A Biphasic Calcium Sulphate/Hydroxyapatite Carrier Containing Bone Morphogenic Protein-2 and Zoledronic Acid Generates Bone.

ABSTRACT: In orthopedic surgery, large amount of diseased or injured bone routinely needs to be replaced. Autografts are mainly used but their availability is limited. Commercially available bone substitutes allow bone ingrowth but lack the capacity to induce bone formation. Thus, off-the-shelf osteoinductive bone substitutes that can replace bone grafts are required. We tested the carrier properties of a biphasic, calcium sulphate and hydroxyapatite ceramic material, containing a combination of recombinant human bone morphogenic protein-2 (rhBMP-2) to induce bone, and zoledronic acid (ZA) to delay early resorption. In-vitro, the biphasic material released 90% of rhBMP-2 and 10% of ZA in the first week. No major changes were found in the surface structure using scanning electron microscopy (SEM) or in the mechanical properties after adding rhBMP-2 or ZA. In-vivo bone formation was studied in an abdominal muscle pouch model in rats (n = 6/group). The mineralized volume was significantly higher when the biphasic material was combined with both rhBMP-2 and ZA (21.4 ± 5.5 mm(3)) as compared to rhBMP-2 alone (10.9 ± 2.1 mm(3)) when analyzed using micro computed tomography (μ-CT) (p < 0.01). In the clinical setting, the biphasic material combined with both rhBMP-2 and ZA can potentially regenerate large volumes of bone.

SUBMITTER: Raina DB

PROVIDER: S-EPMC4870695 | biostudies-other | 2016

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:Background:The treatment of fracture- or non-union-related infections has persistently been a major challenge for both patients and treating surgeons. With rising aging of patients and increasing comorbidities, combined with the heterogeneity of germs and any number of multi-resistance against standard antibiotics, a successful treatment is increasingly difficult. One potential solution could be a custom-made individualized antibacterial coating of standard implants with a biphasic degradable biocarrier (Cerament G/V, supplied by Bonesupport AB, Lund, Sweden) that releases high doses of antibiotics around the bone-implant-interface. Here, we describe our technique of coating intramedullary nails, plates and press-fit shoulder endoprostheses which may prevent bacterial adhesion and biofilm formation. So far, there is very limited experience in individual coating of implants in hip or knee endoprostheses to prevent reoccurrence of surgical-site infection. Currently, no reports are available for coating of stems of shoulder prosthesis and nails or plates for fracture fixation. Methods:Here, we show our first experiences with a new individualized surgical technique of coating these implants with a resorbable antibiotic-loaded hydroxyapatite/calcium sulphate biocomposite to prevent biofilm formation and thereby recurrence of bone or joint infection. We describe three cases for coating of plates and nails for fracture fixation and coating of stems of a shoulder prosthesis. Results:No adverse events of the resorbable bone graft substitute were observed. In all of the cases, no recurrence of the infection was observed and osseointegration was achieved. After implant coating of the shoulder prosthesis, no radiological signs of loosening were detected. Conclusion:We present a new surgical approach of a surface coating of plates, intramedullary nails or prostheses. The osteoconductive- and anti-inflammatory effect of the gentamicin- or vancomycin-loaded hydroxyapatite/calcium sulphate bone graft substitutes shows promising results.

Project description:Background: Bone-graft substitutes are commonly used for the augmentation of traumatic bone defects in tibial plateau fractures. However, their clinical performance compared with that of autologous bone-grafting, the gold standard in bone defect reconstruction, still remains under debate. This study investigates the differences in quality of life, pain, and radiographic outcomes in the treatment of tibial plateau fracture-associated bone defects with either autologous bone grafts or a bioresorbable hydroxyapatite and calcium sulfate cement (CERAMENT BONE VOID FILLER [CBVF]; BONESUPPORT).Methods: In this study, 135 patients with acute depression and split-depression fractures of the proximal part of the tibia (OTA/AO types 41-B2 and 41-B3) were enrolled in a prospective, controlled, randomized, multicenter trial including 20 hospitals in Germany. Patients were randomized to receive either autologous iliac bone graft or CBVF for reconstruction of the bone defect. The primary outcome measures were the Short Form (SF)-12 version 2 Physical Component Summary (PCS) score at week 26 (the study was designed to show noninferiority of the CBVF with regard to the PCS with a prespecified margin of -5 points) and the pain level at 26 weeks postoperatively measured by a visual analog scale (VAS). The secondary outcomes were the SF-12 version 2 Mental Component Summary (MCS) and SF-12 PCS scores at weeks 1, 6, and 12 and bone-healing on radiographs.Results: Age, sex, fixation methods, and fracture pattern were comparable in both groups. There were no significant differences (p > 0.05) in the SF-12 PCS or VAS scores at postoperative week 26. There was a significant reduction of blood loss (p = 0.007) and pain levels (p = 0.008) at postoperative day 1 in the CBVF group. The rates of fracture-healing, defect remodeling, and articular subsidence were not significantly different (p > 0.05) in both groups.Conclusions: Bioresorbable CBVF was noninferior to autologous bone graft with regard to both patient-reported and radiographic outcomes in tibial plateau fractures of OTA/AO types 41-B2 and 41-B3.Level of evidence: Therapeutic Level I. See Instructions for Authors for a complete description of levels of evidence.

Dataset Information

A Biphasic Calcium Sulphate/Hydroxyapatite Carrier Containing Bone Morphogenic Protein-2 and Zoledronic Acid Generates Bone.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets