Hysteresis in Lanthanide Aluminum Oxides Observed by Fast Pulse CV Measurement.
Ontology highlight
ABSTRACT:
SUBMITTER: Zhao C
PROVIDER: S-EPMC5456006 | biostudies-other | 2014 Oct
REPOSITORIES: biostudies-other
Similar Datasets
Project description:A powerful characterization technique, pulse capacitance-voltage (CV) technique, was used to investigate oxide traps before and after annealing for lanthanide zirconium oxide thin films deposited on n-type Si (111) substrates at 300 °C by liquid injection Atomic Layer Deposition (ALD). The results indicated that: (1) more traps were observed compared to the conventional capacitance-voltage characterization method in LaZrOx; (2) the time-dependent trapping/de-trapping was influenced by the edge time, width and peak-to-peak voltage of a gate voltage pulse. Post deposition annealing was performed at 700 °C, 800 °C and 900 °C in N₂ ambient for 15 s to the samples with 200 ALD cycles. The effect of the high temperature annealing on oxide traps and leakage current were subsequently explored. It showed that more traps were generated after annealing with the trap density increasing from 1.41 × 1012 cm-2 for as-deposited sample to 4.55 × 1012 cm-2 for the 800 °C annealed one. In addition, the leakage current density increase from about 10-⁶ A/cm² at Vg = +0.5 V for the as-deposited sample to 10-3 A/cm² at Vg = +0.5 V for the 900 °C annealed one.
| S-EPMC5455481 | biostudies-other
Project description:The steadfast rule of a ferromagnetic hysteresis loop claims its saturation positioned within the first and third quadrants, whereas its saturation positioned in the second and fourth quadrants (named as self-reversed magnetic hysteresis) is usually taken as an experimental artifact and is always intentionally ignored. In this report, a new insight in this unique hysteresis phenomenon and its modulation were discussed in depth. Different iron oxides (magnetite, maghemite and hematite) with varying dimensions were soaked in FeCl3 aqueous solution and absorbed Fe3+ cations due to their negative enough surface zeta potentials. These iron oxides@Fe3+ core-shell products exhibit well pronounced self-reversed magnetic hysteresis which concurrently have typical diamagnetic characteristics and essential ferromagnetic features. The presence of pre-magnetized Fe3+ shell and its negatively magnetic exchange coupling with post-magnetized iron-oxide core is the root cause for the observed phenomena. More strikingly, this self-reversed magnetic hysteresis can be readily modulated by changing the core size or by simply controlling Fe3+ concentration in aqueous solution. It is anticipated that this work will shed new light on the development of spintronics, magnetic recording and other magnetically-relevant fields.
| S-EPMC5318991 | biostudies-literature
Project description:The synthesis of a new solid solution of the oxyhydroxide Ga5-xAlxO7(OH) is investigated via solvothermal reaction between gallium acetylacetonate and aluminum isopropoxide in 1,4-butanediol at 240 °C. A limited compositional range of 0 ? x ? 1.5 is produced, with the hexagonal unit cell parameters refined from powder X-ray diffraction (XRD) showing a linear contraction in unit cell volume with an increase in Al content. Solid-state 27Al and 71Ga nuclear magnetic resonance (NMR) spectroscopies show a strong preference for Ga to occupy the tetrahedral sites and Al to occupy the octahedral sites. Using isopropanol as the solvent, ?-Ga2-xAlxO3 defect spinel solid solutions with x ? 1.8 can be prepared at 240 °C in 24 h. These materials are nanocrystalline, as evidenced by their broad diffraction profiles; however, the refined cubic lattice parameter shows a linear relationship with the Ga:Al content, and solid-state NMR spectroscopy again shows a preference for Al to occupy the octahedral sites. Thermal decomposition of Ga5-xAlxO7(OH) occurs via poorly ordered materials that resemble ?-Ga2-xAlxO3 and ?-Ga2-xAlxO3, but ?-Ga2-xAlxO3 transforms above 750 °C to monoclinic ?-Ga2-xAlxO3 for 0 ? x ? 1.3 and to hexagonal ?-Ga2-xAlxO3 for x = 1.8, with intermediate compositions of 1.3 < x < 1.8 giving mixtures of the ?- and ?-polymorphs. Solid-state NMR spectroscopy shows only the expected octahedral Al for ?-Ga2-xAlxO3, and for ?-Ga2-xAlxO3, the ?1:2 tetrahedral:octahedral Al ratio is in good agreement with the results of Rietveld analysis of the average structures against powder XRD data. Relative energies calculated by periodic density functional theory confirm that there is an ?5.2 kJ mol-1 penalty for tetrahedral rather than octahedral Al in Ga5-xAlxO7(OH), whereas this penalty is much smaller (?2.0 kJ mol-1) for ?-Ga2-xAlxO3, in good qualitative agreement with the experimental NMR spectra.
| S-EPMC7081611 | biostudies-literature
Project description:Recently, it has been shown that under pressure, unexpected and counterintuitive chemical compounds become stable. Laser shock experiments (A. Rode, unpublished) on alumina (Al2O3) have shown non-equilibrium decomposition of alumina with the formation of free Al and a mysterious transparent phase. Inspired by these observations, we have explored the possibility of the formation of new chemical compounds in the system Al-O. Using the variable-composition structure prediction algorithm USPEX, in addition to the well-known Al2O3, we have found two extraordinary compounds Al4O7 and AlO2 to be thermodynamically stable in the pressure ranges 330-443 GPa and above 332 GPa, respectively. Both of these compounds at the same time contain oxide O(2-) and peroxide O2(2-) ions, and both are insulating. Peroxo-groups are responsible for gap states, which significantly reduce the electronic band gap of both Al4O7 and AlO2.
| S-EPMC4381618 | biostudies-other
Project description:We use a recently developed plasma-flow reactor to experimentally investigate the formation of oxide nanoparticles from gas phase metal atoms during oxidation, homogeneous nucleation, condensation, and agglomeration processes. Gas phase uranium, aluminum, and iron atoms were cooled from 5000?K to 1000?K over short-time scales (?t?<?30?ms) at atmospheric pressures in the presence of excess oxygen. In-situ emission spectroscopy is used to measure the variation in monoxide/atomic emission intensity ratios as a function of temperature and oxygen fugacity. Condensed oxide nanoparticles are collected inside the reactor for ex-situ analyses using scanning and transmission electron microscopy (SEM, TEM) to determine their structural compositions and sizes. A chemical kinetics model is also developed to describe the gas phase reactions of iron and aluminum metals. The resulting sizes and forms of the crystalline nanoparticles (FeO-wustite, eta-Al2O3, UO2, and alpha-UO3) depend on the thermodynamic properties, kinetically-limited gas phase chemical reactions, and local redox conditions. This work shows the nucleation and growth of metal oxide particles in rapidly-cooling gas is closely coupled to the kinetically-controlled chemical pathways for vapor-phase oxide formation.
| S-EPMC6041320 | biostudies-literature
Project description:The breaking of time reversal symmetry (TRS) in three-dimensional (3D) topological insulators (TIs), and thus the opening of a 'Dirac-mass gap' in the linearly dispersed Dirac surface state, is a prerequisite for unlocking exotic physical states. Introducing ferromagnetic long-range order by transition metal doping has been shown to break TRS. Here, we present the study of lanthanide (Ln) doped Bi2Te3, where the magnetic doping with high-moment lanthanides promises large energy gaps. Using molecular beam epitaxy, single-crystalline, rhombohedral thin films with Ln concentrations of up to ~35%, substituting on Bi sites, were achieved for Dy, Gd, and Ho doping. Angle-resolved photoemission spectroscopy shows the characteristic Dirac cone for Gd and Ho doping. In contrast, for Dy doping above a critical doping concentration, a gap opening is observed via the decreased spectral intensity at the Dirac point, indicating a topological quantum phase transition persisting up to room-temperature.
| S-EPMC4621505 | biostudies-literature
Project description: Not available
| S-EPMC7808260 | biostudies-literature
Project description:Activation of oxygen redox during the first cycle has been reported as the main trigger of voltage hysteresis during further cycles in high-energy-density Li-rich 3d-transition-metal layered oxides. However, it remains unclear whether hysteresis only occurs due to oxygen redox. Here, it is identified that the voltage hysteresis can highly correlate to cationic reduction during discharge in the Li-rich layered oxide, Li1.2 Ni0.4 Mn0.4 O2 . In this material, the potential region of discharge accompanied by hysteresis is apparently separated from that of discharge unrelated to hysteresis. The quantitative analysis of soft/hard X-ray absorption spectroscopies discloses that hysteresis is associated with an incomplete cationic reduction of Ni during discharge. The galvanostatic intermittent titration technique shows that the inevitable energy consumption caused by hysteresis corresponds to an overpotential of 0.3 V. The results unveil that hysteresis can also be affected by cationic redox in Li-rich layered cathodes, implying that oxygen redox cannot be the only reason for the evolution of voltage hysteresis. Therefore, appropriate control of both cationic and anionic redox of Li-rich layered oxides will allow them to reach their maximum energy density and efficiency.
| S-EPMC9376854 | biostudies-literature
Project description:Transparent conducting oxides exhibit giant optical nonlinearities in the near-infrared window where their linear index approaches zero. Despite the magnitude and speed of these nonlinearities, a "killer" optical application for these compounds has yet to be found. Because of the absorptive nature of the typically used intraband transitions, out-of-plane configurations with short optical paths should be considered. In this direction, we propose an alternative frequency-resolved optical gating scheme for the characterization of ultra-fast optical pulses that exploits near-zero-index aluminium zinc oxide thin films. Besides the technological advantages in terms of manufacturability and cost, our system outperforms commercial modules in key metrics, such as operational bandwidth, sensitivity, and robustness. The performance enhancement comes with the additional benefit of simultaneous self-phase-matched second and third harmonic generation. Because of the fundamental importance of novel methodologies to characterise ultra-fast events, our solution could be of fundamental use for numerous research labs and industries.
| S-EPMC9209551 | biostudies-literature
Project description:Methane oxychlorination (MOC) is a promising reaction for the production of liquefied methane derivatives. Even though catalyst design is still in its early stages, the general trend is that benchmark catalyst materials have a redox-active site, with, e.g., Cu2+, Ce4+, and Pd2+ as prominent showcase examples. However, with the identification of nonreducible LaOCl moiety as an active center for MOC, it was demonstrated that a redox-active couple is not a requirement to establish a high activity. In this work, we show that Mg2+-Al3+-based mixed-metal oxide (MMO) materials are highly active and stable MOC catalysts. The synergistic interaction between Mg2+ and Al3+ could be exploited due to the fact that a homogeneous distribution of the chemical elements was achieved. This interaction was found to be crucial for the unexpectedly high MOC activity, as reference MgO and γ-Al2O3 materials did not show any significant activity. Operando Raman spectroscopy revealed that Mg2+ acted as a chlorine buffer and subsequently as a chlorinating agent for Al3+, which was the active metal center in the methane activation step. The addition of the redox-active Eu3+ to the nonreducible Mg2+-Al3+ MMO catalyst enabled further tuning of the catalytic performance and made the EuMg3Al MMO catalyst one of the most active MOC catalyst materials reported so far. Combined operando Raman/luminescence spectroscopy revealed that the chlorination behavior of Mg2+ and Eu3+ was correlated, suggesting that Mg2+ also acted as a chlorinating agent for Eu3+. These results indicate that both redox activity and synergistic effects between Eu, Mg, and Al are required to obtain high catalytic performance. The importance of elemental synergy and redox properties is expected to be translatable to the oxychlorination of other hydrocarbons, such as light alkanes, due to large similarities in catalytic chemistry.
| S-EPMC10127201 | biostudies-literature