Co-electrodeposition of hard Ni-W/diamond nanocomposite coatings.

ABSTRACT: Electroplated hard chrome coating is widely used as a wear resistant coating to prolong the life of mechanical components. However, the electroplating process generates hexavalent chromium ion which is known carcinogen. Hence, there is a major effort throughout the electroplating industry to replace hard chrome coating. Composite coating has been identified as suitable materials for replacement of hard chrome coating, while deposition coating prepared using traditional co-deposition techniques have relatively low particles content, but the content of particles incorporated into a coating may fundamentally affect its properties. In the present work, Ni-W/diamond composite coatings were prepared by sediment co-electrodeposition from Ni-W plating bath, containing suspended diamond particles. This study indicates that higher diamond contents could be successfully co-deposited and uniformly distributed in the Ni-W alloy matrix. The maximum hardness of Ni-W/diamond composite coatings is found to be 2249 ± 23 Hv due to the highest diamond content of 64 wt.%. The hardness could be further enhanced up to 2647 ± 25 Hv with heat treatment at 873 K for 1 h in Ar gas, which is comparable to hard chrome coatings. Moreover, the addition of diamond particles could significantly enhance the wear resistance of the coatings.

SUBMITTER: Zhang X

PROVIDER: S-EPMC4770281 | biostudies-other | 2016

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Synthesis and Performance Evaluation of Pulse Electrodeposited Ni-AlN Nanocomposite Coatings.

Project description:This research work presents the microscopic analysis of pulse electrodeposited Ni-AlN nanocomposite coatings using SEM and AFM techniques and their performance evaluation (mechanical and electrochemical) by employing nanoindentation and electrochemical methods. The Ni-AlN nanocomposite coatings were developed by pulse electrodeposition. The nickel matrix was reinforced with various amounts of AlN nanoparticles (3, 6, and 9?g/L) to develop Ni-AlN nanocomposite coatings. The effect of reinforcement concentration on structure, surface morphology, and mechanical and anticorrosion properties was studied. SEM and AFM analyses indicate that Ni-AlN nanocomposite coatings have dense, homogenous, and well-defined pyramid structure containing uniformly distributed AlN particles. A decent improvement in the corrosion protection performance is also observed by the addition of AlN particles to the nickel matrix. Corrosion current was reduced from 2.15 to 1.29??A?cm-2 by increasing the AlN particles concentration from 3 to 9?g/L. It has been observed that the properties of Ni-AlN nanocomposite coating are sensitive to the concentration of AlN nanoparticles used as reinforcement.

| S-EPMC5830284 | biostudies-literature

Magnetron Sputtering vs. Electrodeposition for Hard Chrome Coatings: A Comparison of Environmental and Economic Performances.

Project description:The coating of materials with specific films is widely used to improve material properties and many technologies exist to perform it. In the last few years, the replacement of wet electrodeposition processes has been continuously encouraged in the EU due to the problematic waste management linked to those processes. In this paper, magnetron sputtering is studied as an alternative to conventional electrodeposition by comparing the technologies' environmental impacts and costs. From the study, it appears that while magnetron sputtering greatly reduces hexavalent chromium emissions over the production, it has an increased electricity consumption mostly due to its lower production capacity, thus leading to more greenhouse gas emissions. Furthermore, a short discussion on the quantification of the impact of hexavalent chromium emissions is conducted. Regarding costs, the electrodeposition process has a lower cost of investment and of consumables, but requires more work time for the different steps of the process, making the total price per functional unit roughly equal. However, the cost per functional unit strongly depends on assumptions on the required work time, for which a sensitivity study is performed. Finally, the impacts of these two competing coating processes are discussed to complete the technological comparison for the case of hard chromium deposition.

| S-EPMC8307072 | biostudies-literature

Ultrasonic-assisted electrodeposition of Cu-Sn-TiO<sub>2</sub> nanocomposite coatings with enhanced antibacterial activity.

Project description:Copper-based coatings are known for their high antibacterial activity. In this study, nanocomposite Cu-Sn-TiO2 coatings were obtained by electrodeposition from an oxalic acid bath additionally containing 4 g/dm3 TiO2 with mechanical and ultrasonic agitation. Ultrasound treatment was performed at 26 kHz frequency and 32 W/dm3 power. The influence of agitation mode and the current load on the inclusion and distribution of the TiO2 phase in the Cu-Sn metallic matrix were evaluated. Results indicated that ultrasonic agitation decreases agglomeration of TiO2 particles and allows for the deposition of dense Cu-Sn-TiO2 nanocomposites. It is shown that nanocomposite Cu-Sn-TiO2 coatings formed by ultrasonic-assisted electrodeposition exhibit excellent antimicrobial properties against E. coli bacteria.

| S-EPMC8233381 | biostudies-literature

Electrodeposition of Mesoporous Ni-Rich Ni-Pt Films for Highly Efficient Methanol Oxidation.

Project description:The use of soft templates for the electrosynthesis of mesoporous materials has shown tremendous potential in energy and environmental domains. Among all the approaches that have been featured in the literature, block copolymer-templated electrodeposition had robustness and a simple method, but it practically cannot be used for the synthesis of mesoporous materials not based on Pt or Au. Nonetheless, extending and understanding the possibilities and limitations of block copolymer-templated electrodeposition to other materials and substrates is still challenging. Herein, a critical analysis of the role of the solution's primary electroactive components and the applied potential were performed in order to understand their influences on the mesostructure of Ni-rich Ni-Pt mesoporous films. Among all the components, tetrahydrofuran and a platinum (IV) complex were shown to be crucial for the formation of a truly 3D mesoporous network. The electrosynthesized well-ordered mesoporous Ni-rich Ni-Pt deposits exhibit excellent electrocatalytic performance for methanol oxidation in alkaline conditions, improved stability and durability after 1000 cycles, and minimal CO poisoning.

| S-EPMC7466700 | biostudies-literature

Healable Supracolloidal Nanocomposite Water-Borne Coatings.

Project description:Water-borne coatings often contain nanofillers to enhance their mechanical or optical properties. The aggregation of these fillers may, however, lead to undesired effects such as brittle and opaque coatings, reducing their performance and lifetime. By controlling the distribution and structural arrangement of the nanofillers in the coatings and inserting reversible chemical bonds, both the elasticity and strength of the coatings may be effectively improved, while healing properties, via the reversible chemistry, extend the coating's lifetime. Aqueous dispersions of polymer-core/silica-corona supracolloidal particles were used to prepare water-borne coatings. Polymer and silica nanoparticles were prefunctionalized with thiol/disulfide groups during the supracolloid assembly. Disulfide bridges were further established between a cross-linker and the supracolloids during drying and coating formation. The supracolloidal nanocomposite coatings were submitted to intentional (physical) damages, i.e., blunt and sharp surface scratches or cut through into two pieces, and subsequently UV irradiated to induce the recovery of the damage(s). The viscoelasticity and healing properties of the coatings were examined by dynamic, static, and surface mechanical analyses. The nanocomposite coatings showed a great extent of interfacial restoration of cut damage and surface scratches. The healing properties are strongly related to the coating's viscoelasticity and interfacial (re)activation of the disulfide bridges. Nanocomposite coatings with silica concentrations below their critical volume fraction show higher in situ healing efficiency, as compared to coatings with higher silica concentration. This work provides insights into the control of nanofillers distribution in water-borne coatings and strategies to increase the coating lifetime via mechanical damage recovery.

| S-EPMC11320382 | biostudies-literature

Barrier Diamond-like Carbon Coatings on Polydimethylsiloxane Substrate.

Project description:The plasma modification of polydimethylsiloxane (PDMS) substrates is one way to change their surface geometry, which enables the formation of wrinkles. However, these changes are very often accompanied by the process of restoring the hydrophobic properties of the modified material. In this work, the RF PACVD device (radio frequency plasma-assisted chemical vapor deposition) was used, with which the plasma treatment of PDMS substrates was carried out in argon, nitrogen, oxygen, and methane atmospheres at variable negative biases ranging from 100 V to 500 V. The obtained results show the stability of contact angles for deionized water only in the case of surfaces modified by diamond-like carbon (DLC) coatings. The influence of the applied production conditions on the thickness (between 10 and 30 nm) and chemical structure (ID/IG between 0.41 and 0.8) of DLC coatings is discussed. In the case of plasma treatments with other gases introduced into the working chamber, the phenomenon of changing from hydrophilic to hydrophobic properties after the modification processes was observed. The presented results confirm the barrier nature of the DLC coatings produced on the PDMS substrate.

| S-EPMC9181918 | biostudies-literature

The Effect of Surfactant Content over Cu-Ni Coatings Electroplated by the sc-CO₂ Technique.

Project description:Co-plating of Cu-Ni coatings by supercritical CO₂ (sc-CO₂) and conventional electroplating processes was studied in this work. 1,4-butynediol was chosen as the surfactant and the effects of adjusting the surfactant content were described. Although the sc-CO₂ process displayed lower current efficiency, it effectively removed excess hydrogen that causes defects on the coating surface, refined grain size, reduced surface roughness, and increased electrochemical resistance. Surface roughness of coatings fabricated by the sc-CO₂ process was reduced by an average of 10%, and a maximum of 55%, compared to conventional process at different fabrication parameters. Cu-Ni coatings produced by the sc-CO₂ process displayed increased corrosion potential of ~0.05 V over Cu-Ni coatings produced by the conventional process, and 0.175 V over pure Cu coatings produced by the conventional process. For coatings ~10 µm thick, internal stress developed from the sc-CO₂ process were ~20 MPa lower than conventional process. Finally, the preferred crystal orientation of the fabricated coatings remained in the (111) direction regardless of the process used or surfactant content.

| S-EPMC5506913 | biostudies-other

Mesoporous silica films as hard templates for electrodeposition of nanostructured gold.

Project description:Metallic nanostructures have widespread applications in fields including materials science, electronics and catalysis. Mesoporous silica films synthesised by evaporation induced self-assembly and electrochemically assisted self-assembly with pores below 10 nm were used as hard templates for the electrodeposition of Au nanostructures. Electrodeposition conditions were optimised based on pore orientation and size. The growth of nanostructures was initiated at the electrode surface as confirmed by microscopy. The hard templates and Au electrodeposits were characterised electrochemically as well as with X-ray diffraction, small angle scattering and transmission electron microscopy. Finally, mesoporous silica hard templates were removed by hydrofluoric acid etching and stable Au nanoparticles on different electrode surfaces were achieved.

| S-EPMC9642781 | biostudies-literature

Aqueous Cationic Fluorinated Polyurethane for Application in Novel UV-Curable Cathodic Electrodeposition Coatings.

Project description:Aqueous polyurethane is an environmentally friendly, low-cost, high-performance resin with good abrasion resistance and strong adhesion. Cationic aqueous polyurethane is limited in cathodic electrophoretic coatings due to its complicated preparation process and its poor stability and single performance after emulsification and dispersion. The introduction of perfluoropolyether alcohol (PFPE-OH) and light curing technology can effectively improve the stability of aqueous polyurethane emulsions, and thus enhance the functionality of coating films. In this paper, a new UV-curable fluorinated polyurethane-based cathodic electrophoretic coating was prepared using cationic polyurethane as a precursor, introducing PFPE-OH capping, and grafting hydroxyethyl methacrylate (HEMA). The results showed that the presence of perfluoropolyether alcohol in the structure affected the variation of the moisture content of the paint film after flash evaporation. Based on the emulsion particle size and morphology tests, it can be assumed that the fluorinated cationic polyurethane emulsion is a core-shell structure with hydrophobic ends encapsulated in the polymer and hydrophilic ends on the outer surface. After abrasion testing and baking, the fluorine atoms of the coating were found to increase from 8.89% to 27.34%. The static contact angle of the coating to water was 104.6 ± 3°, and the water droplets rolled off without traces, indicating that the coating is hydrophobic. The coating has excellent thermal stability and tensile properties. The coating also passed the tests of impact resistance, flexibility, adhesion, and resistance to chemical corrosion in extreme environments. This study provides a new idea for the construction of a new and efficient cathodic electrophoretic coating system, and also provides more areas for the promotion of cationic polyurethane to practical applications.

| S-EPMC10535655 | biostudies-literature

Niobia Nanofiber-Reinforced Protective Niobium Oxide/Acrylate Nanocomposite Coatings.

Project description:In the present study, the corrosion resistance of a new niobium oxide/acrylate hybrid nanocomposite coating doped with niobia nanofibers is investigated. Nanofibers were initially synthesized from niobium(V) chloride precursor in a novel autoclave approach before fabricating the base coating from a two-step process involving the syntheses of acrylate resin via free radical polymerization and niobium oxide gel from niobium ethoxide via a sol-gel technique. Variants of the synthesized nanocomposite coating were incorporated with varying concentrations of niobia nanofibers before spin-coating on Q235 steel substrates to inhibit corrosive electrolytic ion percolation and further enhance corrosion resistance when treated with chloride-enriched corrosive media. The corrosion resistance of these nanocomposite coatings increased with nanofiber content up to an optimum concentration due to the corrosion-inhibiting and protective effects of niobium barrier layers within these coatings. The presence of the niobia nanofibers also promoted improved surface contact angle and toughened mechanical strengths.

| S-EPMC7711932 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data