Waste Minimization Protocols for the Process of Synthesizing Zeolites from South African Coal Fly Ash.

ABSTRACT: Production of a high value zeolite from fly ash has been shown to be an avenue for the utilization of South African fly ash which presently constitutes a huge disposal problem. The synthesis of zeolites Na-P1 and analcime on a micro-scale has been successful and preliminary investigation shows that scale-up synthesis is promising. However, the post-synthesis supernatant waste generated contains high levels of NaOH that may constitute a secondary disposal problem. A waste minimization protocol was developed to reduce the volume of waste generated with a view to enhancing the feasibility of the scale synthesis. Series of experiments were conducted in 100 mL jacketed batch reactors. Fly ash was reacted with 5 Mol NaOH on a 1:1 mass basis during the aging step, followed by hydrothermal treatment in which ultrapure water was added to the slurry. This study shows that by re-introducing the supernatant waste into the experiments in such a way that it supplies the required reagent (NaOH) for the zeolite synthesis, zeolite Na-P1 and analcime can be synthesized. It also shows that the synthesis process can be altered to allow up to 100% re-use of the supernatant waste to yield high value zeolitic products. This study effectively constructed two protocols for the minimization of waste generated during the synthesis of zeolites from South African coal fly ash. This result could be used to establish a basis for legal and environmental aspects involved in the commission of a full-scale plant synthesizing zeolites NaP1 and analcime.

SUBMITTER: Plessis PWD

PROVIDER: S-EPMC5452509 | biostudies-other | 2013 Apr

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:Geopolymers are inorganic polymers formed from the alkaline activation of amorphous alumino-silicate materials resulting in a three-dimensional polymeric network. As a class of materials, it is seen to have the potential of replacing ordinary Portland cement (OPC), which for more than a hundred years has been the binder of choice for structural and building applications. Geopolymers have emerged as a sustainable option vis-à-vis OPC for three reasons: (1) their technical properties are comparable if not better; (2) they can be produced from industrial wastes; and (3) within reasonable constraints, their production requires less energy and emits significantly less CO₂. In the Philippines, the use of coal ash, as the alumina- and silica- rich geopolymer precursor, is being considered as one of the options for sustainable management of coal ash generation from coal-fired power plants. However, most geopolymer mixes (and the prevalent blended OPC) use only coal fly ash. The coal bottom ash, having very few applications, remains relegated to dumpsites. Rice hull ash, from biomass-fired plants, is another silica-rich geopolymer precursor material from another significantly produced waste in the country with only minimal utilization. In this study, geopolymer samples were formed from the mixture of coal ash, using both coal fly ash (CFA) and coal bottom ash (CBA), and rice hull ash (RHA). The raw materials used for the geopolymerization process were characterized using X-ray fluorescence spectroscopy (XRF) for elemental and X-ray diffraction (XRD) for mineralogical composition. The raw materials' thermal stability and loss on ignition (LOI) were determined using thermogravimetric analysis (TGA) and reactivity via dissolution tests and inductively-coupled plasma mass spectrometry (ICP) analysis. The mechanical, thermal and microstructural properties of the geopolymers formed were analyzed using compression tests, Fourier transform infra-red spectroscopy (FTIR), scanning electron microscopy (SEM) and thermogravimetric analysis (TGA). Using a Scheffé-based mixture design, targeting applications with low thermal conductivity, light weight and moderate strength and allowing for a maximum of five percent by mass of rice hull ash in consideration of the waste utilization of all three components, it has been determined that an 85-10-5 by weight ratio of CFA-CBA-RHA activated with 80-20 by mass ratio of 12 M NaOH and sodium silicate (55% H₂O, modulus = 3) produced geopolymers with a compressive strength of 18.5 MPa, a volumetric weight of 1660 kg/m³ and a thermal conductivity of 0.457 W/m-°C at 28-day curing when pre-cured at 80 °C for 24 h. For this study, the estimates of embodied energy and CO₂ were all below 1.7 MJ/kg and 0.12 kg CO₂/kg, respectively.

Project description:This study evaluated the physicochemical and mineralogical properties, mobile chemical species bioavailability and translocation in Brassica juncea and Spinacea oleracea L. plants of a South African coal-fired power utility. Coal-fly-ash (CFA) disposal is associated with various environmental and health risks, including air, soil, surface, and groundwater pollution due to the leaching of toxic heavy metals; these ends up in food webs affecting human health, while repeated inhalation causes bronchitis, silicosis, hair loss, and lung cancer. The morphology and chemical and mineralogical composition of CFA were determined using Scanning Electron Microscopy (SEM), X-ray fluorescence (XRF), and X-ray diffraction, respectively. In pot-culture experiments, S. oleracea L. and B. juncea plants were grown in three sets of pots containing CFA (Set 1), soil (Set 2), and a mixture of CFA plus soil at a ratio of 1:1 (50% CFA: 50% soil, Set 3), while no plants were grown in Set 4 as a control for the leachate samples. SEM showed that the surface morphology of CFA has a lower degree of sphericity with the irregular agglomerations of many particles. XRF results revealed that CFA contains 43.65%, 22.68%, and 10.89% of SiO₂, Al₂O3, and Fe₂O3, respectively, which indicates that CFA is an aluminosilicate material. X-ray diffraction (XRD) showed that CFA contains mullite as a major phase, followed by quartz mineral phases. Chemical species such as B, Ba, Mo, and Cr were occurring at higher concentrations in the leachates for most weeks in the pot-culture experiments, especially for CFA and soil + CFA growth media. However, there was a common trend for all growth media of chemical-species concentrations declining with time, which might have been caused by plant uptake or wash-off with water during irrigation; even for the growth media as well, where no plants were grown. Chemical species, such as Fe, Mn, B, Ba, and Zn, accumulated highly in most parts of the plant species. However, B. juncea showed higher potential to accumulate chemical species as compared to S. oleracea L. Bioconcentration and translocation factors (BF and TF) showed that B. juncea was the most effective in terms of bioconcentration and translocation of most of the chemical species. This indicates that B. juncea has potential in application for the phytoremediation of CFA dumps, and could contribute to the remediation of CFA dumps and the reduction of potential health and environmental impact associated with CFA.

Dataset Information

Waste Minimization Protocols for the Process of Synthesizing Zeolites from South African Coal Fly Ash.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets