Optical Fiber Embedded in Epoxy Glass Unidirectional Fiber Composite System.

ABSTRACT: We aimed to embed silica optical fibers in composites (epoxy vinyl ester matrix reinforced with E-glass unidirectional fibers in mass fraction of 60%) in order to further monitor the robustness of civil engineering structures (such as bridges). A simple system was implemented using two different silica optical fibers (F1-double coating of 172 µm diameter and F2-single coating of 101.8 µm diameter respectively). The optical fibers were dynamically tensile tested and Weibull plots were traced. Interfacial adhesion stress was determined using pull-out test and stress values were correlated to fracture mechanisms based on SEM observations. In the case of the optical fiber (OF) (F1)/resin system and OF (F1)/composite system, poor adhesion was reported that may be correlated to interface fracture at silica core level. Relevant applicable results were determined for OF (F2)/composite system.

SUBMITTER: Severin I

PROVIDER: S-EPMC5453130 | biostudies-other | 2013 Dec

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Mechanical and Tribological Behavior of Functionally Graded Unidirectional Glass Fiber-Reinforced Epoxy Composites.

Project description:This paper aims to assess experimentally the mechanical and tribological behavior of conventional and functionally graded (FG) polymeric matrix composites reinforced with continuous glass fibers. The small punch test (SPT) and a pin-on-disc device were used in the present work to examine the mechanical and wear behavior, respectively. The hand lay-up technique was used in the present investigation to manufacture the conventional and FG composites. Various wooden looms with different nailed spacing were employed to manufacture the FG composites. According to test type, the FG composite is composed of four and ten layers, with a different glass fiber volume of fraction (Vf%) for each layer. In addition, the finite element simulation based on Hashin's failure criterion and cohesive zone modeling was used to show the progressive failure and give more explanation regarding the flexural behavior of such composites. The present results indicate that the wear rate of an FG composite could be affected by many factors, including the disk speed, applied load, the composite layers number, and average glass fiber volume fraction. On the other hand, the arrangement of layers in the composite materials by variation of Vf% for each layer can improve the wear rate and value of the ultimate load before the fracture of the composite material when subjected to SPT. The experimental and numerical results for all SPT specimens showed that the fracture of the SPT specimens began beneath the punch tip and grew along the fiber direction. The ultimate flexural capacity of FG composites increased by 30% compared with the conventional composites.

| S-EPMC9147567 | biostudies-literature

Ballistic Impact Behaviour of Glass/Epoxy Composite Laminates Embedded with Shape Memory Alloy (SMA) Wires.

Project description:This paper aims to estimate the enhancement in the energy absorption characteristics of the glass fiber reinforced composites (GFRP) by embedding prestrained pseudo-elastic shape memory alloy (SMA) that was used as a secondary reinforcement. The pseudo-elastic SMA (PE-SMA) embedded were in the form of wires and have an equiatomic composition (i.e., 50%-50%) of nickel (Ni) and titanium (Ti). These specimens are fabricated using a vacuum-assisted resin infusion process. The estimation is done for the GFRP and SMA/GFRP specimens at four different impact velocities (65, 75, 85, and 103 m/s) using a gas-gun impact set-up. At all different impact velocities, the failure modes change as we switch from GFRP to SMA/GFRP specimen. In the SMA/GFRP specimen, the failure mode changed from delamination in the primary region to SMA-pull out and SMA deformation. This leads to an increase in the ballistic limit. It is observed that energy absorbed by SMA/GFRP specimens is higher than the GFRP specimens subjected to the same levels of impact energy. To understand the damping capabilities of SMA embedment, vibration signals are captured, and the damping ratio is calculated. SMA dampens the vibrations imparted by the projectile to the specimen. The damping ratio of the SMA/GFRP specimens is higher than the GFRP specimens. The damping effect is more prominent below the ballistic limit when the projectile got rebounded (65 m/s).

| S-EPMC7796393 | biostudies-literature

A dataset of micro-scale tomograms of unidirectional glass fiber/epoxy and carbon fiber/epoxy composites acquired via synchrotron computed tomography during <i>in-situ</i> tensile loading.

Project description:We have performed synchrotron computed tomography on two different fiber-reinforced composites while they were being continuously in-situ loaded in 0° tension. One material is a glass/epoxy laminate and the other is a carbon/epoxy laminate. The voxel size is 1.1?µm, which allows clear recognition of the glass fibers, but not distinct individual carbon fibers. For each material, four loading steps are selected with approximately 0, 40, 73, and 95% of the failure load, and the 3D images of the four volumes from each material are overlaid. A volume of interest in the middle 0° ply is chosen and located in the 3D image of each loading step (Fig. 1). The cropped volumes of interest for each material are presented in this publication and are publicly available on Mendeley Data[1]. As examples of two frequently-used type of unidirectional fiber-reinforced composites, the presented data can be used for different microstructural analyses, including investigation of the 3D variability in fiber distribution and orientation, and their evolution during tensile loading. For example, we have performed fiber orientation analysis on this data, using our digital image correlation-based technique, in [2]. Moreover, real-time formation of fiber breaks with tensile loading can be investigated in the data.

| S-EPMC7806803 | biostudies-literature

Cross-Scale Industrial Manufacturing of Multifunctional Glass Fiber/Epoxy Composite Tubes via a Purposely Modified Filament Winding Production Line

Project description: Not available

| S-EPMC11207220 | biostudies-literature

A multimodal data-set of a unidirectional glass fibre reinforced polymer composite.

Project description:A unidirectional (UD) glass fibre reinforced polymer (GFRP) composite was scanned at varying resolutions in the micro-scale with several imaging modalities. All six scans capture the same region of the sample, containing well-aligned fibres inside a UD load-carrying bundle. Two scans of the cross-sectional surface of the bundle were acquired at a high resolution, by means of scanning electron microscopy (SEM) and optical microscopy (OM), and four volumetric scans were acquired through X-ray computed tomography (CT) at different resolutions. Individual fibres can be resolved from these scans to investigate the micro-structure of the UD bundle. The data is hosted at https://doi.org/10.5281/zenodo.1195879 and it was used in Emerson et al. (2018) [1] to demonstrate that precise and representative characterisations of fibre geometry are possible with relatively low X-ray CT resolutions if the analysis method is robust to image quality.

| S-EPMC6060273 | biostudies-literature

The Effect of Cellulose Nanocrystal Coatings on the Glass Fiber-Epoxy Interphase.

Project description:This study focuses on understanding the effect of cellulose nanocrystals (CNCs) on glass fiber/epoxy interfacial interactions. The glass fibers (GF) were coated with solutions containing cellulose nanomaterial. The parameters that were investigated were the CNC surface chemistry, concentration, and dispersing medium, i.e., aqueous solution only versus emulsions. To determine the effect of the CNC coatings on the interfacial adhesion, specimens of a single GF in an epoxy matrix were prepared for GF coating by varying the coating formulations. The interfacial shear stress (IFSS) was determined by the single fiber fragmentation test (SFFT). Following the SFFT, the samples were investigated by cross-polarized microscopy in order to understand the fracture modes which are related to the nature of the interphase. According to the SFFT data and photoelastic fracture patterns, both the emulsion and aqueous coatings containing cellulose nanocrystals functionalized with methyl(triphenyl) phosphonium (CNCPh) improve the IFSS in comparison to coated GFs without CNCs.

| S-EPMC6630561 | biostudies-literature

Graphene-Based Materials as Strain Sensors in Glass Fiber/Epoxy Model Composites.

Project description:The ability of graphene-based materials to act as strain sensors in glass fiber/epoxy model composites by using Raman spectroscopy has been investigated. The strain reporting performance of two types of graphene nanoplatelets (GNPs) was compared with that of graphene produced by chemical vapor deposition (CVD). The strain sensitivity of the thicker GNPs was impeded by their limited aspect ratio and weak interaction between flakes and fibers. The discontinuity of the GNP coating and inconsistency in properties among individual platelets led to scatter in the reported strains. In comparison, continuous and homogeneous CVD grown graphene was more accurate as a strain sensor and suitable for point-by-point strain reporting. The Raman mapping results of CVD graphene and its behavior under cyclic deformation show reversible and reliable strain sensing at low strain levels (up to 0.6% matrix strain), above which interfacial sliding of the CVD graphene layer was observed through an in situ Raman spectroscopic study.

| S-EPMC7007000 | biostudies-literature

Enhanced Mechanical Properties of Multiscale Carbon Fiber/Epoxy Unidirectional Composites with Different Dimensional Carbon Nanofillers.

Project description:Ammonia modified graphene-carbon nanotubes/continuous carbon fiber reinforced epoxy unidirectional multiscale composites (AMGNS-MWCNT/CFEP) were prepared by adding ammonia modified graphene and carbon nanotubes to an epoxy matrix to reduce agglomeration of carbon nanofillers in the epoxy matrix and improve composites properties. Fourier transform infrared spectroscopy (FTIR), scanning electron microscope (SEM), and universal testing machines were used to characterize the properties of carbon nanofillers, AMGNS-MWCNT/epoxy nanocomposites, and AMGNS-MWCNT/CFEP unidirectional composites. When the AMGNS-MWCNT content was 1.0 wt%, flexural strength, the flexural modulus and interlaminar shear strength of AMGNS-MWCNT/CFEP unidirectional composites reached the maximum value of 1520.3 MPa, 138.88 GPa, and 87.80 MPa, respectively, which were 12.5%, 9.42%, and 10.1% higher than that of carbon fiber reinforced epoxy unidirectional composites (CFEP). The synergistic mechanism of two carbon nanofillers in the matrix is discussed.

| S-EPMC7558300 | biostudies-literature

The Influence of Flame Retardants on Combustion of Glass Fiber-Reinforced Epoxy Resin.

Project description:For the first time, next to the flammability tests (LOI, UL-94 HB, VBB, TGA), experimental tests and computer simulation have been conducted on the flame spread and combustion of glass fiber-reinforced epoxy resins (GFRER) with 6% graphene and 6% DDM-DOPO flame-retardant additives. The downward rates of flame spread (ROS) in opposed flow with oxidizer and the upward ROS along GFRER composites have been first measured as well as the distribution of temperature over the combustion surface of the composites with flame-retardant additives and without them. The LOI and UL-94 HB tests showed a reduction in the flammability of GFRER when flame retardants were added and predicted a higher effectiveness of DDM-DOPO compared to graphene. Adding DDM-DOPO resulted in increasing the rate of formation of the volatile pyrolysis products and their yield, indicating, together with the other data obtained, the gas phase mechanism of the flame retardant's action. Adding graphene resulted in an increase in the soot release on the burning surface and an increase in the amount of non-volatile pyrolysis products on the burning surface, reducing the amount of fuel that participated in the oxidation reactions in the gas phase. The developed numerical combustion model for GFRER with a DDM-DOPO additive, based on the action of DDM-DOPO as a flame retardant acting in the gas phase, satisfactorily predicts the effect of this flame retardant on the reduction in downward ROS over GFRER for 45-50% oxygen concentrations. The developed model for GFRER with graphene additive, based on a reduction in the amount of fuel and increase in the amount of incombustible volatile pyrolysis products when graphene is added, predicts with good accuracy downward ROS over GFRER depending on oxygen concentration.

| S-EPMC9416137 | biostudies-literature

Glass Fiber-Epoxy Composites with Boron Nitride Nanotubes for Enhancing Interlaminar Properties in Structures.

Project description:Hybrid composite materials are a class of materials where more than one type of reinforcement is integrated into a matrix to achieve superior properties. This typically involves nanoparticle fillers employed within traditional advanced composites with fiber reinforcements such as carbon or glass. The current study builds on previous investigations of boron nitride nanotube (BNNT) hybrid composites, specifically glass fiber (GF)-epoxy/BNNT composite laminates. GF is an effective and affordable primary reinforcement fiber in many applications, and boron nitride nanotubes (BNNTs) exhibit impressive mechanical properties comparable to carbon nanotubes (CNTs) with distinct functional properties, such as electrical insulation, which is desirable in manufacturing insulating composites when combined with GF. GF-epoxy/BNNT composite laminates, incorporating BNNT materials with different loadings (1 and 2 wt %) and purity, were manufactured using a hand layup technique and prepared for three-point bending, modified Charpy, dynamic mechanical analysis (DMA), and fracture toughness (mode I and mode II) measurements. A comprehensive microscopy study was also performed using scanning electron microscopy (SEM) showing prominent failure mechanism, nanotube dispersion, and their mode of reinforcement in different loading scenarios. Enhanced properties, including a 43% increase in mode II fracture toughness, were observed in hybrid composites with 1 wt % BNNT compared to the GF composites with neat epoxy, and the reinforcement mechanisms were discussed.

| S-EPMC8973038 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data