Impact Behavior of Three Notched All-Ceramic Restorations after Soaking in Artificial Saliva.

ABSTRACT: Biomechanics play a critical role in influencing the clinical applications of all-ceramic dental restorations. The restorative biomaterials have to demonstrate mechanical durability in the oral environment because they are always exposed to a variety of oral environments. This study was designed to evaluate the effect of soaking time, notch and saliva pH values on the impact energy of three commonly used all-ceramic materials for CAD/CAM. The leucite-reinforced glass ceramic (ProCAD), lithium disilicate glass ceramic (IPS e.max CAD) and zirconia-based ceramic materials (IPS e.max ZirCAD) were used. The experimental results indicated that the impact energy of ProCAD decreased with an increase in soaking time, but not for IPS e.max CAD and IPS e.max ZirCAD. The impact energy of the zirconia system was higher than leucite-reinforced and lithium disilicate-based ceramic systems. When subjected to preformed 0.5 mm U-shape notch on the bar specimen of 3 mm thick, the impact energy of the all-ceramic restorations revealed a markedly reduction of about 80%-90%, almost irrespective of dental compositions, which indicated the effect of flaw to a great degree. No statistically significant influence (p > 0.05) of pH values (4, 7 and 9) on impact energy was found for each group. It is concluded that the no matter which all-ceramic materials were used, it was appreciably sensitive to the presence of notches. The ceramic composition and microstructure have been shown to affect mechanical durability.

SUBMITTER: Yan M

PROVIDER: S-EPMC5455632 | biostudies-other | 2015 Jul

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:ObjectivesThe aim was to assess how incorporating a short-fiber composite (SFC) core would affect the fracture behavior of direct and indirect overlays. Furthermore, to examine the relationship between the thickness ratio of SFC core to particulate-filled composite (PFC) veneering and the fracture-behavior of bilayered-structured restorations.Materials and methodsA total of 120 molars were used to create MOD cavities, with palatal cusps removed. Four different groups of direct overlays were then made (n = 15/group), all of which featured a SFC core (everX Flow) with varying thicknesses (0, 1, 4, and 5 mm), as well as a surface layer of PFC (G-aenial Posterior), with the overall thickness of the bilayered-structured restoration set at 5 mm. Additionally, four groups of CAD/CAM restorations were created (Cerasmart 270 and Initial LiSi Block), with or without 2 mm of SFC core reinforcement. Following the fabrication of these restorations, cyclic fatigue aging was carried out for a total of 500,000 cycles, with an applied maximum load (Fmax) of 150 N. Subsequently, each restoration underwent quasi-static loading until fracture. The fracture mode was subsequently evaluated using optical microscopy and SEM.ResultsThere were no statistically significant differences (p > 0.05) observed in the fracture resistance of indirect overlays reinforced with a 2-mm SFC core compared to those made solely from restorative materials. Direct overlays constructed using plain SFC or with a 4-mm layer thickness of SFC core exhibited significantly higher fracture resistance values (2674 ± 465 and 2537 ± 561 N) (p < 0.05) when compared to all other groups tested, according to the statistical analysis ANOVA.ConclusionsThe most effective method for restoring large MOD cavities was found to be direct restoration using SFC either alone or as a bulk core in combination with PFC composite.Clinical relevanceThe use of SFC as bulk reinforcing base will significantly improve the loading performance of directly layered restorations.

Dataset Information

Impact Behavior of Three Notched All-Ceramic Restorations after Soaking in Artificial Saliva.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets