Damp Heat Treatment of Cu(In,Ga)Se2 Solar Cells with Different Sodium Content.

ABSTRACT: Long term stability is crucial to maturing any photovoltaic technology. We have studied the influence of sodium, which plays a key role in optimizing the performance of Cu(In,Ga)Se2 (CIGSe) solar cells, on the long-term stability of flexible CIGSe solar cells on polyimide foil. The standardized procedure of damp heat exposure (85% relative humidity at 85 °C) was used to simulate aging of the unencapsulated cells in multiple time steps while they were characterized by current-voltage analysis, capacitance-voltage profiling, as well as electroluminescence imaging. By comparing the aging process to cells that were exposed to heat only, it could be confirmed that moisture plays the key role in the degradation process. We found that cells with higher sodium content suffer from a more pronounced degradation. Furthermore, the experimental results indicate the superposition of an enhancing and a deteriorating mechanism during the aging process. We propose an explanation based on the corrosion of the planar contacts of the solar cell.

SUBMITTER: Daume F

PROVIDER: S-EPMC5452750 | biostudies-other | 2013 Nov

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Electron-Selective TiO2 Contact for Cu(In,Ga)Se2 Solar Cells.

Project description:The non-toxic and wide bandgap material TiO2 is explored as an n-type buffer layer on p-type Cu(In,Ga)Se2 (CIGS) absorber layer for thin film solar cells. The amorphous TiO2 thin film deposited by atomic layer deposition process at low temperatures shows conformal coverage on the CIGS absorber layer. Solar cells from non-vacuum deposited CIGS absorbers with TiO2 buffer layer result in a high short-circuit current density of 38.9?mA/cm(2) as compared to 36.9?mA/cm(2) measured in the reference cell with CdS buffer layer, without compromising open-circuit voltage. The significant photocurrent gain, mainly in the UV part of the spectrum, can be attributed to the low parasitic absorption loss in the ultrathin TiO2 layer (~10?nm) with a larger bandgap of 3.4?eV compared to 2.4?eV of the traditionally used CdS. Overall the solar cell conversion efficiency was improved from 9.5% to 9.9% by substituting the CdS by TiO2 on an active cell area of 10.5?mm(2). Optimized TiO2/CIGS solar cells show excellent long-term stability. The results imply that TiO2 is a promising buffer layer material for CIGS solar cells, avoiding the toxic CdS buffer layer with added performance advantage.

| S-EPMC4630620 | biostudies-literature

Effect of Sodium Treatment on the Performance of Electrostatic Spray Assisted Vapour Deposited Copper-poor Cu(In,Ga)(S,Se) 2 Solar Cells.

Project description:In our work, eco-friendly, non-vacuum and low cost Electrostatic Spray Assisted Vapour Deposition (ESAVD) method has been used to produce Cu(In,Ga)(S,Se)2 (CIGS) solar cells. Copper (Cu) deficient (Cu/In?+?Ga?=?0.76) CIGS films were designed to avoid the rather dangerous KCN treatment step for the removal of conductive minor phases of Cu2S/Cu2Se. A simple sodium (Na) treatment method was used to modify the morphology and electronic properties of the absorber and it clearly improved the solar cell performance. The SEM and XRD results testified a slightly increase of the grain size and (112) crystal orientation in the Na-incorporated CIGS thin films. From the Mott-schottky results, it can be seen that the functions of the Na treatment in our non-vacuum deposited CIGS are mainly used for defect passivation and reduction of charge recombination. Photovoltaic characteristics and j-V curve demonstrated that the dipping of CIGS films in 0.2?M NaCl solution for 20?minutes followed by selenization at 550?°C under selenium vapor resulted in the optimum photovoltaic performance, with j sc, V oc, FF and ? of the optimized solar cell of 29.30?mA?cm-2, 0.564?V, 65.59% and 10.83%, respectively.

| S-EPMC5533725 | biostudies-literature

ALD-Zn xTi yO as Window Layer in Cu(In,Ga)Se2 Solar Cells.

Project description:We report on the application of Zn xTi yO deposited by atomic layer deposition (ALD) as buffer layer in thin film Cu(In,Ga)Se2 (CIGS) solar cells to improve the photovoltaic device performance. State-of-the-art CIGS devices employ a CdS/ZnO layer stack sandwiched between the absorber layer and the front contact. Replacing the sputter deposited ZnO with ALD-Zn xTi yO allowed a reduction of the CdS layer thickness without adversely affecting open-circuit voltage ( VOC). This leads to an increased photocurrent density with a device efficiency of up to 20.8% by minimizing the parasitic absorption losses commonly observed for CdS. ALD was chosen as method to deposit homogeneous layers of Zn xTi yO with varying Ti content with a [Ti]/([Ti] + [Zn]) atomic fraction up to ?0.35 at a relatively low temperature of 373 K. The Ti content influenced the absorption behavior of the Zn xTi yO layer by increasing the optical bandgap >3.5 eV in the investigated range. Temperature-dependent current-voltage ( I- V) measurements of solar cells were performed to investigate the photocurrent blocking behavior observed for high Ti content. Possible conduction band discontinuities introduced by Zn xTi yO are discussed based on X-ray photoelectron spectroscopy (XPS) measurements.

| S-EPMC6302902 | biostudies-literature

Understanding the Impact of Cu-In-Ga-S Nanoparticles Compactness on Holes Transfer of Perovskite Solar Cells.

Project description:Although a compact holes-transport-layer (HTL) film has always been deemed mandatory for perovskite solar cells (PSCs), the impact their compactness on the device performance has rarely been studied in detail. In this work, based on a device structure of FTO/CIGS/perovskite/PCBM/ZrAcac/Ag, that effect was systematically investigated with respect to device performance along with photo-physics characterization tools. Depending on spin-coating speed, the grain size and coverage ratio of those CIGS films on FTO substrates can be tuned, and this can result in different hole transfer efficiencies at the anode interface. At a speed of 4000 r.p.m., the band level offset between the perovskite and CIGS modified FTO was reduced to a minimum of 0.02 eV, leading to the best device performance, with conversion efficiency of 15.16% and open-circuit voltage of 1.04 V, along with the suppression of hysteresis. We believe that the balance of grain size and coverage ratio of CIGS interlayers can be tuned to an optimal point in the competition between carrier transport and recombination at the interface based on the proposed mechanism. This paper definitely deepens our understanding of the hole transfer mechanism at the interface of PSC devices, and facilitates future design of high-performance devices.

| S-EPMC6410191 | biostudies-literature

Refractive indices of layers and optical simulations of Cu(In,Ga)Se2 solar cells.

Project description:Cu(In,Ga)Se2 based solar cells have reached efficiencies close to 23%. Further knowledge-driven improvements require accurate determination of the material properties. Here, we present refractive indices for all layers in Cu(In,Ga)Se2 solar cells with high efficiency. The optical bandgap of Cu(In,Ga)Se2 does not depend on the Cu content in the explored composition range, while the absorption coefficient value is primarily determined by the Cu content. An expression for the absorption spectrum is proposed, with Ga and Cu compositions as parameters. This set of parameters allows accurate device simulations to understand remaining absorption and carrier collection losses and develop strategies to improve performances.

| S-EPMC5954485 | biostudies-literature

Microscopic origins of performance losses in highly efficient Cu(In,Ga)Se2 thin-film solar cells.

Project description:Thin-film solar cells based on polycrystalline absorbers have reached very high conversion efficiencies of up to 23-25%. In order to elucidate the limiting factors that need to be overcome for even higher efficiency levels, it is essential to investigate microscopic origins of loss mechanisms in these devices. In the present work, a high efficiency (21% without anti-reflection coating) copper indium gallium diselenide (CIGSe) solar cell is characterized by means of a correlative microscopy approach and corroborated by means of photoluminescence spectroscopy. The values obtained by the experimental characterization are used as input parameters for two-dimensional device simulations, for which a real microstructure was used. It can be shown that electrostatic potential and lifetime fluctuations exhibit no substantial impact on the device performance. In contrast, nonradiative recombination at random grain boundaries can be identified as a significant loss mechanism for CIGSe solar cells, even for devices at a very high performance level.

| S-EPMC7442832 | biostudies-literature

Surface/Interface Effects by Alkali Postdeposition Treatments of (Ag,Cu)(In,Ga)Se2 Thin Film Solar Cells.

Project description:Ag alloying and the introduction of alkali elements through a postdeposition treatment are two approaches to improve the performance of Cu(In,Ga)Se2 (CIGS) thin film solar cells. In particular, a postdeposition treatment of an alkali metal fluoride of the absorber has shown a beneficial effect on the solar cells performance due to an increase in the open circuit voltage (V OC) for both (Ag,Cu)(In,Ga)Se2 (ACIGS) and CIGS based solar cells. Several reasons have been suggested for the improved V OC in CIGS solar cells including absorber surface and interface effects. Less works investigated how the applied postdeposition treatment influences the ACIGS absorber surface and interface properties and the subsequent buffer layer growth. In this work we employed hard X-ray photoelectron spectroscopy to study the chemical and electronic properties at the real functional interface between a CdS buffer and ACIGS absorbers that have been exposed to different alkali metal fluoride treatments during preparation. All samples show an enhanced Ag content at the CdS/ACIGS interface as compared to ACIGS bulk-like composition, and it is also shown that this enhanced Ag content anticorrelates with Ga content. The results indicate that the absorber composition at the near-surface region changes depending on the applied alkali postdeposition treatment. The Cu and Ga decrease and the Ag increase are stronger for the RbF treatment as compared to the CsF treatment, which correlates with the observed device characteristics. This suggests that a selective alkali postdeposition treatment could change the ACIGS absorber surface composition, which can influence the solar cell behavior.

| S-EPMC8790805 | biostudies-literature

Alkali Dispersion in (Ag,Cu)(In,Ga)Se2 Thin Film Solar Cells-Insight from Theory and Experiment.

Project description:Silver alloying of Cu(In,Ga)Se2 absorbers for thin film photovoltaics offers improvements in open-circuit voltage, especially when combined with optimal alkali-treatments and certain Ga concentrations. The relationship between alkali distribution in the absorber and Ag alloying is investigated here, combining experimental and theoretical studies. Atom probe tomography analysis is implemented to quantify the local composition in grain interiors and at grain boundaries. The Na concentration in the bulk increases up to ∼60 ppm for [Ag]/([Ag] + [Cu]) = 0.2 compared to ∼20 ppm for films without Ag and up to ∼200 ppm for [Ag]/([Ag] + [Cu]) = 1.0. First-principles calculations were employed to evaluate the formation energies of alkali-on-group-I defects (where group-I refers to Ag and Cu) in (Ag,Cu)(In,Ga)Se2 as a function of the Ag and Ga contents. The computational results demonstrate strong agreement with the nanoscale analysis results, revealing a clear trend of increased alkali bulk solubility with the Ag concentration. The present study, therefore, provides a more nuanced understanding of the role of Ag in the enhanced performance of the respective photovoltaic devices.

| S-EPMC7898268 | biostudies-literature

In-Situ Probing Plasmonic Energy Transfer in Cu(In, Ga)Se2 Solar Cells by Ultrabroadband Femtosecond Pump-Probe Spectroscopy.

Project description:In this work, we demonstrated a viable experimental scheme for in-situ probing the effects of Au nanoparticles (NPs) incorporation on plasmonic energy transfer in Cu(In, Ga)Se2 (CIGS) solar cells by elaborately analyzing the lifetimes and zero moment for hot carrier relaxation with ultrabroadband femtosecond pump-probe spectroscopy. The signals of enhanced photobleach (PB) and waned photoinduced absorption (PIA) attributable to surface plasmon resonance (SPR) of Au NPs were in-situ probed in transient differential absorption spectra. The results suggested that substantial carriers can be excited from ground state to lower excitation energy levels, which can reach thermalization much faster with the existence of SPR. Thus, direct electron transfer (DET) could be implemented to enhance the photocurrent of CIGS solar cells. Furthermore, based on the extracted hot carrier lifetimes, it was confirmed that the improved electrical transport might have been resulted primarily from the reduction in the surface recombination of photoinduced carriers through enhanced local electromagnetic field (LEMF). Finally, theoretical calculation for resonant energy transfer (RET)-induced enhancement in the probability of exciting electron-hole pairs was conducted and the results agreed well with the enhanced PB peak of transient differential absorption in plasmonic CIGS film. These results indicate that plasmonic energy transfer is a viable approach to boost high-efficiency CIGS solar cells.

| S-EPMC4683378 | biostudies-other

Four-Fold Multi-Modal X-ray Microscopy Measurements of a Cu(In,Ga)Se2 Solar Cell.

Project description:Inhomogeneities and defects often limit the overall performance of thin-film solar cells. Therefore, sophisticated microscopy approaches are sought to characterize performance and defects at the nanoscale. Here, we demonstrate, for the first time, the simultaneous assessment of composition, structure, and performance in four-fold multi-modality. Using scanning X-ray microscopy of a Cu(In,Ga)Se2 (CIGS) solar cell, we measured the elemental distribution of the key absorber elements, the electrical and optical response, and the phase shift of the coherent X-rays with nanoscale resolution. We found structural features in the absorber layer-interpreted as voids-that correlate with poor electrical performance and point towards defects that limit the overall solar cell efficiency.

| S-EPMC7796438 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data