Fabrication of Cellulose Film with Enhanced Mechanical Properties in Ionic Liquid 1-Allyl-3-methylimidaxolium Chloride (AmimCl).

ABSTRACT: More and more attention has been paid to environmentally friendly bio-based renewable materials as the substitution of fossil-based materials, due to the increasing environmental concerns. In this study, regenerated cellulose films with enhanced mechanical property were prepared via incorporating different plasticizers using ionic liquid 1-allyl-3-methylimidazolium chloride (AmimCl) as the solvent. The characteristics of the cellulose films were investigated by scanning electron microscopy (SEM), atomic force microscopy (AFM), thermal analysis (TG), X-ray diffraction (XRD), 13C Solid-state cross-polarization/magic angle spinning nuclear magnetic resonance (CP/MAS NMR) and tensile testing. The results showed that the cellulose films exhibited a homogeneous and smooth surface structure. It was noted that the thermal stability of the regenerated cellulose film plasticized with glycerol was increased compared with other regenerated cellulose films. Furthermore, the incorporation of plasticizers dramatically strengthened the tensile strength and improved the hydrophobicity of cellulose films, as compared to the control sample. Therefore, these notable results exhibited the potential utilization in producing environmentally friendly cellulose films with high performance properties.

SUBMITTER: Pang J

PROVIDER: S-EPMC5452314 | biostudies-other | 2013 Mar

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Fabrication of Cellulose Nanocrystal/Silver/Alginate Bionanocomposite Films with Enhanced Mechanical and Barrier Properties for Food Packaging Application.

Project description:Eco-friendly cellulose nanocrystal/silver/alginate (CNC/Ag/Alg) bionanocomposite films were successfully prepared by blending of CNC with Ag/Alg solution. The CNC was fabricated from cellulose microcrystal (CMC) by acid hydrolysis method. The Ag nanoparticles (AgNPs) were generated by using Alg as a reducing agent through hydrothermal process. AgNPs-included composite films showed characteristic plasmonic effect of the AgNPs with the maximum absorption at 491 nm and they also showed high ultraviolet (UV) barrier properties. The CNC/Ag/Alg composite films were analyzed by using scanning electron microscopy, transmission electron microscopy, optical microscopy, Fourier transform infrared spectroscopy, and X-ray diffraction technique. Depending on the type of nanofillers, tensile strength of the composite films increased by 39-57% and water vapor permeation decreased by 17-36% compared with those of the neat Alg films. The Ag/Alg and CNC/Ag/Alg films showed brown color as detected from the increase of both 'b' and 'a' parameters by colorimeter. The UV and water barrier properties of Alg based composite films were found higher than the Alg films. The obtained results suggested that the prepared composite films can be used in food packaging applications.

| S-EPMC6915576 | biostudies-literature

Biodegradable Cellulose Film Prepared From Banana Pseudo-Stem Using an Ionic Liquid for Mango Preservation.

Project description:The excessive use and disposal of plastic packaging materials have drawn increasing concerns from the society because of the detrimental effect on environment and ecosystems. As the most widely used fruit packing material, polyethylene (PE) film is not suitable for long-term preservation of some tropical fruits, such as mangos, due to its inferior gas permeability. Cellulose based film can be made from renewable resources and is biodegradable and environmental-friendly, which makes it a promising alternative to PE as a packaging material. In this study, cellulose film synthesized from delignified banana stem fibers via an ionic liquid 1-Allyl-3-methylimidazolium chloride ([AMIm][Cl]) were evaluated as packing material for mangos preservation. The moisture vapor transmission rate and gas transmission rate of the synthesized cellulose film were 1,969.1 g/(m2⋅24 h) and 10,015.4 ml/(m2⋅24 h), respectively, which are significantly higher than those of commercial PE films. The high permeability is beneficial to the release of ethylene so that contribute to extend fruit ripening period. As a result, cellulose film packaging significantly decreased the disease and color indexes of mangos, while prolonged the storage and shelf life of marketable fruits. In addition, the cellulose film was decomposed in soils in 4 weeks, indicating an excellent biodegradability as compared to the PE plastic film.

| S-EPMC7933007 | biostudies-literature

Phosphonium Ionic Liquid-Infused Poly(vinyl chloride) Surfaces Possessing Potent Antifouling Properties.

Project description:Microbial fouling is a costly issue, which impacts a wide range of industries, such as healthcare, food processing, and construction industries, and improved strategies to reduce the impact of fouling are urgently required. Slippery liquid-infused porous surfaces (SLIPSs) have recently been developed as a bioinspired approach to prevent antifouling. Here, we report the development of slippery, superhydrophilic surfaces by infusing roughened poly(vinyl chloride) (PVC) substrates with phosphonium ionic liquids (PILs). These surfaces were capable of reducing viable bacterial adherence by Staphylococcus aureus and Pseudomonas aeruginosa by >6 log10 cfu mL-1 after 24 h under static conditions relative to control PVC. Furthermore, we report the potential of a series of asymmetric quaternary alkyl PILs with varying alkyl chain lengths (C4-C18) and counteranions to act as antimicrobial agents against both Gram +ve and Gram -ve bacteria and illustrate their potential as antimicrobial alternatives to traditional fluorinated lubricants commonly used in the synthesis of SLIPSs.

| S-EPMC7160832 | biostudies-literature

Electroactive ?-Phase, Enhanced Thermal and Mechanical Properties and High Ionic Conductivity Response of Poly (Vinylidene Fluoride)/Cellulose Nanocrystal Hybrid Nanocomposites.

Project description:Cellulose nanocrystals (CNCs) were incorporated into poly (vinylidene fluoride) (PVDF) to tailor the mechanical and dielectric properties of this electroactive polymer. PVDF/CNC nanocomposites with concentrations up to 15 wt.% were prepared by solvent-casting followed by quick vacuum drying in order to ensure the formation of the electroactive ?-phase. The changes induced by the presence of CNCs on the morphology of PVDF and its crystalline structure, thermal properties, mechanical performance and dielectric behavior are explored. The results suggest a relevant role of the CNC surface -OH groups, which interact with PVDF fluorine atoms. The real dielectric constant ?' of nanocomposites at 200 Hz was found to increase by 3.6 times up to 47 for the 15 wt.% CNC nanocomposite due to an enhanced ionic conductivity provided by CNCs. The approach reported here in order to boost the formation of the ?-phase of PVDF upon the incorporation of CNCs serves to further develop cellulose-based multifunctional materials.

| S-EPMC7040804 | biostudies-literature

Structural Changes of Bagasse dusring the Homogeneous Esterification with Maleic Anhydride in Ionic Liquid 1-Allyl-3-methylimidazolium Chloride.

Project description:The maleation of bagasse could greatly increase the compatibility between bagasse and composite matrixes, and the percentage of substitution (PS) of bagasse maleates could be regulated in the homogeneous system. However, due to the complicated components and the linkages of bagasse, it was difficult to control the reaction behaviors of each component. In this paper, the detailed structural changes of bagasse during the homogeneous maleation in ionic liquid 1-allyl-3-methylimidazolium chloride (AmimCl) were comparatively investigated with the three main components (cellulose, hemicelluloses, and lignin) from bagasse. The PS of the maleated bagasse was 12.52%, and the PS of the maleated cellulose, hemicelluloses, and lignin were 13.50%, 10.89%, and 14.03%, respectively. Fourier translation infrared (FT-IR) and NMR analyses confirmed that the three main components were all involved in the homogeneous maleation. ¹H-13C HSQC analysis indicated that the predominant monoesterification of cellulose, diesterification of hemicelluloses and lignin, and the degradation of the three main components simultaneously occurred. Besides, the quantitative analysis from ¹H-13C HSQC revealed the relative PS of reactive sites in each component. 31P NMR results showed that the reactivity of lignin aliphatic hydroxyls was higher than that of phenolic ones, and the reactivity of phenolic hydroxyls followed the order of p-hydroxyphenyl hydroxyls > guaiacyl hydroxyls > syringyl hydroxyls.

| S-EPMC6415262 | biostudies-literature

The Relationship between Crystal Structure and Mechanical Performance for Fabrication of Regenerated Cellulose Film through Coagulation Conditions.

Project description:Cellulose films regenerated from aqueous alkali-urea solution possess different properties depending on coagulation conditions. However, the correlation between coagulant species and properties of regenerated cellulose (RC) films has not been clarified yet. In this study, RC films were prepared from cellulose nanofiber (CNF) and microcrystalline cellulose (MCC) under several coagulation conditions. Cellulose dissolved in aqueous LiOH-urea solution was regenerated using various solvents at ambient temperature to investigate the effects of their dielectric constant on the properties of RC film. The crystal structure, mechanical properties, and surface morphology of prepared RC films were analyzed using X-ray diffraction (XRD), tensile tester, and atomic probe microscopy (AFM), respectively. It is revealed that the preferential orientation of (110) and (020) crystal planes, which are formed by inter- and intramolecular hydrogen bonding in cellulose crystal regions, changed depending on coagulant species. Furthermore, we found out that tensile strength, elongation at break, and crystal structure properties of RC films strongly correlate to the dielectric constant of solvents used for the coagulation process. This work, therefore, would be able to provide an indicator to control the mechanical performance of RC film depending on its application and to develop detailed researches on controlling the crystal structure of cellulose.

| S-EPMC8708383 | biostudies-literature

Using Carboxymethyl Cellulose as the Additive With Enzyme-Catalyzed Carboxylated Starch to Prepare the Film With Enhanced Mechanical and Hydrophobic Properties.

Project description:Carboxymethyl cellulose, a hydrophobic derivative from cellulose that can be prepared from different biomass, has been widely applied in food, medicine, chemical, and other industries. In this work, carboxymethyl cellulose was used as the additive to improve the hydrophobicity and strength of carboxylated starch film, which is prepared from starch catalyzed by bio-α-amylase. This study investigated the effects of different bio-α-amylase dosages (starch 0.5%, starch 1%) and different activation times (10, 30 min) on starch to prepare the carboxylated starch. The effects of different carboxymethyl cellulose content on the carboxylated starch film were investigated by analysis viscosity, fourier-transform infrared spectroscopy, thermogravimetric analysis, differential scanning calorimetry, x-ray powder diffraction, scanning electron microscope, and contact angle. The results showed that preparing carboxylated starch using activated starch increased the carboxyl content, which could improve the effectiveness of the activated enzyme compared to prolonging the activation time. The carboxyl starch prepared by enzyme catalysis had a lower gelatinization temperature, and enzyme activation destroyed the crystallization area of the starch, thus facilitating the carboxylation reaction. The addition of 15% carboxymethyl cellulose improved the mechanical properties of the prepared film with maximum tensile strength of 44.8 MPa. Carboxymethyl cellulose effectively improved the hydrophobicity of the starch film with the addition amount of 10-30%, while hydrophobic property was stable at 66.8° when the addition amount was exceeded to 35%. In this work, it can be found that carboxymethyl cellulose improve the mechanical and hydrophobic properties of starch film, laying the foundation for the application of carboxylated starch materials.

| S-EPMC7884610 | biostudies-literature

Mechanical and self-recovery properties of supramolecular ionic liquid elastomers based on host-guest interactions and correlation with ionic liquid content.

Project description:Supramolecular materials have received considerable attention due to their higher fracture energy and self-recovery capability compared to conventional chemically cross-linked materials. Herein, we focus on the mechanical properties and self-recovery behaviours of supramolecular polymeric elastomers swollen with ionic liquid. We also gained insight into the correlation between ionic liquid content and mechanical properties. These supramolecular polymers with ionic liquid can be easily prepared from bulk copolymerization of the host-guest complex (peracetylated cyclodextrin and adamantane derivatives) and alkyl acrylates and subsequent immersion in ionic liquid such as 1-ethyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide. The supramolecular polymeric elastomers showed a self-recovery ability, which the conventional chemically cross-linked elastomers with ionic liquid cannot achieve.

| S-EPMC9066642 | biostudies-literature

Fabrication, Corrosion, and Mechanical Properties of Magnetron Sputtered Cu-Zr-Al Metallic Glass Thin Film.

Project description:The appearance of thin film metallic glasses (TFMGs) is gaining increasing interest because of their unique mechanical and anticorrosion properties and potential engineering applications. In this study, Cu-Zr-Al ternary thin film metallic glasses were fabricated by using DC magnetron sputtering equipment with various target powers. The evolution of the structure was systematically investigated by grazing incidence X-ray diffractometer, scanning electron microscopy, and transmission electron microscopy. The deposition rate increases with the increasing of applied target power. The as-deposited thin films show an amorphous structure. The compositional fluctuations on the nanometer scale indicate the presence of two Cu- and Zr-rich amorphous phases. The electrochemical corrosion measurements indicated that Cu-Zr-Al thin film metallic glasses had good corrosion resistance in the sulfuric acid solution. Nanoindentation results showed that the mechanical deformation was found to be homogenous and reproducible with a high value range for the hardness and modulus.

| S-EPMC6947152 | biostudies-literature

Enhanced Silk Fibroin/Sericin Composite Film: Preparation, Mechanical Properties and Mineralization Activity.

Project description:The periosteum plays an important role in bone formation and reconstruction. One of the reasons for the high failure rate of bone transplantation is the absence of the periosteum. Silk fibroin (SF) and silk sericin (SS) have excellent biocompatibility and physicochemical properties, which have amazing application prospects in bone tissue engineering, but lacked mechanical properties. We developed a series of SF/SS composite films with improved mechanical properties using boiling water degumming, which caused little damage to SF molecular chains to retain larger molecules. The Fourier transform infrared spectroscopy and X-ray diffraction results showed that there were more β-sheets in SF/SS films than in Na2CO3 degummed SF film, resulting in significantly improved breaking strength and toughness of the composite films, which were increased by approximately 1.3 and 1.7 times, respectively. The mineralization results showed that the hydroxyapatite (HAp) deposition rate on SF/SS composite films was faster than that on SF film. The SF/SS composite films effectively regulated the nucleation, growth and aggregation of HAp-like minerals, and the presence of SS accelerated the early mineralization of SF-based materials. These composite films may be promising biomaterials in the repair and regeneration of periosteum.

| S-EPMC9227074 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data