Microstructural Evolution and Dynamic Softening Mechanisms of Al-Zn-Mg-Cu Alloy during Hot Compressive Deformation.

ABSTRACT: The hot deformation behavior and microstructural evolution of an Al-Zn-Mg-Cu (7150) alloy was studied during hot compression at various temperatures (300 to 450 °C) and strain rates (0.001 to 10 s-1). A decline ratio map of flow stresses was proposed and divided into five deformation domains, in which the flow stress behavior was correlated with different microstructures and dynamic softening mechanisms. The results reveal that the dynamic recovery is the sole softening mechanism at temperatures of 300 to 400 °C with various strain rates and at temperatures of 400 to 450 °C with strain rates between 1 and 10 s-1. The level of dynamic recovery increases with increasing temperature and with decreasing strain rate. At the high deformation temperature of 450 °C with strain rates of 0.001 to 0.1 s-1, a partially recrystallized microstructure was observed, and the dynamic recrystallization (DRX) provided an alternative softening mechanism. Two kinds of DRX might operate at the high temperature, in which discontinuous dynamic recrystallization was involved at higher strain rates and continuous dynamic recrystallization was implied at lower strain rates.

SUBMITTER: Shi C

PROVIDER: S-EPMC5453149 | biostudies-other | 2014 Jan

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Restirring and Reheating Effects on Microstructural Evolution of Al-Zn-Mg-Cu Alloy during Underwater Friction Stir Additive Manufacturing.

Project description:Friction stir additive manufacturing (FSAM) can be potentially used for fabricating high-performance components owing to its advantages of solid-state processing. However, the inhomogeneous microstructures and mechanical properties of the build attributed to the complex process involving restirring and reheating deserve attention. This study is based on the previous research of the underwater FSAMed 7A04 aluminum alloy and adopts a quasi in situ experimental method, i.e., after each pass of the underwater FSAM, samples were taken from the build for microstructural observation to investigate the restirring and reheating effects on microstructural evolution during the underwater FSAM. Fine-grain microstructures were formed in the stir zone during the single-pass underwater FSAM. After restirring, the grain size at the bottom of the overlapping region decreased from 1.97 to 0.87 μm, the recrystallization degree reduced from 74.0% to 29.8%, and the initial random texture transformed into a strong shear texture composed of the C {110}<11¯0>. After reheating, static recrystallization occurred in the regions close to the new additive zones, increasing the grain size and recrystallization degree. This study not only revealed the microstructural evolution during the underwater FSAM but also provided a guideline for further optimization of the mechanical properties of the Al−Zn−Mg−Cu alloy build.

| S-EPMC9181392 | biostudies-literature

Hot Deformation Behavior and Dynamic Softening Mechanism in 7B50 Aluminum Alloy.

Project description:The hot deformation behavior and dynamic softening mechanism of 7B50 aluminum alloy were studied via isothermal compression experiments in the range of 320-460 °C/0.001-1.0 s-1. According to the flow curves obtained from the experiments, the flow behavior of this alloy was analyzed, and the Zener-Hollomon (Z) parameter equation was established. The hot processing maps of this alloy were developed based on the dynamic material model, and the optimal hot working region was determined to be 410-460 °C/0.01-0.001 s-1. The electron backscattered diffraction (EBSD) microstructure analysis of the deformed sample shows that the dynamic softening mechanism and microstructure evolution strongly depend on the Z parameter. Meanwhile, a correlation between the dynamic softening mechanism and the lnZ value was established. Dynamic recovery (DRV) was the only softening mechanism during isothermal compression with lnZ ≥ 20. Discontinuous dynamic recrystallization (DDRX) becomes the dominant dynamic recrystallization (DRX) mechanism under deformation conditions of 15 < lnZ < 20. Meanwhile, the size and percentage of DDRXed grains increased with decreasing lnZ values. The geometric dynamic recrystallization (GDRX) mechanism and continuous dynamic recrystallization (CDRX) mechanism coexist under deformation conditions with lnZ ≤ 15.

| S-EPMC10456416 | biostudies-literature

Comparison of Hot Deformation Behavior Characteristics Between As-Cast and Extruded Al-Zn-Mg-Cu (7075) Aluminum Alloys with a Similar Grain Size.

Project description:The hot compressive behavior and processing maps of as-cast and extruded 7075 aluminum alloys with a similar grain size (320-350 m) were studied and compared, which allows us to directly observe the effect of segregated phases in the as-cast microstructure on the deformation behavior and hot workability of 7075 alloys. In the as-cast alloy, the compound phases segregated along the interdendritic interfaces within the interiors of original grains provided the additional sites for continuous dynamic recrystallization via the particle stimulation nucleation mechanism. As a result, the as-cast alloy exhibited higher fractions of recrystallized grains and smaller grain sizes than the extruded alloy after compression. The stress exponent values of the as-cast alloy were smaller than those of the extruded alloy. In the processing maps, the domain associated with high power dissipation efficiencies (≥35%) occurred in a wider temperature range in the as-cast alloy compared to the extruded alloy. The segregated phases that remained undissolved in the as-cast alloy after compressive deformation could be effectively eliminated during the solid solution treatment (753 K for 2 h) for T6 aging applied after hot compression. The current results suggest the possibility and advantage of omitting the extrusion step when preparing 7xxx aluminum forging or extrusion feedstocks for hot working. The proposed method can be applied to other precipitation hardenable aluminum alloys.

| S-EPMC6926894 | biostudies-literature

Characterisation of a High-Performance Al-Zn-Mg-Cu Alloy Designed for Wire Arc Additive Manufacturing.

Project description:Ever-increasing demands of industrial manufacturing regarding mechanical properties require the development of novel alloys designed towards the respective manufacturing process. Here, we consider wire arc additive manufacturing. To this end, Al alloys with additions of Zn, Mg and Cu have been designed considering the requirements of good mechanical properties and limited hot cracking susceptibility. The samples were produced using the cold metal transfer pulse advanced (CMT-PADV) technique, known for its ability to produce lower porosity parts with smaller grain size. After material simulations to determine the optimal heat treatment, the samples were solution heat treated, quenched and aged to enhance their mechanical performance. Chemical analysis, mechanical properties and microstructure evolution were evaluated using optical light microscopy, scanning electron microscopy, energy dispersive X-ray spectroscopy, X-ray fluorescence analysis and X-ray radiography, as well as tensile, fatigue and hardness tests. The objective of this research was to evaluate in detail the mechanical properties and microstructure of the newly designed high-performance Al-Zn-based alloy before and after ageing heat treatment. The only defects found in the parts built under optimised conditions were small dispersed porosities, without any visible cracks or lack of fusion. Furthermore, the mechanical properties are superior to those of commercial 7xxx alloys and remarkably independent of the testing direction (parallel or perpendicular to the deposit beads). The presented analyses are very promising regarding additive manufacturing of high-strength aluminium alloys.

| S-EPMC7178362 | biostudies-literature

Precipitation of a new platelet phase during the quenching of an Al-Zn-Mg-Cu alloy.

Project description:A previously undescribed high aspect ratio strengthening platelet phase, herein named the Y-phase, has been identified in a commercial Al-Zn-Mg-Cu alloy. Differential scanning calorimetry indicates that this phase only precipitates at temperature and cooling rate of about 150-250 °C and 0.05-300 K/s, respectively. This precipitate is shown to be responsible for a noticeable improvement in mechanical properties. Aberration corrected scanning transmission electron microscopy demonstrates the minimal thickness (~1.4 nm) precipitate plates are isostructural to those of the T1 (Al2CuLi) phase observed in Al-Cu-Li alloys. Low voltage chemical analysis by energy dispersive X-ray spectroscopy and electron energy loss spectroscopy gives evidence of the spatial partitioning of the Al, Cu and Zn within the Y-phase, as well as demonstrating the incorporation of a small amount of Mg.

| S-EPMC4793252 | biostudies-literature

Study on Mg/Al Weld Seam Based on Zn-Mg-Al Ternary Alloy.

Project description:Based on the idea of alloying welding seams, a series of Zn-xAl filler metals was calculated and designed for joining Mg/Al dissimilar metals by gas tungsten arc (GTA) welding. An infrared thermography system was used to measure the temperature of the welding pool during the welding process to investigate the solidification process. It was found that the mechanical properties of the welded joints were improved with the increasing of the Al content in the Zn-xAl filler metals, and when Zn-30Al was used as the filler metal, the ultimate tensile strength could reach a maximum of 120 MPa. The reason for the average tensile strength of the joint increasing was that the weak zone of the joint using Zn-30Al filler metal was generated primarily by α-Al instead of MgZn2. When Zn-40Al was used as the filler metal, a new transition zone, about 20 μm-wide, appeared in the edge of the fusion zone near the Mg base metal. Due to the transition zones consisting of MgZn₂- and Al-based solid solution, the mechanical property of the joints was deteriorated.

| S-EPMC5453102 | biostudies-other

Microstructure Evolution and Localized Corrosion Susceptibility of an Al-Zn-Mg-Cu-Zr 7xxx Alloy with Minor Cr Addition.

Project description:Microstructure optimization of Al-Zn-Mg-Cu-Zr aluminum alloys, particularly through recrystallization inhibition, for improved strength and corrosion resistance properties has been an important consideration in alloy development for aerospace applications. Addition of rare earth elements, sometimes combined with Cr, has been found to be beneficial in this regard. In this study, the role of a single addition of 0.1 wt.% Cr on microstructure evolution of an Al-Zn-Mg-Cu-Zr (7449) alloy during processing was systematically investigated by optical light microscopy, scanning electron microscopy, electron backscatter diffraction and scanning transmission electron microscopy. Susceptibility to localized corrosion after aging to T4, T6 and T76 conditions was evaluated by potentiodynamic polarization (PDP) measurements and an intergranular corrosion (IGC) test. A decrease in recrystallized fraction with 0.1 wt.% Cr addition was observed, which is attributed to the formation of Cu- and Zn-containing E (Al18Mg3Cr2) dispersoids and the larger as-cast grain size. Moreover, the depletion of alloying elements from solid solution due to the formation of the Cu- and Zn-containing E (Al18Mg3Cr2) dispersoids and η Mg(Zn,Cu,Al)2 phase at its interface affects grain-boundary precipitation. The observed decrease in localized corrosion susceptibility with minor Cr addition is correlated with the microstructure and equally discussed.

| S-EPMC9918105 | biostudies-literature

Influence of Homogenization on Microstructural Response and Mechanical Property of Al-Cu-Mn Alloy.

Project description:The evolution of the microstructures and properties of large direct chill (DC)-cast Al-Cu-Mn alloy ingots during homogenization was investigated. The results revealed that the Al-Cu-Mn alloy ingots had severe microsegregation and the main secondary phase was Al₂Cu, with minimal Al₇Cu₂Fe phase. Numerous primary eutectic phases existed in the grain boundary and the main elements were segregated at the interfaces along the interdendritic region. The grain boundaries became discontinuous, residual phases were effectively dissolved into the matrix, and the segregation degree of all elements was reduced dramatically during homogenization. In addition, the homogenized alloys exhibited improved microstructures with finer grain size, higher number density of dislocation networks, higher density of uniformly distributed θ' or θ phase (Al₂Cu), and higher volume fraction of high-angle grain boundaries compared to the nonhomogenized samples. After the optimal homogenization scheme treated at 535 °C for 10 h, the tensile strength and elongation% were about 24 MPa, 20.5 MPa, and 1.3% higher than those of the specimen without homogenization treatment.

| S-EPMC6025167 | biostudies-literature

Nanotomographic evaluation of precipitate structure evolution in a Mg-Zn-Zr alloy during plastic deformation.

Project description:Magnesium and its alloys attract increasingly wide attention in various fields, ranging from transport to medical solutions, due to their outstanding structural and degradation properties. These properties can be tailored through alloying and thermo-mechanical processing, which is often complex and multi-step, thus requiring in-depth analysis. In this work, we demonstrate the capability of synchrotron-based nanotomographic X-ray imaging methods, namely holotomography and transmission X-ray microscopy, for the quantitative 3D analysis of the evolution of intermetallic precipitate (particle) morphology and distribution in magnesium alloy Mg-5.78Zn-0.44Zr subjected to a complex multi-step processing. A rich history of variation of the intermetallic particle structure in the processed alloy provided a testbed for challenging the analytical capabilities of the imaging modalities studied. The main features of the evolving precipitate structure revealed earlier by traditional light and electron microscopy methods were confirmed by the 3D techniques of synchrotron-based X-ray imaging. We further demonstrated that synchrotron-based X-ray imaging enabled uncovering finer details of the variation of particle morphology and number density at various stages of processing-above and beyond the information provided by visible light and electron microscopy.

| S-EPMC7527343 | biostudies-literature

Simultaneous increase in strength and ductility by decreasing interface energy between Zn and Al phases in cast Al-Zn-Cu alloy.

Project description:Cast-Al alloys that include a high amount of the second element in their matrix have comparatively high strength but low ductility because of the high volume fraction of strengthening phases or undesirable inclusions. Al-Zn alloys that have more than 30?wt% Zn have a tensile strength below 300?MPa, with elongation under 5% in the as-cast state. However, we found that after substitution of 2% Zn by Cu, the tensile strength of as-cast Al-Zn-Cu alloys was 25% higher and ductility was four times higher than for the corresponding Al-35% Zn alloy. Additionally, for the Al-43% Zn alloy with 2% Cu after 1?h solution treatment at 400?°C and water quenching, the tensile strength unexpectedly reached values close to 600?MPa. For the Al-33% Zn alloy with 2% Cu, the tensile strength was 500?MPa with 8% ductility. The unusual trends of the mechanical properties of Al-Zn alloys with Cu addition observed during processing from casting to the subsequent solution treatment were attributed to the precipitation of Zn in the Al matrix. The interface energy between the Zn particles and the Al matrix decreased when using a solution of Cu in Zn.

| S-EPMC5610273 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data