Study on Surface Permeability of Concrete under Immersion.
Ontology highlight
ABSTRACT:
SUBMITTER: Liu J
PROVIDER: S-EPMC5453065 | biostudies-other | 2014 Jan
REPOSITORIES: biostudies-other
Similar Datasets
Project description:Deposition of chloride ions in the surface layer of concrete is investigated in this study. In real concrete structure, chloride ions from the service environment can penetrate into concrete and deposit in the surface layer, to form the boundary condition for further diffusion towards the interior. The deposit amount of chloride ions in the surface layer is normally a function of time, rather than a constant. In the experimental investigation, concrete specimens with different mix proportions are immersed in NaCl solution with a mass concentration of 5%, to simulate the shallow immersion condition in sea water, and the surface chloride concentrations are measured at different ages. It is found that the surface chloride concentration increases following the increasing immersion durations, and varies from a weight percentage of 0.161%-0.781% in concretes with different mix proportions. The w/c (water-to-cement ratio) influences the surface chloride concentration significantly, and the higher the w/c is, the higher the surface chloride concentration will be, at the same age. However, following the prolonging of immersion duration, the difference in surface chloride concentration induced by w/c becomes smaller and smaller. The incorporation of fly ash leads to higher surface chloride concentration. The phenomena are explained based on pore structure analyses.
| S-EPMC5456130 | biostudies-other
Project description:The research reported herein studied the permeability of concrete containing recycled-concrete aggregate (RA), superfine phosphorous slag (PHS), and ground granulated blast-furnace slag (GGBS) with and without stress. Test results showed that the chloride diffusion coefficient of RA concrete (RAC) without external loads decreased with time, and the permeability of RAC is much lower than that of the reference concrete due to the on-going hydration and the pozzolanic reaction provided by the PHS and GGBS additives in the RAC mixture. The permeability of chloride under flexural load is much more sensitive than that under compressive load due to the differences in porosity and cracking pattern. At low compressive stress levels, the permeability of chloride decreased by the closing of pores and microcracks within RAC specimens. However, in a relatively short time the chloride diffusion coefficient and the chloride content increased rapidly with the increase of compressive stress when it exceeded a threshold stress level of approximate 35% of the ultimate compressive strength. Under flexural stress, the chloride transport capability increased with the increase of stress level and time. At high compressive and flexural stress levels, creep had a significant effect on the permeability of chloride in the RAC specimens due to the damage from the nucleation and propagation of microcracks over time. It is apparent that mortar cracking has more of a significant effect on the chloride transport in concrete than cracking in the interfacial transition zone (ITZ).
| S-EPMC5502916 | biostudies-other
Project description:To study the permeability of superabsorbent polymer (SAP) modified concrete and the effect of internal pore characteristics on the permeability of concrete specimens, the results of the water penetration under pressure test, the mercury intrusion porosimetry (MIP) test, and scanning electron microscopy (SEM) of SAP concrete were obtained and analyzed. The research shows that the addition of an appropriate amount of SAP can effectively improve the anti-permeability performance of concrete. After adding 0.2~0.6% SAP of cement quality to concrete, the penetration height value was reduced by 35~45%, the porosity was increased by 21-95%, and the tortuosity is increased by 14-15%, and all indicators show regular changes with the increase in SAP usage. Adding SAP to concrete changes the internal connection state of concrete, thereby further improving its impermeability by reducing the capillary pressure and changing the shape of the pores. The liquid permeation resistance is increased by the "threshold effect" inside concrete; this "threshold effect" is caused by the addition of SAP.
| S-EPMC7435898 | biostudies-literature
Project description:Pervious concrete is considered to be porous concrete because of its pore structure and excellent permeability. In general, larger porosity will increase the permeability coefficient, but will significantly decrease the compressive strength. The effects of water-cement ratio, fiber types, and fiber content on the permeability coefficient, porosity, compressive strength, and flexural strength were investigated. The pore tortuosity of the pervious concrete was determined by volumetric analysis and two-dimensional cross-sectional image analysis. The concept and calculation method of porosity tortuosity were further proposed. Results show that the permeability coefficient of the pervious concrete is the most suitable with a water-cement ratio of 0.30; the water permeability of the pervious concrete is influenced by fiber diameter. The permeability coefficient of pervious concrete with polypropylene thick fiber (PPTF) is greater than that with copper coated steel fiber (CCF) and the polypropylene fiber (PPF). The permeability coefficient is related to tortuosity and porosity, but when porosity is the same, the permeability coefficient may be different. Finally, general relations between the permeability coefficient and porosity tortuosity are constructed.
| S-EPMC7013612 | biostudies-literature
Project description:In order to study the deterioration and mechanism of dry-wet cycles and sulfate attack on the performance of concrete in seaside and saline areas, the deterioration of compressive strength of concrete with different water cement ratios under different erosion environments (sodium sulfate soaking at room temperature and coupling of dry-wet cycling and sodium sulfate) was studied here. At the same time, ICT (industrial computed tomography) and NMR (nuclear magnetic resonance) techniques were used to analyze the internal pore structure of concrete under different erosion environments. The results show that the compressive strength under different erosion environments increases first and then decreases, and the dry-wet cycle accelerates the sulfate erosion. With the increase of dry and wet cycles, larger pores are filled with erosion products and developed into small pores in the early stage of erosion; in the later stage of erosion, the proportion of larger pores increases, and cracks occur inside the sample. In the process of sulfate soaking and erosion, the smaller pores in the concrete account for the majority. As the sulfate erosion continues, the T2 spectrum distribution curve gradually moves right, and the signal intensity of the larger pores increases.
| S-EPMC7560325 | biostudies-literature
Project description:To study the variation law of ultrasonic parameters of self-compacting concrete before and after damage under uniaxial compression test conditions, the C30 self-compacting concrete blocks stored for 7 days and 28 days were subjected to ultrasonic nondestructive testing, and the variation law of the sound time, amplitude, and sound velocity before and after the damage of self-compacting concrete blocks was emphatically analyzed. The concrete acoustic detection software was introduced to judge and analyze the abnormal values of the parameters of each measuring point, and the defect distribution map of each test block was obtained. The results showed that after curing the self-compacting concrete test block for 7 days and 28 days, the average value of sound time before and after the failure of each measuring point of the test block is small, and the average value of sound time before the failure is less than that after; the average amplitude after failure is smaller than that before failure, and the amplitude of some measuring points will be smaller than that before. The average sound velocity after failure is less than that before failure, and the internal defects appear and the structure is not dense. This study provides a theoretical basis for the application of ultrasonic detection technology in the field of self-compacting concrete and also provides a practical basis for the stability monitoring and failure warning of self-compacting concrete.
| S-EPMC9267734 | biostudies-literature
Project description:When concrete is subjected to cycles of compression, its strength is lower than the statically determined concrete compressive strength. This reduction is typically expressed as a function of the number of cycles. In this work, we study the reduced capacity as a function of a given number of cycles by means of artificial neural networks. We used an input database with 203 datapoints gathered from the literature. To find the optimal neural network, 14 features of neural networks were studied and varied, resulting in the optimal neural net. This proposed model resulted in a maximum relative error of 5.1% and a mean relative error of 1.2% for the 203 datapoints. The proposed model resulted in a better prediction (mean tested to predicted value = 1.00 with a coefficient of variation 1.7%) as compared to the existing code expressions. The model we developed can thus be used for the design and the assessment of concrete structures and provides a more accurate assessment and design than the existing methods.
| S-EPMC6888038 | biostudies-literature
Project description:This paper investigates the effectiveness of a specific crystalline waterproofing admixture (CWA) in concrete as a function of a water-binder ratio. Four concrete mixes with and without CWA were prepared; two of them with a water-binder ratio of 0.45 and two of them with a water-binder ratio of 0.55. Water permeability and compressive strength were tested on hardened concrete specimens and self-healing of cracks over time was observed. Cement paste and CWA paste were prepared to clarify the results obtained on the concrete specimens. SEM and EDS and XRD and FTIR were performed on the hardened pastes to explain the mechanism of CWA working. The results show that the addition of CWA had no significant effect on the compressive strength of the concrete, but reduced the water penetration depth in the concrete, and the reduction was more effective for mixes with lower water-binder ratio. Regarding the self-healing effect, it can be concluded that the addition of CWA improves the crack healing in concrete, but the efficiency of self-healing is highly dependent on the initial crack width. The mechanisms involved in the reduction of water penetration depth and crack healing in concrete can be explained by different mechanisms; one is creation of the CSH gel from unreacted clinker grains, then formation carbonate, and additional mechanism is gel formation (highly expansive Mg-rich hydro-carbonate) from magnesium based additives. The presence of sodium silicate, which would transform into carbonate/bicarbonate, also cannot be excluded.
| S-EPMC8069652 | biostudies-literature