Preparation, Characterization and Thermo-Chromic Properties of EVA/VO₂ Laminate Films for Smart Window Applications and Energy Efficiency in Building.

ABSTRACT: Thermochromic films based on vanadium dioxide (VO₂)/ethylene vinyl acetate copolymer (EVA) composite were developed. The monoclinic VO₂ particles was firstly prepared via hydrothermal and calcination processes. The effects of hydrothermal time and tungsten doping agent on crystal structure and morphology of the calcined metal oxides were reported. After that, 1 wt % of the prepared VO₂ powder was mixed with EVA compound, using two different mixing processes. It was found that mechanical properties of the EVA/VO₂ films prepared by the melt process were superior to those of which prepared by the solution process. On the other hand, percentage visible light transmittance of the solution casted EVA/VO₂ film was greater than that of the melt processed composite film. This was related to the different gel content of EVA rubber and state of dispersion and distribution of VO₂ within the polymer matrix phase. Thermochromic behaviors and heat reflectance of the EVA/VO₂ film were also verified. In overall, this study demonstrated that it was possible to develop a thermochromic film using the polymer composite approach. In this regard, the mixing condition was found to be one of the most important factors affecting morphology and thermo-mechanical properties of the films.

SUBMITTER: Srirodpai O

PROVIDER: S-EPMC5344615 | biostudies-other | 2017 Jan

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:Over the years, vanadium dioxide, (VO2(M1)), has been extensively utilised to fabricate thermochromic thin films with the focus on using external stimuli, such as heat, to modulate the visible through near-infrared transmittance for energy efficiency of buildings and indoor comfort. It is thus valuable to extend the study of thermochromic materials into the mid-infrared (MIR) wavelengths for applications such as smart radiative devices. On top of this, there are numerous challenges with synthesising pure VO2 (M1) thin films, as most fabrication techniques require the post-annealing of a deposited thin film to convert amorphous VO2 into a crystalline phase. Here, we present a direct method to fabricate thicker VO2(M1) thin films onto hot silica substrates (at substrate temperatures of 400 °C and 700 °C) from vanadium pentoxide (V2O5) precursor material. A high repetition rate (10 kHz) femtosecond laser is used to deposit the V2O5 leading to the formation of VO2 (M1) without any post-annealing steps. Surface morphology, structural properties, and UV-visible optical properties, including optical band gap and complex refractive index, as a function of the substrate temperature, were studied and reported below. The transmission electron microscopic (TEM) and X-ray diffraction studies confirm that VO2 (M1) thin films deposited at 700 °C are dominated by a highly texturized polycrystalline monoclinic crystalline structure. The thermochromic characteristics in the mid-infrared (MIR) at a wavelength range of 2.5-5.0 μm are presented using temperature-dependent transmittance measurements. The first-order phase transition from metal-to-semiconductor and the hysteresis bandwidth of the transition were confirmed to be 64.4 °C and 12.6 °C respectively, for a sample fabricated at 700 °C. Thermo-optical emissivity properties indicate that these VO2 (M1) thin films fabricated with femtosecond laser deposition have strong potential for both radiative thermal management or control via active energy-saving windows for buildings, and satellites and spacecraft.

Dataset Information

Preparation, Characterization and Thermo-Chromic Properties of EVA/VO₂ Laminate Films for Smart Window Applications and Energy Efficiency in Building.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure