Dislocation Energetics and Pop-Ins in AlN Thin Films by Berkovich Nanoindentation.
Ontology highlight
ABSTRACT:
SUBMITTER: Jian SR
PROVIDER: S-EPMC5452654 | biostudies-other | 2013 Sep
REPOSITORIES: biostudies-other
Similar Datasets
Project description:Power laws are omnipresent and actively studied in many scientific fields, including plasticity of materials. Here, we report the power-law statistics in the second and subsequent pop-in magnitudes during load-controlled nanoindentation testing, whereas the first pop-in is characterized by Gaussian-like statistics with a well-defined average value. The transition from Gaussian-like to power-law is due to the change in the deformation mechanism from dislocation nucleation to dislocation network evolution in the sharp-indenter induced abruptly decaying stress and dislocation density fields. Based on nanoindentation testing on the (100) and (111) surfaces of body-centered cubic (BCC) iron and the (100) surface of face-centered cubic (FCC) copper, the scaling exponents of the power laws were determined to be 5.6, 3.9, and 6.4, respectively. These power-law exponents are much higher than those typically observed in micro-pillar plasticity (1.0-1.8), suggesting that the nanoindentation plasticity belongs to a different universality class than the micro-pillar plasticity.
| S-EPMC7443148 | biostudies-literature
Project description:In this study, the structural and nanomechanical properties of Cu₂O thin films are investigated by X-ray diffraction (XRD), atomic force microscopy (AFM), scanning electron microscopy (SEM) and nanoindentation techniques. The Cu₂O thin films are deposited on the glass substrates with the various growth temperatures of 150, 250 and 350 °C by using radio frequency magnetron sputtering. The XRD results show that Cu₂O thin films are predominant (111)-oriented, indicating a well ordered microstructure. In addition, the hardness and Young's modulus of Cu₂O thin films are measured by using a Berkovich nanoindenter operated with the continuous contact stiffness measurements (CSM) option. Results indicated that the hardness and Young's modulus of Cu₂O thin films decreased as the growth temperature increased from 150 to 350 °C. Furthermore, the relationship between the hardness and films grain size appears to closely follow the Hall-Petch equation.
| S-EPMC5452851 | biostudies-other
Project description:This work presents an experimental study on the dislocation luminescence in GaN by nanoindentation, cathodoluminescence, and Raman. The dislocation luminescence peaking at 3.12 eV exhibits a series of special properties in the cathodoluminescence measurements, and it completely disappears after annealing at 500°C. Raman spectroscopy shows evidence for existence of vacancies in the indented region. A comprehensive investigation encompassing cathodoluminescence, Raman, and annealing experiments allow the assignment of dislocation luminescence to conduction-band-acceptor transition involving Ga vacancies. The nanoscale plasticity of GaN can be better understood by considering the dislocation luminescence mechanism.
| S-EPMC4275118 | biostudies-literature
Project description:The surfaces of polymer and interfaces between polymer and inorganic particles are of particular importance for the properties of polymers and composites. However, the determination of the properties of surfaces and interfaces poses many challenges due to their extremely small dimensions. Herein, polystyrene and polymethyl methacrylate thin film on silicon wafer was used as a model system for the measurement of the properties of the polymer near free surface and at the polymer-solid interface. Two different methods, i.e., nanoindentation using atomic force microscopy (AFM) and the gold nanoparticle embedding technique, were used for these measurements. The results showed the elastic modulus of PS near the free surface determined by nanoindentation was lower than the bulk value. Based on contact mechanics analysis, nanoparticle embedding also revealed the existence of a lower-modulus, non-glassy layer near the free surface at temperatures below the bulk glass transition temperature (Tg). However, near the polymer-solid interface, the AFM nanoindentation method is not applicable due to the geometry confinement effect. On the other hand, the nanoparticle embedding technique can still correctly reflect the interactions between the polymer and the substrate when compared to the ellipsometry results.
| S-EPMC6523445 | biostudies-literature
Project description:Silicon has such versatile characteristics that the mechanical behavior and deformation mechanism under contact load are still unclear and hence are interesting and challenging issues. Based on combined study using molecular dynamics simulations and experiments of nanoindentation on Si(100), the versatile deformation modes, including high pressure phase transformation (HPPT), dislocation, median crack and surface crack, were found, and occurrence of multiple pop-in events in the load-indentation strain curves was reported. HPPTs are regard as the dominant deformation mode and even becomes the single deformation mode at a small indentation strain (0.107 in simulations), suggesting the presence of a defect-free region. Moreover, the one-to-one relationship between the pop-in events and the deformation modes is established. Three distinct mechanisms are identified to be responsible for the occurrence of multiple pop-in events in sequence. In the first mechanism, HPPTs from Si-I to Si-II and Si-I to bct5 induce the first pop-in event. The formation and extrusion of α-Si outside the indentation cavity are responsible for the subsequent pop-in event. And the major cracks on the surface induces the pop-in event at extreme high load. The observed dislocation burst and median crack beneath the transformation region produce no detectable pop-in events.
| S-EPMC5578969 | biostudies-literature
Project description:The growth of >100-?m-thick diamond layers adherent on aluminum nitride with low thermal boundary resistance between diamond and AlN is presented in this work. The thermal barrier resistance was found to be in the range of 16 m2·K/GW, which is a large improvement on the current state-of-the-art. While thick films failed to adhere on untreated AlN films, AlN films treated with hydrogen/nitrogen plasma retained the thick diamond layers. Clear differences in ?-potential measurement confirm surface modification due to hydrogen/nitrogen plasma treatment. An increase in non-diamond carbon in the initial layers of diamond grown on pretreated AlN is seen by Raman spectroscopy. The presence of non-diamond carbon has minimal effect on the thermal barrier resistance. The surfaces studied with X-ray photoelectron spectroscopy revealed a clear distinction between pretreated and untreated samples. The surface aluminum goes from a nitrogen-rich environment to an oxygen-rich environment after pretreatment. A clean interface between diamond and AlN is seen by cross-sectional transmission electron microscopy.
| S-EPMC6823629 | biostudies-literature
Project description:A key issue for skyrmion dynamics and devices are pinning effects present in real systems. While posing a challenge for the realization of conventional skyrmionics devices, exploiting pinning effects can enable non-conventional computing approaches if the details of the pinning in real samples are quantified and understood. We demonstrate that using thermal skyrmion dynamics, we can characterize the pinning of a sample and we ascertain the spatially resolved energy landscape. To understand the mechanism of the pinning, we probe the strong skyrmion size and shape dependence of the pinning. Magnetic microscopy imaging demonstrates that in contrast to findings in previous investigations, for large skyrmions the pinning originates at the skyrmion boundary and not at its core. The boundary pinning is strongly influenced by the very complex pinning energy landscape that goes beyond the conventional effective rigid quasi-particle description. This gives rise to complex skyrmion shape distortions and allows for dynamic switching of pinning sites and flexible tuning of the pinning.
| S-EPMC9170736 | biostudies-literature
Project description:On length scales from nanometres to metres, partial adhesion of thin films with substrates generates a fascinating variety of patterns, such as 'telephone cord' buckles, wrinkles, and labyrinth domains. Although these patterns are part of everyday experience and are important in industry, they are not completely understood. Here, we report simulation studies of a previously-overlooked phenomenon in which pairs of wrinkles form avoiding pairs, focusing on the case of graphene over patterned substrates. By nucleating and growing wrinkles in a controlled way, we characterize how their morphology is determined by stress fields in the sheet and friction with the substrate. Our simulations uncover the generic behaviour of avoiding wrinkle pairs that should be valid at all scales.
| S-EPMC4355740 | biostudies-literature
Project description:We present the fabrication of nanoscale electroactive thin films that can be engineered to undergo remotely controlled dissolution in the presence of a small applied voltage (+1.25 V) to release precise quantities of chemical agents. These films, which are assembled by using a nontoxic, FDA-approved, electroactive material known as Prussian Blue, are stable enough to release a fraction of their contents after the application of a voltage and then to restabilize upon its removal. As a result, it is possible to externally trigger agent release, exert control over the relative quantity of agents released from a film, and release multiple doses from one or more films in a single solution. These electroactive systems may be rapidly and conformally coated onto a wide range of substrates without regard to size, shape, or chemical composition, and as such they may find use in a host of new applications in drug delivery as well as the related fields of tissue engineering, medical diagnostics, and chemical detection.
| S-EPMC2268127 | biostudies-literature
Project description:Intrinsically conducting polymers (ICPs) have been widely utilized in organic electronics, actuators, electrochromic devices, and sensors. Many potential applications demand the formation of thin polymer films, which can be generated by electrochemical polymerization. Electrochemical methods are quite powerful and versatile and can be utilized for investigation of ICPs, both for educational purposes and materials chemistry research. In this study, we show that potentiodynamic and potentiostatic techniques can be utilized for generating and characterizing thin polymer films under the context of educational chemistry research and state-of-the-art polymer research. First, two well-known bifunctional monomers (with only two linking sites)-aniline and bithiophene-and their respective ICPs-polyaniline (PANI) and polybithiophene (PBTh)-were electrochemically generated and characterized. Tests with simple electrochromic devices based on PANI and PBTh were carried out at different doping levels, where changes in the UV-VIS absorption spectra and color were ascribed to changes in the polymer structures. These experiments may attract students' interest in the electrochemical polymerization of ICPs as doping/dedoping processes can be easily understood from observable color changes to the naked eye, as shown for the two polymers. Second, two new carbazole-based multifunctional monomers (with three or more linking sites)-tris(4-(carbazol-9-yl)phenyl)silanol (TPTCzSiOH) and tris(3,5-di(carbazol-9-yl)phenyl)silanol (TPHxCzSiOH)-were synthesized to produce thin films of cross-linked polymer networks by electropolymerization. These thin polymer films were characterized by electrochemical quartz crystal microbalance (EQCM) experiments and nitrogen sorption, and the results showed a microporous nature with high specific surface areas up to 930 m2g-1. PTPHxCzSiOH-modified glassy carbon electrodes showed an enhanced electrochemical response to nitrobenzene as prototypical nitroaromatic compound compared to unmodified glassy carbon electrodes.
| S-EPMC6723103 | biostudies-literature