Preparation and Characterization of Guar-Montmorillonite Nanocomposites.

ABSTRACT: Polymer-clay nanocomposites are highly sought-after materials, mainly due to their applicability in a variety of avenues. From the standpoint of the preparation of these nanocomposites, however, organic compatibility with clay and adherence to "green chemistry" concepts and principles can be limiting factors. As such, the objective was to prepare a biopolymer-modified clay nanocomposite using a simple and environmentally friendly method of preparation, whereby pre-treatment of the clay for organic compatibility was bypassed. Novel montmorillonite nanocomposites were prepared using neutral guar gum and cationic guar gum. X-ray diffraction (XRD) and transmission electron microscopy (TEM) confirmed the formation of intercalated structures. A monolayer configuration of cationic guar within the interlayer space was indicated by XRD results, while treatment with neutral guar gum resulted in the observance of both monolayer and bilayer configurations. Additionally, TEM results indicated partial exfoliation. Results attributed from 13C cross polarization/magic angle spinning nuclear magnetic resonance spectroscopy (CP/MAS NMR) of the nanocomposites indicated peaks corresponding to the guar constituent, confirming the adsorption of the biopolymer. Inductively coupled plasma emission spectrometry (ICP-ES) results indicated the exchange of cations present in neutral guar gum with the sodium cations of montmorillonite, in the case of the neutral guar nanocomposites.

SUBMITTER: Mansa R

PROVIDER: S-EPMC5452780 | biostudies-other | 2013 Nov

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Preparation and properties of amphiphilic hydrophobically associative polymer/ montmorillonite nanocomposites.

Project description:In this research, a novel amphiphilic hydrophobically associative polymer nanocomposite (ADOS/OMMT) was prepared using acrylamide (AM), sodium 4-vinylbenzenesulfonate (SSS), N, N'-dimethyl octadeyl allyl ammonium bromide (DOAAB) and organo-modified montmorillonite (OMMT) through in situ polymerization. Both X-ray diffraction patterns and transmission electron microscopy images verified the dispersion morphology of OMMT in the copolymer matrix. Then, the effect of the introduction of OMMT layers on the copolymer properties was studied by comparing with pure copolymer AM/SSS/DOAAB (ADOS). The thermal degradation results demonstrated that the thermal stability of the ADOS/OMMT were better than pure copolymer ADOS. During the solution properties tests, ADOS/OMMT nanocomposite was superior to ADOS in viscosifying ability, temperature resistance, salt tolerance, shear resistance and viscoelasticity, which was because OMMT contributed to enhance the hydrophobic association structure formed between polymer molecules. Additionally, the ADOS/OMMT nanocomposite exhibited more excellent interfacial activity and crude oil emulsifiability in comparison to pure copolymer ADOS. These performances indicated ADOS/OMMT nanocomposite had good application prospects in tertiary recovery.

| S-EPMC7277241 | biostudies-literature

Elaboration and Characterization of Active Films Containing Iron-Montmorillonite Nanocomposites for O2 Scavenging.

Project description:Iron particles of sizes between 6 and 20 nm forming aggregates of 57 ± 17 nm were synthesized by chemical reduction of iron precursors on the surface of montmorillonite (MMT). This active MMT-Fe powder was then uniformly distributed in a linear low-density polyethylene (LLDPE) matrix by extrusion at atmospheric conditions, as confirmed by wide-angle X-ray scattering (WAXS), which also detected a partial exfoliation of the nanoclays. Thermogravimetric analysis (TGA) did not detect any significant modification of the degradation temperature between nanocomposites and active nanocomposites. 57Fe Mössbauer spectroscopy evidenced the formation of a majority of iron boride in MMT-Fe as well as in the active film containing it. The LLDPE.Fu15.MMT-Fe3.75 and LLDPE.Fu15.MMT-Fe6.25 films had oxygen-scavenging capacities of 0.031 ± 0.002 and 0.055 ± 0.009 g(O2)/g(Fe), respectively, while the neat powder had an adsorption capacity of 0.122 g(O2)/g(Fe). This result confirms that the fresh film samples were partially oxidized shortly after thermomechanical processing (60% of oxidized species according to Mössbauer spectroscopy). No significant difference in oxygen permeability was observed when MMT-Fe was added. This was related to the relatively small film surface used for measuring the permeability. The reaction-diffusion model proposed here was able to reproduce the observed data of O2 adsorption in an active nanocomposite, which validated the O2 adsorption model previously developed for dried MMT-Fe powder.

| S-EPMC6780512 | biostudies-literature

Non-Isothermal Crystallization Kinetics of Montmorillonite/Polyamide 610 Nanocomposites.

Project description:Non-isothermal crystallization kinetics of montmorillonite (MMT)/polyamide 610 (PA610) composites were readily prepared by in situ melt polymerization followed by a full investigation in terms of their microstructure, performance, and crystallization kinetics. The kinetic models of Jeziorny, Ozawa, and Mo were used in turn to fit the experimental data, in all of which Mo's analytical method was found to be the best model for the kinetic data. Differential scanning calorimetry (DSC) and transmission electron microscopy (TEM) studies were used to investigate the isothermal crystallization behavior and MMT dispersion levels in the MMT/PA610 composites. The experiment results revealed that low MMT content can promote the PA610 crystallization, whilst high MMT content result in MMT agglomeration, and reduce the PA610 crystallization rate.

| S-EPMC10302243 | biostudies-literature

Preparation and characterization of polyhydroxybutyrate/polycaprolactone nanocomposites.

Project description:Polyhydroxybutyrate (PHB)/polycaprolactone (PCL)/stearate Mg-Al layered double hydroxide (LDH) nanocomposites were prepared via solution casting intercalation method. Coprecipitation method was used to prepare the anionic clay Mg-Al LDH from nitrate salt solution. Modification of nitrate anions by stearate anions between the LDH layers via ion exchange reaction. FTIR spectra showed the presence of carboxylic acid (COOH) group which indicates that stearate anions were successfully intercalated into the Mg-Al LDH. The formation of nanocomposites only involves physical interaction as there are no new functional groups or new bonding formed. X-ray diffraction (XRD) and transmission electron microscopy (TEM) indicated that the mixtures of nanocomposites are intercalated and exfoliated types. XRD results showed increasing of basal spacing from 8.66 to 32.97 Å in modified stearate Mg-Al LDH, and TEM results revealed that the stearate Mg-Al LDH layers are homogeneously distributed in the PHB/PCL polymer blends matrix. Enhancement in 300% elongation at break and 66% tensile strength in the presence of 1.0 wt % of the stearate Mg-Al LDH as compare with PHB/PCL blends. Scanning electron microscopy (SEM) proved that clay improves compatibility between polymer matrix and the best ratio 80PHB/20PCL/1stearate Mg-Al LDH surface is well dispersed and stretched before it breaks.

| S-EPMC3926308 | biostudies-other

Preparation and Characterization of Graphene Oxide/Polyaniline/Carbonyl Iron Nanocomposites.

Project description:Nano coatings for anti-corrosion and electromagnetic wave absorbing can simultaneously implement the functions of assimilating electromagnetic waves and reducing the corrosion of materials caused by corrosive environments, such as seawater. In this work, a composite material for both electromagnetic wave absorption and anti-corrosion was prepared by an in-situ chemical oxidation and surface coating method using carbonyl iron powder (CIP), graphene oxide (GO) and aniline (AN). The synthesized composite material was characterized by scanning electron microscopy (SEM), infrared spectroscopy (FT-IR) and XRD. The carbonyl iron powder-graphene oxide-polyaniline (CIP-GO-PANI) composite material was used as the functional filler, and the epoxy resin was the matrix body for preparing the anticorrosive wave-absorbing coating. The results show that CIP had strong wave-absorbing properties, and the anti-corrosion property was greatly enhanced after being coated by GO-PANI.

| S-EPMC8781392 | biostudies-literature

Perovskite LaFeO3/montmorillonite nanocomposites: synthesis, interface characteristics and enhanced photocatalytic activity.

Project description:Perovskite LaFeO3/montmorillonite nanocomposites (LaFeO3/MMT) have been successfully prepared via assembling LaFeO3 nanoparticles on the surface of montmorillonite with citric acid assisted sol-gel method. The results indicated that the uniform LaFeO3 nanoparticles were densely deposited onto the surface of montmorillonite, mainly ranging in diameter from 10 nm to 15 nm. The photocatalytic activity of LaFeO3/MMT was evaluated by the degradation of Rhodamine B (RhB) under visible light irradiation, indicating that LaFeO3/MMT exhibited remarkable adsorption efficiency and excellent photocatalytic activity with the overall removal rate of RhB up to 99.34% after visible light irradiation lasting for 90 min. The interface characteristic and possible degradation mechanism were explored. The interface characterization of LaFeO3/MMT suggested that LaFeO3 nanoparticles could be immobilized on the surface of montmorillonite with the Si-O-Fe bonds. The abundant hydroxyl groups of montmorillonite, semiconductor photocatalysis of LaFeO3 and Fenton-like reaction could enhance the photocatalytic degradation through a synergistic effect. Therefore, the LaFeO3/MMT is a very promising photocatalyst in future industrial application to treat effectively wastewater of dyes.

| S-EPMC4726031 | biostudies-literature

Nanocomposites of Natural Rubber Containing Montmorillonite Modified by Poly(2-oxazolines).

Project description:Nanocomposites with a natural rubber (NR) matrix containing organomodified montmorillonite (MMT) as a precursor of nanoparticles were prepared using two different polyoxazolines as surface modifiers of the MMT. The materials were characterized by X-ray diffraction, transmission electronic microscopy and ultimate mechanical properties, and parameters obtained by DMTA method (storage and loss moduli and loss tangent) were determined. It was found that the effect of nanofillers presence has a significant effect on tensile strength as well as elongation at break, which are higher for materials with higher viscosity due to the presence of carbon blacks compared to the composites without carbon blacks. From the two modifiers, poly(2-ethyl-2-oxazoline) was identified as a prospective modifier for surface modification of MMT used as the possible additive for tyre treads exhibiting optimal balance between fuel consumption and safety of driving concerning breaking action and lateral breakaway.

| S-EPMC11356297 | biostudies-literature

Novel ternary nanocomposites of MWCNTs/PANI/MoS2: preparation, characterization and enhanced electrochemical capacitance.

Project description:In this work, nanoflower-like MoS2 grown on the surface of multi-walled carbon nanotubes (MWCNTs)/polyaniline (PANI) nano-stem is synthesized via a facile in situ polymerization and hydrothermal method. Such a novel hierarchical structure commendably promotes the contact of PANI and electrolyte for faradaic energy storage. In the meanwhile, the double-layer capacitance of MoS2 is effectively used. The morphology and chemical composition of the as-prepared samples are characterized by scanning and transmission electron microscopies, X-ray diffraction and Fourier transform infrared spectra. The electrochemical performance of the samples is evaluated by cyclic voltammogram and galvanostatic charge-discharge measurements. It is found that the specific capacitance of the obtained MWCNTs/PANI/MoS2 hybrid is 542.56 F g-1 at a current density of 0.5 A g-1. Furthermore, the MWCNTs/PANI/MoS2 hybrid also exhibits good rate capability (62.5% capacity retention at 10 A g-1) and excellent cycling stability (73.71% capacitance retention) over 3000 cycles.

| S-EPMC5792917 | biostudies-literature

Facile mass preparation and characterization of Al/copper ferrites metastable intermolecular energetic nanocomposites.

Project description:In the present work, a novel Al/copper ferrites metastable intermolecular energetic nanocomposite was prepared by a simple and mild sol-gel method followed by low temperature calcination, and characterized by various analytical techniques. The X-ray diffraction (XRD) analysis suggests that the products contain crystal forms of aluminum and spinel-type ferrite crystal forms which are CuFe2O4 with many crystal defects. The scanning electron microscopy (SEM) and nitrogen adsorption-desorption analyses reveal that the prepared Al/copper ferrites are mesoporous structures with large specific surface areas of up to 184.47 m2 g-1 and further reveal the pore construction of this material. Its crystal defects and large specific surface area provide the possibility for its excellent catalytic performance. Al/copper ferrites have 45% better exothermic properties with higher energy output efficiency, faster burning rate, and higher reactivity than traditional Al/Fe2O3 prepared by the same method. Due to the synergistic catalytic effect of Cu-Fe oxides, Al/copper ferrites have a better catalytic effect on AP thermal decomposition and can reduce the HTD peak temperature of AP 33% more than Al/Fe2O3. The catalytic mechanism of Al/copper ferrites for the thermal decomposition of AP is obtained based on the electron transfer theories, synergistic catalytic mechanism, and the porous structure of Al/copper ferrites. Due to the mild reaction conditions and low calcination temperature, dozens of grams of product can be safely obtained at one time with low cost and easily available raw materials to meet the requirements of propellant up to several kilograms or other industrial applications.

| S-EPMC8694956 | biostudies-literature

Gamma irradiation influence on mechanical, thermal and conductivity properties of hybrid carbon nanotubes/montmorillonite nanocomposites.

Project description:A thermoplastic elastomer (TPE) based nanocomposite with the same weight ratio of hybrid nanofillers composed of carbon nanotubes (CNTs) and montmorillonite nanoclay (DK4) was prepared using a melt blending technique with an internal mixer. The TPE composite was blended from polylactic acid (PLA), liquid natural rubber (LNR) as a compatibilizer and natural rubber (NR) in a volume ratio of 70:10:20, respectively. The weight ratio of CNTs and DK4 was 2.5 wt%. The prepared samples were exposed to gamma radiation at range of 0-250 kGy. After exposure to gamma radiation, the mechanical, thermo-mechanical, thermal and electrical conductivity properties of the composites were significantly higher than unirradiated TPE composites as the irradiation doses increased up to 150 kGy. Transmission electron microscopy (TEM) micrographs revealed the good distribution and interaction between the nano-fillers and the matrix in the prepared TPE hybrid nanocomposites. In summary, the findings from this work definite that gamma irradiation might be a viable treatment to improve the properties of TPE nanocomposite for electronic packaging applications.

| S-EPMC7568474 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data