Tuning the properties of polyhydroxybutyrate films using acetic acid via solvent casting.

ABSTRACT: Biodegradable polyhydroxybutyrate (PHB) films were fabricated using acetic acid as an alternative to common solvents such as chloroform. The PHB films were prepared using a solvent casting process at temperatures ranging from 80 °C to 160 °C. The crystallinity, mechanical properties and surface morphology of the films cast at different temperatures were characterized and compared to PHB films cast using chloroform as a solvent. Results revealed that the properties of the PHB film varied considerably with solvent casting temperature. In general, samples processed with acetic acid at low temperatures had comparable mechanical properties to PHB cast using chloroform. This acetic acid based method is environmentally friendly, cost efficient and allows more flexible processing conditions and broader ranges of polymer properties than traditional methods.

SUBMITTER: Anbukarasu P

PROVIDER: S-EPMC4671097 | biostudies-other | 2015

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Tuning PEG-DA hydrogel properties via solvent-induced phase separation (SIPS)().

Project description:Poly(ethylene glycol) diacrylate (PEG-DA) hydrogels are widely utilized to probe cell-material interactions and ultimately for a material-guided approach to tissue regeneration. In this study, PEG-DA hydrogels were fabricated via solvent-induced phase separation (SIPS) to obtain hydrogels with a broader range of tunable physical properties including morphology (e.g. porosity), swelling and modulus (G'). In contrast to conventional PEG-DA hydrogels prepared from an aqueous precursor solution, the reported SIPS protocol utilized a dichloromethane (DCM) precursor solution which was sequentially photopolymerized, dried and hydrated. Physical properties were further tailored by varying the PEG-DA wt% concentration (5 wt%-25 wt%) and M(n) (3.4k and 6k g mol (-1)). SIPS produced PEG-DA hydrogels with a macroporous morphology as well as increased G' values versus the corresponding conventional PEG-DA hydrogels. Notably, since the total swelling was not significantly changed versus the corresponding conventional PEG-DA hydrogels, pairs or series of hydrogels represent scaffolds in which morphology and hydration or G' and hydration are uncoupled. In addition, PEG-DA hydrogels prepared via SIPS exhibited enhanced degradation rates.

| S-EPMC3433064 | biostudies-literature

Preparation of Crystallites for Oriented Poly(Lactic Acid) Films Using a Casting Method under a Magnetic Field.

Project description:Poly-l-lactic acid (PLLA) has biocompatibility and unique characteristics such as piezoelectric properties. This attracts attention not only in the environmental field but also in the biomedical and electronic materials fields. In recent years, the literature about orienting PLLA crystals has been promoting new applications for PLLA such as high strength fiberization and piezoelectric properties. This paper presents a new technique to orient the PLLA crystalline through casting under magnetic irradiation. The advantage of this technique is that it is possible to radiate the magnetic field to the PLLA crystalline in an extremely low viscosity environment. Moreover, the heat treatment condition was optimized in order to improve the low crystallinity of casting, and it succeeded in producing a PLLA film with a high degree of orientation and high crystallinity. Furthermore, PLLA/1-butyl-3-methylimidazolium dibutylphosphate (bmimjdbp) composite films were prepared under the same conditions, and this also succeeded in the further improvement of crystallinity.

| S-EPMC6403967 | biostudies-literature

Facile Fabrication of Porous Conductive Thermoplastic Polyurethane Nanocomposite Films via Solution Casting.

Project description:Porous conductive polymers are one of important materials, featuring lightweight, large specific surface area and high porosity. Non-solvent induced phase separation is widely employed to prepare porous polymer sheet materials. Through utilizing water vapor in ambient environment as the non-solvent, a facile approach was developed to produce porous conductive polymer nanocomposites using the conventional solution-casting method. Without using any non-solvent liquids, porous carbon nanofiber/thermoplastic polyurethane (CNF/TPU) nanocomposites were prepared directly by solution casting of their dimethylformamide (DMF) solutions under ambient conditions. The strength of the CNF framework played a key role in preventing the collapse of pores during DMF evaporation. The dependence of porous structures on CNF loading was studied by scanning electron microscopy and porosity measurement. The influence of CNF loading on the mechanical properties, electrical conductivity and piezoresistive behavior was explored.

| S-EPMC5727098 | biostudies-literature

Single-step fabrication of quantum funnels via centrifugal colloidal casting of nanoparticle films.

Project description:Centrifugal casting of composites and ceramics has been widely employed to improve the mechanical and thermal properties of functional materials. This powerful method has yet to be deployed in the context of nanoparticles--yet size-effect tuning of quantum dots is among their most distinctive and application-relevant features. Here we report the first gradient nanoparticle films to be constructed in a single step. By creating a stable colloid of nanoparticles that are capped with electronic-conduction-compatible ligands we were able to leverage centrifugal casting for thin-films devices. This new method, termed centrifugal colloidal casting, is demonstrated to form films in a bandgap-ordered manner with efficient carrier funnelling towards the lowest energy layer. We constructed the first quantum-gradient photodiode to be formed in a single deposition step and, as a result of the gradient-enhanced electric field, experimentally measured the highest normalized detectivity of any colloidal quantum dot photodetector.

| S-EPMC4510961 | biostudies-literature

Biodegradation Studies of Polyhydroxybutyrate and Polyhydroxybutyrate-<i>co</i>-Polyhydroxyvalerate Films in Soil.

Project description:Due to increased environmental pressures, significant research has focused on finding suitable biodegradable plastics to replace ubiquitous petrochemical-derived polymers. Polyhydroxyalkanoates (PHAs) are a class of polymers that can be synthesized by microorganisms and are biodegradable, making them suitable candidates. The present study looks at the degradation properties of two PHA polymers: polyhydroxybutyrate (PHB) and polyhydroxybutyrate-co-polyhydroxyvalerate (PHBV; 8 wt.% valerate), in two different soil conditions: soil fully saturated with water (100% relative humidity, RH) and soil with 40% RH. The degradation was evaluated by observing the changes in appearance, chemical signatures, mechanical properties, and molecular weight of samples. Both PHB and PHBV were degraded completely after two weeks in 100% RH soil conditions and showed significant reductions in mechanical properties after just three days. The samples in 40% RH soil, however, showed minimal changes in mechanical properties, melting temperatures/crystallinity, and molecular weight over six weeks. By observing the degradation behavior for different soil conditions, these results can pave the way for identifying situations where the current use of plastics can be replaced with biodegradable alternatives.

| S-EPMC10146786 | biostudies-literature

A novel akermanite/poly (lactic-co-glycolic acid) porous composite scaffold fabricated via a solvent casting-particulate leaching method improved by solvent self-proliferating process.

Project description:Desirable scaffolds for tissue engineering should be biodegradable carriers to supply suitable microenvironments mimicked the extracellular matrices for desired cellular interactions and to provide supports for the formation of new tissues. In this work, a kind of slightly soluble bioactive ceramic akermanite (AKT) powders were aboratively selected and introduced in the PLGA matrix, a novel l-lactide modified AKT/poly (lactic-co-glycolic acid) (m-AKT/PLGA) composite scaffold was fabricated via a solvent casting-particulate leaching method improved by solvent self-proliferating process. The effects of m-AKT contents on properties of composite scaffolds and on MC3T3-E1 cellular behaviors in vitro have been primarily investigated. The fabricated scaffolds exhibited three-dimensional porous networks, in which homogenously distributed cavities in size of 300-400 μm were interconnected by some smaller holes in a size of 100-200 μm. Meanwhile, the mechanical structure of scaffolds was reinforced by the introduction of m-AKT. Moreover, alkaline ionic products released by m-AKT could neutralize the acidic degradation products of PLGA, and the apatite-mineralization ability of scaffolds could be largely improved. More valuably, significant promotions on adhesion, proliferation, and differentiation of MC3T3-E1 have been observed, which implied the calcium, magnesium and especially silidous ions released sustainably from composite scaffolds could regulate the behaviors of osteogenesis-related cells.

| S-EPMC5544913 | biostudies-other

Tuning electromagnetic properties of SrRuO<sub>3</sub> epitaxial thin films via atomic control of cation vacancies.

Project description:Elemental defect in transition metal oxides is an important and intriguing subject that result in modifications in variety of physical properties including atomic and electronic structure, optical and magnetic properties. Understanding the formation of elemental vacancies and their influence on different physical properties is essential in studying the complex oxide thin films. In this study, we investigated the physical properties of epitaxial SrRuO3 thin films by systematically manipulating cation and/or oxygen vacancies, via changing the oxygen partial pressure (P(O2)) during the pulsed laser epitaxy (PLE) growth. Ru vacancies in the low-P(O2)-grown SrRuO3 thin films induce lattice expansion with the suppression of the ferromagnetic T C down to ~120?K. Sr vacancies also disturb the ferromagnetic ordering, even though Sr is not a magnetic element. Our results indicate that both A and B cation vacancies in an ABO3 perovskite can be systematically engineered via PLE, and the structural, electrical, and magnetic properties can be tailored accordingly.

| S-EPMC5599527 | biostudies-literature

Tuning the Surface Properties of Poly(Allylamine Hydrochloride)-Based Multilayer Films.

Project description:The layer-by-layer (LbL) method of polyelectrolyte multilayer (PEM) fabrication is extremely versatile. It allows using a pair of any oppositely charged polyelectrolytes. Nevertheless, it may be difficult to ascribe a particular physicochemical property of the resulting PEM to a structural or chemical feature of a single component. A solution to this problem is based on the application of a polycation and a polyanion obtained by proper modification of the same parent polymer. Polyelectrolyte multilayers (PEMs) were prepared using the LbL technique from hydrophilic and amphiphilic derivatives of poly(allylamine hydrochloride) (PAH). PAH derivatives were obtained by the substitution of amine groups in PAH with sulfonate, ammonium, and hydrophobic groups. The PEMs were stable in 1 M NaCl and showed three different modes of thickness growth: exponential, mixed exponential-linear, and linear. Their surfaces ranged from very hydrophilic to hydrophobic. Root mean square (RMS) roughness was very variable and depended on the PEM composition, sample environment (dry, wet), and the polymer constituting the topmost layer. Atomic force microscopy (AFM) imaging of the surfaces showed very different morphologies of PEMs, including very smooth, porous, and structured PEMs with micellar aggregates. Thus, by proper choice of PAH derivatives, surfaces with different physicochemical features (growth type, thickness, charge, wettability, roughness, surface morphology) were obtained.

| S-EPMC8125107 | biostudies-literature

Role of Doping Agent Degree of Sulfonation and Casting Solvent on the Electrical Conductivity and Morphology of PEDOT:SPAES Thin Films.

Project description:Poly(3,4-ethylenedioxythiophene) (PEDOT) plays a key role in the field of electrically conducting materials, despite its poor solubility and processability. Various molecules and polymers carrying sulfonic groups can be used to enhance PEDOT's electrical conductivity. Among all, sulfonated polyarylether sulfone (SPAES), prepared via homogenous synthesis with controlled degree of sulfonation (DS), is a very promising PEDOT doping agent. In this work, PEDOT was synthesized via high-concentration solvent-based emulsion polymerization using 1% w/w of SPAES with different DS as dopant. It was found that the PEDOT:SPAESs obtained have improved solubility in the chosen reaction solvents, i.e., N, N-dimethylformamide, dimethylacetamide, dimethyl sulfoxide, and N-methyl-2-pyrrolidone and, for the first time, the role of doping agent, DS and polymerization solvents were investigated analyzing the electrical properties of SPAESs and PEDOT:SPAES samples and studying the different morphology of PEDOT-based thin films. High DS of SPAES, i.e., 2.4 meq R-SO3-× g-1 of polymer, proved crucial in enhancing PEDOT's electrical conductivity. Furthermore, the DMSO capability to favor PEDOT and SPAES chains rearrangement and interaction results in the formation of a polymer film with more homogenous morphology and higher conductivity than the ones prepared from DMAc, DMF, and NMP.

| S-EPMC7926741 | biostudies-literature