Sputtered Modified Barium Titanate for Thin-Film Capacitor Applications.

ABSTRACT: New apparatus and a new process for the sputter deposition of modified barium titanate thin-films were developed. Films were deposited at temperatures up to 900 °C from a Ba₀.96Ca0.04Ti0.82Zr0.18O₃ (BCZTO) target directly onto Si, Ni and Pt surfaces and characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). Film texture and crystallinity were found to depend on both deposition temperature and substrate: above 600 °C, the as-deposited films consisted of well-facetted crystallites with the cubic perovskite structure. A strongly textured Pt (111) underlayer enhanced the (001) orientation of BCZTO films deposited at 900 °C, 10 mtorr pressure and 10% oxygen in argon. Similar films deposited onto a Pt (111) textured film at 700 °C and directly onto (100) Si wafers showed relatively larger (011) and diminished intensity (00ℓ) diffraction peaks. Sputter ambients containing oxygen caused the Ni underlayers to oxidize even at 700 °C: Raising the process temperature produced more diffraction peaks of NiO with increased intensities. Thin-film capacitors were fabricated using ~500 nm thick BCZTO dielectrics and both Pt and Ni top and bottom electrodes. Small signal capacitance measurements were carried out to determine capacitance and parallel resistance at low frequencies and from these data, the relative permittivity (er) and resistivity (r) of the dielectric films were calculated; values ranged from ~50 to >2,000, and from ~10⁴ to ~1010 Ω∙cm, respectively.

SUBMITTER: Reynolds GJ

PROVIDER: S-EPMC5448959 | biostudies-other | 2012 Apr

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Electrical Properties of Thin-Film Capacitors Fabricated Using High Temperature Sputtered Modified Barium Titanate.

Project description:Simple thin-film capacitor stacks were fabricated from sputter-deposited doped barium titanate dielectric films with sputtered Pt and/or Ni electrodes and characterized electrically. Here, we report small signal, low frequency capacitance and parallel resistance data measured as a function of applied DC bias, polarization versus applied electric field strength and DC load/unload experiments. These capacitors exhibited significant leakage (in the range 8-210 μA/cm²) and dielectric loss. Measured breakdown strength for the sputtered doped barium titanate films was in the range 200 kV/cm -2 MV/cm. For all devices tested, we observed clear evidence for dielectric saturation at applied electric field strengths above 100 kV/cm: saturated polarization was in the range 8-15 μC/cm². When cycled under DC conditions, the maximum energy density measured for any of the capacitors tested here was ~4.7 × 10-2 W-h/liter based on the volume of the dielectric material only. This corresponds to a specific energy of ~8 × 10-3 W-h/kg, again calculated on a dielectric-only basis. These results are compared to those reported by other authors and a simple theoretical treatment provided that quantifies the maximum energy that can be stored in these and similar devices as a function of dielectric strength and saturation polarization. Finally, a predictive model is developed to provide guidance on how to tailor the relative permittivities of high-k dielectrics in order to optimize their energy storage capacities.

| S-EPMC5448953 | biostudies-other

Chemical Solution Deposition of Barium Titanate Thin Films with Ethylene Glycol as Solvent for Barium Acetate.

Project description:Chemical solution deposition (CSD) of BaTiO3 (BT) or BT-based thin films relies on using a carboxylic acid and alcohol as the solvents for alkaline-earth carboxylate and transition-metal alkoxide, respectively; however, the esterification reaction of the solvents may lead to in-situ water formation and precipitation. To avoid such an uncontrolled reaction, we developed a route in which ethylene glycol (EG) is used as the solvent for Ba-acetate. The EG-based BT coating solutions are stable for at least a few months. The thermal decomposition of the BT xerogel obtained by drying the EG-based solutions depends on the choice of the solvent for the Ti-alkoxide as well: in the case of EG and 2-methoxyethanol solvents carbon residues are removed at only about 1100 °C, while in the case of ethanol it is concluded at about 700 °C. About 100 nm thick BT films derived from the EG-ethanol solution deposited on platinized silicon reveal dense, crack-free columnar microstructure. They exhibit local ferro- and piezoelectric properties. The macroscopic polarization-electric field loops were obtained up to a quite high electric field of about 2.4 MV/cm. The EG-ethanol based CSD route is a viable alternative to the established acetic acid-alcohol route for BT and BT-based films.

| S-EPMC9230800 | biostudies-literature

Transparent Thin-Film Transistors Based on Sputtered Electric Double Layer.

Project description:Electric-double-layer (EDL) thin-film transistors (TFTs) have attracted much attention due to their low operation voltages. Recently, EDL TFTs gated with radio frequency (RF) magnetron sputtered SiO₂ have been developed which is compatible to large-area electronics fabrication. In this work, fully transparent Indium-Gallium-Zinc-Oxide-based EDL TFTs on glass substrates have been fabricated at room temperature for the first time. A maximum transmittance of about 80% has been achieved in the visible light range. The transparent TFTs show a low operation voltage of 1.5 V due to the large EDL capacitance (0.3 µF/cm² at 20 Hz). The devices exhibit a good performance with a low subthreshold swing of 130 mV/dec and a high on-off ratio > 10⁵. Several tests have also been done to investigate the influences of light irradiation and bias stress. Our results suggest that such transistors might have potential applications in battery-powered transparent electron devices.

| S-EPMC5506904 | biostudies-literature

Oxidation-Induced Structure Transformation: Thin-Film Synthesis and Interface Investigations of Barium Disilicide toward Potential Photovoltaic Applications.

Project description:Barium disilicide (BaSi2) has been regarded as a promising absorber material for high-efficiency thin-film solar cells. However, it has confronted issues related to material synthesis and quality control. Here, we fabricate BaSi2 thin films via an industrially applicable sputtering process and uncovered the mechanism of structure transformation. Polycrystalline BaSi2 thin films are obtained through the sputtering process followed by a postannealing treatment. The crystalline quality and phase composition of sputtered BaSi2 are characterized by Raman spectroscopy and X-ray diffraction (XRD). A higher annealing temperature can promote crystallization of BaSi2, but also causes an intensive surface oxidation and BaSi2/SiO2 interfacial diffusion. As a consequence, an inhomogeneous and layered structure of BaSi2 is revealed by Auger electron spectroscopy (AES) and transmission electron microscopy (TEM). The thick oxide layer in such an inhomogeneous structure hinders further both optical and electrical characterizations of sputtered BaSi2. The structural transformation process of sputtered BaSi2 films then is studied by the Raman depth-profiling method, and all of the above observations come to an oxidation-induced structure transformation mechanism. It interprets interfacial phenomena including surface oxidation and BaSi2/SiO2 interdiffusion, which lead to the inhomogeneous and layered structure of sputtered BaSi2. The mechanism can also be extended to epitaxial and evaporated BaSi2 films. In addition, a glimpse toward future developments in both material and device levels is presented. Such fundamental knowledge on structural transformations and complex interfacial activities is significant for further quality control and interface engineering on BaSi2 films toward high-efficiency solar cells.

| S-EPMC6150650 | biostudies-literature

A Sputtered Silicon Oxide Electrolyte for High-Performance Thin-Film Transistors.

Project description:Low operating voltages have been long desired for thin-film transistors (TFTs). However, it is still challenging to realise 1-V operation by using conventional dielectrics due to their low gate capacitances and low breakdown voltages. Recently, electric double layers (EDLs) have been regarded as a promising candidate for low-power electronics due to their high capacitance. In this work, we present the first sputtered SiO2 solid-state electrolyte. In order to demonstrate EDL behaviour, a sputtered 200 nm-thick SiO2 electrolyte was incorporated into InGaZnO TFTs as the gate dielectric. The devices exhibited an operating voltage of 1 V, a threshold voltage of 0.06 V, a subthreshold swing of 83 mV dec-1 and an on/off ratio higher than 105. The specific capacitance was 0.45 µF cm-2 at 20 Hz, which is around 26 times higher than the value obtained from thermally oxidised SiO2 films with the same thickness. Analysis of the microstructure and mass density of the sputtered SiO2 films under different deposition conditions indicates that such high capacitance might be attributed to mobile protons donated by atmospheric water. The InGaZnO TFTs with the optimised SiO2 electrolyte also showed good air stability. This work provides a new pathway to the realisation of high-yield low-power electronics.

| S-EPMC5429786 | biostudies-literature

Inert gas bubble formation in magnetron sputtered thin-film CdTe solar cells.

Project description:Cadmium telluride (CdTe) solar cells are deposited in current production using evaporation-based tech- niques. Fabricating CdTe solar cells using magnetron sputtering would have the advantage of being more cost-efficient. Here, we show that such deposition results in the incorporation of the magnetron working gas Ar, within the films. Post deposition processing with CdCl2 improves cell efficiency and during which stacking faults are removed. The Ar then accumulates into clusters leading to the creation of voids and blisters on the surface. Using molecular dynamics, the penetration threshold energies are determined for both Ar and Xe, with CdTe in both zinc-blende and wurtzite phases. These calculations show that more Ar than Xe can penetrate into the growing film with most penetration across the (111) surface. The mechanisms and energy barriers for interstitial Ar and Xe diffusion in zinc-blende are determined. Barriers are reduced near existing clusters, increasing the probability of capture-based cluster growth. Barriers in wurtzite are higher with non-Arrhenius behaviour observed. This provides an explanation for the increase in the size of voids observed after stacking fault removal. Blister exfoliation was also modelled, showing the formation of shallow craters with a raised rim.

| S-EPMC7426057 | biostudies-literature

Fabrication of Crack-Free Barium Titanate Thin Film with High Dielectric Constant Using Sub-Micrometric Scale Layer-by-Layer E-Jet Deposition.

Project description:Dense and crack-free barium titanate (BaTiO₃, BTO) thin films with a thickness of less than 4 μm were prepared by using sub-micrometric scale, layer-by-layer electrohydrodynamic jet (E-jet) deposition of the suspension ink which is composed of BTO nanopowder and BTO sol. Impacts of the jet height and line-to-line pitch of the deposition on the micro-structure of BTO thin films were investigated. Results show that crack-free BTO thin films can be prepared with 4 mm jet height and 300 μm line-to-line pitch in this work. Dielectric constant of the prepared BTO thin film was recorded as high as 2940 at 1 kHz at room temperature. Meanwhile, low dissipation factor of the BTO thin film of about 8.6% at 1 kHz was also obtained. The layer-by-layer E-jet deposition technique developed in this work has been proved to be a cost-effective, flexible and easy to control approach for the preparation of high-quality solid thin film.

| S-EPMC5456538 | biostudies-other

Transition from Reconstruction toward Thin Film on the (110) Surface of Strontium Titanate.

Project description:The surfaces of metal oxides often are reconstructed with a geometry and composition that is considerably different from a simple termination of the bulk. Such structures can also be viewed as ultrathin films, epitaxed on a substrate. Here, the reconstructions of the SrTiO3 (110) surface are studied combining scanning tunneling microscopy (STM), transmission electron diffraction, and X-ray absorption spectroscopy (XAS), and analyzed with density functional theory calculations. Whereas SrTiO3 (110) invariably terminates with an overlayer of titania, with increasing density its structure switches from n × 1 to 2 × n. At the same time the coordination of the Ti atoms changes from a network of corner-sharing tetrahedra to a double layer of edge-shared octahedra with bridging units of octahedrally coordinated strontium. This transition from the n × 1 to 2 × n reconstructions is a transition from a pseudomorphically stabilized tetrahedral network toward an octahedral titania thin film with stress-relief from octahedral strontia units at the surface.

| S-EPMC4834633 | biostudies-literature

Applications of thin-film sandwich crystallization platforms.

Project description:Examples are shown of protein crystallization in, and data collection from, solutions sandwiched between thin polymer films using vapour-diffusion and batch methods. The crystallization platform is optimal for both visualization and in situ data collection, with the need for traditional harvesting being eliminated. In wells constructed from the thinnest plastic and with a minimum of aqueous liquid, flash-cooling to 100 K is possible without significant ice formation and without any degradation in crystal quality. The approach is simple; it utilizes low-cost consumables but yields high-quality data with minimal sample intervention and, with the very low levels of background X-ray scatter that are observed, is optimal for microcrystals.

| S-EPMC4822989 | biostudies-literature

Fabrication, Corrosion, and Mechanical Properties of Magnetron Sputtered Cu-Zr-Al Metallic Glass Thin Film.

Project description:The appearance of thin film metallic glasses (TFMGs) is gaining increasing interest because of their unique mechanical and anticorrosion properties and potential engineering applications. In this study, Cu-Zr-Al ternary thin film metallic glasses were fabricated by using DC magnetron sputtering equipment with various target powers. The evolution of the structure was systematically investigated by grazing incidence X-ray diffractometer, scanning electron microscopy, and transmission electron microscopy. The deposition rate increases with the increasing of applied target power. The as-deposited thin films show an amorphous structure. The compositional fluctuations on the nanometer scale indicate the presence of two Cu- and Zr-rich amorphous phases. The electrochemical corrosion measurements indicated that Cu-Zr-Al thin film metallic glasses had good corrosion resistance in the sulfuric acid solution. Nanoindentation results showed that the mechanical deformation was found to be homogenous and reproducible with a high value range for the hardness and modulus.

| S-EPMC6947152 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data