Calcium Phosphate Bone Cements Including Sugar Surfactants: Part Two-Injectability, Adhesive Properties and Biocompatibility.
Ontology highlight
ABSTRACT:
SUBMITTER: Bercier A
PROVIDER: S-EPMC5445814 | biostudies-other | 2010 Dec
REPOSITORIES: biostudies-other
Publications
Calcium Phosphate Bone Cements Including Sugar Surfactants: Part Two-Injectability, Adhesive Properties and Biocompatibility.
Bercier Ariane A Gonçalves Stéphane S Autefage Helène H Briand-Mesange Fabienne F Lignon Olivier O Fitremann Juliette J
Materials (Basel, Switzerland) 20101202 12
Addition of sugar surfactants, sucrose fatty acid esters and alkylpolyglucosides to a calcium phosphate cement, designed for bone reconstruction, is described. Thanks to their adsorption at the surface of the calcium phosphate particles, the sugar surfactants allowed a full injectability and brought a very good workability. Injectability was measured by monitoring force-distance curves. With some of the selected sugar surfactants adhesive properties of the cement pastes were also observed, which ...[more]
Similar Datasets
Project description:Calcium phosphate bone cements (CPCs) with antibacterial properties are demanded for clinical applications. In this study, we demonstrated the use of a relatively simple processing route based on preparation of silver-doped CPCs (CPCs-Ag) through the preparation of solid dispersed active powder phase. Real-time monitoring of structural transformations and kinetics of several CPCs-Ag formulations (Ag = 0 wt %, 0.6 wt % and 1.0 wt %) was performed by the Energy Dispersive X-ray Diffraction technique. The partial conversion of ?-tricalcium phosphate (TCP) phase into the dicalcium phosphate dihydrate (DCPD) took place in all the investigated cement systems. In the pristine cement powders, Ag in its metallic form was found, whereas for CPC-Ag 0.6 wt % and CPC-Ag 1.0 wt % cements, CaAg(PO?)? was detected and Ag (met.) was no longer present. The CPC-Ag 0 wt % cement exhibited a compressive strength of 6.5 ± 1.0 MPa, whereas for the doped cements (CPC-Ag 0.6 wt % and CPC-Ag 1.0 wt %) the reduced values of the compressive strength 4.0 ± 1.0 and 1.5 ± 1.0 MPa, respectively, were detected. Silver-ion release from CPC-Ag 0.6 wt % and CPC-Ag 1.0 wt % cements, measured by the Atomic Emission Spectroscopy, corresponds to the average values of 25 µg/L and 43 µg/L, respectively, rising a plateau after 15 days. The results of the antibacterial test proved the inhibitory effect towards pathogenic Escherichia coli for both CPC-Ag 0.6 wt % and CPC-Ag 1.0 wt % cements, better performances being observed for the cement with a higher Ag-content.
| S-EPMC4932467 | biostudies-literature
Project description:In the framework of new materials for orthopedic applications, Magnesium Phosphate-based Cements (MPCs) are currently the focus of active research in biomedicine, given their promising features; in this field, the loading of MPCs with active molecules to be released in the proximity of newly forming bone could represent an innovative approach to enhance the in vivo performances of the biomaterial. In this work, we describe the preparation and characterization of MPCs containing citrate, an ion naturally present in bone which presents beneficial effects when released in the proximity of newly forming bone tissue. The cements were characterized in terms of handling properties, setting time, mechanical properties, crystallinity, and microstructure, so as to unravel the effect of citrate concentration on the features of the material. Upon incubation in aqueous media, we demonstrated that citrate could be successfully released from the cements, while contributing to the alkalinization of the surroundings. The cytotoxicity of the materials toward human fibroblasts was also tested, revealing the importance of a fine modulation of released citrate to guarantee the biocompatibility of the material.
| S-EPMC8011797 | biostudies-literature
Project description:Calcium phosphate ceramics are frequently applied to stimulate regeneration of bone in view of their excellent biological compatibility with bone tissue. Unfortunately, these bioceramics are also highly brittle. To improve their toughness, fibers can be incorporated as the reinforcing component for the calcium phosphate cements. Herein, we functionalize the surface of poly(vinyl alcohol) fibers with thermoresponsive poly(N-isopropylacrylamide) brushes of tunable thickness to improve simultaneously fiber dispersion and fiber-matrix affinity. These brushes shift from hydrophilic to hydrophobic behavior at temperatures above their lower critical solution temperature of 32 °C. This dual thermoresponsive shift favors fiber dispersion throughout the hydrophilic calcium phosphate cements (at 21 °C) and toughens these cements when reaching their hydrophobic state (at 37 °C). The reinforcement efficacy of these surface-modified fibers was almost double at 37 versus 21 °C, which confirms the strong potential of thermoresponsive fibers for reinforcement of calcium phosphate cements.
| S-EPMC6676411 | biostudies-literature
Project description:Thanks to their biocompatibility, biodegradability, injectability and self-setting properties, calcium phosphate cements (CPCs) have been the most economical and effective biomaterials of choice for use as bone void fillers. They have also been extensively used as drug delivery carriers owing to their ability to provide for a steady release of various organic molecules aiding the regeneration of defective bone, including primarily antibiotics and growth factors. This review provides a systematic compilation of studies that reported on the controlled release of drugs from CPCs in the last 25 years. The chemical, compositional and microstructural characteristics of these systems through which the control of the release rates and mechanisms could be achieved have been discussed. In doing so, the effects of (i) the chemistry of the matrix, (ii) porosity, (iii) additives, (iv) drug types, (v) drug concentrations, (vi) drug loading methods and (vii) release media have been distinguished and discussed individually. Kinetic specificities of in vivo release of drugs from CPCs have been reviewed, too. Understanding the kinetic and mechanistic correlations between the CPC properties and the drug release is a prerequisite for the design of bone void fillers with drug release profiles precisely tailored to the application area and the clinical picture. The goal of this review has been to shed light on these fundamental correlations.
| S-EPMC8379446 | biostudies-literature
Project description:Tricalcium silicate (TCS)-based materials produce calcium hydroxide as a byproduct of their hydration reaction. The present study investigated whether calcium ion release (CIR) affects their biological and antimicrobial properties when used as pulp protection materials. The effect of incorporation of micro-silica and calcium phosphate monobasic to radiopacified TCS-based materials was investigated. The commercial TCS-based Biodentine, Bio-C Pulpo, TotalFill Root Repair Material, TheraCal LC and a base/liner- ACTIVA BioACTIVE (Activa) were also evaluated. The hydration and CIR were monitored and correlated with biocompatibility and antimicrobial assessment of eluates. Overall, the additives altered the hydration and leaching profile of the prototype cements. The micro-silica inclusion resulted in a decreased long-term calcium hydroxide formation which was associated with neutralised cytotoxicity and antibacterial activity. Calcium phosphate did not alter the leaching profile, although a stronger antibacterial effect was induced. The commercial materials also had different CIR profiles. The water-based ones had higher CIR, and this was associated with stronger antimicrobial effect but not enhanced biological activity. Both TheraCal LC and Activa exhibited poor degree of conversion, low CIR, acceptable biocompatibility and moderate antibacterial activity. A positive correlation of CIR with antibacterial effectiveness was observed (0.3?<?r?<?0.49; p?=?0.021, p?=?0.011 for the two test bacterial cultures). No relation was shown between CIR and cytotoxicity (0.3?<?r?<?0.49; p?=?0.150, p?=?0.068 for the two cell cultures studied). The additives modified the CIR. The antimicrobial properties were dependent on the CIR; the cytotoxicity of the materials was unaffected.
| S-EPMC6910940 | biostudies-literature
Project description:BackgroundThe purpose of this preliminary study was to assess the in vivo performance of synthetic, cotton wool-like nanocomposites consisting of a biodegradable poly(lactide-co-glycolide) fibrous matrix and containing either calcium phosphate nanoparticles (PLGA/CaP 60:40) or silver doped CaP nanoparticles (PLGA/Ag-CaP 60:40). Besides its extraordinary in vitro bioactivity the latter biomaterial (0.4 wt% total silver concentration) provides additional antimicrobial properties for treating bone defects exposed to microorganisms.Materials and methodsBoth flexible artificial bone substitutes were implanted into totally 16 epiphyseal and metaphyseal drill hole defects of long bone in sheep and followed for 8 weeks. Histological and histomorphological analyses were conducted to evaluate the biocompatibility and bone formation applying a score system. The influence of silver on the in vivo performance was further investigated.ResultsSemi-quantitative evaluation of histology sections showed for both implant materials an excellent biocompatibility and bone healing with no resorption in the adjacent bone. No signs of inflammation were detectable, either macroscopically or microscopically, as was evident in 5 µm plastic sections by the minimal amount of inflammatory cells. The fibrous biomaterials enabled bone formation directly in the centre of the former defect. The area fraction of new bone formation as determined histomorphometrically after 8 weeks implantation was very similar with 20.5 ± 11.2 % and 22.5 ± 9.2 % for PLGA/CaP and PLGA/Ag-CaP, respectively.ConclusionsThe cotton wool-like bone substitute material is easily applicable, biocompatible and might be beneficial in minimal invasive surgery for treating bone defects.
| S-EPMC3092473 | biostudies-literature
Project description:Biologically active metal ions in low doses have the potential to accelerate bone defect healing. For successful remodelling the interaction of bone graft materials with both bone-forming osteoblasts and bone resorbing osteoclasts is crucial. In the present study brushite forming calcium phosphate cements (CPC) were doped with Co2+, Cu2+ and Cr3+ and the influence of these materials on osteoclast differentiation and activity was examined. Human osteoclasts were differentiated from human peripheral blood mononuclear cells (PBMC) both on the surface and in indirect contact to the materials on dentin discs. Release of calcium, phosphate and bioactive metal ions was determined using ICP-MS both in the presence and absence of the cells. While Co2+ and Cu2+ showed a burst release, Cr3+ was released steadily at very low concentrations (below 1 ?M) and both calcium and phosphate release of the cements was considerably changed in the Cr3+ modified samples. Direct cultivation of PBMC/osteoclasts on Co2+ cements showed lower attached cell number compared to the reference but high activity of osteoclast specific enzymes tartrate resistant acid phosphatase (TRAP), carbonic anhydrase II (CAII) and cathepsin K (CTSK) and significantly increased gene expression of vitronectin receptor. Indirect cultivation with diluted Co2+ cement extracts revealed highest resorbed area compared to all other modifications and the reference. Cu2+ cements had cytotoxic effect on PBMC/osteoclasts during direct cultivation, while indirect cultivation with diluted extracts from Cu2+ cements did not provoke cytotoxic effects but a strictly inhibited resorption. Cr3+ doped cements did not show cytotoxic effects at all. Gene expression and enzyme activity of CTSK was significantly increased in direct culture. Indirect cultivation with Cr3+ doped cements revealed significantly higher resorbed area compared to the reference. In conclusion Cr3+ doped calcium phosphate cements are an innovative cement modification because of their high cytocompatibility and support of active resorption by osteoclasts.
| S-EPMC5538673 | biostudies-literature
Project description:This study investigated the effects of incorporating glucose microparticles (GMPs) and poly(lactic-co-glycolic acid) microparticles (PLGA MPs) within a calcium phosphate cement on the cement's handling, physicochemical properties, and the respective pore formation. Composites were fabricated with two different weight fractions of GMPs (10 and 20 wt%) and two different weight fractions of PLGA MPs (10 and 20 wt%). Samples were assayed for porosity, pore morphology, and compressive mechanical properties. An in vitro degradation study was also conducted. Samples were exposed to a physiological solution for 3 days, 4 wks, and 8 wks in order to understand how the inclusion of GMPs and PLGA MPs affects the composite's porosity and mass loss over time. GMPs and PLGA MPs were both successfully incorporated within the composites and all formulations showed an initial setting time that is appropriate for clinical applications. Through a main effects analysis, we observed that the incorporation of GMPs had a significant effect on the overall porosity, mean pore size, mode pore size, and in vitro degradation rate of PLGA MPs as early as after 3 days (p < 0.05). After 4 wks and 8 wks, these same properties were affected by the inclusion of both types of MPs (p < 0.05). Advanced polymer chromatography confirmed that the degradation of PLGA MPs coincided with an increase in composite porosity, mean pore size, and mode pore size. Finally, it was observed that the inclusion of GMPs slowed the degradation of PLGA MPs in vitro and reduced the solution acidity due to PLGA degradation products. Our results suggest that the dual inclusion of GMPs and PLGA MPs is a valuable approach for the generation of early macropores, while also mitigating the effect of acidic degradation products from PLGA MPs on their degradation kinetics.Statement of significanceA multitude of strategies and techniques have been investigated for the introduction of macropores with calcium phosphate cements (CPC). However, many of these strategies take several weeks to months to generate a maximal porosity or the degradation products of the porogen can trigger a localized inflammatory response in vivo. As such, it was hypothesized that the fast dissolution of glucose microparticles (GMPs) in a CPC composite also incorporating poly(lactic-co-glycolic acid) (PLGA) microparticles (MPs) will create an initial macroporosity and increase the surface area within the CPC, thus enhancing the diffusion of PLGA degradation products and preventing a significant decrease in pH. Furthermore, as PLGA degradation occurs over several weeks to months, additional macroporosity will be generated at later time points within CPCs. The results offer a new method for generating macroporosity in a multimodal fashion that also mitigates the effects of acidic degradation products.
| S-EPMC6650161 | biostudies-literature
Project description:Calcium phosphate cements are of great interest for researchers and their applications in medical practice expanded. Nevertheless, they have a number of drawbacks including the insufficient level of mechanical properties and low degradation rate. Struvite (MgNH4PO4) -based cements, which grew in popularity in recent years, despite their neutral pH and acceptable mechanical performance, release undesirable NH4 + ions during their resorption. This issue could be avoided by replacement of ammonia ions in the cement liquid with sodium, however, such cements have a pH values of 9-10, leading to cytotoxicity. Thus, the main goal of this investigation is to optimize the composition of cements to achieve the combination of desirable properties: neutral pH, sufficient mechanical properties, and the absence of cytotoxicity, applying Na2HPO4-based cement liquid. For this purpose, cement powders precursors in the CaO-MgO-P2O5 system were synthesized by one-pot process in a wide composition range, and their properties were investigated. The optimal performance was observed for the cements with (Ca + Mg)/P ratio of 1.67, which are characterized by newberyite phase formation during setting reaction, pH values close to 7, sufficient compressive strength up to 22 ± 3 MPa (for 20 mol.% of Mg), dense microstructure and adequate matrix properties of the surface. This set of features make those materials promising candidates for medical applications.
| S-EPMC7217922 | biostudies-literature
Project description:Many medical procedures could benefit from the use of tissue sealants which allow for reduced surgery time, limited blood loss, easier tissue handling, and fewer postoperative complications. The safety and biocompatibility of surgical sealants are of paramount importance therefore, the aim of this study is to investigate the biocompatibility of NE'X Glue Surgical Adhesive. Chemical characterization (VOC and elements), cytotoxicity (MEM elution), genotoxicity (AMES and MLA), endotoxin contamination, sensitization potential, intracutaneous reactivity, acute and subchronic systemic toxicity with implantation as well as pyrogenicity were evaluated to investigate the biocompatibility of the NE'X Glue Surgical Adhesive. Studies were conducted according to ISO 10993 standards. The biocompatibility requirements with accordance to ISO 10993-1 for NE'X Glue were met. In vitro studies showed that NE'X Glue surgical adhesive is non-cytotoxic and non-mutagenic. Also, in vivo studies demonstrated that NE'X Glue shows no signs of toxicity, has no pyrogenic potential, and is non-sensitizing and non-irritating. The chemical characterization showed that no compounds were identified above Analytical Evaluation Threshold (AET), and no elements with concentrations higher than element-specific PDE (µg/day) were detected. NE'X Glue Surgical Adhesive is a versatile and promising new surgical sealant with a wide range of potential applications and very good*0* biocompatibility.
| S-EPMC9325888 | biostudies-literature