Facile Solvothermal Synthesis and Gas Sensitivity of Graphene/WO₃ Nanocomposites.

ABSTRACT: Graphene has attracted enormous attention owing to its extraordinary properties, while graphene-based nanocomposites hold promise for many applications. In this paper, we present a two-step exploitation method for preparation of graphene oxides and a facile solvothermal route for preparation of few-layer graphene nanosheets and graphene/WO₃ nanocomposites in an ethanol-distilled water medium. The as-synthesized samples were characterized by using field emission scanning electron microscopy (FE-SEM), high-resolution transmission electron microscopy (HRTEM), ultraviolet-visible (UV-vis) spectroscopy, Raman spectroscopy, X-ray diffraction (XRD), thermogravimetric-differential thermal analysis (TG-DTA) and gas-sensing test. The resistivity of the thick-film gas sensors based on sandwich-like graphene/WO₃ nanocomposites can be controlled by varying the amount of graphene in the composites. Graphene/WO₃ nanocomposites with graphene content higher than 1% show fast response, high selectivity and fine sensitivity to NOx.

SUBMITTER: Gui Y

PROVIDER: S-EPMC5455935 | biostudies-other | 2014 Jun

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Ultrahigh Selective Room-Temperature Ammonia Gas Sensor Based on Tin-Titanium Dioxide/reduced Graphene/Carbon Nanotube Nanocomposites by the Solvothermal Method.

Project description:Resistive-based gas sensors have been considered as the most favorable gas sensors for detection of toxic gases and volatile organic compounds (VOCs) because of their simple structure, low cost, high sensitivity, ease of use, and high stability. Unfortunately, wide application of resistive-based gas sensors is limited by their low selectivity. In this article, we present the fabrication of ultrahigh selective NH3 gas sensor based on tin-titanium dioxide/reduced graphene/carbon nanotube (Sn-TiO2@rGO/CNT) nanocomposites. The Sn-TiO2@rGO/CNT nanocomposites with different molar ratios of Sn/Ti (1:10, 3:10, and 5:10) were synthesized via the solvothermal method. Characterizations by scanning electron microscopy, transmission electron microscopy, and X-ray photoelectron spectroscopy confirmed the decoration of Sn-TiO2 nanoparticles on rGO/CNT nanocomposite surfaces. The Sn-TiO2@rGO/CNT nanocomposite gas sensor exhibited high response and ultrahigh selectivity to NH3 against toluene, dimethylformamide, acetone, ethanol, methanol, isopropanol, formaldehyde, hydrogen, carbon dioxide, acetylene, and VOCs in paint thinners at room temperature. The Sn-TiO2@rGO/CNT nanocomposite gas sensor with molar ratio of Sn/Ti = 1:10 showed the highest response to NH3 over other molar ratios of Sn/Ti as well as pure rGO/CNT and Sn-TiO2 gas sensors. The ammonia-sensing mechanisms of the Sn-TiO2@rGO/CNT gas sensor were proposed based on the formation of p-n heterojunctions of p-type rGO/CNT and n-type Sn-TiO2 nanoparticles via a low-temperature oxidizing reaction process.

| S-EPMC6796937 | biostudies-literature

Facile Synthesis of Sn/Nitrogen-Doped Reduced Graphene Oxide Nanocomposites with Superb Lithium Storage Properties.

Project description:Sn/Nitrogen-doped reduced graphene oxide (Sn@N-G) composites have been successfully synthesized via a facile method for lithium-ion batteries. Compared with the Sn or Sn/graphene anodes, the Sn@N-G anode exhibits a superb rate capability of 535 mAh g-1 at 2C and cycling stability up to 300 cycles at 0.5C. The improved lithium-storage performance of Sn@N-G anode could be ascribed to the effective graphene wrapping, which accommodates the large volume change of Sn during the charge-discharge process, while the nitrogen doping increases the electronic conductivity of graphene, as well as provides a large number of active sites as reservoirs for Li+ storage.

| S-EPMC6723252 | biostudies-literature

Facile synthesis of pristine graphene-palladium nanocomposites with extraordinary catalytic activities using swollen liquid crystals.

Project description:Amazing conductivity, perfect honeycomb sp(2) arrangement and the high theoretical surface area make pristine graphene as one of the best materials suited for application as catalyst supports. Unfortunately, the low reactivity of the material makes the formation of nanocomposite with inorganic materials difficult. Here we report an easy approach to synthesize nanocomposites of pristine graphene with palladium (Pd-G) using swollen liquid crystals (SLCs) as a soft template. The SLC template gives the control to deposit very small Pd particles of uniform size on G as well as RGO. The synthesized nanocomposite (Pd-G) exhibited exceptionally better catalytic activity compared with Pd-RGO nanocomposite in the hydrogenation of nitrophenols and microwave assisted C-C coupling reactions. The catalytic activity of Pd-G nanocomposite during nitrophenol reduction reaction was sixteen times higher than Pd nanoparticles and more than double than Pd-RGO nanocomposite. The exceptionally high activity of pristine graphene supported catalysts in the organic reactions is explained on the basis of its better pi interacting property compared to partially reduced RGO. The Pd-G nanocomposite showed exceptional stability under the reaction conditions as it could be recycled upto a minimum of 15 cycles for the C-C coupling reactions without any loss in activity.

| S-EPMC5020490 | biostudies-literature

Facile and Robust Solvothermal Synthesis of Nanocrystalline CuInS? Thin Films.

Project description:This work demonstrates that the solvothermal synthesis of nanocrystalline CuInS? thin films using the amino acid l-cysteine as sulfur source is facile and robust against variation of reaction time and temperature. Synthesis was carried out in a reaction time range of 3?48 h (at 150 °C) and a reaction temperature range of 100?190 °C (for 18 h). It was found that at least a time of 6 h and a temperature of 140 °C is needed to produce pure nanocrystalline CuInS? thin films as proven by X-ray and electron diffraction, high-resolution transmission electron microscopy, and energy-dispersive X-ray spectroscopy. Using UV-vis spectroscopy, a good absorption behavior as well as direct band gaps between 1.46 and 1.55 eV have been determined for all grown films. Only for a reaction time of 3 h and temperatures below 140 °C CuInS? is not formed. This is attributed to the formation of metal ion complexes with l-cysteine and the overall slow assembly of CuInS?. This study reveals that the reaction parameters can be chosen relatively free; the reaction is completely nontoxic and precursors and solvents are rather cheap, which makes this synthesis route interesting for industrial up scaling.

| S-EPMC6027332 | biostudies-literature

Thermally reduced kaolin-graphene oxide nanocomposites for gas sensing.

Project description:Highly sensitive graphene-based gas sensors can be made using large-area single layer graphene, but the cost of large-area pure graphene is high, making the simpler reduced graphene oxide (rGO) an attractive alternative. To use rGO for gas sensing, however, require a high active surface area and slightly different approach is needed. Here, we report on a simple method to produce kaolin-graphene oxide (GO) nanocomposites and an application of this nanocomposite as a gas sensor. The nanocomposite was made by binding the GO flakes to kaolin with the help of 3-Aminopropyltriethoxysilane (APTES). The GO flakes in the nanocomposite were contacting neighboring GO flakes as observed by electron microscopy. After thermal annealing, the nanocomposite become conductive as showed by sheet resistance measurements. Based on the conductance changes of the nanocomposite films, electrical gas sensing devices were made for detecting NH3 and HNO3. These devices had a higher sensitivity than thermally annealed multilayer GO films. This kaolin-GO nanocomposite might be useful in applications that require a low-cost material with large conductive surface area including the demonstrated gas sensors.

| S-EPMC5378989 | biostudies-literature

Supercritical CO2 Assisted Solvothermal Preparation of CoO/Graphene Nanocomposites for High Performance Lithium-Ion Batteries.

Project description:Supercritical CO2 (scCO2) is often used to prepare graphene/metal oxide nanocomposite anodes for high performance lithium-ion batteries (LIBs) by the assisted solvothermal method due to its low viscosity, high diffusion, zero surface tension and good surface wettability. However, the formation mechanism of metal oxides and the combination mechanism between metal oxides and graphene in this system are superficial. In this work, a cobalt monoxide/graphene (CoO/G) nanocomposite is fabricated via the scCO2 assisted solvothermal method followed by thermal treatment. We elucidate the mechanism that amorphous intermediates obtain by the scCO2 assisted solvothermal method, and then ultrafine CoO nanoparticles are crystallized during the heat treatment. In addition, scCO2 can promote CoO to be tightly fixed on the surface of graphene nanosheets by interfacial chemical bonds, which can effectively improve its cycle stability and rate performance. As expected, the CoO/G composites exhibit higher specific capacity (961 mAh g-1 at 100 mA g-1), excellent cyclic stability and rate capability (617 mAh g-1 after 500 cycles at 1000 mA g-1) when applied as an anode of LIB.

| S-EPMC7999444 | biostudies-literature

Facile synthesis of ternary graphene nanocomposites with doped metal oxide and conductive polymers as electrode materials for high performance supercapacitors.

Project description:Supercapacitors (SCs) due to their high energy density, fast charge storage and energy transfer, long charge discharge curves and low costs are very attractive for designing new generation of energy storage devices. In this work we present a simple and scalable synthetic approach to engineer ternary composite as electrode material based on combination of graphene with doped metal oxides (iron oxide) and conductive polymer (polypyrrole) with aims to achieve supercapacitors with very high gravimetric and areal capacitances. In the first step a binary composite with graphene mixed with doped iron oxide (rGO/MeFe2O4) (Me = Mn, Ni) was synthesized using new single step process with NaOH acting as a coprecipitation and GO reducing agent. This rGO/MnFe2O4 composite electrode showed gravimetric capacitance of 147 Fg-1 and areal capacitance of 232 mFcm-2 at scan rate of 5 mVs-1. In the final step a conductive polypyrrole was included to prepare a ternary composite graphene/metal doped iron oxide/polypyrrole (rGO/MnFe2O4/Ppy) electrode. Ternary composite electrode showed significantly improved gravimetric capacitance and areal capacitance of 232 Fg-1 and 395 mFcm-2 respectively indicating synergistic impact of Ppy additives. The method is promising to fabricate advanced electrode materials for high performing supercapacitors combining graphene, doped iron oxide and conductive polymers.

| S-EPMC6461681 | biostudies-literature

Facile One-Pot Solvothermal Synthesis of the RGO/MWCNT/Fe3O4 Hybrids for Microwave Absorption.

Project description:How to effectively regulate the electromagnetic parameters of magnetic composites to achieve better microwave absorption (MA) performances is still a serious challenge. Herein, we constructed nanocomposites composed of magnetic constituents and carbon materials to obtain high-efficiency electromagnetic wave absorbers. Self-assembled, multi-interfacial, and porous RGO/MWCNT/Fe3O4 hybrids (GMFs) were synthesized via in situ one-pot solvothermal method. The growth mechanism of the GMFs would be that the defects on reduced graphene oxide (RGO) provide sites for the crystallization of Fe3O4. Also, the RGO and Fe3O4 were further linked by the cross-connection of multiwalled carbon nanotubes (MWCNTs), which acted as a bridge. The MA mechanism of GMFs was studied while considering the synergistic effects between the three components (RGO, MWCNT, and raspberry-shaped Fe3O4) and their multi-interfacial and porous structure. Also, the MA performance of the GMFs was conducted. The GMFs exhibited a maximum reflection loss (RL) value of -61.29 dB at 10.48 GHz with a thickness of 2.6 mm when the contents of RGO and MWCNT were 6.3 and 1.3 wt %, respectively. The RL values (≤-10 dB) were observed to be in the range of 8.96-12.32 GHz, and the effective microwave absorption bandwidth was tunable from 3.52 to 18 GHz by changing the sample thickness. The results revealed that the multi-interfacial and porous structure of the GMFs is beneficial to MA performance by inducing multiscatterings. Since no toxic solvents were used, this method is environmentally friendly and has potential for large-scale production. The prepared GMFs may have a wide range of applications in MA materials against electromagnetic interference pollution.

| S-EPMC7033987 | biostudies-literature

Facile synthesis of hydrophilic magnetic graphene nanocomposites via dopamine self-polymerization and Michael addition for selective enrichment of N-linked glycopeptides.

Project description:The development of methods to effectively capture N-glycopeptides from the complex biological samples is crucial to N-glycoproteome profiling. Herein, the hydrophilic chitosan-functionalized magnetic graphene nanocomposites (denoted as Fe3O4-GO@PDA-Chitosan) were designed and synthesized via a simple two-step modification (dopamine self-polymerization and Michael addition). The Fe3O4-GO@PDA-Chitosan nanocomposites exhibited good performances with low detection limit (0.4 fmol·?L-1), good selectivity (mixture of bovine serum albumin and horseradish peroxidase tryptic digests at a molar ration of 10:1), good repeatability (4 times), high binding capacity (75?mg·g-1). Moreover, Fe3O4-GO@PDA-Chitosan nanocomposites were further utilized to selectively enrich glycopeptides from human renal mesangial cell (HRMC, 200??g) tryptic digest, and 393 N-linked glycopeptides, representing 195 different glycoproteins and 458 glycosylation sites were identified. This study provides a feasible strategy for the surface functionalized novel materials for isolation and enrichment of N-glycopeptides.

| S-EPMC6952460 | biostudies-literature

Facile Solvothermal Synthesis of CuCo₂S₄ Yolk-Shells and Their Visible-Light-Driven Photocatalytic Properties.

Project description:In this present work, we synthesized a yolk-shell shaped CuCo₂S₄ by a simple anion exchange method. The morphological and structural properties of the as-synthesized sample were characterized using X-ray diffraction (XRD), UV-vis diffuse reflectance spectra (UV-vis DRS), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The SEM and TEM results confirmed that the uniform yolk-shell structure was formed during the solvothermal process. The band gap was about 1.41 eV, which have been confirmed by UV⁻vis DRS analysis. The photocatalytic property was evaluated by the photocatalytic degradation of methylene blue (MB) dye as a target pollutant under the visible-light irradiation. The experimental results confirmed the potential application of yolk-shell shape CuCo₂S₄ in visible-light photocatalytic applications.

| S-EPMC6265846 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data