Influence of Size on the Microstructure and Mechanical Properties of an AISI 304L Stainless Steel-A Comparison between Bulk and Fibers.

ABSTRACT: In this work, the mechanical properties and microstructural features of an AISI 304L stainless steel in two presentations, bulk and fibers, were systematically studied in order to establish the relationship among microstructure, mechanical properties, manufacturing process and effect on sample size. The microstructure was analyzed by XRD, SEM and TEM techniques. The strength, Young's modulus and elongation of the samples were determined by tensile tests, while the hardness was measured by Vickers microhardness and nanoindentation tests. The materials have been observed to possess different mechanical and microstructural properties, which are compared and discussed.

SUBMITTER: Baldenebro-Lopez FJ

PROVIDER: S-EPMC5455263 | biostudies-other | 2015 Jan

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Formation of Nanospikes on AISI 420 Martensitic Stainless Steel under Gallium Ion Bombardment.

Project description:The focused ion beam (FIB) has proven to be an extremely powerful tool for the nanometer-scale machining and patterning of nanostructures. In this work, we experimentally study the behavior of AISI 420 martensitic stainless steel when bombarded by Ga+ ions in a FIB system. The results show the formation of nanometer sized spiky structures. Utilizing the nanospiking effect, we fabricated a single-tip needle with a measured 15.15 nanometer curvature radius and a microneedle with a nanometer sized spiky surface. The nanospikes can be made straight or angled, depending on the incident angle between the sample and the beam. We also show that the nanospiking effect is present in ferritic AISI 430 stainless steel. The weak occurrence of the nanospiking effect in between nano-rough regions (nano-cliffs) was also witnessed for austenitic AISI 316 and martensitic AISI 431 stainless steel samples.

| S-EPMC6836003 | biostudies-literature

Datasets on the corrosion behaviour of nanostructured AISI 316 stainless steel treated by SMAT.

Project description:The present paper contains the experimental datasets on the corrosion behaviour of nanostructured AISI 316 stainless steel (SS) through polarization tests in 0.6 M NaCl aqueous solution at room temperature. The nanostructured layers were first obtained through surface mechanical attrition treatment (SMAT) method and the data information on the corrosion behaviour of the nanostructured layer was thereafter collected. Through potentiodynamic polarization tests and electrochemical impedance spectroscopy (EIS) studies, the experimental datasets were obtained to investigate the combined effects of SMAT and low temperature annealing on the corrosion behaviour of 316 SS. The experimental datasets obtained include the open circuit potential (OCP), corrosion current densities, corrosion potential, Nyquist, impedance and phase angle. The datasets provided in this article will be of great help to most aerospace, automobile, and manufacturing industries in determining the actual and practical corrosion behaviour of AISI 316 SS in corrosive and aggressive environment.

| S-EPMC6554219 | biostudies-literature

Preparation of Porous Stainless Steel Hollow-Fibers through Multi-Modal Particle Size Sintering towards Pore Engineering.

Project description:The sintering of metal powders is an efficient and versatile technique to fabricate porous metal elements such as filters, diffusers, and membranes. Neck formation between particles is, however, critical to tune the porosity and optimize mass transfer in order to minimize the densification process. In this work, macro-porous stainless steel (SS) hollow-fibers (HFs) were fabricated by the extrusion and sintering of a dope comprised, for the first time, of a bimodal mixture of SS powders. The SS particles of different sizes and shapes were mixed to increase the neck formation between the particles and control the densification process of the structure during sintering. The sintered HFs from particles of two different sizes were shown to be more mechanically stable at lower sintering temperature due to the increased neck area of the small particles sintered to the large ones. In addition, the sintered HFs made from particles of 10 and 44 ?m showed a smaller average pore size (<1 ?m) as compared to the micron-size pores of sintered HFs made from particles of 10 ?m only and those of 10 and 20 ?m. The novel HFs could be used in a range of applications, from filtration modules to electrochemical membrane reactors.

| S-EPMC5618125 | biostudies-literature

Dataset of the synthesis parameters to deposit YSZ on stainless steel AISI 316L by sputtering technique.

Project description:The data presented in this article are related to the research previously published "improvement of adhesion and barrier properties of biomedical stainless steel by deposition of YSZ coatings using RF magnetron sputtering". It contains the structural, morphological, compositional and electrochemical characterization of bare AISI 316L substrate which was used as a substrate to coat with yttria-stabilized zirconia (YSZ). The chemical composition and topography analyses from X-ray photoelectron spectroscopy (XPS), Auger electron spectroscopy (AES) and micrographs from atomic force microscopy (AFM) as well as the roughness value of the YSZ-sputtered coating on AISI 316L substrates are presented as complementary data of the article.

| S-EPMC6811928 | biostudies-literature

Microstructure and Mechanical Properties of Butt Joints between Stainless Steel SUS304L and Aluminum Alloy A6061-T6 by TIG Welding.

Project description:The tungsten inert gas (TIG) welding method most commonly used to weld ferrous metals, nonferrous metals, and other metals since it is simple, easily implemented, and achieves consistent high-quality welds. In this study, butt joints produced between aluminum alloy A6061-T6 and stainless steel SUS304L have been achieved by using TIG welding with ER4047 filler metal. The macrostructure and microstructure of the resulting specimens were analyzed by means of an optical microscope (OM), a scanning electron microscope (SEM), and an energy dispersive X-ray spectrometer (EDS). A uniform intermetallic layer was found at the interface between the stainless steel and the weld seam having a thickness of 2 µm, and the intermetallic compound (IMC) includes Fe?Al13, Fe?Al?, and FeAl? phases. The micro-hardness and tensile strength of the weld joints were also investigated. Due to Si content in the compensating metal, there was a prevention of iron diffusion into the aluminum, thus hindering the development of the IMC layer and reducing its thickness in such a way that the weld joint strength increases. The analyzed results show that the average micro-hardness of the stainless steel, weld seam, aluminum alloys, and IMC layer were 218 HV, 88.3 HV, 63.3 HV, and 411 HV, respectively. The fracture occurred at the brazed interface, and the ultimate tensile strength value reached 225 MPa.

| S-EPMC6073269 | biostudies-literature

Corrosion Behavior of AISI 304 Stainless Steel Reinforcements in SCBA-SF Ternary Ecological Concrete Exposed to MgSO4.

Project description:In this study, ternary ecological concrete (TEC) mixtures were produced with partial substitution of the ordinary Portland cement (OPC) by 10%, 20%, and 30% of sugar cane bagasse ash (SCBA) and silica fume (SF); a control mixture (100% OPC) was prepared according to ACI 211.1 standard. The studied TEC specimens were reinforced with AISI 304 stainless steel and AISI 1018 carbon steel rebars. TEC reinforced specimens were immersed in two different electrolytes, a control (DI-water) and 3.5 wt.% MgSO4 solution, for 180 days. The electrochemical corrosion was monitored by corrosion potential (Ecorr) according to ASTM C-876-15 standard, and the linear polarization resistance (LPR) technique using ASTM G59 standard. The Ecorr and current density icorr results show that AISI 304 stainless steel rebars have a high corrosion resistance, with icorr values below 0.1 µA/cm2, which is interpreted as a level of negligible corrosion. The best corrosion performance was found for the TEC mixture made with a 20% addition of blend of sugar cane bagasse ash-silica fume (SCBA-SF) to the OPC.

| S-EPMC7288276 | biostudies-literature

Compressibility of 304 Stainless Steel Powder Metallurgy Materials Reinforced with 304 Short Stainless Steel Fibers.

Project description:Powder metallurgy (P/M) technique is usually used for manufacturing porous metal materials. However, some P/M materials are limitedly used in engineering for their performance deficiency. A novel 304 stainless steel P/M material was produced by a solid-state sintering of 304 stainless steel powders and 304 short stainless steel fibers, which were alternately laid in layers according to mass ratio. In this paper, the compressive properties of the P/M materials were characterized by a series of uniaxial compression tests. The effects of fiber content, compaction pressure and high temperature nitriding on compressive properties were investigated. The results indicated that, without nitriding, the samples changed from cuboid to cydariform without damage in the process of compression. The compressive stress was enhanced with increasing fiber content ranging from 0 to 8 wt.%. For compaction pressure from 55 to 75 MPa, greater compaction pressure improved compressive stress. Moreover, high temperature nitriding was able to significantly improve the yield stress, but collapse failure eventually occurred.

| S-EPMC5456726 | biostudies-other

Interfacial Chemistry Investigation of Initial Fouling Conditions in Isocyanate Production: The Antifouling Performance of AISI 316L Stainless Steel.

Project description:The fouling of AISI 316L stainless steel during themanufacture of polymeric methylene diphenyl diisocyanate (pMDI) has been investigated. Studies have been carried out using a laboratory-based rig that simulates the process chemistry of the production plant. A variety of solution concentrations and treatment times have been employed to represent different stages in the production process. Following exposure, steel coupons have been removed and studied by X-ray photoelectron spectroscopy (XPS) and time-of-flight secondary ion mass spectrometry (ToF-SIMS). The thickness of the fouling layer, determined by XPS, is found to vary inversely with exposure time and solution concentration. This is a result of the solubility of the different pMDI derivatives that have been formed at different stages, and a reaction scheme is developed to explain these inverse relationships. ToF-SIMS indicates the formation of metal chlorides as a result of the initial treatment of the steel in the reaction vessel with hydrogen chloride. Fragment ions characteristic of reacted and unreacted pMDI (at m/z = 106 and 132 au, respectively) were used as an indicator of the degree of reacted isocyanate groups within the fouling layer and show a decrease with increasing exposure time, as a result of the formation of intermediates such as amines, ureas, carbodiimides, and uretonimines. The ToF-SIMS data was also processed by principal component analysis (PCA). This generally reinforced the conclusions reached by XPS and ToF-SIMS but, in addition, gave confidence in the repeatability of the analyses with the repeat data (of four analyses) clustering very tightly in the PCA score plots.

| S-EPMC8515391 | biostudies-literature

Effect of Rolling Temperature on Microstructure Evolution and Mechanical Properties of AISI316LN Austenitic Stainless Steel.

Project description:The impacts of rolling temperature on phase transformations and mechanical properties were investigated for AISI 316LN austenitic stainless steel subjected to rolling at cryogenic and room temperatures. The microstructure evolution and the mechanical properties were investigated by means of optical, scanning, and transmission electron microscopy, an X-ray diffractometer, microhardness tester, and tensile testing system. Results showed that strain-induced martensitic transformation occurred at both deformation temperatures, and the martensite volume fraction increased with the deformation. Compared with room temperature rolling, cryorolling substantially enhanced the martensite transformation rate. At 50% deformation, it yielded the same fraction as the room temperature counterpart at 90% strain, while at 70%, it totally transformed the austenite to martensite. The strength and hardness of the stainless steel increased remarkably with the deformation, but the corresponding elongation decreased dramatically. Meanwhile, the tensile fracture morphology changed from a typical ductile rupture to a mixture of ductile and quasi-cleavage fracture. The phase transformation and deformation mechanisms differed at two temperatures, with the martensite deformation contributing to the former, and austenite deformation to the latter. Orientations between the transformed martensite and its parent phase followed the K?S (Kurdjumov?Sachs) relationship.

| S-EPMC6165331 | biostudies-other

Corrosion behavior of metastable AISI 321 austenitic stainless steel: Investigating the effect of grain size and prior plastic deformation on its degradation pattern in saline media.

Project description:The role of grain size and strain rate on the corrosion behavior of plastically-deformed Ti-stabilized austenitic stainless steel (AISI 321) in saline media was investigated. The as-received coarse-grained alloy (CG: ~37 µm) was subjected to thermomechanical processing to develop fine (FG: ~3 µm) and ultrafine (UFG: ~0.24 µm) grained structures. These samples were deformed under high (dynamic) and low (quasi-static) strain-rate conditions to a similar true strain of ~0.86. Microstructural analyses on specimens after deformation prior to corrosion study suggests a shift from the estimated stacking fault energy value of the steel. Electrochemical tests confirm the highest corrosion resistance for UFG specimens due to the formation of the most stable adsorbed passive film. This is followed by FG and CG specimens in that order. For the three grain sizes, the corrosion resistance of specimen deformed under quasi-static loading condition is higher than that subjected to dynamic impact loading while the corrosion resistance of undeformed samples is the least. This work also confirms the non-detrimental effect of TiCs in AISI 321 austenitic stainless steel on its corrosion resistance. However, TiNs were observed to be detrimental by promoting pitting corrosion due to galvanic coupling of TiNs with their surrounding continuous phase. The mechanism of pitting in AISI 321 in chloride solution is proposed.

| S-EPMC6702197 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data