Recyclability of Concrete Pavement Incorporating High Volume of Fly Ash.

ABSTRACT: Recyclable concrete pavement was made from fly ash and crushed limestone sand and gravel as aggregates so that the concrete pavement could be recycled to raw materials for cement production. With the aim to use as much fly ash as possible for the sustainable development of society, while achieving adequate strength development, pavement concrete having a cement-replacement ratio of 40% by mass was experimentally investigated, focusing on the strength development at an early age. Limestone powder was added to improve the early strength; flexural strength at two days reached 3.5 MPa, the minimum strength for traffic service in Japan. The matured fly ash concrete made with a cement content of 200 kg/m3 achieved a flexural strength almost equal to that of the control concrete without fly ash. Additionally, Portland cement made from the tested fly ash concrete was tested to confirm recyclability, with the cement quality meeting the Japanese classification of ordinary Portland cement. Limestone-based recyclable fly ash concrete pavement is, thus, a preferred material in terms of sustainability.

SUBMITTER: Yoshitake I

PROVIDER: S-EPMC5455502 | biostudies-other | 2015 Aug

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Accelerated and natural carbonation of concrete with high volumes of fly ash: chemical, mineralogical and microstructural effects.

Project description:Today, a rather poor carbonation resistance is being reported for high-volume fly ash (HVFA) binder systems. This conclusion is usually drawn from accelerated carbonation experiments conducted at CO2 levels that highly exceed the natural atmospheric CO2 concentration of 0.03-0.04%. However, such accelerated test conditions may change the chemistry of the carbonation reaction (and the resulting amount of CH and C-S-H carbonation), the nature of the mineralogical phases formed (stable calcite versus metastable vaterite, aragonite) and the resulting porosity and pore size distribution of the microstructure after carbonation. In this paper, these phenomena were studied on HVFA and fly ash + silica fume (FA + SF) pastes after exposure to 0.03-0.04%, 1% and 10% CO2 using thermogravimetric analysis, quantitative X-ray diffraction and mercury intrusion porosimetry. It was found that none of these techniques unambiguously revealed the reason for significantly underestimating carbonation rates at 1% CO2 from colorimetric carbonation test results obtained after exposure to 10% CO2 that were implemented in a conversion formula that solely accounts for the differences in CO2 concentration. Possibly, excess water production due to carbonation at too high CO2 levels with a pore blocking effect and a diminished solubility for CO2 plays an important role in this.

| S-EPMC6366180 | biostudies-literature

Experimental Investigation and Analytical Modeling of Chloride Diffusivity of Fly Ash Concrete.

Project description:Owing to its importance in the assessment of reinforced concrete structures, it is essential to determine the chloride diffusivity of fly ash concrete. This paper presents an investigation into the diffusion characteristics of chloride ions in fly ash concrete. Through experiment, the relationship between chloride diffusivity and curing age up to 1800 days is measured and the effects of curing age, water/binder ratio, aggregate volume fraction, and fly ash content (i.e., percentage of total cementitious material by mass) on chloride diffusivity are evaluated. It is found that the chloride diffusivity decreases with the increase of curing age, aggregate volume fraction, and fly ash content, but increases with the increase of water/binder ratio. In analytical modeling, an equivalent aggregate model is constructed and the equivalent interfacial transition zone (ITZ) thickness is derived analytically. With the equivalent aggregate model, three-phase fly ash concrete reduces to a two-phase composite material. By extending the Maxwell method, the chloride diffusivity of fly ash concrete is formulated. Finally, the validity of the analytical method is verified by experimental results.

| S-EPMC7079598 | biostudies-literature

Life Cycle Assessment and Impact Correlation Analysis of Fly Ash Geopolymer Concrete.

Project description:Geopolymer concrete (GPC) has drawn widespread attention as a universally accepted ideal green material to improve environmental conditions in recent years. The present study systematically quantifies and compares the environmental impact of fly ash GPC and ordinary Portland cement (OPC) concrete under different strength grades by conducting life cycle assessment (LCA). The alkali activator solution to fly ash ratio (S/F), sodium hydroxide concentration (CNaOH), and sodium silicate to sodium hydroxide ratio (SS/SH) were further used as three key parameters to consider their sensitivity to strength and CO2 emissions. The correlation and influence rules were analyzed by Multivariate Analysis of Variance (MANOVA) and Gray Relational Analysis (GRA). The results indicated that the CO2 emission of GPC can be reduced by 62.73%, and the correlation between CO2 emission and compressive strength is not significant for GPC. The degree of influence of the three factors on the compressive strength is CNaOH (66.5%) > SS/SH (20.7%) > S/F (9%) and on CO2 emissions is S/F (87.2%) > SS/SH (10.3%) > CNaOH (2.4%). Fly ash GPC effectively controls the environmental deterioration without compromising its compressive strength; in fact, it even in favor.

| S-EPMC8658180 | biostudies-literature

Influence of Fly Ash Additive on the Properties of Concrete with Slag Cement.

Project description:This paper presents research on the impact of fly ash addition on selected physical and mechanical parameters of concrete made with slag cement. Experimental tests were carried out to measure the migration of chloride ions in concrete, the tightness of concrete exposed to water under pressure, and the compressive strength and tensile strength of concrete during splitting. Six series of concrete mixes made with CEM IIIA 42.5 and 32.5 cement were tested. The base concrete mix was modified by adding fly ash as a partial cement substitute in the amounts of 25% and 33%. A comparative analysis of the obtained results indicates a significant improvement in tightness, especially in concrete based on CEM IIIA 32.5 cement and resistance to chloride ion penetration for the concretes containing fly ash additive. In the concretes containing fly ash additive, a slower rate of initial strength increase and high strength over a long period of maturation are shown. In accordance with the presented research results, it is suggested that changes to the European standardization system be considered, to allow the use of fly ash additive in concrete made with CEM IIIA 42.5 or 32.5 cement classes. Such a solution is not currently acceptable in standards in some European Countries.

| S-EPMC7435652 | biostudies-literature

Scheffe's Simplex Optimization of Flexural Strength of Quarry Dust and Sawdust Ash Pervious Concrete for Sustainable Pavement Construction.

Project description:Pervious concrete provides a tailored surface course with high permeability properties which permit the easy flow of water through a larger interconnected porous structure to prevent flooding hazards. This paper reports the modeling of the flexural properties of quarry dust (QD) and sawdust ash (SDA) blended green pervious concrete for sustainable road pavement construction using Scheffe's (5,2) optimization approach. The simplex mixture design method was adapted to formulate the mixture proportion to eliminate the set-backs encountered in empirical or trials and the error design approach, which consume more time and resources to design with experimental runs required to evaluate the response function. For the laboratory evaluation exercise, a maximum flexural strength of 3.703 N/mm2 was obtained with a mix proportion of 0.435:0.95:0.1:1.55:0.05 for water, cement, QD, coarse aggregate and SDA, respectively. Moreover, the minimal flexural strength response of 2.504 N/mm2 was obtained with a mix ratio of 0.6:0.75:0.3:4.1:0.25 for water, cement, QD, coarse aggregate and SDA, respectively. The test of the appropriateness of the developed model was statistically verified using the Student' t-test and an analysis of variance (ANOVA), and was confirmed to be acceptable based on computational outcomes at the 95% confidence interval. Furthermore, the scanning electron microscopy (SEM) and energy dispersive X-ray (EDX) were used to evaluate the morphological and mineralogical behavior of green prior concrete samples with various additive mixture compositions. The addition of QD and SDA, on the other hand, aided the creation of porous microstructures in the concrete matrix due to fabric changes in the concrete mixture, potentially aided by the formation of cementitious compounds such as calcium aluminate hydrate and calcium silicate hydrate.

| S-EPMC9863484 | biostudies-literature

Data for the physical and mechanical properties of high volume fly ash cement paste composites.

Project description:The data presented herein are compiled of the research summary of "Characterization of High-Volume Fly-Ash Cement Paste for Sustainable Construction Application" (Aydin and Arel, 2017) [1]. This data article provides general information about the ASTM Class C and Class F fly ash cement paste composites composed of silica fume, lime, water reducing admixtures in three different level of workability (0 mm, 100 mm and 200 mm). The dataset here also helps the readers to understand the links with the basic properties of the ingredients, for example, how can porosity be predicted based on the mixture design? how can the strength of the material be linked with the basic strengths of the constituent ingredients?.

| S-EPMC5711659 | biostudies-literature

Modeling of Compressive Strength for Self-Consolidating High-Strength Concrete Incorporating Palm Oil Fuel Ash.

Project description:Modeling is a very useful method for the performance prediction of concrete. Most of the models available in literature are related to the compressive strength because it is a major mechanical property used in concrete design. Many attempts were taken to develop suitable mathematical models for the prediction of compressive strength of different concretes, but not for self-consolidating high-strength concrete (SCHSC) containing palm oil fuel ash (POFA). The present study has used artificial neural networks (ANN) to predict the compressive strength of SCHSC incorporating POFA. The ANN model has been developed and validated in this research using the mix proportioning and experimental strength data of 20 different SCHSC mixes. Seventy percent (70%) of the data were used to carry out the training of the ANN model. The remaining 30% of the data were used for testing the model. The training of the ANN model was stopped when the root mean square error (RMSE) and the percentage of good patterns was 0.001 and ≈100%, respectively. The predicted compressive strength values obtained from the trained ANN model were much closer to the experimental values of compressive strength. The coefficient of determination (R²) for the relationship between the predicted and experimental compressive strengths was 0.9486, which shows the higher degree of accuracy of the network pattern. Furthermore, the predicted compressive strength was found very close to the experimental compressive strength during the testing process of the ANN model. The absolute and percentage relative errors in the testing process were significantly low with a mean value of 1.74 MPa and 3.13%, respectively, which indicated that the compressive strength of SCHSC including POFA can be efficiently predicted by the ANN.

| S-EPMC5503044 | biostudies-other

Evaluation of the Chemical and Mechanical Properties of Hardening High-Calcium Fly Ash Blended Concrete.

Project description:High-calcium fly ash (FH) is the combustion residue from electric power plants burning lignite or sub-bituminous coal. As a mineral admixture, FH can be used to produce high-strength concrete and high-performance concrete. The development of chemical and mechanical properties is a crucial factor for appropriately using FH in the concrete industry. To achieve sustainable development in the concrete industry, this paper presents a theoretical model to systematically evaluate the property developments of FH blended concrete. The proposed model analyzes the cement hydration, the reaction of free CaO in FH, and the reaction of phases in FH other than free CaO. The mutual interactions among cement hydration, the reaction of free CaO in FH, and the reaction of other phases in FH are also considered through the calcium hydroxide contents and the capillary water contents. Using the hydration degree of cement, the reaction degree of free CaO in FH, and the reaction degree of other phases in FH, the proposed model evaluates the calcium hydroxide contents, the reaction degree of FH, chemically bound water, porosity, and the compressive strength of hardening concrete with different water to binder ratios and FH replacement ratios. The evaluated results are compared to experimental results, and good consistencies are found.

| S-EPMC5512662 | biostudies-other

Effects of Incorporating High-Volume Fly Ash into Tricalcium Silicate on the Degree of Silicate Polymerization and Aluminum Substitution for Silicon in Calcium Silicate Hydrate.

Project description:This study assesses the quantitative effects of incorporating high-volume fly ash (HVFA) into tricalcium silicate (C₃S) paste on the hydration, degree of silicate polymerization, and Al substitution for Si in calcium silicate hydrate (C-S-H). Thermogravimetric analysis and isothermal conduction calorimetry showed that, although the induction period of C₃S hydration was significantly extended, the degree of hydration of C₃S after the deceleration period increased due to HVFA incorporation. Synchrotron-sourced soft X-ray spectromicroscopy further showed that most of the C₃S in the C₃S-HVFA paste was fully hydrated after 28 days of hydration, while that in the pure C₃S paste was not. The chemical shifts of the Si K edge peaks in the near-edge X-ray fine structure of C-S-H in the C₃S-HVFA paste directly indicate that Al substitutes for Si in C-S-H and that the additional silicate provided by the HVFA induces an enhanced degree of silicate polymerization. This new spectromicroscopic approach, supplemented with 27Al and 29Si magic-angle spinning nuclear magnetic resonance spectroscopy and transmission electron microscopy, turned out to be a powerful characterization tool for studying a local atomic binding structure of C-S-H in C₃S-HVFA system and presented results consistent with previous literature.

| S-EPMC5459114 | biostudies-other

Preparation of Ultrafine Fly Ash-Based Superhydrophobic Composite Coating and Its Application to Foam Concrete.

Project description:The waterproof and thermal insulation property of foamed concrete is very important. In this study, the ultrafine fly ash (UFA)-based superhydrophobic composite coating was applied onto foam concrete. The UFA-based base coating that closely adhered to the concrete initially improved the waterproofness of the test block, and the silane coupling agent-modified UFA-based surface coating further achieved superhydrophobicity. The UFA on the coating surface and the asperities on the surface jointly formed a lotus leaf-like rough micro-nanostructure. The 154.34° water drop contact angle and 2.41° sliding angle on No. 5 coating were reached, indicating that it was a superhydrophobic surface. The water absorption ratios of the composite coating block were 1.87% and 16.6% at 4 h and 7 days, which were reduced by 97% and 75% in comparison with the original foam concrete. The compressive strength and heat conductivity coefficient after soaking for 4 h of the composite coating block were higher than 4.0 MPa and 0.225 W·m-1·K-1, respectively. The UFA-based superhydrophobic composite coating proposed in this study and applied onto foam concrete is simple and cheap, requires no precise instrument, and can be applied in a large area.

| S-EPMC7650569 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data