Heteroepitaxial Cu2O thin film solar cell on metallic substrates.

ABSTRACT: Heteroepitaxial, single-crystal-like Cu2O films on inexpensive, flexible, metallic substrates can potentially be used as absorber layers for fabrication of low-cost, high-performance, non-toxic, earth-abundant solar cells. Here, we report epitaxial growth of Cu2O films on low cost, flexible, textured metallic substrates. Cu2O films were deposited on the metallic templates via pulsed laser deposition under various processing conditions to study the influence of processing parameters on the structural and electronic properties of the films. It is found that pure, epitaxial Cu2O phase without any trace of CuO phase is only formed in a limited deposition window of P(O2) - temperature. The (00l) single-oriented, highly textured, Cu2O films deposited under optimum P(O2) - temperature conditions exhibit excellent electronic properties with carrier mobility in the range of 40-60 cm(2) V(-1) s(-1) and carrier concentration over 10(16) cm(-3). The power conversion efficiency of 1.65% is demonstrated from a proof-of-concept Cu2O solar cell based on epitaxial Cu2O film prepared on the textured metal substrate.

SUBMITTER: Wee SH

PROVIDER: S-EPMC4635375 | biostudies-other | 2015

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Peel-and-stick: fabricating thin film solar cell on universal substrates.

Project description:Fabrication of thin-film solar cells (TFSCs) on substrates other than Si and glass has been challenging because these nonconventional substrates are not suitable for the current TFSC fabrication processes due to poor surface flatness and low tolerance to high temperature and chemical processing. Here, we report a new peel-and-stick process that circumvents these fabrication challenges by peeling off the fully fabricated TFSCs from the original Si wafer and attaching TFSCs to virtually any substrates regardless of materials, flatness and rigidness. With the peel-and-stick process, we integrated hydrogenated amorphous silicon (a-Si:H) TFSCs on paper, plastics, cell phone and building windows while maintaining the original 7.5% efficiency. The new peel-and-stick process enables further reduction of the cost and weight for TFSCs and endows TFSCs with flexibility and attachability for broader application areas. We believe that the peel-and-stick process can be applied to thin film electronics as well.

| S-EPMC3533453 | biostudies-other

Photoelectrochemical performance of a spin coated TiO2 protected BiVO4-Cu2O thin film tandem cell for unassisted solar water splitting† † Electronic supplementary information (ESI) available. See DOI: https://doi.org/10.1039/d2ra05774c

Project description:A tandem cell consisting of a Mo-BiVO4/TiO2/FeOOH photoanode–Cu2O/TiO2/MoS2 photocathode was prepared for unassisted solar water splitting. The protective TiO2 layer was prepared by a cost-effective spin coating technique. The individual Mo-BiVO4/TiO2/FeOOH photoanode and the Cu2O/TiO2/MoS2 photocathode yielded a current density of ∼0.81 mA cm−2 at 1.23 V vs. RHE and ∼−1.88 mA cm−2 at 0 V vs. RHE, respectively under 100 mW cm−2 xenon lamp illumination. From the individual photoelectrochemical analysis, we identify the operating points of the tandem cell as 0.66 V vs. RHE and 0.124 mA cm−2. The positive current density from the operating points proves the possibility of non-zero operation of the tandem cell. Finally, a two-electrode Mo-BiVO4/TiO2/FeOOH-Cu2O/TiO2/MoS2 tandem cell was constructed and analysed for unassisted operation. The obtained unassisted current density of the tandem cell was ∼65.3 μA cm−2 with better stability compared to the bare BiVO4-Cu2O tandem cell. The results prove that the spin coated TiO2 protective layer can be a viable approach to protect the photoelectrodes from photocorrosion with better stability and enhanced photoelectrochemical (PEC) performance. Mo-BiVO4/TiO2/FeOOH photoanode–Cu2O/TiO2/MoS2 photocathode tandem cells with photoelectrochemical stability testing.

| S-EPMC9627459 | biostudies-literature

Numerical studies on a ternary AgInTe<sub>2</sub> chalcopyrite thin film solar cell.

Project description:This paper theoretically outlines a new n-AlSb/p-AgInTe2/p+-BaSi2 solar cell. The dominance of several factors such as depth, carrier density and defects of every layer on the photovoltaic (PV) outcome has been ascertained applying Solar Cell Capacitance Simulator (SCAPS)-1D computer-based simulator. The AgInTe2 (AIT) solar cell has been probed for finding the role of BaSi2 as a back surface field (BSF) layer. It is revealed that the device power conversion efficiency (PCE) increments from 30% to 34% owing to the use of BaSi2 semiconducting BSF with VOC = 0.90 V, JSC = 43.75 mA/cm2, FF = 86.42%, respectively. The rippling of the output parameters with respect to the change in series and shunt resistances has also been probed and demonstrated. All the findings reveal the prospect of n-AlSb/p-AIT/p+-BaSi2 dual-heterojunction thin film photovoltaic cell.

| S-EPMC10432989 | biostudies-literature

Nanoscale Chemical Analysis of Thin Film Solar Cell Interfaces Using Tip-Enhanced Raman Spectroscopy.

Project description:Interfacial regions play a key role in determining the overall power conversion efficiency of thin film solar cells. However, the nanoscale investigation of thin film interfaces using conventional analytical tools is challenging due to a lack of required sensitivity and spatial resolution. Here, we surmount these obstacles using tip-enhanced Raman spectroscopy (TERS) and apply it to investigate the absorber (Sb2Se3) and buffer (CdS) layers interface in a Sb2Se3-based thin film solar cell. Hyperspectral TERS imaging with 10 nm spatial resolution reveals that the investigated interface between the absorber and buffer layers is far from uniform, as TERS analysis detects an intermixing of chemical compounds instead of a sharp demarcation between the CdS and Sb2Se3 layers. Intriguingly, this interface, comprising both Sb2Se3 and CdS compounds, exhibits an unexpectedly large thickness of 295 ± 70 nm attributable to the roughness of the Sb2Se3 layer. Furthermore, TERS measurements provide compelling evidence of CdS penetration into the Sb2Se3 layer, likely resulting from unwanted reactions on the absorber surface during chemical bath deposition. Notably, the coexistence of ZnO, which serves as the uppermost conducting layer, and CdS within the Sb2Se3-rich region has been experimentally confirmed for the first time. This study underscores TERS as a promising nanoscale technique to investigate thin film inorganic solar cell interfaces, offering novel insights into intricate interface structures and compound intermixing.

| S-EPMC10982994 | biostudies-literature

Enhancing Silicon Solar Cell Performance Using a Thin-Film-like Aluminum Nanoparticle Surface Layer.

Project description:Solar cells play an increasing role in global electricity production, and it is critical to maximize their conversion efficiency to ensure the highest possible production. The number of photons entering the absorbing layer of the solar cell plays an important role in achieving a high conversion efficiency. Metal nanoparticles supporting localized surface plasmon resonances (LSPRs) have for years been suggested for increasing light in-coupling for solar cell applications. However, most studies have focused on materials exhibiting strong LSPRs, which often come with the drawback of considerable light absorption within the solar spectrum, limiting their applications and widespread use. Recently, aluminum (Al) nanoparticles have gained increasing interest due to their tuneable LSPRs in the ultraviolet and visible regions of the spectrum. In this study, we present an ideal configuration for maximizing light in-coupling into a standard textured crystalline silicon (c-Si) solar cell by determining the optimal Al nanoparticle and anti-reflection coating (ARC) parameters. The best-case parameters increase the number of photons absorbed by up to 3.3%. We give a complete description of the dominating light-matter interaction mechanisms leading to the enhancement and reveal that the increase is due to the nanoparticles optically exhibiting both particle- and thin-film characteristics, which has not been demonstrated in earlier works.

| S-EPMC10891793 | biostudies-literature

Non-stick syringe needles: Beneficial effects of thin film metallic glass coating.

Project description:This paper reports on the use of Zr-based (Zr53Cu33Al9Ta5) thin film metallic glass (TFMG) for the coating of syringe needles and compares the results with those obtained using titanium nitride and pure titanium coatings. TFMG coatings were shown to reduce insertion forces by ?66% and retraction forces by ?72%, when tested using polyurethane rubber block. The benefits of TFMG-coated needles were also observed when tested using muscle tissue from pigs. In nano-scratch tests, the TFMG coatings achieved a coefficient of friction (COF) of just ?0.05, which is about one order of magnitude lower than those of other coatings. Finite-element modeling also indicates a significant reduction in injection and retraction forces. The COF can be attributed to the absence of grain boundaries in the TFMG coating as well as a smooth surface morphology and low surface free energy.

| S-EPMC5004157 | biostudies-literature

Combinatorial development of antibacterial Zr-Cu-Al-Ag thin film metallic glasses.

Project description:Metallic alloys are normally composed of multiple constituent elements in order to achieve integration of a plurality of properties required in technological applications. However, conventional alloy development paradigm, by sequential trial-and-error approach, requires completely unrelated strategies to optimize compositions out of a vast phase space, making alloy development time consuming and labor intensive. Here, we challenge the conventional paradigm by proposing a combinatorial strategy that enables parallel screening of a multitude of alloys. Utilizing a typical metallic glass forming alloy system Zr-Cu-Al-Ag as an example, we demonstrate how glass formation and antibacterial activity, two unrelated properties, can be simultaneously characterized and the optimal composition can be efficiently identified. We found that in the Zr-Cu-Al-Ag alloy system fully glassy phase can be obtained in a wide compositional range by co-sputtering, and antibacterial activity is strongly dependent on alloy compositions. Our results indicate that antibacterial activity is sensitive to Cu and Ag while essentially remains unchanged within a wide range of Zr and Al. The proposed strategy not only facilitates development of high-performing alloys, but also provides a tool to unveil the composition dependence of properties in a highly parallel fashion, which helps the development of new materials by design.

| S-EPMC4882501 | biostudies-literature

Preclinical studies of non-stick thin film metallic glass-coated syringe needles.

Project description:Our objective in this study was to determine the biocompatibility and hemocompatibility of thin film metallic glass (TFMG) and its potential use in hypodermic needles for intramuscular or intravenous injection. Mouse and rabbit models were employed under approval from the Institutional Animal Care and Use Committee (n = 5/group, two groups in total for both animal models). Platelet-rich plasma (PRP) was collected from the whole blood of rabbits (ear vein) without anti-coagulant for use in in vitro coagulation tests. Histological analysis and optical microscopy were used to assess the endothelial structure of the inner lining of veins after being punctured with needles and detained for 3 days. Histological analysis of ear vein sections revealed that the extent of endothelial damage after puncturing with a TFMG-coated needle was 33% less than that produced by bare needles. Our results confirm that the deposition of a thin TFMG layer (e.g., Zr53Cu33Al9Ta5) on the surface of hypodermic needle can have remarkably clinical benefits, including anti-adhesion, reduced invasion, and minimal endothelial damage. Our results also confirm the good biocompatibility and hemocompatibility of the TFMG coatings.

| S-EPMC7679377 | biostudies-literature

Quantum size effects on the work function of metallic thin film nanostructures.

Project description:In this paper, we present the direct observation of quantum size effects (QSE) on the work function in ultrathin Pb films. By using scanning tunneling microscopy and spectroscopy, we show that the very existence of quantum well states (QWS) in these ultrathin films profoundly affects the measured tunneling decay constant kappa, resulting in a very rich phenomenon of "quantum oscillations" in kappa as a function of thickness, L, and bias voltage, V(s). More specifically, we find that the phase of the quantum oscillations in kappa vs. L depends sensitively upon the bias voltage, which often results in a total phase reversal at different biases. On the other hand, at very low sample bias (|V(s)| < 0.03 V) the measurement of kappa vs. L accurately reflects the quantum size effect on the work function. In particular, the minima in the quantum oscillations of kappa vs. L occur at the locations where QWS cross the Fermi energy, thus directly unraveling the QSE on the work function in ultrathin films, which was predicted more than three decades ago. This further clarifies several contradictions regarding the relationship between the QWS locations and the work function.

| S-EPMC2919909 | biostudies-literature

SiOxNy back-contact barriers for CZTSe thin-film solar cells.

Project description:The formation of molybdenum diselenide (MoSe2) is widely observed at the back-contact interface for copper zinc tin selenide (CZTSe) thin-film solar cells. Depending on individual selenium (Se) supply and thermal conditions for forming CZTSe absorbers on molybdenum (Mo) substrates, the thickness of MoSe2 can vary from a few hundreds of nanometers up to ≈ 1 μm, which is comparable to the commonly adopted thickness of 1 ~ 1.5 μm for CZTSe absorbers. In this study, for controlling the thickness of interfacial MoSe2, thin diffusion barrier layers of silicon oxynitride (SiOxNy) are deposited onto Mo layers prior to the growth of CZTSe absorbers in the fabrication process. As a result, a reduction in the thicknesses of MoSe2 layers is achieved. In terms of energy conversion efficiency (η), CZTSe solar cells grown on Mo/SiOxNy back contacts suffer a deterioration as the SiOxNy layers get thicker. CZTSe solar cells grown on Mo/SiOxNy/Mo back contacts preserve their efficiencies at ≈ 11% with thin 10 nm SiOxNy layers.

| S-EPMC7802926 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data