PMMA interlayer-modulated memory effects by space charge polarization in resistive switching based on CuSCN-nanopyramids/ZnO-nanorods p-n heterojunction.

ABSTRACT: Resistive switching (RS) devices are commonly believed as a promising candidate for next generation nonvolatile resistance random access memory. Here, polymethylmethacrylate (PMMA) interlayer was introduced at the heterointerface of p-CuSCN hollow nanopyramid arrays and n-ZnO nanorod arrays, resulting in a typical bipolar RS behavior. We propose the mechanism of nanostructure trap-induced space charge polarization modulated by PMMA interlayer. At low reverse bias, PMMA insulator can block charges through the heterointerface, and V(-)Cu and V(+)o trapped states are respectively created on both sides of PMMA, resulting in a high resistance state (HRS) due to wider depletion region. At high reverse bias, however, electrons and holes can cross PMMA interlayer by Fowler-Nordeim tunneling due to a massive tilt of energy band, and then inject into the traps of ZnO and CuSCN, respectively. V(+)Cu and V(-)O trapped states are created, resulting in the formation of degenerate semiconductors on both sides of PMMA. Therefore, quantum tunneling and space charge polarization lead to a low resistance state (LRS). At relatively high forward bias, subsequently, the trapped states of V(-)Cu and V(+)o are recreated due to the opposite injection of charges, resulting in a recovery of HRS. The introduction of insulating interlayer at heterointerface, point a way to develop next-generation nonvolatile memories.

SUBMITTER: Cheng B

PROVIDER: S-EPMC4673466 | biostudies-other | 2015

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Stable and Multilevel Data Storage Resistive Switching of Organic Bulk Heterojunction.

Project description:Organic nonvolatile memory devices have a vital role for the next generation of electrical memory units, due to their large scalability and low-cost fabrication techniques. Here, we show bipolar resistive switching based on an Ag/ZnO/P3HT-PCBM/ITO device in which P3HT-PCBM acts as an organic heterojunction with inorganic ZnO protective layer. The prepared memory device has consistent DC endurance (500 cycles), retention properties (104 s), high ON/OFF ratio (105), and environmental stability. The observation of bipolar resistive switching is attributed to creation and rupture of the Ag filament. In addition, our conductive bridge random access memory (CBRAM) device has adequate regulation of the current compliance leads to multilevel resistive switching of a high data density storage.

| S-EPMC7912748 | biostudies-literature

Multimode resistive switching in single ZnO nanoisland system.

Project description:Resistive memory has attracted a great deal of attention as an alternative to contemporary flash memory. Here we demonstrate an interesting phenomenon that multimode resistive switching, i.e. threshold-like, self-rectifying and ordinary bipolar switching, can be observed in one self-assembled single-crystalline ZnO nanoisland with base diameter and height ranging around 30 and 40 nm on Si at different levels of current compliance. Current-voltage characteristics, conductive atomic force microscopy (C-AFM), and piezoresponse force microscopy results show that the threshold-like and self-rectifying types of switching are controlled by the movement of oxygen vacancies in ZnO nanoisland between the C-AFM tip and Si substrate while ordinary bipolar switching is controlled by formation and rupture of conducting nano-filaments. Threshold-like switching leads to a very small switching power density of 1 × 10(3) W/cm(2).

| S-EPMC3740279 | biostudies-other

Efficient Photocatalytic Hydrogen Evolution over TiO2-X Mesoporous Spheres-ZnO Nanorods Heterojunction.

Project description:Photocatalytic water splitting into hydrogen is regarded as one of the key solutions to the deterioration of the global environment and energy. Due to the significantly reduced grain boundaries, ZnO nanorods facilitate a fast electron transfer through their smooth tunnels and are well suited as a photocatalyst. However, the photocatalytic hydrogen evolution performance of pristine ZnO nanorods is still low due to the high recombination rate of photogenerated electron-hole pairs and the less light absorption. Here, a novel structure about black ZnO nanorods (NRs)/TiO2-X mesoporous spheres (MSs) heterojunction has been prepared and the photocatalytic hydrogen evolution performance has been explored. The photocatalytic activity test results showed that ZnO NRs/TiO2-X MSs exhibited higher catalytic activity than ZnO NRs for hydrogen production. Compared to the pure ZnO NRs photoanode, the photocurrent of ZnO NRs/TiO2-X MSs heterojunction photoanode could reach 0.41 mA/cm2 in view of the expanding spectral response region and effective inhibition of e-/h+ recombination at the same condition. Using a relatively integrated experimental investigation and mechanism analysis, we scrutinized that after being treated with NaBH4, TiO2 MSs introduce oxygen vacancies expanding the photocatalytic activity of pure TiO2, and improving conductivity and charge transport capabilities through coating on ZnO NRs. More importantly, the results provide a promising approach in the NRs/MSs composite structure serving as photoanodes for photocatalytic hydrogen production.

| S-EPMC7690575 | biostudies-literature

Bi-stable resistive switching characteristics in Ti-doped ZnO thin films.

Project description:Ti-doped ZnO (ZnO/Ti) thin films were grown on indium tin oxide substrates by a facile electrodeposition route. The morphology, crystal structure and resistive switching properties were examined, respectively. The morphology reveals that grains are composed of small crystals. The (002) preferential growth along c-axis of ZnO/Ti could be observed from structural analysis. The XPS study shows the presence of oxygen vacancies in the prepared films. Typical bipolar and reversible resistance switching effects were observed. High ROFF/RON ratios (approximately 14) and low operation voltages within 100 switching cycles are obtained. The filament theory and the interface effect are suggested to be responsible for the resistive switching phenomenon.

| S-EPMC3623890 | biostudies-literature

Ultraviolet Photodetector Based on Poly(3,4-Ethylenedioxyselenophene)/ZnO Core-Shell Nanorods p-n Heterojunction.

Project description:In this work, we successfully assembled an organic-inorganic core-shell hybrid p-n heterojunction ultraviolet photodetector by the electropolymerization deposition of poly(3,4-ethylenedioxyselenophene) (PEDOS) on the surface of zinc oxide nanoarrays (ZnO NRs). The structures of composite were confirmed by FTIR, UV-Vis, XRD and XPS. Mott-Schottky analysis was used to study the p-n heterojunction structure. The photodetection properties of ZnO NRs/PEDOS heterojunction ultraviolet photodetector were systematically investigated current-voltage (I-V) and current-time (I-t) analysis under different bias voltages. The results showed that PEDOS films uniformly grew on ZnO NRs surface and core-shell structure was formed. The p-n heterojunction structure was formed with strong built-in electric field between ZnO NRs and PEDOS. Under the irradiation of UV light, the device showed a good rectification behavior. The responsivity, detection rate and the external quantum efficiency of the ultraviolet photodetector reached to 247.7 A/W, 3.41 × 1012 Jones and 84,000% at 2 V bias, respectively. The rise time (τr) and fall time (τf) of ZnO NRs/PEDOS UV photodetector were obviously shortened compared to ZnO UV photodetector. The results show that the introduction of PEDOS effectively improves the performance of the UV photodetector.

| S-EPMC9314489 | biostudies-literature

Resistive Switching Characteristics of Li-Doped ZnO Thin Films Based on Magnetron Sputtering.

Project description:A kind of devices Pt/Ag/ZnO:Li/Pt/Ti with high resistive switching behaviors were prepared on a SiO2/Si substrate by using magnetron sputtering method and mask technology, composed of a bottom electrode (BE) of Pt/Ti, a resistive switching layer of ZnO:Li thin film and a top electrode (TE) of Pt/Ag. To determine the crystal lattice structure and the Li-doped concentration in the resulted ZnO thin films, X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) tests were carried out. Resistive switching behaviors of the devices with different thicknesses of Li-doped ZnO thin films were studied at different set and reset voltages based on analog and digital resistive switching characteristics. At room temperature, the fabricated devices represent stable bipolar resistive switching behaviors with a low set voltage, a high switching current ratio and a long retention up to 104 s. In addition, the device can sustain an excellent endurance more than 103 cycles at an applied pulse voltage. The mechanism on how the thicknesses of the Li-doped ZnO thin films affect the resistive switching behaviors was investigated by installing conduction mechanism models. This study provides a new strategy for fabricating the resistive random access memory (ReRAM) device used in practice.

| S-EPMC6515171 | biostudies-literature

Resistive switching of Au/ZnO/Au resistive memory: an in situ observation of conductive bridge formation.

Project description:A special chip for direct and real-time observation of resistive changes, including set and reset processes based on Au/ZnO/Au system inside a transmission electron microscope (TEM), was designed. A clear conducting bridge associated with the migration of Au nanoparticles (NPs) inside a defective ZnO film from anode to cathode could be clearly observed by taking a series of TEM images, enabling a dynamic observation of switching behaviors. A discontinuous region (broken region) nearby the cathode after reset process was observed, which limits the flow of current, thus a high resistance state, while it will be reconnected to switch the device from high to low resistance states through the migration of Au NPs after set process. Interestingly, the formed morphology of the conducting bridge, which is different from the typical formation of a conducting bridge, was observed. The difference can be attributed to the different diffusivities of cations transported inside the dielectric layer, thereby significantly influencing the morphology of the conducting path. The current TEM technique is quite unique and informative, which can be used to elucidate the dynamic processes in other devices in the future.

| S-EPMC3494527 | biostudies-other

CdSe-CdTe Heterojunction Nanorods: Role of CdTe Segment in Modulating the Charge Transfer Processes.

Project description:Heterojunction nanorods having dissimilar semiconductors possess charge transfer (CT) properties and are proposed as active elements in optoelectronic systems. Herein, we describe the synthetic methodologies for controlling the charge carrier recombination dynamics in CdSe-CdTe heterojunction nanorods through the precise growth of CdTe segment from one of the tips of CdSe nanorods. The location of heterojunction was established through a point-by-point collection of the energy-dispersive X-ray spectra using scanning transmission electron microscopy. The possibilities of the growth of CdTe from both the tips of CdSe nanorods and the overcoating of CdTe over CdSe segment were also ruled out. The CT emission in the heterojunction nanorods originates through an interfacial excitonic recombination and was further tuned to the near-infrared region by varying the two parameters: the aspect ratio of CdSe and the length of CdTe segment. These aspects are evidenced from the emission lifetime and the femtosecond transient absorption studies.

| S-EPMC6641699 | biostudies-literature

TEM Nanostructural Investigation of Ag-Conductive Filaments in Polycrystalline ZnO-Based Resistive Switching Devices.

Project description:Memristive devices based on a resistive switching mechanism are considered very promising for nonvolatile memory and unconventional computing applications, even though many details of the switching mechanisms are not yet fully understood. Here, we report a nanostructural study by means of high-resolution transmission electron microscopy and spectroscopy techniques of a Ag/ZnO/Pt memristive device. To ease the localization of the filament position for its characterization, we propose to use the guiding effect of regular perturbation arrays obtained by FIB technology to assist the filament formation. HRTEM and EDX were used to identify the composition and crystalline structure of the so-obtained conductive filaments and surrounding regions. It was determined that the conducting paths are composed mainly of monocrystalline Ag, which remains polycrystalline in some circumstances, including the zone where the switching occurs and at secondary filaments created at the grain boundaries of the polycrystalline ZnO matrix. We also observed that the ZnO matrix shows a degraded quality in the switching zone, while it remains unaltered in the rest of the memristive device.

| S-EPMC8008384 | biostudies-literature

Hydrothermally Grown In-doped ZnO Nanorods on p-GaN Films for Color-tunable Heterojunction Light-emitting-diodes.

Project description:The incorporation of doping elements in ZnO nanostructures plays an important role in adjusting the optical and electrical properties in optoelectronic devices. In the present study, we fabricated 1-D ZnO nanorods (NRs) doped with different In contents (0% ~ 5%) on p-GaN films using a facile hydrothermal method, and investigated the effect of the In doping on the morphology and electronic structure of the NRs and the electrical and optical performances of the n-ZnO NRs/p-GaN heterojunction light emitting diodes (LEDs). As the In content increased, the size (diameter and length) of the NRs increased, and the electrical performance of the LEDs improved. From the electroluminescence (EL) spectra, it was found that the broad green-yellow-orange emission band significantly increased with increasing In content due to the increased defect states (oxygen vacancies) in the ZnO NRs, and consequently, the superposition of the emission bands centered at 415 nm and 570 nm led to the generation of white-light. These results suggest that In doping is an effective way to tailor the morphology and the optical, electronic, and electrical properties of ZnO NRs, as well as the EL emission property of heterojunction LEDs.

| S-EPMC4437377 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data