Origin of giant piezoelectric effect in lead-free K1-xNaxTa1-yNbyO3 single crystals.

ABSTRACT: A series of high-quality, large-sized (maximum size of 16 × 16 × 32 mm(3)) K1-xNaxTa1-yNbyO3 (x = 0.61, 0.64, and 0.70 and corresponding y = 0.58, 0.60, and 0.63) single crystals were grown using the top-seed solution growth method. The segregation of the crystals, which allowed for precise control of the individual components of the crystals during growth, was investigated. The obtained crystals exhibited excellent properties without being annealed, including a low dielectric loss (0.006), a saturated hysteresis loop, a giant piezoelectric coefficient d33 (d33 = 416 pC/N, determined by the resonance method and d33(*) = 480 pC/N, measured using a piezo-d33 meter), and a large electromechanical coupling factor, k33 (k33 = 83.6%), which was comparable to that of lead zirconate titanate. The reason the piezoelectric coefficient d33 of K0.39Na0.61Ta0.42Nb0.58O3 was larger than those of the other two crystals grown was elucidated through first-principles calculations. The obtained results indicated that K1-xNaxTa1-yNbyO3 crystals can be used as a high-quality, lead-free piezoelectric material.

SUBMITTER: Tian H

PROVIDER: S-EPMC4861918 | biostudies-other | 2016

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Growth and Characterization of Lead-free Piezoelectric Single Crystals.

Project description:Lead-free piezoelectric materials attract more and more attention owing to the environmental toxicity of lead-containing materials. In this work, we review our first attempts of single crystal grown by the top-seeded solution growth method of BaTiO₃ substituted with zirconium and calcium (BCTZ) and (K0.5Na0.5)NbO₃ substituted with lithium, tantalum, and antimony (KNLSTN). The growth methodology is optimized in order to reach the best compositions where enhanced properties are expected. Chemical analysis and electrical characterizations are presented for both kinds of crystals. The compositionally-dependent electrical performance is investigated for a better understanding of the relationship between the composition and electrical properties. A cross-over from relaxor to ferroelectric state in BCTZ solid solution is evidenced similar to the one reported in ceramics. In KNLSTN single crystals, we observed a substantial evolution of the orthorhombic-to-tetragonal phase transition under minute composition changes.

| S-EPMC5458931 | biostudies-other

Giant electric-field-induced strain in lead-free piezoelectric materials.

Project description:First-principles calculations are performed to investigate the structures, electrical, and magnetic properties of compressive BiFeO3 films under electric-field and pressure perpendicular to the films. A reversible electric-field-induced strain up 10% is achieved in the compressive BiFeO3 films. The giant strain originates from rhombohedral-tetragonal (R-T) phase transition under electric-filed, and is recoverable from tetragonal-rhombohedral (T-R) phase transition by compressive stress. Additionally, the weak ferromagnetism in BiFeO3 films is largely changed in R-T phase transition under electric-filed and T-R phase transition under pressure - reminiscent of magnetoelectric effect and magnetoelastic effect. These results suggest exciting device opportunities arising from the giant filed-induced strain, large magnetoelectric effect and magnetoelastic effect.

| S-EPMC4853793 | biostudies-other

Giant strain with ultra-low hysteresis and high temperature stability in grain oriented lead-free K0.5Bi0.5TiO3-BaTiO3-Na0.5Bi0.5TiO3 piezoelectric materials.

Project description:We synthesized grain-oriented lead-free piezoelectric materials in (K0.5Bi0.5TiO3-BaTiO3-xNa0.5Bi0.5TiO3 (KBT-BT-NBT) system with high degree of texturing along the [001]c (c-cubic) crystallographic orientation. We demonstrate giant field induced strain (~0.48%) with an ultra-low hysteresis along with enhanced piezoelectric response (d33 ~ 190pC/N) and high temperature stability (~160°C). Transmission electron microscopy (TEM) and piezoresponse force microscopy (PFM) results demonstrate smaller size highly ordered domain structure in grain-oriented specimen relative to the conventional polycrystalline ceramics. The grain oriented specimens exhibited a high degree of non-180° domain switching, in comparison to the randomly axed ones. These results indicate the effective solution to the lead-free piezoelectric materials.

| S-EPMC4341219 | biostudies-literature

Giant photovoltaic effect of ferroelectric domain walls in perovskite single crystals.

Project description:The photovoltaic (PV) effect in polar materials offers great potential for light-energy conversion that generates a voltage beyond the bandgap limit of present semiconductor-based solar cells. Ferroelectrics have received renewed attention because of the ability to deliver a high voltage in the presence of ferroelastic domain walls (DWs). In recent years, there has been considerable debate over the impact of the DWs on the PV effects, owing to lack of information on the bulk PV tensor of host ferroelectrics. In this article, we provide the first direct evidence of an unusually large PV response induced by ferroelastic DWs-termed 'DW'-PV effect. The precise estimation of the bulk PV tensor in single crystals of barium titanate enables us to quantify the giant PV effect driven by 90° DWs. We show that the DW-PV effect arises from an effective electric field consisting of a potential step and a local PV component in the 90° DW region. This work offers a starting point for further investigation into the DW-PV effect of alternative systems and opens a reliable route for enhancing the PV properties in ferroelectrics based on the engineering of domain structures in either bulk or thin-film form.

| S-EPMC4595799 | biostudies-other

Heterogeneity Challenges in Multiple-Element-Modified Lead-Free Piezoelectric Ceramics.

Project description:We report on a heterogeneity study, down to the atomic scale, on a representative multiple-element-modified ceramic based on potassium sodium niobate (KNN): 0.95(Na0.49K0.49Li0.02)(Nb0.8Ta0.2)O3-0.05CaZrO3 with 2 wt % MnO2. We show that different routes for incorporating the MnO2 (either before or after the calcination step) affect the phase composition and finally the functionality of the material. According to X-ray diffraction and scanning electron microscopy analyses, the ceramics consist of orthorhombic and tetragonal perovskite phases together with a small amount of Mn-rich secondary phase. The addition of MnO2 after the calcination results in better piezoelectric properties, corresponding to a ratio between the orthorhombic and tetragonal perovskite phases that is closer to unity. We also show, using microscopy techniques combined with analytical tools, that Zr-rich, Ta-rich and Mn-rich segregations are present on the nano and atomic levels. With this multi-scale analysis approach, we demonstrate that the functional properties are sensitive to minor modifications in the synthesis route, and consequently to different material properties on all scales. We believe that detecting and learning how to control these modifications will be a step forward in overcoming the irreproducibility problems with KNN-based materials.

| S-EPMC6947271 | biostudies-literature

Direct Writing of Patterned, Lead-Free Nanowire Aligned Flexible Piezoelectric Device.

Project description:A high-performance flexible piezoelectric nanogenerator (PNG) is fabricated by a direct writing method, which acquires both patterned piezoelectric structure and aligned piezoelectric nanowires simultaneously. The voltage output of the as-prepared PNG is nearly 400% compared with that of the traditional spin-coated device due to the effective utilization of stress. This facile printing approach provides an efficient strategy for significant improvement of the piezoresponse.

| S-EPMC5089621 | biostudies-literature

Sintering of Lead-Free Piezoelectric Sodium Potassium Niobate Ceramics.

Project description:The potassium sodium niobate, K0.5Na0.5NbO₃, solid solution (KNN) is considered as one of the most promising, environment-friendly, lead-free candidates to replace highly efficient, lead-based piezoelectrics. Since the first reports of KNN, it has been recognized that obtaining phase-pure materials with a high density and a uniform, fine-grained microstructure is a major challenge. For this reason the present paper reviews the different methods for consolidating KNN ceramics. The difficulties involved in the solid-state synthesis of KNN powder, i.e., obtaining phase purity, the stoichiometry of the perovskite phase, and the chemical homogeneity, are discussed. The solid-state sintering of stoichiometric KNN is characterized by poor densification and an extremely narrow sintering-temperature range, which is close to the solidus temperature. A study of the initial sintering stage revealed that coarsening of the microstructure without densification contributes to a reduction of the driving force for sintering. The influences of the (K + Na)/Nb molar ratio, the presence of a liquid phase, chemical modifications (doping, complex solid solutions) and different atmospheres (i.e., defect chemistry) on the sintering are discussed. Special sintering techniques, such as pressure-assisted sintering and spark-plasma sintering, can be effective methods for enhancing the density of KNN ceramics. The sintering behavior of KNN is compared to that of a representative piezoelectric lead zirconate titanate (PZT).

| S-EPMC5458861 | biostudies-other

Stable and High Piezoelectric Output of GaN Nanowire-Based Lead-Free Piezoelectric Nanogenerator by Suppression of Internal Screening.

Project description:A piezoelectric nanogenerator (PNG) that is based on c-axis GaN nanowires is fabricated on flexible substrate. In this regard, c-axis GaN nanowires were grown on GaN substrate using the vapor-liquid-solid (VLS) technique by metal organic chemical vapor deposition. Further, Polydimethylsiloxane (PDMS) was coated on nanowire-arrays then PDMS matrix embedded with GaN nanowire-arrays was transferred on Si-rubber substrate. The piezoelectric performance of nanowire-based flexible PNG was measured, while the device was actuated using a cyclic stretching-releasing agitation mechanism that was driven by a linear motor. The piezoelectric output was measured as a function of actuation frequency ranging from 1 Hz to 10 Hz and a linear tendency was observed for piezoelectric output current, while the output voltages remained constant. A maximum of piezoelectric open circuit voltages and short circuit current were measured 15.4 V and 85.6 nA, respectively. In order to evaluate the feasibility of our flexible PNG for real application, a long term stability test was performed for 20,000 cycles and the device performance was degraded by less than 18%. The underlying reason for the high piezoelectric output was attributed to the reduced free carriers inside nanowires due to surface Fermi-level pinning and insulating metal-dielectric-semiconductor interface, respectively; the former reduced the free carrier screening radially while latter reduced longitudinally. The flexibility and the high aspect ratio of GaN nanowire were the responsible factors for higher stability. Such higher piezoelectric output and the novel design make our device more promising for the diverse range of real applications.

| S-EPMC6027358 | biostudies-literature

Inversion symmetry and bulk Rashba effect in methylammonium lead iodide perovskite single crystals.

Project description:Methylammonium lead iodide perovskite (MAPbI3) exhibits long charge carrier lifetimes that are linked to its high efficiency in solar cells. Yet, the mechanisms governing these unusual carrier dynamics are not completely understood. A leading hypothesis-disproved in this work-is that a large, static bulk Rashba effect slows down carrier recombination. Here, using second harmonic generation rotational anisotropy measurements on MAPbI3 crystals, we demonstrate that the bulk structure of tetragonal MAPbI3 is centrosymmetric with I4/mcm space group. Our calculations show that a significant Rashba splitting in the bandstructure requires a non-centrosymmetric lead iodide framework, and that incorrect structural relaxations are responsible for the previously predicted large Rashba effect. The small Rashba splitting allows us to compute effective masses in excellent agreement with experiment. Our findings rule out the presence of a large static Rashba effect in bulk MAPbI3, and our measurements find no evidence of dynamic Rashba effects.

| S-EPMC5940805 | biostudies-other

Morphology of Melt-Quenched Lead Telluride Single Crystals.

Project description:Metastable single crystals of nonstoichiometric Pb1-xTe are obtained by rapid cooling from the melt. The composition and crystallographic morphology are studied using X-ray diffraction, scanning electron microscopy, energy-dispersive X-ray spectroscopy, and electron backscatter diffraction. Most single crystals have cubic, pyramidal, or hemispherical shapes with sizes ranging from 50 to 400 μm. All crystals adopt the same face-centered cubic rock salt structure, and the crystal growth direction is ⟨100⟩. The bulk part of the rapidly cooled material solidifies in the form of a Te-rich polycrystalline material in which grains are separated by the PbTe-Te eutectic phase. The stabilization of nonstoichiometric Pb1-xTe provides further scope for the optimization of lead telluride-based thermoelectric materials.

| S-EPMC7883344 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data