Cathodic Polarization Coats Titanium Based Implant Materials with Enamel Matrix Derivate (EMD).

ABSTRACT: The idea of a bioactive surface coating that enhances bone healing and bone growth is a strong focus of on-going research for bone implant materials. Enamel matrix derivate (EMD) is well documented to support bone regeneration and activates growth of mesenchymal tissues. Thus, it is a prime candidate for coating of existing implant surfaces. The aim of this study was to show that cathodic polarization can be used for coating commercially available implant surfaces with an immobilized but functional and bio-available surface layer of EMD. After coating, XPS revealed EMD-related bindings on the surface while SIMS showed incorporation of EMD into the surface. The hydride layer of the original surface could be activated for coating in an integrated one-step process that did not require any pre-treatment of the surface. SEM images showed nano-spheres and nano-rods on coated surfaces that were EMD-related. Moreover, the surface roughness remained unchanged after coating, as it was shown by optical profilometry. The mass peaks observed in the matrix-assisted laser desorption/ionization time-of-flight mass spectroscopy (MALDI-TOF MS) analysis confirmed the integrity of EMD after coating. Assessment of the bioavailability suggested that the modified surfaces were active for osteoblast like MC3M3-E1 cells in showing enhanced Coll-1 gene expression and ALP activity.

SUBMITTER: Frank MJ

PROVIDER: S-EPMC5453263 | biostudies-other | 2014 Mar

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:BackgroundLong-term success of implant restoration depends on many factors one of them is the sufficient implant stability which is lowered in compromised bone density sites such as the maxilla as it is categorized as type III & IV bone, so searching for a new innovation and updates in implant material and features is very mandatory. So, the aim of this study was to compare between two implant materials (roxolid and traditional titanium) on the primary and secondary stability of implant retained maxillary overdenture.MethodsEighteen completely edentulous patients were selected. All patients received maxillary implant-retained overdentures and lower complete dentures; patients were divided equally into two groups according to the type of implant materials. Group A received a total number of 36 implants made of roxolid material and Group B received a total number of 36 implants made of traditional titanium alloys. Implant stability was assessed using ostell device, the primary implant stability was measured at the day of implant installation however, secondary implant stability was measured after six weeks of implant placement. Paired t-test was used to compare between primary and secondary stability in the same group and an independent t-test was used to compare between the two groups with a significant level < 0.05.ResultsIndependent t-test revealed a significant difference between the two groups with p -value = 0.0141 regarding primary stability and p-value < 0.001 regarding secondary stability, as roxolid implant group was statistically higher stability than titanium group in both. Paired t- test showed a statistically significant difference in roxolid implant group with p-value = 0.0122 however, there was non-statistically significant difference in titanium group with p-value = 0.636. Mann Whitney test showed a significant difference between the two groups regarding amount of change in stability with p value = 0.191. roxolid implant group showed a higher amount of change in stability than the titanium implant group.ConclusionWithin the limitation of this study, it could be concluded that: Roxolid implants showed promising results regarding primary and secondary stability compared to conventional Titanium implants and can be a better alternative in implant retained maxillary overdentures.Trial registrationRetrospectively NCT06334770 at 26-3-2024.

Project description:The major challenge for dentistry is to provide the patient an oral rehabilitation to maintain healthy bone conditions in order to reduce the time for loading protocols. Advancement in implant surface design is necessary to favour and promote the osseointegration process. The surface features of titanium dental implant can promote a relevant influence on the morphology and differentiation ability of mesenchymal stem cells, induction of the osteoblastic genes expression and the release of extracellular matrix (ECM) components. The present study aimed at evaluating the in vitro effects of two different dental implants with titanium surfaces, TEST and CTRL, to culture the human periodontal ligament stem cells (hPDLSCs). Expression of ECM components such as Vimentin, Fibronectin, N-cadherin, Laminin, Focal Adhesion Kinase (FAK) and Integrin beta-1 (ITGB1), and the osteogenic related markers, as runt related transcription factor 2 (RUNX2) and alkaline phosphatase (ALP), were investigated. Human PDLSCs cultured on the TEST implant surface demonstrated a better cell adhesion capability as observed by Scanning Electron Microscopy (SEM) and immunofluorescence analysis. Moreover, immunofluorescence and Western blot experiments showed an over expression of Fibronectin, Laminin, N-cadherin and RUNX2 in hPDLSCs seeded on TEST implant surface. The gene expression study by RT-PCR validated the results obtained in protein assays and exhibited the expression of RUNX2, ALP, Vimentin (VIM), Fibronectin (FN1), N-cadherin (CDH2), Laminin (LAMB1), FAK and ITGB1 in hPDLSCs seeded on TEST surface compared to the CTRL dental implant surface. Understanding the mechanisms of ECM components release and its regulation are essential for developing novel strategies in tissue engineering and regenerative medicine. Our results demonstrated that the impact of treated surfaces of titanium dental implants might increase and accelerate the ECM apposition and provide the starting point to initiate the osseointegration process.

Dataset Information

Cathodic Polarization Coats Titanium Based Implant Materials with Enamel Matrix Derivate (EMD).

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets