Fabrication of in-situ grown graphene reinforced Cu matrix composites.

ABSTRACT: Graphene/Cu composites were fabricated through a graphene in-situ grown approach, which involved ball-milling of Cu powders with PMMA as solid carbon source, in-situ growth of graphene on flaky Cu powders and vacuum hot-press sintering. SEM and TEM characterization results indicated that graphene in-situ grown on Cu powders guaranteed a homogeneous dispersion and a good combination between graphene and Cu matrix, as well as the intact structure of graphene, which was beneficial to its strengthening effect. The yield strength of 244 MPa and tensile strength of 274 MPa were achieved in the composite with 0.95 wt.% graphene, which were separately 177% and 27.4% enhancement over pure Cu. Strengthening effect of in-situ grown graphene in the matrix was contributed to load transfer and dislocation strengthening.

SUBMITTER: Chen Y

PROVIDER: S-EPMC4725871 | biostudies-other | 2016

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Heteroatom Modification Enhances Corrosion Durability in High-Mechanical-Performance Graphene-Reinforced Aluminum Matrix Composites.

Project description:The antagonism between strength and corrosion resistance in graphene-reinforced aluminum matrix composites is an inherent challenge to designing reliable structural components. Heteroatom microstructural modification is highly appreciated to conquer the obstacle. Here, a bottom-up strategy to exploit the heterogeneous phase interface to enable high corrosion durability is proposed. Deformation-driven metallurgy derived from severe plastic deformation is developed to produce Mg-alloyed fluorinated graphene structures with homogeneous dispersion. These structures allow for absorbing corrosion products, forming a dense protective layer against corrosion, and local micro-tuning of the suppression of charge transfer. This results in superior corrosion resistance with an outstanding strength-ductility balance of the composites via ultrafine-grained and precipitation strengthening. The anti-corrosion polarization resistance remains 89% of the initial state after 2-month immersion in chloride-containing environment, while the ultra-tensile strength and elongation of 532 ± 39 MPa and 17.3 ± 1.2% are obtained. The economical strategy of heteroatom modification broadens the horizon for anti-corrosion engineering in aluminum matrix composites, which is critical for the design of carbonaceous nanomaterial-reinforced composites to realize desired performances for practical applications.

| S-EPMC9376822 | biostudies-literature

Microstructure and nanoindentation behavior of Cu composites reinforced with graphene nanoplatelets by electroless co-deposition technique.

Project description:A reduced graphene oxide/copper (RGO/Cu) composite was fabricated by a surfactant free, electroless co-deposition technique. The graphene oxide (GO) sheets were reduced and RGO homogeneous distributed into the copper matrix. On the basis of nanoindentation, the presence of RGO and the increase of its content in matrix significantly raised the hardness of RGO/Cu composites. Here, the relevant strengthening effect and mechanisms involved in RGO-reinforced Cu composites were systematically evaluated. Especially, the addition of RGO in Cu matrix led to the compressive micro-strain, and the resulted distortion of the lattice parameter was calculated based on Cohen's method. However, excessive addition of GO in the electrolyte could decrease the mechanical performance due to agglomeration of RGO. Apparently, the optimal concentration for GO dispersion in co-deposition solution was deserved to discuss. After a serious of relative experiments, we could get a conclusion that this method provided a new pathway for embedded graphene into the metal matrix to improve the mechanical properties of RGO-reinforced materials.

| S-EPMC5431065 | biostudies-literature

Characterization of Wood and Graphene Nanoplatelets (GNPs) Reinforced Polymer Composites.

Project description:This paper investigates the utilization of commercial masterbatches of graphene nanoplatelets to improve the properties of neat polymer and wood fiber composites manufactured by conventional processing methods. The effect of aspect ratio of the graphene platelets (represented by the different number of layers in the nanoplatelet) on the properties of high-density polyethylene (HDPE) is discussed. The composites were characterized for their mechanical properties (tensile, flexural, impact) and physical characteristics (morphology, crystallization, and thermal stability). The effect of the addition of nanoplatelets on the thermal conductivity and diffusivity of the reinforced polymer with different contents of reinforcement was also investigated. In general, the mechanical performance of the polymer was enhanced at the presence of either of the reinforcements (graphene or wood fiber). The improvement in mechanical properties of the nanocomposite was notable considering that no compatibilizer was used in the manufacturing. The use of a masterbatch can promote utilization of nano-modified polymer composites on an industrial scale without modification of the currently employed processing methods and facilities.

| S-EPMC7254240 | biostudies-literature

Balancing Strength and Ductility in Al Matrix Composites Reinforced by Few-Layered MoS2 through In-Situ Formation of Interfacial Al12Mo.

Project description:In this work, few-layered MoS2 (FLM) nanosheet-reinforced Al matrix composites are developed through powder metallurgy and hot extrusion. The microstructure, mechanical properties, and strengthening mechanisms have been systematically investigated. It is found that Al12Mo and Al2S3 can be formed in-situ during the sintering process, resulting in the improvement of interfacial bonding between FLM and Al matrix. With 1.5 wt.% of FLM addition, an improved tensile strength of 234 MPa with a high elongation of 17% can be obtained. Moreover, the strengthening mechanisms are also demonstrated to be grain refinement, dislocation strengthening, and load transfer, and the calculation indicates that load transfer is the main contribution factor. This work will inspire more new designs of metal matrix composites with balanced strength and ductility.

| S-EPMC8269559 | biostudies-literature

Self-Assembly of Graphene-Encapsulated Cu Composites for Nonenzymatic Glucose Sensing.

Project description:Cu has recently received great interest as a potential candidate for glucose sensing to overcome the problems with noble metals. In this work, reduced graphene oxide-encapsulated Cu nanoparticles (Cu@RGO) have been prepared via an electrostatic self-assembly method. This core/shell composites were found to be more stable than conventional Cu-decorated graphene composites and bare copper nanoparticles in an air atmosphere because the graphene shell can effectively protect the Cu nanoparticles from oxidation. In addition, the obtained Cu@RGO composites also showed an outstanding electrocatalytic activity toward glucose oxidation with a wide linear detection range of 1 μM to 2 mM, low detection limit of 0.34 μM (S/N = 3), and a sensitivity of 150 μA mM-1 cm-2. Moreover, Cu@RGO composites exhibited a satisfactory reproducibility, selectivity, and long effective performance. These excellent properties indicated that Cu@RGO nanoparticles have great potential application in glucose detection.

| S-EPMC6045414 | biostudies-literature

Microstructure and mechanical behavior of metallic glass fiber-reinforced Al alloy matrix composites.

Project description:Metallic glass-reinforced metal matrix composites are an emerging class of composite materials. The metallic nature and the high mechanical strength of the reinforcing phase offers unique possibilities for improving the engineering performance of composites. Understanding the structure at the amorphous/crystalline interfaces and the deformation behavior of these composites is of vital importance for their further development and potential application. In the present work, Zr-based metallic glass fibers have been introduced in Al7075 alloy (Al-Zn-Mg-Cu) matrices using spark plasma sintering (SPS) producing composites with low porosity. The addition of metallic glass reinforcements in the Al-based matrix significantly improves the mechanical behavior of the composites in compression. High-resolution TEM observations at the interface reveal the formation of a thin interdiffusion layer able to provide good bonding between the reinforcing phase and the Al-based matrix. The deformation behavior of the composites was studied, indicating that local plastic deformation occurred in the matrix near the glassy reinforcements followed by the initiation and propagation of cracks mainly through the matrix. The reinforcing phase is seen to inhibit the plastic deformation and retard the crack propagation. The findings offer new insights into the mechanical behavior of metal matrix composites reinforced with metallic glasses.

| S-EPMC4828712 | biostudies-literature

Aluminium matrix tungsten aluminide and tungsten reinforced composites by solid-state diffusion mechanism.

Project description:In-situ processing of tungsten aluminide and tungsten reinforced aluminium matrix composites from elemental tungsten (W) and aluminium (Al) was investigated by thermal analysis and pulsed current processing (PCP). The formation mechanism of tungsten aluminides in 80 at.% Al-20 at.% W system was controlled by atomic diffusion. The particle size of W and Al in the starting powder mixture regulated the phase formation and microstructure. PCP of micron sized elemental Al and W resulted in formation of particulate reinforcements, W, Al4W and Al12W, dispersed in Al matrix. W particles were surrounded by a ~3 μm thick dual-layer structure of Al12W and Al4W. The hardness of Al matrix, containing Al12W reinforcements, was increased by 50% compared to pure Al, from 0.3 GPa to 0.45 GPa and W reinforcements showed a hardness of 4.35 GPa. On PCP of 80 at.% Al-20 at.% W mixture with particle size of W and Al ~70 nm, resulted in formation of Al4W as major phase along with small fractions of Al5W and unreacted W phase. This suggested strongly that the particle size of the starting elemental Al and W could be the controlling parameter in processing and tailoring of phase evolution, microstructure of particulate reinforced Al matrix composite.

| S-EPMC5620082 | biostudies-literature

Novel Alumina Matrix Composites Reinforced with MAX Phases-Microstructure Analysis and Mechanical Properties.

Project description:This article describes the manufacturing of alumina composites with the addition of titanium aluminum carbide Ti3AlC2, known as MAX phases. The composites were obtained by the powder metallurgy technique with three types of mill (horizontal mill, attritor mill, and planetary mill), and were consolidated with the use of the Spark Plasma Sintering method at 1400 °C, with dwelling time 10 min. The influence of the Ti3AlC2 MAX phase addition on the microstructure and mechanical properties of the obtained composites was analyzed. The structure of the MAX phase after the sintering process was also investigated. The chemical composition and phase composition analysis showed that the Ti3AlC2 addition preserved its structure after the sintering process. The increase in fracture toughness for all series of composites has been noted (over 20% compared to reference samples). Detailed stereological analysis of the obtained microstructures also could determine the influence of the applied mill on the homogeneity of the final microstructure and the properties of obtained composites.

| S-EPMC9571909 | biostudies-literature

A Facile Route to Synthesize Nanographene Reinforced PBO Composites Fiber via in Situ Polymerization.

Project description:The polymer matrix with introduced carbon-based nanofiber displays fascinating properties. They have inspired extensive research on the synthesis of polymer composites, which have been applied in catalysis, electronics, and energy storage. In this report, we reported a facile and efficient method to prepare poly(p-phenylene benzobisoxazole) (PBO)/nanographene (PNG) composites fibers via in-situ polymerization, accompanied by the reduction from (nanographene oxide) NGO to (nanographene) NG. By tuning the ratio of feeding PBO monomer to NGO, various composites fibers with 0.1⁻1 wt % contents of NG were obtained. The efficient PBO chains grafting made NG uniformly disperse in the PBO matrix, and it also increased the uniformity of the packing orientation of PBO chains. Consequently, the tensile strength, tensile modulus, and thermal stability of the obtained PNG composites fibers had been improved significantly. In addition, the composites fibers with 0.5 wt % NG exhibited a 25% increment in tensile strength, and a 41% enhancement in tensile modulus compared with neat PBO fibers. It reveals an excellent reinforcement to PBO composites fibers with NG.

| S-EPMC6432332 | biostudies-literature

Electrochemical Characterization and Inhibiting Mechanism on Calcium Leaching of Graphene Oxide Reinforced Cement Composites.

Project description:Calcium leaching is a degradation progress inside hardened cement composites, where Ca2+ ions in cement pore solution can migrate into the aggressive solution. In this work, calcium leaching of graphene oxide (GO) reinforced cement composites was effectively characterized by combined techniques of electrochemical impedance spectroscopy (EIS) and scanning electron microscope (SEM). Inhibiting mechanism of GO on calcium leaching of the composites was also examined. The obtained results show that the diameter of the semi-circle of the Nyquist curves of leached samples with GO addition decreased less than that of controlled samples. After leaching for 35 days, loss rate of model impedance RCCP of leached samples with 0, 0.05, 0.1, 0.15, and 0.2 wt.% GO addition was 94.85%, 84.07%, 79.66%, 75.34%, and 68.75%, respectively. Therefore, GO addition can significantly mitigate calcium leaching of cement composites, since it can absorb Ca2+ ions in cement pore solution, as well as improve the microstructure of the composites. In addition, coupling leaching depth and compressive strength loss were accurately predicted by using the impedance RCCP.

| S-EPMC6409634 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data