Characterization of spherical domains at the polystyrene thin film-water interface.

ABSTRACT: Spherical domains that readily form at the polystyrene (PS)-water interface were studied and characterized using atomic force microscopy (AFM). The study showed that these domains have similar characteristics to micro- and nanobubbles, such as a spherical shape, smaller contact angle, low line tension, and they exhibit phase contrast and the coalescence phenomenon. However, their insensitivity to lateral force, absence of long-range hydrophobic attraction, and the presence of possible contaminants and scratches on these domains suggested that these objects are most likely blisters formed by the stretched PS film. Furthermore, the analysis of the PS film before and after contact with water suggested that the film stretches and deforms after being exposed to water. The permeation of water at the PS-silicon interface, caused by osmosis or defects present on the film, can be a reasonable explanation for the nucleation of these spherical domains.

SUBMITTER: Ahmad K

PROVIDER: S-EPMC4901549 | biostudies-other | 2016

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Publications

Characterization of spherical domains at the polystyrene thin film-water interface.

Ahmad Khurshid K Zhao Xuezeng X Pan Yunlu Y Hussain Danish D

Beilstein journal of nanotechnology 20160420

Spherical domains that readily form at the polystyrene (PS)-water interface were studied and characterized using atomic force microscopy (AFM). The study showed that these domains have similar characteristics to micro- and nanobubbles, such as a spherical shape, smaller contact angle, low line tension, and they exhibit phase contrast and the coalescence phenomenon. However, their insensitivity to lateral force, absence of long-range hydrophobic attraction, and the presence of possible contaminan ...[more]

PMID: 27335748

Similar Datasets

Interface-induced nonswitchable domains in ferroelectric thin films.

Project description:Engineering domains in ferroelectric thin films is crucial for realizing technological applications including non-volatile data storage and solar energy harvesting. Size and shape of domains strongly depend on the electrical and mechanical boundary conditions. Here we report the origin of nonswitchable polarization under external bias that leads to energetically unfavourable head-to-head domain walls in as-grown epitaxial PbZr(0.2)Ti(0.8)O3 thin films. By mapping electrostatic potentials and electric fields using off-axis electron holography and electron-beam-induced current with in situ electrical biasing in a transmission electron microscope, we show that electronic band bending across film/substrate interfaces locks local polarization direction and further produces unidirectional biasing fields, inducing nonswitchable domains near the interface. Presence of oxygen vacancies near the film surface, as revealed by electron-energy loss spectroscopy, stabilizes the charged domain walls. The formation of charged domain walls and nonswitchable domains reported in this study can be an origin for imprint and retention loss in ferroelectric thin films.

| S-EPMC8491438 | biostudies-literature

Electrical in-situ characterisation of interface stabilised organic thin-film transistors.

Project description:We report on the electrical in-situ characterisation of organic thin film transistors under high vacuum conditions. Model devices in a bottom-gate/bottom-contact (coplanar) configuration are electrically characterised in-situ, monolayer by monolayer (ML), while the organic semiconductor (OSC) is evaporated by organic molecular beam epitaxy (OMBE). Thermal SiO2 with an optional polymer interface stabilisation layer serves as the gate dielectric and pentacene is chosen as the organic semiconductor. The evolution of transistor parameters is studied on a bi-layer dielectric of a 150 nm of SiO2 and 20 nm of poly((±)endo,exo-bicyclo[2.2.1]hept-5-ene-2,3-dicarboxylic acid, diphenylester) (PNDPE) and compared to the behaviour on a pure SiO2 dielectric. The thin layer of PNDPE, which is an intrinsically photo-patternable organic dielectric, shows an excellent stabilisation performance, significantly reducing the calculated interface trap density at the OSC/dielectric interface up to two orders of magnitude, and thus remarkably improving the transistor performance.

| S-EPMC4599138 | biostudies-literature

Graphene and water-based elastomers thin-film composites by dip-moulding.

Project description:Thin-film elastomers (elastic polymers) have a number of technologically significant applications ranging from sportswear to medical devices. In this work, we demonstrate that graphene can be used to reinforce 20 micron thin elastomer films, resulting in over 50% increase in elastic modulus at a very low loading of 0.1 wt%, while also increasing the elongation to failure. This loading is below the percolation threshold for electrical conductivity. We demonstrate composites with both graphene oxide and reduced graphene oxide, the reduction being undertaken in-situ or ex-situ using a biocompatible reducing agent in ascorbic acid. The ultrathin films were cast by dip moulding. The transparency of the elastomer films allows us to use optical microscopy image and confirm the uniform distribution as well as the conformation of the graphene flakes within the composite.

| S-EPMC4913555 | biostudies-literature

Cerium oxide nanoparticles embedded thin-film nanocomposite nanofiltration membrane for water treatment.

Project description:In this paper, a new approach to synthesize thin-film nanocomposite membranes using cerium oxide (CeO2) nanoparticles (NPs) by pre-seeding interfacial polymerization method was reported. Prepared membranes were examined using contact angle, molecular weight cut-off (MWCO), scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR) and scanning probe microscopy (SPM) to observe its hydrophilicity, pore size, morphology, surface chemistry, and roughness, respectively. Surface charges of the prepared membranes were also qualitatively calculated with the help of contact angle measurements by using the Grahame equation. MWCO studies revealed >90% polyethylene glycol (M.W. 1500 Da) rejection, which was fitted in the range of nanofiltration. By increasing the concentration of CeO2 NPs, flux (33.12 to 41.28 L/m2h), hydrophilicity (77.3 to 51.1°) and surface charges (-7.58 to -13.39 mC/m2) of the membranes was successfully improved, and also showed the high (>90%) salt rejections. The CeO2 embedded membrane was also found out in successful prevention from the attack of bacteria (Escherichia coli) compared to pure polyamide (PA) membrane and confirmed through SEM and viable cell count method. The membrane performances were also evaluated using seawater for fouling study and found that CeO2 embedded surface increased the rejection of hydrophobic contaminants, and notably reduced the fouling.

| S-EPMC5862962 | biostudies-literature

In Situ Neutron Reflectometry Study of Solid Electrolyte Interface (SEI) Formation on Tungsten Thin-Film Electrodes.

Project description:Tungsten, a non-Li-intercalating material, was used as a platform to study solid-electrolyte interface/interphase (SEI) formation in lithium hexafluorphosphate in mixed diethyl carbonate (DEC)/ethylene carbonate electrolyte solutions using in situ neutron reflectometry (NR). A NR measurement determines the neutron scattering length density (SLD)-depth profile, from which a composition-depth profile can be inferred. Isotopic labeling/contrast variation measurements were conducted using a series of three electrolyte solutions: one with both solvents deuterated, one with neither deuterated, and another with only DEC deuterated. A two-layer SEI formed upon polarization to +0.25 V vs Li/Li+. Insensitivity of the inner SEI layer to solvent deuteration suggested limited incorporation of hydrogen atoms from the solvent molecules. Its low SLD indicates that Li2O could be a major constituent. The outer SEI layer SLD scaled with that of the solution, indicating that it either had solution-filled porosity, incorporated hydrogen atoms from the solvent, or both. Returning the electrode to +2.65 V removed lithium from both surface layers, though the effect was more pronounced for the inner layer. Potential cycling had the effect of increasing the solution-derived species content in the inner SEI and decreased the contrast between the inner and outer layers, possibly indicating intermixing of the layers.

| S-EPMC7470620 | biostudies-literature

Enhanced photon management in silicon thin film solar cells with different front and back interface texture.

Project description:Light trapping and photon management of silicon thin film solar cells can be improved by a separate optimization of the front and back contact textures. A separate optimization of the front and back contact textures is investigated by optical simulations taking realistic device geometries into consideration. The optical simulations are confirmed by experimentally realized 1 μm thick microcrystalline silicon solar cells. The different front and back contact textures lead to an enhancement of the short circuit current by 1.2 mA/cm(2) resulting in a total short circuit current of 23.65 mA/cm(2) and an energy conversion efficiency of 8.35%.

| S-EPMC4969606 | biostudies-literature

Water-Soluble Epitaxial NaCl Thin Film for Fabrication of Flexible Devices.

Project description:We studied growth mechanisms of water-soluble NaCl thin films on single crystal substrates. Epitaxial growth of NaCl(100) on Si(100) and domain-matched growth of NaCl(111) on c-sapphire were obtained at thicknesses below 100 nm even at room temperature from low lattice mismatches in both cases. NaCl thin film, which demonstrates high solubility selectivity for water, was successfully applied as a water-soluble sacrificial layer for fabrication of several functional materials, such as WO3 nano-helix and Sn doped In2O3 nano-branches.

| S-EPMC5562699 | biostudies-other

Oxidation-Induced Structure Transformation: Thin-Film Synthesis and Interface Investigations of Barium Disilicide toward Potential Photovoltaic Applications.

Project description:Barium disilicide (BaSi2) has been regarded as a promising absorber material for high-efficiency thin-film solar cells. However, it has confronted issues related to material synthesis and quality control. Here, we fabricate BaSi2 thin films via an industrially applicable sputtering process and uncovered the mechanism of structure transformation. Polycrystalline BaSi2 thin films are obtained through the sputtering process followed by a postannealing treatment. The crystalline quality and phase composition of sputtered BaSi2 are characterized by Raman spectroscopy and X-ray diffraction (XRD). A higher annealing temperature can promote crystallization of BaSi2, but also causes an intensive surface oxidation and BaSi2/SiO2 interfacial diffusion. As a consequence, an inhomogeneous and layered structure of BaSi2 is revealed by Auger electron spectroscopy (AES) and transmission electron microscopy (TEM). The thick oxide layer in such an inhomogeneous structure hinders further both optical and electrical characterizations of sputtered BaSi2. The structural transformation process of sputtered BaSi2 films then is studied by the Raman depth-profiling method, and all of the above observations come to an oxidation-induced structure transformation mechanism. It interprets interfacial phenomena including surface oxidation and BaSi2/SiO2 interdiffusion, which lead to the inhomogeneous and layered structure of sputtered BaSi2. The mechanism can also be extended to epitaxial and evaporated BaSi2 films. In addition, a glimpse toward future developments in both material and device levels is presented. Such fundamental knowledge on structural transformations and complex interfacial activities is significant for further quality control and interface engineering on BaSi2 films toward high-efficiency solar cells.

| S-EPMC6150650 | biostudies-literature

Electrocatalytic water oxidation by a molecular catalyst incorporated into a metal-organic framework thin film.

Project description:A molecular water oxidation catalyst, [Ru(tpy)(dcbpy)(OH2)](ClO4)2 (tpy = 2,2':6',2''-terpyridine, dcbpy = 2,2'-bipyridine-5,5'-dicarboxylic acid) [1], has been incorporated into FTO-grown thin films of UiO-67 (UiO = University of Oslo), by post-synthetic ligand exchange. Cyclic voltammograms (0.1 M borate buffer at pH = 8.4) of the resulting UiO67-[RuOH2]@FTO show a reversible wave associated with the RuIII/II couple in the anodic scan, followed by a large current response that arises from electrocatalytic water oxidation beyond 1.1 V vs. Ag/AgCl. Water oxidation can be observed at an applied potential of 1.5 V over the timescale of hours with a current density of 11.5 ?A cm-2. Oxygen evolution was quantified in situ over the course of the experiment, and the Faradaic efficiency was calculated as 82%. Importantly, the molecular integrity of [1] during electrocatalytic water oxidation is maintained even on the timescale of hours under turnover conditions and applied voltage, as evidenced by the persistence of the wave associated with the RuIII/II couple in the CV. This experiment highlights the capability of metal organic frameworks like UiO-67 to stabilize the molecular structure of catalysts that are prone to form higher clusters in homogenous phase.

| S-EPMC6095457 | biostudies-literature

Organic Nanobowls Modified Thin Film Composite Membrane for Enhanced Purification Performance toward Different Water Resources.

Project description:The structure and composition of nanofillers have a significant influence on polyamide nanofiltration (NF) membranes. In this work, an asymmetric organic nanobowl containing a concave cavity was synthesized and incorporated into a polyamide layer to prepare thin film nanocomposite (TFN) membranes via an interfacial polymerization process. Benefiting from the hydrophilicity, hollow cavity and charge property of the compatible organic nanobowls, the separation performance of the developed TFN membrane was significantly improved. The corresponding water fluxes increased to 119.44 ± 5.56, 141.82 ± 3.24 and 130.27 ± 2.05 L/(m2·h) toward Na2SO4, MgCl2 and NaCl solutions, respectively, with higher rejections, compared with the control thin film composite (TFC) and commercial (CM) membranes. Besides this, the modified TFN membrane presented a satisfying purification performance toward tap water, municipal effluent and heavy metal wastewater. More importantly, a better antifouling property of the TFN membrane than TFC and CM membranes was achieved with the assistance of organic nanobowls. These results indicate that the separation performance of the TFN membrane can be elevated by the incorporation of organic nanobowls.

| S-EPMC8151631 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data