumption reduction in building materials, preparing shape-stabilized phase-change materials using bio-porous carbon materials from renewable organic waste to building envelope materials is an effective strategy. In this work, pine cone porous biomass carbon (PCC) was prepared via a chemical activation method using renewable biomaterial pine cone as a precursor and potassium hydroxide (KOH) as an activator. Polyethylene glycol (PEG) and octadecane (OD) were loaded into PCC using the vacuum impregnation method to prepare polyethylene glycol/pine cone porous biomass carbon (PEG/PCC) and octadecane/pine cone porous biomass carbon (OD/PCC) shape-stabilized phase-change materials. PCCs with a high specific surface area and pore volume were obtained by adjusting the calcination temperature and amount of KOH, which was shown as a caterpillar-like and block morphology. The shape-stabilized PEG/PCC and OD/PCC composites showed high phase-change enthalpies of 144.3 J/g and 162.3 J/g, and the solar-thermal energy conversion efficiencies of the PEG/PCC and OD/PCC reached 79.9% and 84.8%, respectively. The effects of the contents of PEG/PCC and OD/PCC on the temperature-controlling capability of rigid polyurethane foam composites were further investigated. The results showed that the temperature-regulating and temperature-controlling capabilities of the energy-storing rigid polyurethane foam composites were gradually enhanced with an increase in the phase-change material content, and there was a significant thermostatic plateau in energy absorption at 25 °C and energy release at 10 °C, which decreased the energy consumption.

| S-EPMC10534447 | biostudies-literature

Preparation of a Sustainable Shape-Stabilized Phase Change Material for Thermal Energy Storage Based on Mg2+-Doped CaCO3/PEG Composites.

Project description:The properties of polyethylene glycol-6000 (PEG)/MgCaCO3, a low-cost shape-selective phase change material (ss-PCM), make it highly suitable for solar thermal applications. Nanosized porous MgO-doped CaCO3 with Mg molar concentrations of 5%, 10%, and 15% were synthesized using a hydrothermal technique. The prepared MgO-CaCO3 matrices were then impregnated with PEG to obtain PEG/MgCaCO3 as an ss-PCM. Samples identified as PEG-5MgCaCO3 (P-5-MCC), PEG-10MgCaCO3 (P-10-MCC), and PEG-15MgCaCO3 (P-15-MCC) were prepared and studied. Interestingly, P-10-MCC has the smallest particle size together with a good porous structure compared to the other two materials. The results of thermogravimetric analyses and differential scanning calorimetry indicate that the small particle size and porous structure facilitate the impregnation of approximately 69% of the PEG into the 10-MCC matrix. The latent heat and energy storage efficiency of PEG in the P-10-MCC sample are 152.5 J/g and 96.48%, respectively, which are significantly higher than those of comparable materials. Furthermore, in addition to the improvement of the thermal conductivity of the P-10-MCC, its supercooling is also reduced to some extent. The combined mesoporous and macro-porous structure of P-10-MCC is critical to retaining a large amount of PEG within the matrix, resulting in a high latent heat in the operating temperature range of 35-57 °C. The P-10MCC sample also demonstrates a high energy storage capacity (98.59%), high thermal energy storage/release rates, and exceptional shape-stabilized PCM properties.

| S-EPMC8306958 | biostudies-literature

Fast Thermal Response of Shape-Stabilized Thermal Storage Materials: The Case of Interconnected Netlike Graphene/Hexadecane/HDPE Composites.

Project description:Fast thermal response and sensitivity of organic latent heat storage materials with inherent low thermal conductivity to external temperatures is still a challenge in their practical applications. Herein, a shape-stable heat storage material composite, composed of interconnected netlike graphene, hexadecane, and commonly used high-density polyethylene (HDPE), was obtained using a convenient melt blending method. The start melting temperature, melting temperature, and end melting temperature of the obtained shape-stabilized thermal storage materials are presented, indicating that the response rate of the composites to ambient temperature could be indeed increased. This is because the interconnected netlike graphene with high conductivity intercalated into the HDPE matrix provided many conductive pathways for heat transfer. Therefore, the thermal conductivity of the composites is increased to 0.67 W/(m·K), which is about 123% higher than that of pure hexadecane. Meanwhile, the structure of polyethylene and hexadecane is similar, and hexadecane is uniformly dispersed in polyethylene and perfectly combined with polyethylene, which can effectively prevent the leakage of hexadecane during the phase transition. Thus, the obtained composites may play an important role in thermal management applications such as heat collection, transportation, thermal power conversion, and so forth.

| S-EPMC7271351 | biostudies-literature

Bio-based sunflower carbon/polyethylene glycol shape-stabilized phase change materials for thermal energy storage.

Project description:The exploitation of shape-stabilized phase change materials with high thermal conductivity and energy storage capacity is an effective strategy for improving energy efficiency. In this work, sunflower stem carbon/polyethylene glycol (SS-PEG) and sunflower receptacle carbon/polyethylene glycol (SR-PEG) shape-stabilized phase change materials, utilizing sunflower stem and receptacle biomass carbon with high specific surface area and pore volume obtained by carbonization as frameworks and polyethylene glycol as an energy storage material, were prepared by the vacuum impregnation method. The ability to load polyethylene glycol into the pore structure of carbon materials in different sunflower parts was mainly investigated, and the micro-morphology, compositional structure and thermal properties were characterized and analyzed using SEM, IR spectroscopy, XRD, DSC and TG techniques. The results showed that the carbonized sunflower stems maintained the sieve pore structure, and the carbonized sunflower receptacle was a macroporous structure containing a large number of three-dimensional interconnections. At the same time, the interaction between polyethylene glycol and each carbon material occurred through physisorption. The melting enthalpies of SS-PEG and SR-PEG shape-stabilized phase change materials were 153.4 J g-1 and 171.5 J g-1, respectively, and the loading rates reached 81.9% and 91.5%, with initial thermal decomposition temperatures (T 5%) of 344 °C and 368 °C.

| S-EPMC11294913 | biostudies-literature

Shortwave Infrared Imaging with J-Aggregates Stabilized in Hollow Mesoporous Silica Nanoparticles.

Project description:Tissue is translucent to shortwave infrared (SWIR) light, rendering optical imaging superior in this region. However, the widespread use of optical SWIR imaging has been limited, in part, by the lack of bright, biocompatible contrast agents that absorb and emit light above 1000 nm. J-Aggregation offers a means to transform stable, near-infrared (NIR) fluorophores into red-shifted SWIR contrast agents. Here we demonstrate that J-aggregates of NIR fluorophore IR-140 can be prepared inside hollow mesoporous silica nanoparticles (HMSNs) to result in nanomaterials that absorb and emit SWIR light. The J-aggregates inside PEGylated HMSNs are stable for multiple weeks in buffer and enable high resolution imaging in vivo with 980 nm excitation.

| S-EPMC6746239 | biostudies-literature

Mesoporous CLEAs-silica composite microparticles with high activity and enhanced stability.

Project description:A novel enzyme immobilization approach was used to generate mesoporous enzymes-silica composite microparticles by co-entrapping gelatinized starch and cross-linked phenylalanine ammonia lyase (PAL) aggregates (CLEAs) containing gelatinized starch into biomemitic silica and subsequently removing the starch by α-amylase treatment. During the preparation process, the gelatinzed starch served as a pore-forming agent to create pores in CLEAs and biomimetic silica. The resulting mesoporous CLEAs-silica composite microparticles exhibited higher activity and stability than native PAL, conventional CLEAs, and PAL encapsulated in biomimetic silica. Furthermore, the mesoporous CLEAs-silica composite microparticles displayed good reusability due to its suitable size and mechanical properties, and had excellent stability for storage. The superior catalytic performances were attributed to the combinational unique structure from the intra-cross-linking among enzyme aggregates and hard mesoporous silica shell, which not only decreased the enzyme-support negative interaction and mass-transfer limitations, but also improved the mechanical properties and monodispersity. This approach will be highly beneficial for preparing various bioactive mesoporous composites with excellent catalytic performance.

| S-EPMC4570996 | biostudies-literature

Pore structure modified diatomite-supported PEG composites for thermal energy storage.

Project description:A series of novel composite phase change materials (PCMs) were tailored by blending PEG and five kinds of diatomite via a vacuum impregnation method. To enlarge its pore size and specific surface area, different modification approaches including calcination, acid treatment, alkali leaching and nano-silica decoration on the microstructure of diatomite were outlined. Among them, 8?min of 5?wt% NaOH dissolution at 70?°C has been proven to be the most effective and facile. While PEG melted during phase transformation, the maximum load of PEG could reach 70 wt.%, which was 46% higher than that of the raw diatomite. The apparent activation energy of PEG in the composite was 1031.85?kJ·mol(-1), which was twice higher than that of the pristine PEG. Moreover, using the nano-silica decorated diatomite as carrier, the maximum PEG load was 66?wt%. The composite PCM was stable in terms of thermal and chemical manners even after 200 cycles of melting and freezing. All results indicated that the obtained composite PCMs were promising candidate materials for building applications due to its large latent heat, suitable phase change temperature, excellent chemical compatibility, improved supercooling extent, high thermal stability and long-term reliability.

| S-EPMC5007675 | biostudies-literature

composite DNA storage

Project description:DNA storage of digital media using composite DNA

| PRJEB32427 | ENA

Antibacterial and osteogenic activities of clindamycin-releasing mesoporous silica/carboxymethyl chitosan composite hydrogels.

Project description:Conventional treatment of jaw bone infection is often ineffective at controlling bacterial infection and enhancing bone regeneration. Biodegradable composite hydrogels comprised of carboxymethyl chitosan (CMCS) and clindamycin (CDM)-loaded mesoporous silica nanoparticles (MCM-41), possessing dual antibacterial activity and osteogenic potency, were developed in the present study. CDM was successfully loaded into both untreated and plasma-treated MCM-41 nanoparticles, denoted as (p)-MCM-41, followed by the incorporation of each of CDM-loaded (p)-MCM-41 into CMCS. The resulting CDM-loaded composite hydrogels, (p)-MCM-41-CDM-CMCS, demonstrated slow degradation rates (about 70% remaining weight after 14-day immersion), while the CDM-free composite hydrogel entirely disintegrated after 4-day immersion. The plasma treatment was found to improve drug loading capacity and slow down initial drug burst effect. The prolonged releases of CDM from both (p)-MCM-41-CDM-CMCS retained their antibacterial effect against Streptococcus sanguinis for at least 14 days in vitro. In vitro assessment of osteogenic activity showed that the CDM-incorporated composite hydrogel was cytocompatible to human mesenchymal stem cells (hMSCs) and induced hMSC mineralization via p38-dependent upregulated alkaline phosphatase activity. In conclusion, novel (p)-MCM-41-CDM-CMCS hydrogels with combined controlled release of CDM and osteogenic potency were successfully developed for the first time, suggesting their potential clinical benefit for treatment of intraoral bone infection.

| S-EPMC8441126 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data