Synthesis and Characterization of Encapsulated Nanosilica Particles with an Acrylic Copolymer by in Situ Emulsion Polymerization Using Thermoresponsive Nonionic Surfactant.

ABSTRACT: Nanocomposites of encapsulated silica nanoparticles were prepared by in situ emulsion polymerization of acrylate monomers. The synthesized material showed good uniformity and dispersion of the inorganic components in the base polymer, which enhances the properties of the nanocomposite material. A nonionic surfactant with lower critical solution temperature (LCST) was used to encapsulate the silica nanoparticles in the acrylic copolymer matrix. This in situ method combined the surface modification and the encapsulation in a single pot, which greatly simplified the process compared with other conventional methods requiring separate processing steps. The morphology of the encapsulated nanosilica particles was investigated by dynamic light scattering (DLS) and transmission electron microscopy (TEM), which confirmed the uniform distribution of the nanoparticles without any agglomerations. A neat copolymer was also prepared as a control sample. Both the neat copolymer and the prepared nanocomposite were characterized by Fourier transform infrared spectroscopy (FTIR), thermal gravimetric analyses (TGA), dynamic mechanical thermal analysis (DMTA) and the flame resistance test. Due to the uniform dispersion of the non-agglomerated nanoparticles in the matrix of the polymer, TGA and flame resistance test results showed remarkably improved thermal stability. Furthermore, DMTA results demonstrated an enhanced storage modulus of the nanocomposite samples compared with that of the neat copolymer, indicating its superior mechanical properties.

SUBMITTER: Yazdimamaghani M

PROVIDER: S-EPMC5452656 | biostudies-other | 2013 Aug

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Fructose-Based Acrylic Copolymers by Emulsion Polymerization.

Project description:The exploration of a renewable resource for the preparation of waterborne copolymers was conducted. Low molar mass sugar resources were selected for their wide availability. A fructose-based monomer (MF) bearing a methacrylate radically polymerizable group was successfully synthesized. The latter was shown to be able to homopolymerize in emulsion. The high Tg of the resulting polymer (about 115 °C) makes it of particular interest for adhesive and coating applications where hard materials are necessary to ensure valuable properties. As a result, its incorporation in waterborne acrylic containing formulations as an equivalent to petrochemical-based methyl methacrylate was investigated. It was found that the bio-based monomer exhibited similar behavior to that of common methacrylates, as shown by polymerization kinetics and particle size evolution. Furthermore, the homogeneous incorporation of the sugar units into the acrylate chains was confirmed by a unique glass transition temperature in differential scanning calorimeter (DSC). The potential of MF for the production of waterborne copolymers was greatly valued by the successful increase of formulation solids content up to 45 wt %. Interestingly, polymer insolubility in tetrahydrofurane increased with time due to further reactions occurring in storage. Most likely, the partial deprotection of sugar units was the reason for the creation of hydrogen bonding and, thus, physically insoluble entangled chains. This behavior highlights opportunities to make use of hydroxyl groups either for further functionalization or, eventually, for achieving enhanced adhesion on casted substrates.

| S-EPMC6415512 | biostudies-literature

Synthesis and Characterization of All-Acrylic Tetrablock Copolymer Nanoparticles: Waterborne Thermoplastic Elastomers via One-Pot RAFT Aqueous Emulsion Polymerization.

Project description:Reversible addition-fragmentation chain transfer (RAFT) aqueous emulsion polymerization is used to prepare well-defined ABCB tetrablock copolymer nanoparticles via sequential monomer addition at 30 °C. The A block comprises water-soluble poly(2-(N-acryloyloxy)ethyl pyrrolidone) (PNAEP), while the B and C blocks comprise poly(t-butyl acrylate) (PtBA) and poly(n-butyl acrylate) (PnBA), respectively. High conversions are achieved at each stage, and the final sterically stabilized spherical nanoparticles can be obtained at 20% w/w solids at pH 3 and at up to 40% w/w solids at pH 7. A relatively long PnBA block is targeted to ensure that the final tetrablock copolymer nanoparticles form highly transparent films on drying such aqueous dispersions at ambient temperature. The kinetics of polymerization and particle growth are studied using 1H nuclear magnetic resonance spectroscopy, dynamic light scattering, and transmission electron microscopy, while gel permeation chromatography analysis confirmed a high blocking efficiency for each stage of the polymerization. Differential scanning calorimetry and small-angle X-ray scattering studies confirm microphase separation between the hard PtBA and soft PnBA blocks, and preliminary mechanical property measurements indicate that such tetrablock copolymer films exhibit promising thermoplastic elastomeric behavior. Finally, it is emphasized that targeting an overall degree of polymerization of more than 1000 for such tetrablock copolymers mitigates the cost, color, and malodor conferred by the RAFT agent.

| S-EPMC10902817 | biostudies-literature

Surfactant-Free RAFT Emulsion Polymerization of Styrene Using Thermoresponsive macroRAFT Agents: Towards Smart Well-Defined Block Copolymers with High Molecular Weights.

Project description:The combination of reversible addition⁻fragmentation chain transfer (RAFT) and emulsion polymerization has recently attracted much attention as a synthetic tool for high-molecular-weight block copolymers and their micellar nano-objects. Up to recently, though, the use of thermoresponsive polymers as both macroRAFT agents and latex stabilizers was impossible in aqueous media due to their hydrophobicity at the usually high polymerization temperatures. In this work, we present a straightforward surfactant-free RAFT emulsion polymerization to obtain thermoresponsive styrenic block copolymers with molecular weights of around 100 kDa and their well-defined latexes. The stability of the aqueous latexes is achieved by adding 20 vol % of the cosolvent 1,4-dioxane (DOX), increasing the phase transition temperature (PTT) of the used thermoresponsive poly(N-acryloylpyrrolidine) (PAPy) macroRAFT agents above the polymerization temperature. Furthermore, this cosolvent approach is combined with the use of poly(N,N-dimethylacrylamide)-block-poly(N-acryloylpiperidine-co-N-acryloylpyrrolidine) (PDMA-b-P(APi-co-APy)) as the macroRAFT agent owning a short stabilizing PDMA end block and a widely adjustable PTT of the P(APi-co-APy) block in between 4 and 47 °C. The temperature-induced collapse of the latter under emulsion polymerization conditions leads to the formation of RAFT nanoreactors, which allows for a very fast chain growth of the polystyrene (PS) block. In dynamic light scattering (DLS), as well as cryo-transmission electron microscopy (cryoTEM), moreover, all created latexes indeed reveal a high (temperature) stability and a reversible collapse of the thermoresponsive coronal block upon heating. Hence, this paper pioneers a versatile way towards amphiphilic thermoresponsive high-molecular-weight block copolymers and their nano-objects with tailored corona switchability.

| S-EPMC6418535 | biostudies-literature

Quest for Thermoresponsive Block Copolymer Nanoparticles with Liquid-Crystalline Surfactant Cores.

Project description:This work reports on the preparation and characterization of anisotropic composition nanoparticles based on the electrostatic binding of dodecyltrimethylammonium surfactant to poly(acrylic acid) blocks of diblock copolymers with poly(ethylene oxide) (PEO) and poly(N-isopropyl acrylamide) (PNIPAm). These nanoparticles form kinetically stable dispersions and display liquid-crystalline cores with a micellar cubic structure, as determined by small-angle X-ray scattering. Mixtures with different proportions of the two block copolymers and stoichiometric amounts of C12TA+ were prepared and their behavior was compared with that of the parent nanoparticles. Upon heating, dilute dispersions (0.01 and 0.1 wt %) analyzed by dynamic light scattering display a slight decrease in the hydrodynamic radius, consistent with the dehydration of PNIPAm and mixed PNIPAm-PEO blocks at the shell. At higher concentrations, 2 wt %, the nanoparticles with pure PNIPAm shell undergo macroscopic phase separation above 32 °C. Nanoparticles with a pure PEO shell do not display temperature sensitivity. For the mixtures, no visual change is observed, but the dynamic light scattering results evidence the formation of clusters, whose size and reversibility depend on the PEO/PNIPAm proportion. This indicates the formation of mixed nanoparticles containing both PEO and PNIPAm blocks. Nuclear Overhauser enhancement spectroscopy NMR analyses of the mixtures do not show the correlation peak expected for PEO and PNIPAm blocks in close proximity, suggesting their segregation at the nanoparticle shell. On the basis of these results, we discuss the possibilities of the neutral blocks distribution on the shell of mixed nanoparticles. Overall, we have confirmed that these nanoparticles may display a temperature-controlled reversible aggregation while preserving their internal liquid-crystalline structures.

| S-EPMC6644550 | biostudies-literature

Synthesis, Polymerization, and Assembly of Nanosilica Particles below the Isoelectric Point.

Project description:The particle growth of silica below the isoelectric point plays a key role in oil well cements, production of silica gels and production of nanosilica by dissolving silicates. In this article, we study the particle growth of silica below the isoelectric point using olivine, a silicate mineral, and sodium silicate solutions as silica sources in acid, where the particle size, soluble silica concentration, specific surface area and gelling time were measured. The size of the primary particles detected by laser light scattering is 3 nm in the experiments with sodium silicate solutions. These particles grow then by aggregation forming linear chains which in time will start to branch. The particle growth follows a quadratic polynomial function and particles as large as 100 and 500 nm are detected in the final stages of experiments using sodium silica solutions and olivine, respectively. Based on these findings, a comprehensive model describing the silica particle development below the isoelectric point is proposed. This model gives fundamental information about the growth mechanism and the properties of silica (e.g., particle size of the primary particles, size of the aggregates) at the different growth stages.

| S-EPMC5745517 | biostudies-literature

Mechanistic formation of drug-encapsulated Janus particles through emulsion solvent evaporation.

Project description:Janus particles are emerging as structurally unique drug carriers with the potential to deliver multiple drugs and agents. Although synthesis methods have been extensively explored to fabricate Janus particles, it remains a challenge to generate drug-loaded Janus particles through an economical, high throughput technique. Here, we report the formation of the first drug-loaded, micro-scale Janus particles prepared using a single-step emulsion solvent evaporation approach. Our results revealed that both the net charge of drug molecules (i.e. glibenclamide, tolbutamine, rapamycin and lidocaine) and polymer weight ratio (i.e. poly(lactic-co-glycolic) and polycaprolactone) were critical in determining the formation of Janus particles. The formation of drug-loaded Janus particles was proven to be thermodynamically-driven in accordance to the classical equilibrium spreading coefficient theory, which is strongly governed by interfacial tensions. Specifically, comparable interfacial tensions between the two interacting polymers with the water phase were identified to be key criteria to achieve the Janus particles hemispheric structure. Such interfacial tensions were amenable, and were found to be highly dependent on the interfacial charge density attributed to both drug and polymer ratio. Hereby, this study provides a mechanistic insight into the fabrication of drug-loaded Janus particles and paves an important path towards large-scale production of Janus particles using a simplified, single-step emulsion solvent evaporation strategy.

| S-EPMC9080239 | biostudies-literature

Hybrid nanostructured particles via surfactant-free double miniemulsion polymerization.

Project description:Double emulsions are complex fluid systems, in which droplets of a dispersed liquid phase contain even smaller dispersed liquid droplets. Particularly, water-in-oil-in-water double emulsions provide significant advantages over simple oil-in-water emulsions for microencapsulation, such as carrier of both aqueous and oily payloads and sustained release profile. However, double emulsions are thermodynamically unstable systems consisting typically of relatively large droplets. Here we show that nanoscale water-in-oil-in-water double emulsions can be prepared by adding a silica precursor polymer, hyperbranched polyethoxysiloxane, to the oil phase without any additional surfactants. The resulting double miniemulsions are transformed to robust water@SiO2@polymer@SiO2 nanocapsules via conversion of the precursor to silica and polymerization of the oil phase. Other intriguing nanostructures like nanorattles and Janus-like nanomushrooms can also be obtained by changing preparation conditions. This simple surfactant-free double miniemulsion polymerization technique opens a promising avenue for mass production of various complex hybrid nanostructures that are amenable to numerous applications.

| S-EPMC5953918 | biostudies-literature

RAFT-mediated Pickering emulsion polymerization with cellulose nanocrystals grafted with random copolymer as stabilizer.

Project description:The synthesis of a RAFT-mediated Pickering emulsion was firstly achieved by using cellulose nanocrystals (CNCs) grafted with a random copolymer as the stabilizer. Firstly, poly(acrylonitrile-r-butyl acrylate) (poly(AN-r-nBA)) was synthesized by Cu(0)-mediated CRP, which was further modified via a click chemistry strategy to obtain poly(ethylene tetrazole-r-butyl acrylate) (poly(VT-r-nBA)). Then, poly(VT-r-nBA) was grafted onto the CNCs through a Mitsunobu reaction to obtain poly(VT-r-nBA)-g-CNCs. Stabilized by poly(VT-r-nBA)-g-CNCs, an O/W RAFT-mediated Pickering emulsion was formed for the preparation of well-controlled poly(methyl methacrylate) (PMMA) particles with water-soluble potassium persulfate (KPS) as an initiator and oil-soluble 4-cyanopentanoic acid dithiobenzoate (CPADB) as a chain transfer agent. Rheological analysis suggested that the prepared Pickering emulsion possessed good stability under the influences of changes in strain, time, frequency and temperature. Furthermore, the recycling and further utilization of the poly(VT-r-nBA)-g-CNCs could be simply realized through centrifugal separation.

| S-EPMC9084400 | biostudies-literature

Polymeric Surfactant (PIBSA-X) Facilitates the Formation of a Water-in-Oil Emulsion Reactor for the Preparation of Ultrasmall Nanosilica.

Project description:Despite the widespread application of ultrasmall nanosilica, solving its aggregation problem during the preparation process remains a challenge. In this paper, ultrasmall nanosilica with a controllable size and aggregates were prepared through the water-in-oil (W/O) emulsion method by using polyisobutylene succinic anhydride-type polymeric surfactants (PIBSA-X) as an isolating agent. PIBSA-X polymeric surfactants with different hydrophilic groups were prepared using industrial-grade PIBSA, which can form stable W/O-type emulsions well. Subsequently, the W/O-type emulsion droplets were used as reactors and tetraethyl orthosilicate was hydrolyzed under ammonia alkaline conditions to synthesize ultrasmall nanosilica (10 nm). Furthermore, the morphological evolution of nanosilica aggregates can be tuned by varying the oil/water ratio, which controls the emulsion droplets. A possible mechanism is proposed to explain why the emulsion method approach affords nanosilica aggregates with various morphologies and pellet size in water-in-oil (W/O-type) emulsion droplets. This study provides a precise and simple synthetic method for the development of ultrasmall nanosilica, which has good potential to be industrialized.

| S-EPMC10688208 | biostudies-literature

Protein aggregation with poly(vinyl) alcohol surfactant reduces double emulsion-encapsulated mammalian cell-free expression.

Project description:Development of artificial cell models requires encapsulation of biomolecules within membrane-bound compartments. There have been limited studies of using mammalian cell-free expression (CFE) system as the 'cytosol' of artificial cells. We exploit glass capillary droplet microfluidics for the encapsulation of mammalian CFE within double emulsion templated vesicles. The complexity of the physicochemical properties of HeLa cell-free lysate poses a challenge compared with encapsulating simple buffer solutions. In particular, we discovered the formation of aggregates in double emulsion templated vesicles encapsulating mammalian HeLa CFE, but not with bacterial CFE. The aggregates did not arise from insolubility of the proteins made from CFE nor due to the interaction of mammalian CFE with the organic solvents in the middle phase of the double emulsions. We found that aggregation is dependent on the concentration of poly(vinyl) alcohol (PVA) surfactant, a critical double emulsion-stabilizing surfactant, and the lysate concentration in mammalian CFE. Despite vesicle instability and reduced protein expression, we demonstrate protein expression by encapsulating mammalian CFE system. Using mass spectrometry and Western blot, we identified and verified that actin is one of the proteins inside the mammalian CFE that aggregated with PVA surfactant. Our work establishes a baseline description of mammalian CFE system encapsulated in double emulsion templated vesicles as a platform for building artificial cells.

| S-EPMC5373588 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data